Sulfate adsorption in forest soils is a process of sulfur dynamics playing an important role in plant uptake, cation movement, acid neutralization capacity and so on. The relationship between sulfate adsorption and some physicochemical properties of four forest soils was investigated. Extractable sulfate contents and sulfate adsorption capacity (SAC) in the forest soils varied much among study sites. Extractable sulfate contents were more in sub-surface soils with lower organic matter and greater Al and Fe oxides than in surface soils. The average contents of $Al_d$ and $Fe_d$ in the sub-surface soils were 8.49 and $12.45g\;kg^{-1}$, respectively. Soil pH, cation exchange capacity and clay content were positively correlated with the extractable sulfate contents and SAC. Organic carbon content, however, was negatively correlated with the extractable sulfate contents, implying the competitive adsorption of sulfate with soil organic matter. Considerably significant correlation was found between inorganic + amorphous Al and Fe oxides and the sulfate adsorption, but crystalline Al and other fractions of Fe oxide showed no correlation. Relatively close relationship between the adsorbed sulfates and soil pH, cation exchange capacity, or amorphous Al oxides indicates that the accelerated soil acidification may substantially reduce the potential for sulfate adsorption contributing to sulfur flux in forest ecosystems.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.171.1-171.1
• /
• 2016

재료의 표면 강화 방법 중의 하나인 질화공정을 이용하여 탄소강 S45C 소재의 질화 거동에 대하여 연구하였다. $520^{\circ}C$ 온도에서 질화 공정을 진행하여 공정시간에 따른 Kn값을 수소 센서로 측정하여 공정시간에 따른 N-potential의 변화와 그에 따른 화합물층 성장 및 화합물층의 상변화에 대해 관찰하였다. 화합물 층의 미세구조 변화는 광학현미경 및 주사전자현미경을 통해 관찰하였다. 가스 질화 처리 후 표면경도는 약 600Hv의 경도값이 측정되었고, 공정 시간이 늘어남에 따라 화합물층 및 경화깊이가 증가되고 표면 화합물이 성장하여 porous가 감소하는 것을 확인 할 수 있다. 경화깊이는 1440분 일 때 약 0.5mm 경화 깊이를 얻었고, 화합물층의 성장은 ${\varepsilon}$상(Fe2-3N)과 ${\gamma}$'상(Fe4N)으로 두 개의 상으로 형성되는 것을 관찰할 수 있었다. 시험 결과를 바탕으로 S45C 소재의 탄소 함량에 따른 lehrer diagram을 열역학 적으로 계산하고 화합물층의 형성 기구에 대해 비교 분석하였다.

• Journal of Welding and Joining
• /
• v.6 no.4
• /
• pp.16-26
• /
• 1988

The effect of carbon content on hot cracking of welded carbon steel was investigated Eight steel plates whose carbon content range from 0.02 to 0.23 percent were welded by autogeous gas tungsten are process. Constant strain was applied to the hot crack test specimen under the strain rate of 0.15 mm per second during welding. The hot cracking susceptibility ws high in the rnage of 0.02-0.05 and 0.12-0.23 percent carbon contents. The critical carbon content immune to hot cracking is in the range from 0.07 to 0.12 percent carbon. By electron probe microanalyser, amanganese segregation was not seen significantly in the whole carbon range. But segregation of silicon was higher in the region of low carbon contents. However, sulphur was segregated remarkably in the region betwen 0.18 and 0.23 percent carbon by peritectic reaction. Very smal lamount of dnedritic structure was observed in the region from 0.02 to 0.05 percent carbon by peritectic reaction. Very small amount of dendritic structure was observed in the region from 0.02 to 0.05 percent carbon but the predominant solidification structure was smooth by cellular growth. The higher the carbon content is, the more the columnar dendritic structure was observed.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.86-86
• /
• 2003

주편은 1차 냉각 지역인 수냉 몰드를 통과한 후, 2차 냉각 지역에서 guide roll, pinch roll 그리고 driven roll등에 의해 반복적인 압축하중을 받고 있으며, roll과 roll사이에서는 철정압에 의한 주편 bulging 현상이 발생하고 주편의 표면은 인장응력을 받게 된다. 특히 연속주조 중 주편의 변형기구가 단순 탄소성 변형 이 아닌 creep에 의한 변형임을 고려할 때, 2차 냉각 지역에서 주편의 표면은 전술한 압축 및 인장변형 이 반복되는 저주기 고온 피로 환경을 거침을 알 수 있다. 본 연구에서는 탄소함량에 따른 주편의 bulging시의 크랙 발생에 미치는 저주기 고온 피로의 효과를 조사하였다. 또한, 용체화 처리 온도에서 시험 온도까지의 냉각 속도의 영향을 조사하기 위하여 1$^{\circ}C$/s 및 1$0^{\circ}C$/s로 냉각 속도를 변화시켜 열간 연성 곡선을 작성하였다. 본 연구에서 얻어진 결과는 다음과 같다. 저탄소강의 경우는 저주기 피로의 영향이 관찰되지 않았으며, 중탄소강의 경우, 저온에서는 저주기 피로로 인해 열간 연성이 증가하였으나, 고온에서는 변형유기 페라이트의 생성으로 인해 열간 연성 이 감소하였다. 고탄소강의 경우는 저주기 피로로 인하여 열간 연성이 모든 온도 구간에서 증가하였다. 또한 용체화 처리후 시험 온도까지의 냉각 속도가 감소함에 따라 열간 연성이 증가하였는데, 이는 입 계 석출물의 조대화로 인해 열간 연성이 증가하는 것으로 판단된다.

• Proceedings of the KAIS Fall Conference
• /
• 2012.05a
• /
• pp.33-35
• /
• 2012

본 연구에서는 전이금속 Cu, Mn이 함침된 제올라이트를 사용하여 일산화탄소의 흡착능을 연구하였다. 금속 복합 산화물촉매 제조는 Cu, Mn을 서로 다른 비율로 물리 혼합하여 지지체에 담지하였다. 제올라이트 분자체는 상용 13X를 사용하였다. 함침방법은 과잉용액 함침법을 사용하였고, 건조 후 소성 하여 산화물 형태로 담지하였다. 합성된 개질 흡착제의 표면특성 분석은 $N_2$흡착 및 탈착곡선을 통한 질소흡착 특성 분석으로 기공크기, 기공분포, 비표면적을 구하였으며, FT-IR, X-선 회절분석, 전자주사현미경, $NH_3$-TPD/TPR 으로 특성을 분석하였다. 흡착 실험은 고정층 반응기에서 수행하였으며, 내경 4 mm 석영관에 흡착제를 충진하고 흡착파과곡선을 Gas Chromatograph로 측정하여 Cu-Mn 제올라이트 촉매의 일산화탄소 흡착 성능을 연구하였다. Cu-Mn 함량 비율과 흡착조업조건에 따른 흡착능을 측정하여 최적 흡착조건을 구하였다.

• Applied Chemistry for Engineering
• /
• v.24 no.4
• /
• pp.412-415
• /
• 2013

Palladium on carbon powder was prepared using 1-hexyl-3-methylimidazolium tetrafluoroborate, one of room temperature ionic liquids. The synthesized particles were tested as a hexafluoropropylene hydrogenation catalyst. Moreover, the hydrogenation was performed under various reaction conditions to develop an optimum reaction process. The catalyst prepared by more than 3 wt% of palladium and the unity mole ratio of ionic liquid to palladium precursor showed higher catalytic activity. For reaction conditions, the complete hexafluoropropylene (HFP) conversion was achieved at these conditions; the volume flow ratio of hydrogen to HFP was higher than 1.25 and $GHSV_{HFP}$ was lower than 50000 mL/g-h.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.289-289
• /
• 2010

나노섬유는 지름이 수십에서 수백 나노미터(1나노미터=10억분의1m)에 불과한 초극세 물질로 비표면적이 매우 크고[1], 제작이 간편하여, 사용되어지는 고분자의 종류에 따라 에너지 환경 의료 관련 분야에서 전극소재 필터재 피복재 인공 피부등 다양한 분야에서의 활용이 가능하여 전 세계적으로 연구개발이 활발하게 이루어지고 있다. 그러나 그 자체만으로 응용하기에는 그 기계적 전기적 특성의 한계 때문에 응용의 다양성에 제약을 받고 있다. 그러나 그 자체만으로 응용하기에는 그 기계적 열적 전기적 특성을 가진 탄소나노튜브를 첨가한 복합나노섬유에 의해 그 응용영역의 한계를 넓혀가고 있다.[2] 본 연구에서는 전도성 고분자인 polymethyl methacrylate (PMMA)에 multi-walled carbon nanotubes (MWCNTs)를 첨가한 복합나노섬유를 전기방사법(electrospinning method)을 통해서 제조하였다. [2~3] CNTs 첨가농도에 따른 제조된 복합나노섬유의 형상변화와 섬유내의 CNTs 배열상태를 각각 주사전자 현미경(scanning electron microscope: SEM)과 투과전자현미경(transmission electron microscope: TEM)을 이용하여 관찰하였다. 또한, 복합나노섬유의 광학 특성 변화를 CNTs 첨가농도에 따라서 FT-IR과 Raman spectroscopy등을 이용하여 조사하였으며, 나노섬유의 tensile strength의 측정을 통해 CNTs 함량에 따른 기계적 특성 변화를 분석하였다.

• Proceedings of the Korean Society of Applied Pharmacology
• /
• 1995.04a
• /
• pp.112-112
• /
• 1995

간장 손상시에는 여러 혈청의 효소 활성과 함께 혈청 $\beta$-glucuronidase의 활성도 증가한다는 것이 보고되었으나 심한 간부전이나 간암의 경우 이들의 활성은 오히려 정상치보다 감소하는 것으로 나타났다. Silymarin은 간장 보호효과로 이미 임상에 널리 사용되고 있는 약물로서 김 등에 의해 silymarin이 장내세균의 $\beta$-glucuronidase와 간장의 $\beta$-glucuronidase의 활성을 억제한다는 것이 보고되었다. 이에 연자 둥은 $\beta$-glucuronidase의 저해 효과가 관찰된 영지버섯온 유기용매로 분획하여 간장 보호효과를 검색하였다. 영지버섯의 70% MeOH 추출물(GT)과 그 ether 분획(GE)에 대해 생쥐 1군을 6마리로 하여 20% $CCl_4$0.1$m\ell$/10g(olive oil로 희석)을 경구투여 하였다. 검액 GE는 50mg/kg과 250mg/kg, GT는 100mg/kg과 500mg/kg을 각각 사염화탄소 투여 30분 전에 경구투여 하였으며 사염화탄소를 투여하고 24시간 후에 심장 채혈하고 혈청을 분리하여 혈청성분 및 혈청효소의 활성을 측정하였다. 대조군에는 생리식염수를 투여하였고 양성 비교약물로는 silymarln 100mg/kg을 경구투여 하여 비교 관찰하였다. 실험 결과, 영지버섯의 ether 분획에서는 혈청중 GOT, GPT의 활성과 triglyceride의 함량에 대해 silymarin보다 우수한 효과를 보였으며, 70% MeOH 추출물은 silymarin에 미치지 못했다.

• Proceedings of the Korean Society for Food Science of Animal Resources Conference
• /
• 2005.10a
• /
• pp.172-176
• /
• 2005

본 연구의 목적은 냉동 저장 시 돈육의 부위, 포장방법 및 저장기간이 지방산패에 미치는 영향을 측정하기 위하여 실시하였다. pH는 고지방인 삼겹이 저지방인 등심보다 높은 값을 나타냈다(P<0.05). TBARS 값은 저장기간과 포장방법에 의한 차이는 나타나지 않았으나(P>0.05) 저장 후반부로 갈수록 고지방인 삼겹이 저지방인 등심보다 높게 나타났다. (P<0.05). 유리지방산가는 TBARS 값과 반대로 오히려 저지방인 등심이 고지방인 삼겹보다 높게 나타났다(P<0.05). 과산화물가는 저장기간이 증가함에 따라 값이 증가하였다(P<0.05). 미생물 변화는 저장기간, 포장방법, 지방함량에 따른 뚜렷한 차이는 나타나지 않았다. (P>0.05). 추출된 휘발성 화합물들은 저장기간에 따른 변화가 미미하였고 포장방법에 따른 효과는 나타나지 않았으나 (P>0.05) 탄소수 10개 미만인 2,4-dimethyl-1-heptene, hexanal 그리고 4-methyl-2-hexanone은 저지방인 등심보다 고지방인 삼겹에서 더 많이 검출되었으며, 이와는 반대로 탄소수 10개 이상인 고분자 화합물들은 고지방인 삼겹보다는 오히려 저지방인 등심에서 많이 검출되었다(P< 0.05). 상관관계를 조사한 결과 삼겹에서 유리지방산가와 4-methyl-2-hexanone, 등심에서 유리지방산가와 9-octadecenal을 제외하고는 별다른 유의성이 존재하지 않았다. 이러한 결과는 식육의 냉동보관은 식육내 존재하는 지방의 산화와 미생물 성장을 억제하여 미생물, 효소 그리고 자동산화로 인해 발생되는 여러 가지 2차 생성물의 생성을 저해하는 것으로 판단된다.

• Tribology and Lubricants
• /
• v.24 no.5
• /
• pp.269-274
• /
• 2008

Carbon nanotube composite is considered to be a good candidate material for composite material because of its excellent mechanical property and low density under high temperature as well as good wear and frictional properties. In this study, tribological characteristics of carbon nanotube aluminum composite were evaluated using pin-on-disk wear tester. Spark Plasma Sintering method is more effective than Hot Pressing method in terms of wear and friction. The composite with 1% CNT has the lowest friction and wear characteristic.