• Journal of the Korea Concrete Institute
• /
• v.18 no.4 s.94
• /
• pp.553-558
• /
• 2006

In this study, fluorine-silicate hybrid type crack reducing agent(FS) consisted of fluorine and silicate compounds applied to concrete mix(specification : 25-30-18) between 0.5% and 2.0% at intervals of 0.5% based on cement weight. Experiments for material properties of concrete such as slump, air content and bleeding with elapsed time were performed. Experiment and elucidation for shrinkage crack resistance as well as adiabatic hydration temperature were also carried out. It was appeared that FS addition contributed to lower bleeding and hydration temperature without disturbance of fresh properties of concrete such as slump and air content compared to non-added concrete. Especially, shrinkage crack resistance of concrete resulted from plastic and drying shrinkage could be effectively reduced by the addition of FS ranging from 1.0% to 1.5%.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.4
• /
• pp.359-365
• /
• 2017

This study examined concrete characteristics depending on the replacement ratio of recycled fine aggregates, which suits the KS F 2573 concrete recycled aggregate standard. As physical properties, slump, air content, changes in the elapse of time and compressive strength were studied in order to provide basic data for activation of recycled fine aggregate recycling. As a result of experimenting recycled fine aggregate concrete, the increase in the replacement ratio of recycled aggregates led to the increase in slump and air content. Also, when the replacement ratio of recycled fine aggregates was 30%, it was judged that there was no problem with constructability. When the replacement ratio was 30%, recycled fine aggregate concrete had a similar tendency to natural aggregate concrete at a compressive strength of 24MPa. When the replacement ratio was 30%, at a target strength of 24MPa, recycled fine aggregate concrete had the same physical characteristics as natural aggregate concrete. This means that a replacement ratio of 30% is appropriate for replacement of recycled fine aggregates. In future, there will be a need to improve the quality of recycled fine aggregates for activating the use of recycled fine aggregates and further research will have to evaluate physical properties of recycled fine aggregate concrete using improved recycled fine aggregates.

• Magazine of the Korea Concrete Institute
• /
• v.5 no.1
• /
• pp.165-173
• /
• 1993

본 연구는 고강도 콘크리트 실용화의 일환으로 국내에서 시판되고 있는 고성능 감수제의 품질성능을 평가하기 위한 것이다. 이러한 연구를 위하여 8종류의 고성능 감수제를 대상으로 첨가량에 따른 특성을 비교하였다. 또한 경시변화에 따른 특성을 비교, 분석하기 위하여 슬럼프, 공기량 그리고 압축강도비를 측정하였다. 이 때 고성능 감수제의 품질성능 평가 규준는 JASS 5T-402 규준에 따라 실시하였다. 실험결과 국내에서 시판되는 고성능 감수제는 공기량, 앞축강도비에 대해서는 모두 만족하였지만 슬럼프 경시 저하량은 DA를 제외한 모든 고성능 감수제가 규준치를 초과하였다. 따라서 현장에서 고강도콘크리트를 생산할 경우 배합방법이나 첨가방법을 개선하여 시공성을 확보하는 방안이 필요할 것이다.

• 어항어장
• /
• s.18
• /
• pp.69-77
• /
• 1992

고강도 콘크리트의 실용화 일환으로 설계기준강도 500kg/cm$^2$ 이상인 고강도 콘크리트의 현장 B/P 생산과 실대구조물의 시공성 및 강도, 온도 특성에 관한 연구를 수행하였다. 이러한 연구를 위해 현장 최적배합비 선정과 레미콘 운반시간에 따른 경시변화 시험을 수행하였고 실대구조물의 코아강도 및 콘크리트 내부온도를 측정하였다. 일반 현장재료와 장비의 사용으로도 고강도 콘크리트의 생산과 시공성을 확보할 수 있었으며 실대구조물의 코아강도가 500kg/cm$^2$ 이상을 나타냄으로써 고강도 콘크리트의 실용화에 대한 가능성을 확인할 수 있었다.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.989-992
• /
• 2008

In this paper, we are presenting a case that integrates ultra high strength concrete(150MPa) with surface-exposed concrete. Ahead of the field application, we carried out laboratory experiment and B/P Test for a basic property of concrete(slump flow, air content, 50cm flow time, elapse time change and compression strength) and productivity. The next, we conducted Mock-up Test using simulation specimen to evaluate infilling, surface-finishing and hydration heat of concrete. We had satisfactory results for a basic property and hydration heat of concrete. However at the time of field application, it was occurred rupture of formwork because of high lateral pressure of concrete, and then formwork was reinforced and case-in-place time was adjusted. And regardless of low and high frequency vibration, it occurred to surface-pockmark. In case that applies ultra high strength concrete to surface-exposed concrete, we estimate that it is important of systematic management and improvement of construction.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.04a
• /
• pp.487-492
• /
• 1999

The purpose of this study to find the mixture of concrete for Top-Down method. Throughout test of elapsed time change and L-type flow, it was proposed basic performance and level of top-down method concrete. When change as to elapsed time is considered, so series of F10 added 10% S.P satisfied slump and demanded flow (60$\pm$5cm), and L-type slump, L-type flow satisfied liquidity, it can be considered basic mixture of designed actual frame later.

• Magazine of the Korea Concrete Institute
• /
• v.3 no.2
• /
• pp.97-104
• /
• 1991

고강도 콘크리트의 관용화일환으로 500㎏/㎠ 이상인 고강도 콘크리트의 현장 B/Ptodtks과 실대구조물의 시공성 및 강도, 온도 특성에 관한 연구를 위해 현장 체적백합비 선정과 레미콘 운반시간에 따른 경시변화 시험을 이행하였고 실대구조물의 코아강도 및 콘크리트를 내부온도를 측정하였다. 일반 현장재료와 장비의 사용으로도 고강도 콘크리트의 생산과 시공성을 확보할 수 있었으며 실대구조물의 코아강도가 500㎏/㎠ 이상을 나타내므로써 나타내므로써 고강도 콘크리트의 실용화에 대한 가능성을 확인할 수 있었다.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2019.05a
• /
• pp.195-196
• /
• 2019

The temperature and relative humidity in concrete change with the passage of time depending on factors such as compressive strength. They are also different depending upon internal depth of concrete. In this study, we have measured the change of the temperature and relative humidity in the concrete for two years to act as the parameters to evaluate the concrete durability and effective maintenance.

• Magazine of the Korea Concrete Institute
• /
• v.3 no.4
• /
• pp.125-132
• /
• 1991

$\beta$-NSF 계통의 콘크리트용 고성능감수계를 독자적으로 제조하여(제품C)국내에서 유통되고 있는 $\beta$-NSF계 고성능감수제들과 콘크리트의 유동화특성 및 고강도콘크리트의 특성을 비교검토한 결과는 다음과 같다. 가. $\beta$-NSF계 고성능감수제중에서 M제품과 C제품의 유동화성능 및 고강도성능이 다른 감수제에 비하여 전반적으로 좋게 나타났다. 나. $\beta$-NSF계 고성능감수제를 첨가한 모든 콘크리트는 감수제를 사용하지 않은 일반 콘크리트에 비하여 흐름도의 경시변화가 크며, 동결융해에 대한 저항성이 현저히 떨어지는 것으로 나타났다.

• Proceedings of the Computational Structural Engineering Institute Conference
• /
• 2010.04a
• /
• pp.762-765
• /
• 2010

본 연구에서는 원전격납구조물과 같이 고품질을 요하는 콘크리트의 내구성설계 및 관리에 필요한 구조물 건전성 평가시스템 구축의 일환으로 콘크리트 미세공극구조 형성 예측 프로그램을 개발하였다. 개발된 미세공극구조 형성 예측 프로그램은 콘크리트의 강도 등과 같은 역학적 특성 및 유해이온 확산거동 예측에 활용되는 부분으로서 기존의 연구결과로부터 개발된 모델식들을 바탕으로 개발되었다. 개발된 프로그램은 콘크리트 시험체로부터 구하여진 MIP 실험결과와 비교해 보았으며, 상관성을 검토하였다.