• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.320-323
• /
• 2004

This work investigated fatigue characteristics of aluminum repaired by CFRP composites. Three specimens, cracked aluminum, cracked aluminum patched by CFRP, and plasma-treated aluminum patched by CFRP were used for the fatigue tests. The results showed that the fatigue crack growth behavior of cracked aluminum was improved by repairing the cracked area with composite patch. Specifically, the specimen repaired by composite patch showed about three times more fatigue life than the cracked aluminum. The plasma-treated aluminum repaired by composite patch showed about five times more fatigue life than the cracked aluminum.

• Journal of the Korean Society of Safety
• /
• v.19 no.4 s.68
• /
• pp.31-35
• /
• 2004

The A17075/CFRP multi-layered hybrid laminate material consists of the alternating A17075-T6 sheets and carbon/epoxy prepregs of M40 fade. The influence of volume fraction and fiber orientation of A17075/CFRP layer on flexural properties of A17075/CFRP laminate alternating A17075-T6 and carbon/epoxy prepreg was investigated. The results obtained from the experimental analysis are as follows: 1. In the $0^{\circ}$ fiber orientation, the mont of increase of the flexural rigidity was $20.5\%$ at the $26.5\%$ volume fraction and $38.0\%\;at\;the\;35.7\%$ volume fraction compared with the flexural rigidity level(20.0GPa) of the $10\%$ volume fraction of CFRP. 2. In the $\pm45^{\circ}$ fiber orientation the amount of decrease of the flexural rigidity was $23.5\%\;at\;the\;20.0\%$ volume fraction and $31.5\%\;at\;the\;33.3\%$ volume fraction compared with the flexural rigidity level of the $10\%$ volume fraction of CFRP. 3. In the $0^{\circ}$ fiber orientation, the flexural strength was 481.5MPa at the $10\%$ volume fraction of CFRP and 583.8MPa at the $26.5\%$ volume fraction and 653.7MPa at the $35.7\%$ volume faction. 4. In the $\pm45^{\circ}$ fiber orientation, the flexural strength was 354.0MPa at the $20.0\%$ volume fraction of CFRP and 340.5MPa at the $33.3\%$ volume fraction.

• Polymer(Korea)
• /
• v.24 no.6
• /
• pp.845-853
• /
• 2000

The optimum cure cycle and carbonization condition were selected by the DSC and TGA analysis and green bodies were prepared by the method of hot press molding and then carbonized up to 140$0^{\circ}C$. Additives such as graphite powder, carbon black, milled carbon fiber and carbon fiber mat, which were considered to be effective in improving the interlaminar shear strength, were also added to check their effects on the density and porosity of products. Then, their relations with mechanical properties such as ILSS and flexural strength were investigated. The composites added 9 vol% of graphite powder showed the greatest values of ILSS and flexural strength. Otherwise, in case of adding carbon black, the composites showed the slight improvement of ILSS at its contents of 3 vol% but the flexural strength was decreased. When milled carbon fiber and carbon fiber mat were added, the lack of resin and the heat shrinkage during the carbonization caused the delamination, resulting in decreasing the density, ILSS and flexural strength.

• Journal of Digital Contents Society
• /
• v.18 no.6
• /
• pp.1199-1205
• /
• 2017

Global energy consumption is rapidly increasing yearly due to drastic industrial advances, requiring the development of new energy storage devices. For this reason, supercapacitors with fast charge-discharge, long life cycle and high power density is getting attention, and have been considered as one of the potential energy storage systems. In this research, we developed a supercapacitor that consists of amorphous manganese oxide($MnO_2$) electrodes deposited onto carbon cloth substrates using the hydrothermal method. The Fe-doped amorphous $MnO_2$ samples were characterized by X-ray diffraction(XRD), Energy Dispersive X-ray spectroscopy(EDX), as well as scanning electron microscopy(SEM). The electrochemical analysis of the prepared samples were performed using cyclic voltammetry and galvanostatic charge-discharge measurements in 1M $Na_2SO_4$ electrolyte. The test results demonstrate that the supercapacitor based on the Fe-doped amorphous $MnO_2$ electrodes has a specific capacitance as high as 163F/g at 1A/g current density, and good cycling stability of 87.34% capacitance retention up to 1000 cycles.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.22 no.1
• /
• pp.801-807
• /
• 2021

In various industrial fields and infrastructure based on electronic components, such as communication equipment, transportation, computer networks, and military equipment, the need for electromagnetic pulse shielding has increased. Two methods for applying electromagnetic pulse shielding are effective. The first is construction using shielding materials, such as shielding concrete, shielding doors, and shielding windows. The other is coating shielding paints on non-shielding structures. Electromagnetic pulse shielding paints are made using conductive materials, such as carbon nanotubes, graphite, carbon black, and carbon fiber. In this paint, electromagnetic pulse shielding performance is added to the commonly used water-based paint. In this study, the shielding effectiveness and bonding performance of paints using conductive graphite and carbon black as shielding materials were evaluated to develop electromagnetic pulse shielding inorganic paints. The shielding effectiveness and bonding performance were evaluated by applying six mixtures composed of different kinds and amounts of shielding material. The mixture of conductive graphite and carbon black at a weight ratio of 1:0.2 was the most effective in shielding as 33.6 dB. Furthermore, the mixture produced using conductive graphite only showed the highest bonding performance of 1.06 MPa.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.23 no.4
• /
• pp.180-188
• /
• 2013

The glass of E-glass fiber composition was fabricated by using refused coal ore which is obtained as by-product from Dogye coal mine in Samcheok. We used silica-alumina refused coal ore which has low carbon content relatively, and the amount of refused coal ore has been changed from 0 to 35 % in batch composition. E-glass was fabricated by the melting of mixed batch materials at $1550^{\circ}C$ for 2 hrs with different refused coal ore composition of 0~35 %. We obtained a transparent and clear glass with high visible light transmittance value of 81~84%, thermal expansion coefficient of $5.39{\sim}5.61{\times}10^{-6}/^{\circ}C$ and softening point of $851{\sim}860^{\circ}C$. The glass fiber samples were also obtained through fiberizing equipment at $1150^{\circ}C$, and tested chemical resistance and tensile strength to evaluate the mechanical property as a reinforced glass fiber of composite material. As the result, we identified the properties of E-glass fiber by using refused coal ore are plenty good enough compare to that of normal E-glass without refused coal ore, and confirmed the possibility of refused coal ore as for the raw material of E-glass fiber.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.06a
• /
• pp.680-685
• /
• 2005

Multi-walled carbon nanotubes were purified by using the nitric acid after the mechanical cutting, which carboxylic group might be introduced into the surface of nanotubes. To enhance the dispersion of CNTs, carboxylic groups were substituted in the reaction with octadecyl amine containing a long alkyl group. Nanofibers were manufactured by electrospinning, the solution that mixed with PMMA and ODA-fuctionalized CNTs in dimethyl formamide and dispersed with ultrasonication. Diameter and alignment of nanofibers with various electrospinning parameters, such as the CNT and PMMA concentration in solution, the applied voltage, and the distance to the collector were investigated. As a result, the nanofiber diameter was increased with the increment of PMMA concentration, whereas it was reduced as the applied voltage and the spinning distance was increased. The spinning area became smaller with the distance. The nanofibers were formed without the defect on surface and well aligned in a specific concentration of PMMA and nanotubes.

• Journal of the Korean Applied Science and Technology
• /
• v.32 no.3
• /
• pp.405-411
• /
• 2015

Carbon composites for flexible fiber heating element were examined to improve the electrical conductivity in this study. Carbon composites using carbon black, denka black, super-c, super-p with/without CNF or dispersant such as BCS03 and Sikament-nn were prepared. Carbon composite slurry was coated on plane film and yarns(cotton, polyester) and the performances of prepared heating materials were investigated by checking electrical surface resistance, adhesion strength. The plane heating element using carbon black under natural drying condition($25^{\circ}C$) had better physical properties such as surface resistance(185.3 Ohm/sq) and adhesion strength(above 90%) than those of other carbon composite heating elements. From these results, polyester heating element coated by carbon black showed better electrical line resistance(33.2 kOhm/cm) than cotton heating element. Then, it was found that polyester heating element coated by carbon black with CNF(3 wt%) and BCS03(1 wt%) appeared best properties(0.604 kOhm/cm).

• Composites Research
• /
• v.17 no.3
• /
• pp.38-44
• /
• 2004

The electromagnetic interference (EMI) shielding is very essential for commercial and military purposes. We fabricated multi-walled carbon nanotube (MWNT)/epoxy composites and studied the electromagnetic characteristics of the composites before we study the characteristics of MWNT-added glass fiber-reinforced composites. After setting up the fabrication process, we measured the permittivity of MWNT/epoxy composites with process variables and MWNT concentrations in X-band (8.2GHz~12.4GHz). We also observed re-aggregation phenomenon of MWNTs and investigated its effect on the permittivity. The permittivity of the composites was influenced by the degree of dispersion of MWNTs and increased almost linearly as MWNT concentration increases.

• Composites Research
• /
• v.12 no.3
• /
• pp.1-7
• /
• 1999

New hybrid composite material CPAL(Carbon Patched ALuminum alloy), an Al2024-T3 plate doubleside reinforced with carbon/epoxy laminates were made. Fatigue crack growth tests were carried out at R=0.2, 0.5 in the CPAL specimens. The retardation mechanism and behavior of fatigue crack growth were examined basing on investigation of the crack and the delamination using a X-Ray and a ultrasonic C-Scan. The fatigue crack growth rates of CPAL specimens were remarkedly retarded compared to that of the Al2024-T3 specimen. The retardations amounts of the fatigue crack growth rates get higher in $0^{\circ}$/$90^{\circ}$ CPAL specimen than in $\pm$$45^{\circ}$ CPAL specimen, and get higher at R=0.2 than at R=0.5. The retardation of fatigue crack growth rates in CPAL specimen was generated by the crack bridging mechanism, that is the behavior that the fibers in CFRP layers decrease the COD in the Al2024-T3 plate.