• Journal of the Korea Concrete Institute
• /
• v.29 no.1
• /
• pp.11-21
• /
• 2017

The paper presents experimental results of self-healing effects of OPC-GGBFS paste with cracked and uncracked specimens. The self-healing of cracked specimens is processes of crack closing with re-hydration of unhydrated in crack surface. The OPC paste with GGBFS replacement ratios of 0%, 10%, 20% and 30% were prepared having a constant water-binder ratios of 0.5. The OPC-GGBFS paste specimens immersed in tap-water and sea-water. The temperature of tap and sea-water was $5^{\circ}C$, $15^{\circ}C$ and $25^{\circ}C$. The cracked specimens after deterioration were immersed for 60 days. The relationship between self-healing effect and age-effect was calculate based upon the experimental results. The self-healing effect was measured in ultrasonic pulse velocity (UPV) before and after loading. When the relative change rate of UPV is increases with the increase in GGBFS replacement ratios. Moreover, the self-healing effect is increased with the temperature of tap-water is increase. But the cracked specimens immersed in sea-water was unclear effects of different temperature. Furemore, most of the healing for OPC-GGBFS specimens immersed in tap-water and sea-water occurred during the first 30 days. The self-healing effect until 30 days is higher than that the age-effect. After 30 days, self-effect and age-effect was largely decreases. SEM/EDS analysis of crack on the surface of the specimens in tap-water were covered with aragonite, and sea-water were covered with brucite.

• Korean Journal of Materials Research
• /
• v.6 no.11
• /
• pp.1074-1081
• /
• 1996

Mg-8Li-4AI 합금의 부식특성에 미치는 Y의영향을 전기화학적 분극시험 및 침지시험을 통하여 조사하였다. 전기 화학적 분극시험에서는 Y첨가량이 증가함에 따라 활성화 영역이 감소하엿고 부식전위가 증가하였으며, Y이 4.08wt% 첨가된 경우가 Y이 첨가되지 않은 경우에 비해 부식속도가 크게 감소하였다. 침지시험에서도 Y의 첨가량이 증가함에 따라 Y을 첨가하지 않은 시편에 비하여 무게감량 및 부시속도가 감소하였으며, Y이 첨가되지 않은 합금의 부식속도는 침지시간에 따라 급격히 증가하였지만 Y이 첨가되지 않은 합금의 부식속도는 침지시간에 따라 급격히 증가하였지만 Y이 4.8wt% 첨가된 합금은 96시간 이후부터 더 이상 증가하지 않았다. 이러한 결과는 Y 화합물(Mg24Y5)이 $\alpha$/$\beta$계면에서 희생 양극으로 작용하였기 때문이라고 생각된다. 따라서 Y의 첨가는 Mg-Li-AI 합금의 내식성을 향상시키는 역할을 한 것으로 판단된다.

• Journal of fish pathology
• /
• v.23 no.2
• /
• pp.199-209
• /
• 2010

This study was aimed to investigate the effects in different immersion doses of garlic, Allium sativum, juice to modulate on the nonspecific immune responses of the olive flounder, Paralichthys olivaceus, artificially prechallenged with Streptococcus iniae BS10 and Edwardsiella tarda KE-1, respectively. The nonspecific immune responses of the tested fish were assessed in term of skin mucus lysozyme activity, the change of bacterial cell counts in organs, the number of lymphocytes and neutrophils in blood, and SOD activity. Almost groups of the prechallenged with either S. iniae BS10 or E. tarda KE-1 fish which had been immersed in garlic juice showed the enhanced skin mucus lysozyme activity, the number of lymphocytes and neutrophils in blood, and SOD activity in the kidney but the decreased the number of bacterial cell in surveyed organs. RPS in the group immersed in 0.25 g/L of garlic juice was much higher than in other immersed test groups. These results suggested that the garlic juice immersion can be effective on enhancement of the nonspecific immune responses and the protective ability of olive flounder to the artificial challenge with S. iniae BS10 and E. tarda KE-1.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.29 no.4A
• /
• pp.365-371
• /
• 2009

It is time-consuming to estimate chloride diffusivity of concrete by concentration difference test. For the reason chloride diffusivity of concrete is mainly tested by electrically accelerated method, which is accelerating the movement of chloride ion by potential difference. In this study, portland cement concrete and concrete containing with ground granulated blast-furnace slag (40 and 60% of cement by weight) with water-cementitious material ratio 40, 45, 50 and 60% were manufactured. To compare with chloride diffusivity calculated from the electrically accelerated test and immersed test in artifical seawater, chloride diffusivity tests were conducted. From the results of regression analysis, regression equation between accelerated chloride diffusivity and immersed chloride diffusivity was linear function. And the determinant coefficient was 0.96 for linear equation.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.6
• /
• pp.10-19
• /
• 2016

The objective of this study is to investigate the self-healing properties of ternary blended cement(TBC) paste made with OPC, GGBFS and FA. The influence of OPC-GGBFS-FA on the self-healing ability of ternary blended cement paste was researched by ultrasonic pulse velocity(UPV) measurement. The TBC paste with GGBFS-FA replacement ratios of 20%, 40% and 60% were prepared having a constant water-cementitious materials ratios os 0.5. The research focuses on behavior after 28days(after loading). Four-point bending tests are used to pre-cracked the prismatic specimens at 28days. For specimens (uncracked and cracked) submerged in tap-water and sea-water until 60days. According to the experimental results, the TBC paste system has self-healing ability increased when the fraction of GGBFS increased. Because GGBFS and FA continues to hydrate after 28days, it is likely that hydrated products from GGBFS and FA may modify microstructures, seal these cracks. From these results, it is clear that the crack in all samples experience self-healing and that this occurs mostly in the first 30days of submerging. Futhermore, most of the healing for both specimens of submerged in sea-water and tap-water occurred during the first 30days. Sea-water submerged specimens healed cracks as fast as those in tap-water. Differences in healing effects of submerged in sea-water and tap-water may be attributed to the presence of specific sea-water ions. Therefore, self-healing effects considered age-effects was more strong effect occurred mostly in the first 30days, and then gradually weaken.

• Proceedings of the Korea Society of Poultry Science Conference
• /
• 2002.11a
• /
• pp.126-127
• /
• 2002

본 시험은 게르마늄 침지수 및 사료 첨가급여가 육용오리의 생산능력에 미치는 영향을 구명하기 위하여 1~10 일령에 자연수 또는 게르마늄 침지수를 공급하는 2개 요인에 각각 10~42일령 사료에 게르마늄을 0.0, 0.5 및 1.0% 첨가하는 3개 수준을 조합한 6개 처리에 180수의 육용오리를 2$\times$3요인 배치하여 42일간 사양시험을 실시한 결과는 다음과 같다. 42일령 체중과 1~42일령간의 증체량은 1~10일령 간의 게르마늄 침지수 공급으로 향상되지 않았으며, 10일령 이후 사료의 게르마늄 첨가수준이 1.0%까지 증가함에 따라 점차 증가되는 경향이었으나, 통계적인 유의성은 없었다. 42일령까지의 전 기간 평균 사료요구율도 1~10일령간의 게르마늄 침지수 공급으로 향상되지 않았으며, 10일령 이후 사료에 게르마늄을 0.5% 첨가하였을 때 가장 우수하였으나, 역시 처리간에 유의적인 차이는 인정되지 않았다. 42일간의 사육기간 중 폐사율은 전반적으로 낮았고 처리간에 유의적인 차이가 없었으며, 42일령의 도체율은 사료의 게르마늄 첨가수준이 증가할수록 증가하는 경향을 보였으나 역시 유의적인 차이는 없었다.

• Proceedings of the KIEE Conference
• /
• 2006.07a
• /
• pp.492-493
• /
• 2006

송전 철탑의 도장 도료의 성능 평가는 부착강도시험, 염수분무시험, 내후성시험을 실시하고 있으며, 본 연구에서는 새로운 도장성능 방법인 교류임피던스를 측정하여 철탑 도장 도료의 특성을 평가하였다. 그 결과 우레탄계 2회 도장은 침지 초기와 침지 6일 후 임피던스가 $10^{10}[{\Omega}]$으로 양호한 특성을 보였지만 새롭게 개발된 실록산계 1회 도장은 6일 침지 후 $10^7[{\Omega}]$으로 낮아서 부식방식용 도장 도료로써의 특성은 낮았다. 따라서 철탑 도장 도료는 2회 도장을 실시하는 것이 타당한 것으로 사료된다.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.36 no.8
• /
• pp.889-895
• /
• 2012

Carbon fiber reinforced plastic (CFRP) composites have high specific stiffness and high specific strength. Therefore, they are increasingly being use, instead of conventional metallic materials in the aviation and automobile industries, where there is a strong demand for lightweight materials. In aircraft, the fuselage is exposed to severe conditions of high temperatures and high humidity. Therefore, it is necessary to estimate the strength of CFRP composites under real conditions from the viewpoint of aircraft safety. In this study, CFRP specimens were immersed in distilled water at $75^{\circ}C$ for a long time. Then, tensile tests were performed on these specimens, and the fracture characteristics of the fractured surfaces were analyzed using SEM. A fatigue test was performed on specimens immersed for 300 days with R=0.1, and it was confirmed that the fatigue life deteriorated in immersed specimens compared to specimens that were not immersed.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1995.05a
• /
• pp.784-789
• /
• 1995

핵융합로 제1벽재로서 주목받고 있는 저방사화 Fe-Cr-Mn-W계 오스테나이트 스테인리스강에 소량의 V을 첨가하고 그 기본 조성에 시그마상의 생성억제와 합금의 고온강도 향상에 효과가 있는 질소함량을 변화시켜 전보에서 보고한 소둔열처리의 영향에 이어 미세 조직 특성 및 부식 저항성에 미치는 시효열처리의 영향을 살펴보았다. 부식저항성 평가를 위해서는 양극분극시험, 침지시험 수소취성 시험을 행하였으며, 석출상의 생성양상을 살펴보기 위해서는 광학현미경 관찰, 자성측정, EPR시험 및 경도시험을 행하였다. 시험결과, 질소의 함량이 증가할수록 시그마상의 석출이 억제되는 것을 알 수 있었으며, 시효시 실험합금의 부식저항성은 주로 $600^{\circ}C$부근에서 오스테나이트상의 입계에 석출하는 크롬탄화물과 50$0^{\circ}C$부터 비교적 넓은 온도 구간에 걸쳐 페라이트상으로부터 석출 변태되는 시그마상에 의해 지배되고 있음을 알 수 있었다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.96-96
• /
• 2018

금속재료 중 알루미늄(Al)은 일반적으로 많이 사용되는 철강재에 비해 그 비중이 약 $1/3(2.7g/cm^3)$인 경량이고 열전도율이 약 3배($196kcal/^{\circ}C$, $20^{\circ}C$)로 높은 특성 등을 갖고 있다. 또한 대량생산에 의한 경제성을 가지기 때문에 건축 구조재, 전기 및 가전 등 다양한 산업 분야에서 널리 사용되고 있다. 특히, 위와 같은 특성으로 인해 열교환기의 종류에서 응축기(Condenser) 및 증발기(Evaporator)는 알루미늄(Al)을 널리 사용하고 있다. 하지만 단일 응축기 부품에도 이종 알루미늄 소재가 사용됨에 따라 갈바닉 부식이 발생할 수 있다는 단점이 있다. 따라서 본 연구에서는 현재 상용되고 있는 열교환기 중 응축기에서의 이종 알루미늄 재료로 인해 나타나는 갈바닉 부식 특성을 관찰-분석-연구 하였다. 본 연구에 사용된 알루미늄 재료는 현재 응축기 재료 중에서 각각 Tube와 Fin으로 널리 상용되고 있는 Al 1100과 Al 3003을 사용하였다. 표면 모폴로지는 SEM을 통해 관찰하였고 EDS를 통해 조성원소를 분석하였다. 또한 내식성 평가를 위해 5% NaCl 환경에서의 SST(Salt spray test, 염수분무시험) 시험과 3% NaCl 용액 내 자연침지 시험 및 탈기된 3% NaCl 용액 내 전기화학적 동전위 양극 분극 시험을 진행하였으며 더불어 갈바닉 부식 시험에 따른 혼합 전위 측정 및 외관 관찰을 하였다. 각 재료는 실험에 대해 동일한 표면적을 노출시켜 시험하였다. 5% NaCl 환경에서의 염수분무 시험 결과 Fin(Al 3003)의 경우에는 Tube(Al 1100) 보다 빠른 부식거동을 보이며 국부적인 공식부식(Pitting corrosion)이 촉진되었다. Tube(Al 1100)의 경우에는 치밀한 Al2O3 형성과 부식에 따른 Al(OH)3를 생성함에 따라 Fin(Al 3003)에 비해 느린 부식거동을 보였다. 3% NaCl 용액 내 자연 침지 및 전위 측정 결과 초기 전위는 Fin(Al 3003, 약 -0.85V/SCE)이 Tube(Al 1100, 약 -1.05V/SCE)에 비해 더 높은 값을 가지며 약 72시간 이후 Tube(Al 1100) 시편이 더 안정적인 전위 값을 나타냈다. 이는 안정적인 Al(OH)3 피막 형성에 기인한 것으로 사료된다. 탈기된 3% NaCl 용액 내 전기화학적 동전위 양극 분극 시험 결과 Fin(Al 3003) 시편에서 더 귀한 부식 전위 값을 나타냈지만 부식 전류는 더 낮은 값을 나타냈다. 상기 시험 결과를 바탕으로 Fin-Tube 간 장기간 접촉 시에는 갈바닉 부식이 발생할 수 있을 것으로 사료된다. 갈바닉 부식 시험 결과 초기 혼합 전위는 약 -1.05 V/SCE를 나타냈으며 약 288시간 경과 후 약 -0.85 V/SCE 값을 나타냈다. 이는 자연 전위 측정 및 동전위 양극 분극 시험에서의 부식 전위 값에서 알 수 있듯이 더 비한 전위인 Tube(Al 1100) 시편이 Fin(Al 3003) 시편에 대해 희생양극적(Sacrificial anode)인 역할을 한 것을 확인할 수 있었다. 또한 갈바닉 부식 전위 측정 간 외관 관찰에서도 Tube(Al 1100) 시편은 빠르게 흑변 하는 것을 확인할 수 있었으며 Fin(Al 3003) 시편은 침지 300시간 이후에도 초기와 유사한 표면 상태 및 광택을 유지하였다. 이상의 SST 시험, 자연 침지 시험, 전기화학적 양극 분극 시험 및 갈바닉 부식 시험 결과를 바탕으로 단일 부품 내 이종 알루미늄 소재 간 접촉 및 그에 따른 갈바닉 부식 발생을 확인할 수 있었다. 따라서 동종 성분이라고 할지라도 단일 부품 제작 시에는 그 사용 환경에 따라 이종 금속 재료의 사용에 대한 재고가 필요할 것으로 사료된다.