• Journal of the Korea Concrete Institute
• /
• v.23 no.1
• /
• pp.109-120
• /
• 2011

This paper presents an experimental study results on the crack control of flexure-dominant reinforced concrete beams repaired with strain-hardening cement composite (SHCC). Five RC beams were fabricated and tested until failure. One unrepaired RC beam was a control specimen (CBN) and remaining four speciemens were repaired with SHCC materials. The test parameters included two types of SHCC matrix ductility and two types of repair method (patching and layering). Test results demonstrated that RC beams repaired with SHCC showed no concrete crushing or spalling until final failure, but numerous hair cracks were observed. The control specimen CBN failed due to crushing. It is important to note that SHCC matrix can improve crack-damage mitigation and flexural behavior of RC beams such as flexural strength, post peak ductility, and energy dissipation capacity. In the perspective of crack width, crack widths in RC beams repaired with SHCC had far smaller crack width than the control specimen CBN under the same deflection. Especially, the specimens repaired with SHCC of PVA0.75%+PE0.75% showed a high durability and ductility. The crack width indicates the residual capacity of the beam since SHCC matrix can delay residual capacity degradation of the RC beams.

• Journal of Korean Society of Steel Construction
• /
• v.16 no.1 s.68
• /
• pp.113-121
• /
• 2004

A test program was conducted on full-scale steel moment connections constructed using a T-stiffener. In the T-stiffener connection, the beam-to-column connection was reinforced with the horizontal and vertical element of the T-stiffener to resist moment under severe cyclic loads. A total of five specimens were tested in this study together with a concrete-filled tubular(CFT) column(${\sqsubset}-500{\times}500{\times}12$) and a steel beam($H-506{\times}201{\times}11{\times}19$). For the specimens, the T-stiffener was combined with RBS (also known as "Dog-bone") detail or Horizontal Element Hole(HEH) detail constructed to enhance deformation capacity. The test program showed excellent seismic performance for specimens constructed with an RBS or an HEH. except the specimens had brittle failure of VE. The test results also showed that the connections all developed maximum moments at the face of the column. Such moments were at least 15% and as much as 36% larger than the plastic moment capacity of the beam. based on the actual yield stress of the beam steel.

• Tunnel and Underground Space
• /
• v.27 no.5
• /
• pp.253-262
• /
• 2017

The purpose of this paper is to analyze the crack characteristics by performing the compression test of the rock and concrete specimens. The experiments are carried out by using strain sensors which can measure length change and the AE sensor which can detect the elastic wave from the crack. The crack volumetric strain calculated from measured strain is shown in different shape on the rock and the concrete specimens. This is because the specimens have a different degree of brittleness. However, the crack volumetric strain associated with the fracture and damage was similar to accumulated AE energy of the two specimens. This means that the AE sensor can assess damage in real time without damaging the structure.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.4
• /
• pp.458-466
• /
• 2020

The purpose of this experimental research is to evaluate the compressive and tensile behaviors of high performance hybrid fiber reinforced concrete(HPHFRC) using amorphous steel fiber(ASF) and polyamide fiber(PAF). For this purpose, the HPHFRCs using ASF and PAF were made according to their total volume fraction of 1.0% for target compressive strength of 40MPa and 60MPa, respectively. And then the compressive and tensile behaviors such as the compressive strength, compressive toughness, direct tensile strength, and stress-strain characteristics under compressive and tensile tests were estimated. It was observed from the test results that the compressive strength of HPHFRC was slightly decreased than that of plain concrete, but the compressive toughness, compressive toughness ratio, and direct tensile strength of HPHFRC increased significantly. Also, it was revealed that the plain concrete showed brittle fracture after the maximum stress from the stress-strain curves, but HPHFRC showed strain softening.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.26 no.4A
• /
• pp.743-752
• /
• 2006

Confined concrete has enhanced strength and ductility compared with unconfined strength. Cause of these merits of confined concrete, many researches have been performed for confining effects of concrete and been studied in many fields. Although many researches about concrete confined by FRP sheets have been studied recently, it is difficult to apply concrete confined by FRP in real structures because FRP is a brittle material. In this study, the enhanced strength and ductility of concrete which is confined by steel tubes or steel plates were investigated. Fifty one specimens were tested and each specimen has different confining condition. Test results showed enhanced ductility and strength of confined concrete and concrete models were suggested under various confining conditions by regression of experimental data.

• Journal of the Korean Ceramic Society
• /
• v.39 no.7
• /
• pp.675-679
• /
• 2002

To produce a strengthened glass, single ion exchange properties such as three-point bend strength and residual stress were investigated in soda-lime-silicate substrate glass for display use. The present work showed that the maximum value of strength was 62.5${\times}$10$\sub$6/ kg/㎡ after, the two-step single ion exchange process at 470$^{\circ}C$ for 1 h and 450$^{\circ}C$ for 24 h. As the result of the fracture analysis after bending test, the residual stress on the fractured surface of the strengthened glass increased the flexibility by means of absorbing the elastic deformation energy in the glass. Also, the effects of absorbing the elastic deformation energy were analysed by curvature change, number of multiple crack branches and brittleness.

• Korean Journal of Materials Research
• /
• v.6 no.11
• /
• pp.1136-1145
• /
• 1996

Ai-8wt.5(Ti+Zr)합금을 기계적합금화와 열간압출로 제조하여 Ti에 대한 Zr 첨가비와 등온열처리가 고온인장강도 및 변형거동에 미치는 영향에 대하여 조사하였다. Ti에 대한 Zr 첨가량의 비가 증가함에 따라 열간압출 시편의 상온 및 고온강도가 증가하였고, 40$0^{\circ}C$ 및 51$0^{\circ}C$에서 등온열처리에 따른 강도의 감소도 작게 나타났다. 이는 Zr 첨가량이 증가함에 따라 AI 기지와 AI3Ti에 비해 작은 격자간불일치도를 갖는 AI3(Ti+Zr)금속간화합물이 생성되고 고온열처리에 따른 조대화가 억제되었기 때문으로 판단되었다. 합금의 연성은 Zr 첨가량과 등온열처리에 관계없이 10% 이하로 낮게 나타났으며 인장 시험 온도가 고온일수록 취성파괴인 입계파괴가 지배적으로 일어났다. AI-Ti-Zr 합금의 변형에 필요한 활성화에너지는 순수한 AI 기지의 자기확산에 필요한 활성화에너지 142KJ/mol에 비해 573-783K 온도범위에서 1.5-1.8배 높은 값을 보였으며, Ti에 대한 Zr의 첨가량의 비가 증가할수록 보다 높은 값을 나타내었다.

• Journal of the Korea Concrete Institute
• /
• v.19 no.2
• /
• pp.135-144
• /
• 2007

Recently, fiber-reinforced plastic(FRP) wraps are blown as an effective material for the enhancement and rehabilitation of aged concrete structures. The purpose of this investigation is to experimentally investigate behavior of concrete cylinder wrapped with FRP materials. Experimental parameters include compressive strength of concrete cylinder, FRP material, and confinement ratio. This paper presents the results of experimental studies on the performance of concrete cylinder specimens externally wrapped with aramid, carbon and glass fiber reinforced Polymer sheets. Test specimens were loaded in uniaxial compression. Axial load, axial and lateral strains were investigated to evaluate the stress-strain behavior, ultimate strength ultimate strain etc. Test results showed that the concrete strength and confinement ratio, defined as the ratio of transverse confinement stress and transverse strain were the most influential factors affecting the stress-strain behavior of confined concrete. More FRP layers showed the better confinement by increasing the compressive strength of test cylinders. In case of test cylinders with higher compressive strength, FRP wraps increased the compressive strength but decreased the compressive sham of concrete test cylinders, that resulted in prominent brittle failure mode. The failure of confined concrete was induced by the rupture of FRP material at the stain, being much smaller than the ultimate strain of FRP material.

• Magazine of the Korea Concrete Institute
• /
• v.5 no.3
• /
• pp.179-186
• /
• 1993

본 연구는 무근 폴리에스터 폴리머 콘크리트보의 휨피로 거동을 구명키 위한 것으로서 초기균열깊이와 높이의 비 (a/h)를 0, 0.2, 0.4로 하고 응력수준을 45%, 55%, 65%로 하여 피로 시험을 실시한 것이다. 그 결과 초기균열깊이가 커질수록 피로수명이 짧아졌으며, 피로수명비에 따른 휨인장변형도는 균열깊이가 클수록 작아졌다. 또한 휨탄성계수는 피로수명비 0.2에서 0.6정도까지는 선형적인 변화를 보였으나, 초기와 말기에는 비선형적인 변화를 보여주었다. 그리고 응력수준과 균열깊이가 커질수록 취성적인 성질이 더 크게 나타남을 알 수 있었다.

• Tribology and Lubricants
• /
• v.10 no.3
• /
• pp.62-70
• /
• 1994

An analytical model of the stress field caused by sliding indentation of brittle materials is developed. The complete stress field is treated as the superposition of applied normal and tangential forces with a sliding blister approximation of the localized inelastic deformation occuring just underneath the indenter. It is shown that lateral cracking is produced by the sliding blister stress field and that median cracking is caused by the applied contact forces. The model is combined with an experimental volume change measurements to show that the relative magnitude of tensile stresses governing lateral crack and median crack growth varies with the magnitude of the applied load. This prediction is consistent with the different regimes of experimentally observed cracking in soda-lime glass.