• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.4
• /
• pp.23-30
• /
• 2019

Fiber-Reinforced Cement Composite (FRCC) is known to be effective in mechanical effects such as cracking width control as well as steel anticorrosive effect. In this study, we examined about steel anticorrosive effect by using metal fibers including zinc fibers by accelerated corrosion test. Moreover, it was examined for salt penetration, sacrificial anode effect and formation of electric circuit that was significant effect on the steel anticorrosive effect. As a result, Steel anticorrosive effect was confirmed with mixed metal fibers on FRCC. Especially, In the case of zinc fibers with a high sacrificial anode effect, it was confirmed that the suppression of penetration and corrosion resistance were improved.

• Magazine of the Korea Concrete Institute
• /
• v.10 no.6
• /
• pp.325-333
• /
• 1998

Under the seawater environment, the reinforced concrete structure is deteriorated due to physical and chemical attacks. The main deterioration mechanism is the chloride corrosion of reinforcing steel. The corrosion inhibitors have been used to protect the rebars from corrosion which are susceptible to chlorides in concrete. However, there is not clear conclusion about corrosion inhibitors yet. In this study, it is made the accelerated experiment with 3 kinds of corrosion inhibitors for various chloride ingresses. It is estimated corrosion inhibitors that inhibitors by Half-Cell Potential, corrosion area ratio and weight loss ratio. It is concluded that inhibitors are not effective to corrosion inhibition for excessive chloride ingress. However, the effect of inhibition is directly proportional ot contents of corrosion inhibitors in some chloride ingress.

• Journal of the Korea Concrete Institute
• /
• v.24 no.5
• /
• pp.613-621
• /
• 2012

Steel corrosion is one of the most critical deteriorations in concrete structures due to the problems associated with both durability and structural safety issues. For protection of steel against corrosion problems, researches to improve concrete durability and steel corrosion protection such as rebar coating by hot-dip galvanizing steel have been carried out. This study was performed to quantitatively evaluate anti-corrosion and structural performance of concrete structures reinforced with hot-dip galvanizing steel rebar. Preliminary tests for several metal coatings such as zinc, aluminum, and their alloy (Zn 45% + AL 55%) were performed. After evaluation of corrosive characteristics, Zn was selected for the coating material and the corrosion behaviors in Zn-coated steel were evaluated in various conditions. Furthermore, tensile and adhesive strengths were evaluated for the normal and the hot-dip galvanized steel. The crack patterns and structural behaviors of RC specimens with the normal and coated steel were investigated. Also, corrosion characteristics including corrosion in various coating metal and potential change in metal with notch were evaluated. Structural performances of tensile and adhesive strengths as well as RC beam behavior under flexural/shear loading were evaluated. The test and evaluation results showed that the applicability of hot-dip galvanized steel rebar can be used as corrosion resistant reinforcements for RC structures.

• Journal of the Korea Institute of Building Construction
• /
• v.17 no.2
• /
• pp.157-166
• /
• 2017

In general, carbonation and chlorine ions are the most harmful causes of deterioration of concrete structures. Recently, a method has been developed to control the corrosion of rebar in concrete containing chloride by impregnating a Surface coating material with a inhibitor. In this study, accelerated carbonation and differential thermogravimetric analysis (TG-DTA) and CASS tests were carried out to evaluate the characteristics of Surface coatings containing Organic Corrosion inhibitors which are excellent in corrosion inhibition and fix degradation causes $CO_2$ and $Cl^-$. As a result of the experiment, TG-DTA analysis and accelerated carbonation showed that $CO_2$ was directly reacted with amine derivative in concrete by the incorporation of Organic Corrosion inhibitor. In other words, $CO_2$ was immobilized and carbonation inhibition effect was confirmed. In addition, in the CASS test, the specimen coated with the Surface coating material containing the Organic Corrosion inhibitor with $Cl^-$ fixing property showed no corrosion until the 28th day and had excellent performance in preventing corrosion of a rebar by the chloride ion.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.2
• /
• pp.619-626
• /
• 2020

The development of new antifreeze mixtures containing non-amine-type corrosion inhibitors, which considers environmental protection, has become a major issue. In this study, four non-amine-type corrosion inhibitors were synthesized and used to produce five kinds of new antifreeze for automobiles to evaluate the rate of copper corrosion. The effects were evaluated by the weight change, surface observation, roughness measurement, and measurement of copper elution in the solution. The amount of copper eluted measured by ICP from Sample 4 was small, and the elution rate was prolonged. Sample 4 showed the best anti-corrosion performance owing to a corrosion suppression effect by passivating copper because the metal surface was smooth after the test, and the corrosion product layer was formed evenly on the surface as small local corrosion was observed. The major corrosion inhibitor added to Sample 4 was 1-aminomethyl(N',N'-di(2-hydroxyethyl)benzotrazole, which contained a certain amount in Sample 5 to show relatively high local corrosion but passivation in progress. Therefore, among the four corrosion inhibitors, 1-aminomethyl(N',N'-di(2-hydroxyethyl)benzotrazole had the highest corrosion inhibitory effect. This corrosion inhibitor prevents corrosion by promoting the passivation of copper on the antifreeze.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.8 no.3
• /
• pp.259-271
• /
• 2006

This paper aims to predict the corrosion of a fully cement-grouted rockbolt induced by chloride diffusion in a cement mortar grout. From the viewpoint of the long-term durability, a rockbolt may be deteriorated by chemical components, such as sulphate and chloride, in groundwater. Especially, the steel rod of a rockbolt is corroded mainly by chloride. The rockbolt corrosion results in the volume expansion of a rod and then the cracking of a cement grout. In this study, the chloride diffusion coefficient of a cement mortar grout was used to evaluate the possibility of rockbolt corrosion by chloride, and to predict the long-term durability of a rockbolt. The electric acceleration test method was adopted to measure the chloride diffusion coefficient. In addition, a simple pullout testing system was newly proposed to measure the pullout capacity of a rockbolt more easily in a laboratory condition. From the experiments, it was showed that the chloride could diffuse in the cement grout more easily than in ordinary concrete materials. As a result, it was considered that a rockbolt might be easily corroded in a short term by the diffusion of chemical components with high concentration, although it was fully grouted.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.3
• /
• pp.184-191
• /
• 2023

With increasing corrosion in RC (Reinforced Concrete) structures, cracks occurred due to corrosion products and bearing load resistance decreased. In this study, corrosion was induced through an accelerated corrosion test (ICM: Impressed Current Method) with 140 hours of duration, and changes in USV (Ultra-Sonic Velocity), flexural failure load, and corrosion weight were evaluated before and after corrosion test. Three levels of cover depth (20 mm, 30 mm, and 40 mm) were considered, and the initial cracking period increased and the rust around steel decreased with increasing cover depth. In addition, the USV linearly decreased with decreasing cover depth and increasing amount of corrosion. In the flexural loading test, the bending capacity decreased by more than 10% due to corrosion, but a clear correlation could not be obtained since the corrosion ratio was small, so that the effect of slip was greater than that of reduced cross-sectional area of steel due to corrosion. As cover depth increased, the produced corrosion amount and USV changed with a clear linear relationship, and the cracking period due to corrosion could be estimated by the gradient of the measured corrosion current.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.6
• /
• pp.1-13
• /
• 2022

This study aims to investigate the feasibility of the half-cell potential (HCP) measurements on the concrete surface for evaluation of corrosion rate (or corrosion levels) of reinforcing steel in concrete. A series of experimental study is performed to measure HCP (or corrosion potential, E_corr) and corrosion current density (i_corr) of reinforcing steel in concrete cube specimens, with a side length of 200 mm. Various corrosion levels in a range of 0% to 20% of the test specimens are accelerated by impressing current to the reinforcing steel in concrete immersed in 3.0 % NaCl solution. HCP is measured in accordance with ASTM C876-15, and corrosion current density is determined by using the Stern-Geary equation and measured polarization resistance measured by electrochemical impedance spectroscopy (EIS). As a result, a numerical formula that relates HCP and i_corr in the test specimen is established by a regression analysis of the measured data in this study. It is observed that HCP is linearly correlated with log(i_corr) with a R² greater than 0.87, which is less affected by the experimental variables such as concrete mixture proportion, diameter of reinforcing steel and the amount of applied current in this study. These results exhibit that HCP measurements could be effective for evaluation of corrosion rate (or corrosion levels) of reinforcing steel in concrete in the case of exposed to a certain consistent environment.

• Journal of Conservation Science
• /
• v.25 no.4
• /
• pp.373-381
• /
• 2009

To preserve steel cultural properties on display outdoors, the surface of these relics is processed with a covering treatment, which is a typical anti-corrosion method. Since the registered cultural heritage of Korea No. 78 Locomotive at Jangdan Station of Gyeongui Line will be treated by preservation process and displayed in the open outdoor area, effective surface covering agents were selected through testing to prevent the corrosion of the locomotive. The mixed wax are based on two types of microcrystalline wax which is one of regular surface covering agents for locomotives and bee‘s wax. For the weather resistance test, 3 types of wax were applied to each specimen of the locomotive and the specimens were tested in the Xenon-Arc Accelerated Weathering Tester for 1000 hours in accordance with the ISO 4892-1981 criteria and the test results were compared. As a result, on the surface of the specimen coated with the bee's wax, a whitening event appears after 400 hours which causes aging, and the specimens coated by the microcrystalline wax showed signs of a whitening event after 800 hours. The moisture contact angle with the microcrystalline wax coating was also less than with the bee's wax. Therefore, it was found that the high temperature microcrystalline wax is the most effective coating agent in terms of weather resistance and moisture blocking capability and the high temperature microcrystalline wax was adopted for coating the surface of the locomotive.

• Corrosion Science and Technology
• /
• v.15 no.1
• /
• pp.18-27
• /
• 2016

In this study, the accelerated corrosion test by combined deteriorating action of salt damage and freeze-thaw was investigated. freeze-thaw cycle is one method for corrosion testing; corrosion initiation time was measured in four types of concrete samples, i.e., two samples mixed with fly ash (FA) and blast furnace slag (BS), and the other two samples having two water/cement ratio (W/C = 0.6, 0.35) without admixture (OPC60 and OPC35). The corrosion of rebar embedded in concrete occurred most quickly at the $30^{th}$ freeze-thaw cycle. Moreover, a corrosion monitoring method with a half-cell potential measurement and relative dynamic elastic modulus derived from resonant frequency measures was conducted simultaneously. The results indicated that the corrosion of rebar occurred when the relative dynamic elastic modulus was less than 60%. Therefore, dynamic elastic modulus can be used to detect corrosion of steel bar. The results of the accelerated corrosion test exhibited significant difference according to corrosion periods combined with each test condition. Consequently, the OPC60 showed the lowest corrosion resistance among the samples.