• Clean Technology
• /
• v.25 no.2
• /
• pp.101-106
• /
• 2019

The aim of this study is to investigate the feasibility of an Ni-SA catalyst, which was prepared from nickel, kieselguhr, and alumina, for the hydrogenation of triglyceride in a bench-scale reactor. Ni-SA powders were prepared by precipitating nickel precursors on a silica and alumina support. The powder was reduced in a hydrogen flow, mixed with a saturated palm oil, and then cooled to prepare an Ni-SA catalyst tablet. The sizes of NiO crystals of a commercial Pricat catalyst and the Ni-SA catalyst prepared in this study were $35{\AA}$ and $38{\AA}$, respectively. The pore volume and pore size of the Ni-SA catalyst was much larger than the pore volume and pore size of the Pricat catalyst. In addition, the average particle size of the Ni-SA catalyst was much smaller than that of the Pricat catalyst. The triglyceride hydrogenation reaction was carried out in a semi-batch reactor using catalysts impregnated with oil and molded into tablets. It was found that the Ni-SA catalyst was superior to the commercial Pricat catalyst in triglyceride hydrogenation, which could be ascribed to the raw material and the products being less influenced by the diffusion resistance in the pores of the Ni-SA catalyst. The Ni-SA catalyst prepared in this study has the potential to replace the Pricat catalyst as a catalyst for use in the commercial process for hydrogenation of triglyceride.

• Journal of the Korean Applied Science and Technology
• /
• v.35 no.3
• /
• pp.876-885
• /
• 2018

Utilization of spent RHDM(Residue Hydrodemetallation) catalyst as de-NOx SCR(Selective Catalytic Reduction) catalyst was studied by conducting by heptane cleaning and high-temperature roasting for removal of deposited carbon and sulfur. Followed by oxalic acid leaching was carried out for controlling excess vanadium deposited on spent RHDM catalyst in search of appropriate vanadium loadings for the best SCR performance and the leaching conditions are 5~15wt% concentration of oxalic acid and 5min leaching time at $50^{\circ}C$ with the ultra-sonic agitator. De-NOx activities of prepared and commercial SCR catalyst were measured by the atmospheric SCR catalyst performance test unit, their residual content were also carried out by ICP, C&S Analysis and XRF. Acid leaching (AL-10) catalyst showed the highest de-NOx efficiency of all prepared catalysts and the de-NOx efficiency over wash coated catalyst(WC-AL-10) was equivalent to that of commercial SCR catalyst. Therefore the possibility of using as SCR catalyst for each application by adjusting treatment conditions of spent RHDM catalyst was found and further research will be needed in detail for the its commercialization.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2011.11a
• /
• pp.218-222
• /
• 2011

During the development of the iridium catalyst for domestic production, the catalyst failure, loss, sintering phenomena are observed by high pressure and temperature. By these abnormal failure of catalyst bed, the performance of thruster is degraded. To figure out the detail phenomena on the damaged catalyst bed, a numerical analysis code is developed by assuming the catalyst bed as an one dimensional porous media. The numerical analysis code is validated with experiment data. Thereby, resulting physical phenomena are examined by considering the variation of catalyst bed characteristics incurred by catalyst granule failure. Through these numerical analyses we figure out the effect of the catalyst loss on the decomposition of hydrazine and ammonia.

• Korean Chemical Engineering Research
• /
• v.46 no.1
• /
• pp.137-141
• /
• 2008

Copolymerization of ethylene and ${\alpha}$-olefin using $rac-Et[Ind]_2ZrCl_2/MAO$ catalyst embedded onto polysty-rene was examined. The embedded catalyst was prepared by polymerizing a small amount of styrene with $rac-Et[Ind]_2ZrCl_2$. The catalytic activities of the embedded catalyst were higher than those of the homogeneous catalystregardless of comonomer type and the characteristic of the active sites of the embedded catalyst was not affected duringthe embedding process. Based on the DSC and NMR analyses of the produced copolymers, it was thought that theembedded catalyst had similar or slightly better comonomer incorporation ability. Furthermore, the copolymers produced by the embedded catalyst had higher bulk densities and better particle morphology than those by the homogeneous catalyst.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2009.05a
• /
• pp.53-56
• /
• 2009

In this paper, performance evaluation of catalyst for hydrogen peroxide thruster with drying condition is described. Platinum was selected as a catalyst, and alumina of pellet type was chosen as a catalyst support. Evaporation method known as general method for catalyst production was used to make the catalyst. From previous experiments, it is favorable during catalyst making process that solution of active material has low pH level. Therefore, some kinds of low pH level solution had been tested. The drying temperatures are 25, 50, 70, and $90^{\circ}C$. From experimental results, it shows better performance that drying temperature was $90^{\circ}C$ since the catalyst particle could not be crystallized but be evenly spreaded out due to the rapid evaporation of solvent.

• Aerospace Engineering and Technology
• /
• v.4 no.1
• /
• pp.49-56
• /
• 2005

Hot firing performance test of hydrazine decomposition catalyst used for monopropellant thruster of the satellite and the launch vehicle was performed. Test equipment for catalyst test was developed in collaboration with Hanwha Corp., reaction delay time, catalyst activity and granule stability of the catalyst firing performance were measured and analyzed with the equipment. In addition, the current development of prototype catalyst is introduced.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2007.04a
• /
• pp.163-167
• /
• 2007

Silver is widely used for catalytic decomposition of hydrogen peroxide, but start-up at room temperature is difficult and cannot withstand at high temperature. In this paper, to overcome these short-comings, a dual catalytic bed which consists of a vaporizer catalyst and a high temperature catalyst was studied. Platinum was selected as the vaporizer catalyst and perovskite type catalyst was selected for the high temperature catalyst. Preliminary test demonstrated start-up capability with non-preheating at room temperature and good thermal stability at high temperature.

• Clean Technology
• /
• v.22 no.2
• /
• pp.82-88
• /
• 2016

The loss of activity by coke is an important cause of catalyst deactivation during industrial operation. In this study, hydrogen ratio of reaction condition, which has influenced on coke formation over Pt-Sn catalyst, and regeneration of catalysts activity by coke burning, Pt sintering of coke burning as coke contents, effects of coke formation and deactivation with different Sn contents were confirmed. Pt-Sn-K catalyst supported on θ-alumina and γ-alumina was prepared progressively. Activity of regenerated catalyst for propane dehydrogenation was compared with fresh catalyst by coke burning, after propane dehydrogenation was carried out with different hydrogen ratio at 620 ℃ on fresh catalyst. Regenerated catalyst’s physical characterization such as BET, coke analysis and XRD was investigated. Through catalytic activity test and characterization, Sn contents of catalyst and hydrogen ratio in feed stream could affect coke formation on catalyst surface. Excessive coke makes loss of activity and Pt sintering during air regeneration process.

• Journal of the Korean Applied Science and Technology
• /
• v.37 no.4
• /
• pp.723-732
• /
• 2020

The spent RHDS (Residue HydroDeSulfurization) catalyst is deactivated mainly by deposition of various contaminants such as coke, sulfur and vanadium on the surface of catalyst. To eliminate those contaminants, the following remanufacturing process was conducted. The first, heavy oil on the surface of the spent RHDS catalyst was removed by kerosene and dehydrated. The second, the high temperature incineration was carried out to eliminate coke and sulfur components deposited on the surface of spent RHDS catalyst. The third, the excessive quantity of Vanadium deposited on the surface of catalyst was removed by leaching process as follows: ultrasonic agitation was carried out at 50℃, for 10 seconds with 0.5% and 1% oxalic acid solution. The purpose of this process is to find out regenerated RHDS catalyst can be used as SCR catalyst for NOx reduction by controlling the vanadium residual content of the regenerated RHDS catalyst through leaching process. The composition of regenerated RHDS catalyst was analyzed by XRF and the NOx reduction efficiency was also measured by continuous catalytic fixed bed reactor. As the result, regenerated catalyst, with 0.5% oxalic acid, ultrasonic agitation in 10 seconds, showed the most stable NOx reduction efficiency. Also, in comparison with commercial SCR catalyst, the NOx reduction performance of regenerated catalyst was similar to that of commercial SCR catalyst at the temperature 375℃ and higher whereas was lower than commercial SCR catalyst at the temperature range between 200~250℃. Therefore, it was confirmed that the regenerated catalyst as powder form wash coated on the surface of metal corrugated substrate can be used for commercial SCR catalyst.

• Applied Chemistry for Engineering
• /
• v.10 no.2
• /
• pp.263-267
• /
• 1999

NO removal activity (per unit of mass) of the used catalyst was seriously decreased as low as 27% of the new catalyst. Since the surface area of the used catalyst was 63% of that of the new one, the mojor reason for the lessened activity of the used catalyst compared to the new one may be due to the decreased surface area by sintering and surface concentration of active materials. Poison may be regarded as another important factor, since it affect the active site of catalyst by heavy metals. To recycle the used catalyst, we focused on the removal of poisoning agents from the catalyst. By using $80^{\circ}C$ water for 30 min upto 2 h, the recycled catalyst demonstrated the best activity and efficiency, which may be due to the removal of both K and Na. Although the recovered activity (per unit of surface area) of the catalyst was 79% compared to the new one, the activity (per unit of mass) of the recovered catalyst was only 49% compared of the activity of fresh catalyst.