• Journal of the Korean Society of Marine Environment & Safety
• /
• v.18 no.6
• /
• pp.569-576
• /
• 2012

In general, aluminum alloys forms the passive film($Al_2O_3$, $Al_2O_3{\cdot}3H_2O$) in neutral solution. However, the passive film created on the surface will be destroyed by chloride ions contained in sea water so the corrosion will occur. In this study, in order to solve the problem of corrosion under a seawater environment, potentiostatic protection techniques were applied to Al-4.5%Mg-0.6%Mn aluminum alloy in seawater. At polarization experiments, active state were observed at anodic polarization and concentration polarization by reduction of dissolves oxygen and activation polarization were found at anodic polarization. As a results of potentiostatic experiment, calcareous deposit were created much more as applying time increase from the turning point of the concentration polarization and activation polarization and crevice corrosion was partially observed between calcareous deposit and surface of base metal. Overall potentiostatic anodic polarization experiment was difficult to apply potentiostatic corrosion protection technology by occurrence of active state, whereas potentiostatic cathodic polarization experiment examined optimum corrosion protection condition of -1.1 V~-0.75 V within the range of concentration polarization considered various applying time.

• Analytical Science and Technology
• /
• v.6 no.2
• /
• pp.157-165
• /
• 1993

The potentiostatic etching dissolution method, which had been used for the quantification of precipitates in steel, was applied to investigate the origin of cracks occurred in 304 stainless steel during processing. The morphology of crack propagation was observed by SEM. EDS and EPMA were used for the analysis of chemical composition of large precipitates on the grain boundary. The crystal structure of these large precipitates was determined by X-ray diffraction and electron diffraction. In both a stainless steel plate and a wire, the crack propagated along the grain boundary. Large precipitates on the grain boundary were identified to be $M_2C$ and $M_{23}C_6$. Potentiostatic etching dissolution method was found to be appropriate to the sample preparation for the analysis of precipitates in stainless steel.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.145-145
• /
• 2016

해양환경용 구조물은 극심한 부식 환경에 노출되어 있고 부식손상으로 인한 직간접적 경제적 손실이 발생하고 있는 상황이다. 이에 대한 방식대책으로써 음극방식법이 선박, 교량, 각종 화학장비에 널리 이용되고 있으며, 이러한 산업분야에 가장 흔히 적용되고 있는 음극방식 중 하나가 피방식체에 일정 전류 또는 음극 전위를 인가하는 외부전원법이다. 이는 전도성 부식환경인 해수환경 하에서 철강 및 해양환경용 구조 재료의 내식성을 월등히 향상시킬 수 있기 때문에 설계에 있어서 고급 내식재료 대신 경제적인 상용 재료를 적용할 수 있어 비용 절감효과를 가질 수 있다. 한편 적정 방식전위에서는 부식손상으로부터 강재를 보호하지만, 과방식 전위에서는 취성이 발생함으로써 내구성 감소의 역효과가 나타날 수도 있기 때문에 최적 방식전위의 규명은 반드시 필요하다. 따라서, 본 연구에서는 S355ML강에 대하여 천연해수 용액에서 다양한 정전위를 조건으로 전기화학실험을 실시하여 최적 방식전위를 규명하고자 하였다. 시험편은 에머리 페이퍼로 2000번까지 연마하였고, 아세톤과 증류수로 세척하여 실험하였다. 전기화학(정전위) 실험은 천연해수 속에서 $1.28cm^2$의 면적만을 노출시켜 진행하였으며, OCP로부터 -2.0V까지의 음극분극 곡선을 분석하여 정전위 조건들을 선정하였다. 그리고 외부 직류전원장치를 이용하여 1,200초 동안 다양한 정전위를 인가하였으며, 기준전극은 Ag/AgCl 전극을 이용하였다. 실험 후에는 주사전자현미경과 3D 현미경을 통해 시험편 표면을 관찰하였으며, 그 결과 일부 음극분극 구간에서 강재 표면에 전착물에 의한 뷸균일한 피막이 형성되었다. 또한, 일정 전위구간에서 용해 및 과전압에 대하여 표면손상 정도를 관찰하여, 해수환경 하에서 S355ML강의 최적 방식전위를 규명하였다.

• Journal of the Korean Chemical Society
• /
• v.66 no.6
• /
• pp.436-441
• /
• 2022

Because the nanoporous electrodes has large electrochemical surface areas, extensive studies have been focused on their fabrication methods. In this paper, a method for introducing a nanoporous gold (NPG) structure on the surface of an ultramicroelectrode (UME) using potentiostatic anodization was investigated. A well-defined NPG structure was introduced on the surface of the UME when a potential of 1.3 V was applied in 0.1 M phosphate buffer solution (pH 8) containing 1 M KCl. The anodic oxidation efficiency was investigated by observing the effect of the applied potential, the reaction time, and the size of the electrode on the roughness factor (R_f) of the prepared NPG-UMEs. In a short time of about 10 minutes, NPG-UME with a large R_f value of about 2000 could be prepared, which could be effectively used for electrochemical glucose detection. The results shown in this work are expected to have great applicability when performing electrochemical analysis with a small sample volume.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1996.11b
• /
• pp.475-480
• /
• 1996

Alloy 600 및 Alloy 690의 Caustic 분위기에서, 시편의 포텐셜을 재료의 anodic polarization curve의 active-passive transition 영역의 한 값으로 일정하게 유지함으로서 응력부식균열을 쉽게 유발시키는 정전위 시험방법을 사용하여, 두 합금의 부식저항성을 비교하였다. C-ring형태의 Alloy 600 및 690 시편에 응력을 부과하고 30$0^{\circ}C$의 10% NaOH용액에서 7일간 정전위 응력부식시험을 수행하였다. Alloy 600의 경우, 입계를 따르는 100$\mu$m정도 깊이의 균열이 발생하였으나 Alloy 690의 경우는 균열이 유발되지 않았다. Alloy 690의 경우 부식 시험시간이 경과함에 따라 표면부식전류밀도는 주기적인 Passivation 경향을 보이나 Alloy 600의 경우는 점진적으로 표면부식전류밀도가 증가한다. Alloy 690의 강한 응력부식저항성은 이와 같은 주기적인 Passivation에 의한 것으로 판단된다.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.137.2-137.2
• /
• 2010

본 연구는 스테인리스 스틸(STS)을 직접메탄올 연료전지(DMFC)용 바이폴라 플레이트에 적용하기 위한 것이다. 약산성의 연료전지 환경에서 부식저항성을 향상시키고자 오스테나이트계 STS 316L과 페라이트계 STS 430에 UBM(unbalanced magnetron) DC sputter로 CrN 코팅막을 제작하였다. CrN이 코팅된 스테인리스 스틸은 부식특성, 접촉 저항 및 접촉각 등을 측정하여 무 코팅의 스테인리스 스틸과 특성을 비교하였다. 그리고 이들 재료의 연료전지(DMFC) 적용 가능성을 알아보기 위하여 단위전지로 제작하여 연료전지 성능 등을 측정하고 평가하였다. 무 코팅 스테인리스 스틸(STS 316L, STS 430)과 CrN 코팅 스테인리스 스틸의 부식저항 특성은 동전위와 정전위 실험으로 조사하였다. 동전위 부식 실험은 -0.4~1.0 V로 0.001 M의 황산용액 또는 메탄올을 첨가하여 질소 또는 공기의 환경에서 실험을 실시하였으며, 정전위 부식 실험은 0.4 V 또는 0.6 V에서 진행하였다. 연료전지의 단전지 측정은 실제 DMFC의 운전조건에서 실시하였다. 부식실험과 단전지 실험 전/후 메탈 바이폴라 플레이트의 조직 변화는 SEM을 통해 관찰하였고, 부식산화물의 화학적 조성과 메탈 바이폴라의 표면은 EDS를 이용하여 측정하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.11a
• /
• pp.152-152
• /
• 2012

• The Proceedings of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.11 no.4
• /
• pp.74-81
• /
• 1997

I정전 모-터는 일반적으로 분극전하와 전계의 상호작용을 이용한 것으로서 전계내에 축적되는 전계에너지(W=1/2 *ED)의 힘을 기계적 출력으로 도출하여 이용하는 것이다. 본 논문에서는 유한 요소법을 사용하여 단상 정전 모터의 전계와 등전위분포 및 미소한 토오크를 시뮬레이션을 통하여 구하고 해석하였다. 그 결과 이 모터는 특성상 정전, 역전이 가능하고 고전압에서 응용이 가능하므로 특수기의 서어보모터로 쓸 수 있겠고, 설비중 고압으로 인한 위험이 따르는 곳의 안전예고기, 고전압계, 위상 판별기로도 사용이 가능할 것으로 기대된다.

• Electrical & Electronic Materials
• /
• v.6 no.4
• /
• pp.339-346
• /
• 1993

정전결합 유동가스형 플라즈마 중합장치를 이용하여 여러가지 모노머에 대한 유기고분자 박막을 빗모양 전극위에 형성하고 이들 박막의 감습특성을 검토하기 위해 주파수범위를 60[kHz]-100[kHz]로 변화시켜 가면서 상대습도 20-90[%RH]범위에서 정전용량의 변화를 측정하였다. 상대습도가 증가함에 따라 정전용량은 일반적으로 증가했으며 방전조건중 방전전력이 낮을수록 그리고 중합시간이 짧을수록 정전용량의 증가폭이 크게 나타났다. 그리고 정전용량 측정시 박막에 인가한 전원의 주파수가 낮을수록 정전용량의 변화에 대한 선형성과 증가폭이 분명함을 알았다.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2012.06a
• /
• pp.242-242
• /
• 2012