• Polymer(Korea)
• /
• v.26 no.3
• /
• pp.300-306
• /
• 2002

To study the effect of polymer compositions on the cell adhesion, copolymers of 3-(S)-[(dodecyloxycarbonyl) methyl]-1,4-dioxane-2,5-dione (DMD) and L-lactide were made, where DMD was synthesized form L-malic acid (L-MA) and glycolic acid. Furthermore, the copolymerization of DMD and L-lactide was performed using tin(II) octanoate as a catalyst. As a result of fixing RGD on the copolymer films, the cell adhesive peptide was fixable on the surface of the film. It was found out that the amount of fixation of RGD also increases by the increase in the amount of MA unit introduction. Since it is gradually decomposed over a long period and neither remains nor accumulation occurs, glycolic acid-$\beta$-dodecylmalate -lactic acid (D-PGML) is greatly expected as a potential biomaterial with improved slow degradability.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2000.11a
• /
• pp.46-46
• /
• 2000

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1998.11a
• /
• pp.22-23
• /
• 1998

• Journal of Adhesion and Interface
• /
• v.6 no.1
• /
• pp.11-18
• /
• 2005

The capsules were prepared from a phase change material (PCM) of octadecane as a core material and melamine formaldehyde resin as a shell material. The PCM capsule size was varied in the range of $3{\sim}25{\mu}m$. The core contents and sizes of the PCM capsule, were determined by DSC and SEM, respectively. An acrylic coating material which contains butyl acrylate (BA), methyl metacrylate (MMA) and acrylic acid (AA) were synthesized by emulsion polymerization. The films were prepared from the acrylic emulsion and PCM capsules which have various capsule sizes. From the results of SEM experiment, it was observed that the PCM capsules were well dispersed inside the film and the surface of the film became less rough when the PCM capsule size was small. The swelling ratio of the films were not significantly affected by the PCM capsule size. However, the tensile strength and elongation of the films were greatly decreased with increasing the PCM capsule size.

• Journal of Adhesion and Interface
• /
• v.23 no.3
• /
• pp.94-99
• /
• 2022

Ternary phased graphene/silica/EVOH nanocomposite coating materials were prepared via sol-gel process and solution blending process. From both SEM observations and XRD analysis, the exfoliated structure and dispersion state of graphene nanosheets and silica particles in the nanocomposites as well as the intercalated and exfoliated structure of the prepared graphene oxide were confirmed. The incorporation of GrO and silica at appropriate content resulted in remarkable improvement in oxygen barrier property of the ternary phased nanocompoiste-coated BOPP films, compared with that of binary(silica/EVOH) phased nanocomposite coating films, however, at excess amount of GrO and silica, very slight variation was observed due to incomplete exfoliation, dispersion of graphene tactoids, and formation of micro cracks in the silica clusters. In addition, the transparency of nanocomposite-coated film was investigated by measuring the light transmittance as a function of GrO contents, suggesting the possibility for the application of food packaging films.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.11a
• /
• pp.46.2-46.2
• /
• 2009

휴대전화, 랩톱 컴퓨터 등 각종 모바일기기 및 디스플레이 기기의 경박단소화 및 고기능화에 따라 연성회로기판(FPCB)의 사용량이 증가하고있다. 연성회로기판의 핵심소재인 동박적층필름(FCCL)은 폴리이미드필름과 접착층, Cu 층으로 구성되는데, 이 중접착층으로 사용되는 Ni-20Cr합금은 에칭공정 후 Cr의 잔류에 의해 불량률 증가가 문제되고 있어, Ni-Cr합금 스퍼터링 타깃의 Cr 함량 저감 또는 Cr-free Ni합금 개발 등이 요구되고 있다. 본 연구에서는 차세대 FCCL 본드층에 적합한 Ni기 합금을 개발하기 위한 기초연구로써 Cr 함량 및 가공열처리조건에 따른 미세조직과 집합조직 변화를 조사하였다. 4N급의 고순도Ni과 Cr을 진공 플라즈마 용해장치로 용해하여Ni-xCr (x=5, 10, 15, 20wt.%)합금 잉곳을 만들고, 이를 두께감소율 90%로 냉간압연한 후, $600^{\circ}C$ 및 $800^{\circ}C$에서 10~120분 동안 어닐링하여 시편을 준비하였다. 광학현미경으로 미세조직을 관찰하고, Micro-Vickers 경도시험을 통해 어닐링 조건에 따른 경도변화를 조사하였다. 또한 SEM-EBSD를 이용하여 집합조직 및 입계특성을 분석하였다. $600^{\circ}C$ 어닐링 시 Cr함량이 증가할수록 재결정 완료시간이 증가하여 Ni-20Cr합금의 경우 2시간이상 어닐링에도 재결정이 일어나지 않았다. $800^{\circ}C$ 어닐링 시 10분 어닐링 조건에서 4종류 합금 모두 재결정이 완료되었으며, 동일한 어닐링 조건에서 Cr함량이 증가할수록 결정립이 작아지는 것으로 나타났다. $800^{\circ}C$ 2시간 어닐링 조건에서 Ni-5Cr 합금의 주요 집합조직은 {223}<113>과 {122}<112>로 나타났으며, 이중 {223}<113>은Cr 함량이 증가함에 따라 점차 {122}<112>에 가까운 방향으로 변화되어 Ni-20Cr 합금의 경우 {123}<112>만이 형성되었다. 이러한 집합조직의 변화는 적층결함에너지 감소에 의한 ${\Sigma}3$ 입계의 분율 증가와 밀접한 관련이 있는 것으로 사료된다.

• Journal of Adhesion and Interface
• /
• v.7 no.3
• /
• pp.16-25
• /
• 2006

Water vapour permeable and water resistant film was laminated to made footwear woven fabric and non-woven fabrics by screen type with thermosetting reactive hot melt adhesive. Optimum conditions of each process were investigated, and the properties of film laminated fabric with optimum conditions are evaluated. The results are as follows. Thermosetting reactive polyurethane hot melt is retain proper heat resistance differently thermoplastic hot melt. Optimum melting adhesive process conditions are as follows ; drum temperature $95^{\circ}C$, hose temperature $97^{\circ}C$, feeding pipe temperature $100^{\circ}C$, screen temperature $105^{\circ}C$, pressure of opposite roller $1kgf/cm^2$, pressure of laminating roller $3kgf/cm^2$, finishing speed 15 m/min, melting temperature $120^{\circ}C$, cooling time 20 s, pressing temperature $130^{\circ}C$, pressing time 30 s. As the thickness of film was increased, the water vapour permeability was decreased but water resistance was increased, and the effect of film is dominant over all the others in the air permeability.

• Journal of Adhesion and Interface
• /
• v.18 no.3
• /
• pp.134-140
• /
• 2017

In this study, we made UV cured acrylic pressure sensitive adhesive containing silicone-urethane-acrylate (SUA) oligomer for a coating on protective film and investigated the effect of SUA oligomer content and UV-dose on adhesion properties. The results illustrated that peel strength decreases with increasing oligomer content and UV-dose, while holding power increases. The gel fractions sharply increased after UV irradiation and then remain constant with prolonged UV exposure. From peel-off test, sample S70 (70% oligomer content) shows the best peelability and removability without remaining any mark or adhesive material on the test substrate than S50 (50% oligomer content) and S60 (60% oligomer content). Sample S70 also showed a surface energy lower than $26mJ/m^2$ and a transmittance higher than 95% at UV-dose 1857 and $2270mJ/cm^2$ which met the required properties for protective film application.

• Journal of Adhesion and Interface
• /
• v.17 no.4
• /
• pp.155-162
• /
• 2016

• Composites Research
• /
• v.13 no.4
• /
• pp.42-53
• /
• 2000

A study has been made to establish an optimum condition in the surface treatment and curing method that is important for the fabrication of Al 7075/CFRP laminates. PAA(Phosphoric Acid Anodizing) provided a good adhesive strength and FPL(Sulfuric / Sodium Dichromate Acid Etching) had a similar adhesive strength with PAA. On the other hand, the poor adhesive strength was shown on vapor degrease and CAA(Chromic Acid Anodizing). By using the atomic force microscope(AFM), it was found that the PAA oxide surface obviously had a greater degree of microroughness as compared to vapor degrease, CAA and FPL treated surfaces. These results support the concept of a mechanical interlocking of the adhesive with-in the oxide pores as the predominant adhesion mechanism. In curing methods, the adhesive strength of co-curing method was higher than that of secondary curing method. With respect to stability of specimen shape, the secondary curing method was better than co-curing method. DMA(Dynamic Mechanical Analysis) test revealed $T_g$ in curing times over 60 min is nearly same, so it is estimated they will have similar degree of curing and joint durability in using FM300M adhesive film.