This study was conducted for improvement of meat quality in broiler chcikens. Birds were fed basal diet(control), ferritin, illite, betafin, or wood vinegar counting broiler feed according as broiler growth stage. Birds fed with basal diet, which was distributed under the best environmental condition, were more weight gain than other groups reared under same environmental condition. In the mean weight gain, the ferritin-group showed the highest and the illite-group showed the lowest among the feed additive groups; therefore, the effect of feed requirement change in odor reduction in illite and methyl saving of betafin was lower than those of other feed additives along to pass rear time. Meat quality was appraised by National Livestock Research Institute of RDA. Except the control-group, that had the best feed conversion ratio, the cooking loss of the illite-group was the biggest among groups although the illite-group chickens had a good water hold capacity. Therefore, illite is not good for making merchandise by reason that group chickens get reduction carcass weight after slaughter. On the other hand, the ferritin-group got the highest point of shear stress, cooking loss, and crude fat level. That group showed the best appraise in both breast and leg of sensory test in company and also feed conversion ratio was the highest among feed additive groups. As a result, the ferritin-group might use for making new merchandise among the feed additive groups.

• Journal of the Korean Wood Science and Technology
• /
• v.16 no.4
• /
• pp.48-53
• /
• 1988

This study was carried out to investigate the effects of pressing time and spreading amount, moisture content, gap-distance with butt to butt joint and adhesives on bonding strength in manufacturing the laminated wood with Pitch pine (Pinus rigida). The results obtained were as follows: 1) The pressing time of 12 hours, 10 kilogram per square centimeter of pressure and 200 gram per square meter of spreading amount were required to reach over 50 kilogram per square centimeter (block shear strength) in manufacturing the laminated wood by aqueous vinyl urethane adhesive. 2) The bonding strength decreased with the increase of moisture content of wood. The block shear strength, however, showed over 100 kilogram per square centimeter when the strength test was carried out after air-drying the laminated wood in high moisture content (30-70%). 3) Regardless of direction of load, every flexural property decreased with the increase of gap-distance with butt to butt joint. However, little of every flexural property was changed at 0.5 millimeter of joint-gap distance. The flexural property of vertically laminated wood (perpendicular to glue line to load direction: 1) showed more than that of horizontally laminated wood (parallel to glue line to load direction: //). 4) Among five adhesives used at this experiment, the bonding strength of aqueous vinyl urethane adhesive was the highest in dry bond and wet tests.

• Journal of the Korean Wood Science and Technology
• /
• v.35 no.3
• /
• pp.10-21
• /
• 2007

It is necessary to study about moment performance of glulam-dowel connections which had been applied rotation. To analyze and predict the moment performance, angled to grain load was replaced with parallel to grain load and perpendicular to grain load. The dowel bending strength and dowel bearing strength were tested. And tensile strength test for connections of two different end distances was performed. Specimens of rotation test were composed with different drift pin numbers and drift pin arrangement. Connection deformation was occurred by plastic behavior of drift pin after yield when tensile load applied at connection. And the absorbing drift pin deflection by end distance continued the connection deformation. When rotation applied at connection that 2 drift pins were arranged parallel to grain (b2h), it showed similar performance with tensile perpendicular to grain. And connection that 2 drift pins were arranged perpendicular to grain (b2v) showed similar performance with tensile parallel to grain. Connection capacity that 4 drift pins were arranged rectangular (b4) showed 1.7 times as strong as connection that 2 drift pins were arranged parallel to grain (b2h). These results agreed predicted values and it is available that rotation replaced with tensile load.

• Food Science of Animal Resources
• /
• v.25 no.3
• /
• pp.322-327
• /
• 2005

This study was intended to provide basic information which might be useful in increasing added values to the pork from Korean native black pigs (KNP), through comparative evaluation on carcass characteristics and meat qualities between KNP and four exotic breed groups including Duroc (DD), Landrace (LL), Yorkshire (YY), and LYD-cross (1/4LL 1/4YY, 1/2DD), and the results were summarized as follows. Live weight carcass weight, dressed meat weight, skin weight, fat weight and bone weight of KNP were significantly (p<0.05) lower than those of DD, LL, YY and LYD-cross. Carcass yield and dressed meat yield were also significantly (p<0.05) lower in KNP than other 4 groups, however, total fat, skin, bone, kidney and kidney fat in percentage were significantly (p<0.05) higher for KNP than others. Dressed meat yield was highest for YY, followed by LYD-cross and KNP. Weight of belly was 6.12, 9.43, and 9.52 kg for KNP, YY and LYD-cross, respectively. Percent belly of KNP was $11.11\%$ while other groups ranged from 11.5 to $12.2\%$ Shear force value was not different among the treatments. KNP had significantly (p<0.05) lower water holding capacity (WHC), and cooking loss, but significantly (p<0.05) higher in juiciness comparatively. KNP had significantly (p<0.05) higher $a^{*}$ value while DD had significantly (p<0.05) lower than other breeds.

• Korean journal of food and cookery science
• /
• v.26 no.3
• /
• pp.323-329
• /
• 2010

Studies on the tenderizing effect of fruits has been limited even though fig, kiwifruit, pear, and pineapple cultivated in Korea are utilized commonly during cooking for their proteolytic properties. Therefore, the characteristics of these fruits were investigated by treating beef with their crude protease extracts. The protease effects of crude protease extract from the fruits on casein and myofibrilar protein were in the following order : pineapple > kiwifruit > fig > pear. Electrophoretic analysis results found that pineapple, kiwifruit, and fig cleaved myosin heavy chain into smaller fragments. The myofibrilar fragmentation ratio of crude protease extracts was the highest for pineapple whileas the lowest for pear. Ground fruits (5% and 10%) increased amounts of soluble nitrogen and decreased shear force of beef. Pineapple was the most effective while pear was the least effective. Decrease in springiness and gumminess was observed by texture profile analysis of beef treated with fruits, especially pineapple and kiwifruit. Among the 5% treatments, pineapple and kiwifruit produced the highest tenderness. Additionally, 10% treatment was less preferable than the 5% treatment.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.14 no.11
• /
• pp.5947-5955
• /
• 2013

This study was intended to estimate the axial deformation of joint between pavement modules in the rapid-constructible modular pavement system, and to investigate the applicability of two-phase composites for a joint material, which was composed of cement paste, epoxy, or polyurethane as a matrix and sand as particles. A case which had supports under the pavement module as well as a case which the module was put on roadbed directly were considered in FEM analysis for the axial deformation. The effect of self-weight, live load, thermal change, and drying shrinkage were estimated and the thermal change was found to cause the largest deformation compared to the others. Deformation capacity of two-phase composites was predicted using the modified shear-lag model. In the analytical results for the elastic modulus and maximum tensile strain with different volume fractions of sand, 20~30 % replacement of sand was revealed to satisfy the required strain capacity with economy when if the width of joint was designed to be 15~20 mm.

• Tunnel and Underground Space
• /
• v.30 no.4
• /
• pp.404-416
• /
• 2020

An analytical procedure for calculating the failure load of a V-shaped rock notch under two-dimensional stress conditions was developed based on the slip-line plastic analysis method. The key idea utilized in the development is the fact that the α-line, one of the slip-lines, extends from the rock notch surface to the horizontal surface outside the notch when the rock around the notch is in the plastic state, and that there exists an invariant which is constant along the α-line. Since the stress boundary condition of the horizontal surface outside the rock notch is known, it is possible to calculate the normal and shear stresses acting on the rock notch surface by solving the invariant equation. The notch failure load exerted by the wedge was calculated using the calculated stress components for the notch surface. Rock notch failure analysis was performed by applying the developed analytical procedure. The analysis results show that the failure load of the rock notch increases with exponential nonlinearity as the angle of the notch and the friction of the notch surface increase. The analytical procedure developed in this study is expected to have applications to the study of fracture initiation in rocks through wedge-shaped notch formation, calculation of bearing capacity of the rock foundation, and stability analysis of rock slopes and circular tunnels.

• Korean Journal of Materials Research
• /
• v.4 no.2
• /
• pp.194-205
• /
• 1994

In this research, we attempt to fabricate an excellent CFRC(Carbon Fiber Reinforced Carbon), which has good thermal and mechanical properties, with 8H/satin woven fabric prepreg, high modulus and high strength type continuous carbon fiber and raw coal tar pitch(RCTP) matrix or THF soluble fraction(THFSP) matrix which has good graphitizability. Green bodies were fabricated with hot press molding technique and CFRC samples were made after carbonization, impregnation, recarbonization and graphitization steps. For the purpose of characterization of the physical properties, SEM, polarized light microscope, TGA were observed, and tested flexural strength, modulus and ILSS. After heat treating the THFSP matrix up to $2300^{\circ}C$, the value of $C_0$/2 was 3.380$\AA$, which is analogous to the structure of natural graphite and the value of 2$\theta$ is $26.276^{\circ}$ approached to the Bragg's angle of natural graphite. As a result of TGA to test the high temperature air oxidation, the THFSP matrix, graphitized up to $2300^{\circ}C$, exhibited the best air oxidation resistance. And mechanical properties were increased up to 65~70% as fiber volume fraction increased. Because of the good orientation graphitizability, the fracture surface of THFSP matrix CFRC is very good.

• Journal of Adhesion and Interface
• /
• v.15 no.3
• /
• pp.100-108
• /
• 2014

In this work, a series of molar ratios composed with YD-128 and DDM were chosen based on the viscosity analysis. The mixtures of YD-128 and DDM with the different molar ratios were cured at $170^{\circ}C$ for 15 min followed by post cure at $190^{\circ}C$ for two hours. The thermal properties of the cured samples were investigated with DSC, TGA, DMA, and TMA. The conversion ratio of the mixtures of YD-128 and DDM (1 : 1.1) was calculated by dividing ${\Delta}H$ obtained from DSC experiments for each cured sample by ${\Delta}H$. The TGA data of the cured samples showed that the thermal stability and thermal degradation activation energy were proportional to the amount of DDM in the mixtures. However, the highest tan ${\delta}$, and the lowest thermal expansion data with DMA and TMA respectively were obtained from the stoichiometric mixture of YD-128 and DDM. Furthermore, the different ratio of mixtures were applied to test specimens to be cured at $170^{\circ}C$ to measure single lap shear strength with universal testing machine.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.28 no.2
• /
• pp.228-237
• /
• 2001

It is well known that glass-ionomer cement and compomer can release fluoride which can inhibit the progression of dental caries. The purposes of this study were to evaluate whether the fluoride from fluoride-containing filling materials can penetrate the dentin bonding adhesive and the dentin bonding adhesive can increase the bond strength of resin-modified glass ionomer. The amount of fluoride release from resin-modified glass ionomer and compomer was measured during 28 days of period and statistically analyzed by t-test. The bond strength of each material with/without dentin bonding adhesive was measured and also statistically analyzed by t-test. The distribution of fluoride from each material into the tooth was explored by electron probe microanalysis system(EPMA). The experimental teeth used were second primary molars about to exfoliate. The amount of fluoride release from each material was diminished by dentin bonding adhesive during 28 days(p<0.05) and the bond strength was not increased by dentin adhesive in resin-modified glass ionomer. The bond strength of group VI was not detectable. The distribution of fluoride from each material into teeth was according to dentino-enamel junction and dispersed into pulp from pulpal floor. The widest distribution was shown in resin-modified glass ionomer cement filled without the application of dentin bonding adhesive.