Effects of Adhesion Conditions on Bonding Strength of Pitch Pine Woods for Glued-Laminated Wood

리기다소나무 판재(板材)의 접착조건(接着條件)이 집성재(集成材)의 접착성능(接着性能)에 미치는 영향(影響)

  • Received : 1988.10.05
  • Published : 1988.12.30

Abstract

This study was carried out to investigate the effects of pressing time and spreading amount, moisture content, gap-distance with butt to butt joint and adhesives on bonding strength in manufacturing the laminated wood with Pitch pine (Pinus rigida). The results obtained were as follows: 1) The pressing time of 12 hours, 10 kilogram per square centimeter of pressure and 200 gram per square meter of spreading amount were required to reach over 50 kilogram per square centimeter (block shear strength) in manufacturing the laminated wood by aqueous vinyl urethane adhesive. 2) The bonding strength decreased with the increase of moisture content of wood. The block shear strength, however, showed over 100 kilogram per square centimeter when the strength test was carried out after air-drying the laminated wood in high moisture content (30-70%). 3) Regardless of direction of load, every flexural property decreased with the increase of gap-distance with butt to butt joint. However, little of every flexural property was changed at 0.5 millimeter of joint-gap distance. The flexural property of vertically laminated wood (perpendicular to glue line to load direction: 1) showed more than that of horizontally laminated wood (parallel to glue line to load direction: //). 4) Among five adhesives used at this experiment, the bonding strength of aqueous vinyl urethane adhesive was the highest in dry bond and wet tests.

본(本) 연구(硏究)는 리기다소나무판재(板材)를 이용(利用)하여 집성재(集成材)를 제조(製造)할 경우(境遇), 압체시간(壓締時間) 및 접착제도포량(接着劑塗布量), 목재(木材)의 함수율(含水率), Butt-joint의 틈새간격(間隔) 및 접착제(接着劑)의 종류(種類) 등(等)이 접착강도(接着强度)에 미치는 영향(影響)을 알아보기 위해 수행(遂行)되었다. 1. 리기다소나무집성재(集成材)의 제조(製造)에 수성(水性)비닐우레탄접착제(接着劑)를 사용(使用)한 결과(結果), 접착제도포량(接着劑塗布量) 200g/$m^2$, 압체압력(壓締壓力) 10kg/$cm^2$에서 12시간(時間) 압체(壓締)하면 기준강도(基準强度)(50kg/$cm^2$)이상(以上)에 달(達)하였다. 2. 판재(板材)의 함수율(含水率)의 접착력(接着力)을 크게 감소(減少)시켰으나, 고함수시(高含水時) 접착(接着)한 후(後) 기건(氣乾)하여 접착력(接着力)을 측정(測定)한 결과(結果), 100kg/$cm^2$)이상(以上)의 블록전단강도(剪斷强度)를 나타내었다. 3. 판재(板材)의 Butt joint 부분(部分)의 틈새간격(間隔)이 0.5mm이하(以下)인 경우(境遇), 강도(强度)값은 영향(影響)하지 않았고, 하중방향(荷重方向)이 접착력(接着力)과 수치(垂値)일 때가 수평(水平)일 때보다 강도성태(强度性能)이 양호(良好)하였다. 4. 시험(試驗)에 사용(使用)된 5종(種)의 접착제(接着劑) 중(中) 수성(水性)비닐우레탄수지접착제(樹脂接着劑)가 상태(常態) 및 내수접착력면(耐水接着力面)에서 가장 양호(良好)하였다.

Keywords