• Journal of Sericultural and Entomological Science
• /
• v.35 no.1
• /
• pp.60-68
• /
• 1993

It has been known that the silk degumming treated by hot alkali solution is easy to handle but is liable to yield poor-quality silk due to the degree of degumming loss, incomplete-degumming or over-degumming. Therefore, many studies have been carried out on the silk degumming by enzyme in order to improve the quality of silk. However, no attention has been paid to the physicochemical analysis of enzymatic degummed silk. In this paper, two different degumming methods, soap and enzymatic, are compared in aqueous solution state of silk fibroin. The results can be summarized as follows: There was no significant difference between two solutions on the bases of polarizing microscopy, TEM observation and SDS-PAGE. Spherulite of silk fibroin was not observed in polarizing microscopy, however the leaf-shape fibril structure was developed upon solidification. The size of spherulites of silk fibroin in TEM observation were 30~120nm with a wide range of size distribution. The intrinsic viscosity of enzymatic degummed fibroin solution was lower than that of soap degummed solution. This can be explained that the silk fibroin was more degraded by enzymatic degumming method compared with the soap degumming method. SDS-polyacrylamide gel electrophoresis showed that the fibroin molecule was composed of large component of molecule weight above 50 kd and small component of molecule weight about 20 kd. There was no difference in crystallinity between two degumming methods on the bases of results of DSC thermograms and IR spectra.

• Journal of the Korean Chemical Society
• /
• v.33 no.5
• /
• pp.558-567
• /
• 1989

The synthesis of methanol from carbon dioxide and hydrogen was studied for various compositions of Cu/ZnO catalyst system. Effect of the composition ratio of CuO and ZnO on the catalytic activity in the above reaction and the relationship between the activity and the characteristics of the catalysts were explained from the result of surface area measurements, SEM, XRD, and XPS. The major products of the reaction were methanol and carbon monoxide. The selectivity to methanol increased with increase of the copper oxide content in the catalyst up to CuO: ZnO = 30:70 weight ratio, and decreased rapidly when the content is above 70%. SEM and BET measurements, indicate that this point corresponds to the increasing point of the catalyst crystallite size and the decreasing point of the surface area. As to the Cu/Cu + Zn atomic ratio, the surface concentration of copper measured by XPS decreased remarkably when the copper oxide content in catalyst was higher than 50%. All the unreduced catalysts had almost same binding energy of Cu(2P3) level, but the binding energy for $Cu(2P^3)$ level of reduced catalysts was lowered than that of calcined catalysts. The surface copper species which was in the maximum amount when the CuO:ZnO composition in the catalyst was 30:70, existed as zero valent copper. This result agreed with the experimental result that the highest rate of methanol formation was observed when the CuO content in the catalyst was 30%. It was postulated that these reduced catalysts performed with a relatively strong basicity because the formation rate of acetone was higher than that of propylene in isopropanol decomposition as measured in a pulse type reactor.

• Journal of Korean Society of Environmental Engineers
• /
• v.22 no.12
• /
• pp.2205-2213
• /
• 2000

To investigate removal efficiency of dissolved matter by NF and RO, a pilot plant was operated for six months using groundwater treated by UF membrane. After the pilot plant operation, we performed autopsy test to identify characteristics of foulant attached on the membrane surface applying the used NF and RO in the pilot plant test. In autopsy test, we measured permeate flux and recovery rate of flux by chemical cleaning in each membrane. We also analyzed chemical cleaning disposal to examine component of foulant. Permeate flux of NF and RO1 showed rapid decline after 100 days of operation. Especially, reduction of specific flux in RO1 was more serious than in NF. Specific flux of RO2 with a low recovery rate resulted in gradual flux decline. Removal efficiencies of dissolved inorganic matters as a conductivity were 76.3%, 88.2% and 95.3% respectively for NF, RO1 and RO2, and RO2 presented the highest removal efficiency. And those of dissolved organic matters as TOC were about 80% for both NF and RO. The specific flux of membranes declined gradually from the feed water inlet to outlet of the membrane module and it showed that membrane fouling increased along the feed flow direction. Namely, concentration of pollutants became higher and volume of feed water was less as the feed flow approached to the outlet. It seemed that major foul ants were Ca consolidated into inorganic material and Si consolidated into organic material on the membrane surface. Fe was a great contribution to irreversible fouling. The SEM results indicated that the organic matter was attached to the first layer, closer to the membrane, and then inorganic matter with tetragonal shape layered over them. We could not observe biofouling because microorganism, which was cause of biofouling, was almost pretreated in UF membrane.

• Journal of the Korean Vacuum Society
• /
• v.19 no.3
• /
• pp.224-229
• /
• 2010

Indium oxide $(In_2O_3)$ thin films have been prepared on glass substrate by using radio-frequency reactive magnetron sputtering with changing the oxygen flow ratio. The substrate temperature was kept at a fixed value of $400^{\circ}C$, and the sputtering gas and reactive gas were supplied with argon and oxygen, respectively. The oxygen partial flow ratio was varied by controlling the amount of oxygen with respect to the total mixed gases, 10%, 20%, 30%, 40%, and 50%. The optical, electrical, and structural properties of the deposited thin films were investigated by using ultraviolet-visible-near infrared spectrophotometer, Hall measurement, and X-ray diffractometer and scanning electron microscopy. The $In_2O_3$ thin film deposited at 20% of oxygen flow ratio showed an average transmittance of 86% in the wavelength range of 430~1,100 nm, an electrical resistivity of $1.1{\times}10^{-1}{\Omega}cm$. The results show that the transparent conducting films with optimum conditions can be achieved by controlling the oxygen flow ratio.

• Culinary science and hospitality research
• /
• v.21 no.4
• /
• pp.1-15
• /
• 2015

For the consumption extension of Chinese artichoke(Stachys sieboldii MIQ), the quality characteristics and sensory evaluation of white pan bread prepared with different levels of added Chinese artichoke powder(0, 3, 6, 9, and 12%) were investigated. Volume changes of dough, moisture contents(p<0.001), and baking loss rate(p<0.001) decreased with increasing levels of Chinese artichoke powder. In addition, with an increase in the level of Chinese artichoke powder, the volume and specific volume of white pan breads significantly decreased(p<0.001 and p<0.001, respectively) whereas the weight of white pan breads significantly increased (p<0.001). In terms of color, the lightness(L) decreased, but the redness(a) and yellowness(b) increased with increasing Chinese artichoke powder levels(p<0.001). From the texture profile analysis(TPA) of white pan breads, hardness, chewiness(p<0.05), gumminess(p<0.001), and adhesiveness(p<0.001) increased whereas springiness and cohesiveness(p<0.01) decreased according to the levels of added Chinese artichoke powder. In the attribute difference test, crumb color(p<0.001), grain size(p<0.05) decreased whereas grain uniformity, yeast flavor, acridity flavor(p<0.001), plainer taste(p<0.05), sweet taste(p<0.01), acridity taste(p<0.001), firmness, springiness, moistness, softness, and chewiness increased in accordance with levels of added Chinese artichoke powder. Overall acceptability showed that the sample containing 9% Chinese artichoke powder had the highest score (p<0.001). As a result, the optimal ratio of Chinese artichoke powder for white pan bread was determined to be 9%.

• Applied Chemistry for Engineering
• /
• v.7 no.5
• /
• pp.877-887
• /
• 1996

The ideal membranes for membrane-covered oxygen probes system should be selectively permeable for oxygen and chemically inert, and have good mechanical strength. Polysulfone(PSf) was selected to develop the membrane for membrane-covered oxygen electrodes system. PSf membranes have properties such as good reproducibility, good mechanical strength, chemical inertness, and high heat resistance. PSf membranes were cast from polymer solution on the glass plate at constant temperature, and casting solvents used were tetrahydrofuran(THF), methylene chloride, and N-methyl-2-pyrrolidone(NMP). Tricresyl phosphate(TCP) as plasicizer was added to PSf to increase the softness of membrane. The permeation characteristics were observed for pure oxygen and nitrogen through pure PSf membranes by variable volume method and membrane-covered electrode system. The permeability coefficients of oxygen and nitrogen measured by variable volume method were slightly decreased with increasing of upstream pressure. The permeation properties of PSf membrane using methylene choride as casting solvent were not affected by the PSf amount of polymer solution. The permeability coefficients of oxygen and nitrogen for PSf membrane containing TCP were very slightly lower than those for pure PSf membrane, but ideal separation factors were slightly higher. The flexibility of PSf membrane containing 2wt% TCP was better than that of pure PSf membrane. It was expected that this increase in flexibility would solve the difficulty of fixing the membrane to the cathode. The membrane-covered oxygen probes system was composed of anode, cathode and electrolyte. The type of the anode was Ag/AgCl half-cell, that of cathode was Ag, and the electrolyte was 4N KCl solution. The result of sampled current voltametry for PSf membrane showed the plateu region at -0.3V~-1.0V. The correlation coefficient of oxygen partial pressure versus current for PSf membrane was relatively high, 0.99949. It was concluded that PSf membrane was the good candidate for the membrane-covered oxygen probes system.

• Journal of the Korean Magnetics Society
• /
• v.12 no.5
• /
• pp.184-188
• /
• 2002

The Cu/Ni/Cu(002)/Si(100) films which have perpendicular magnetic anisotropy were deposited by e-beam evaporation methods. From the reflection high energy electron diffraction pattern, the films were confirmed to be grown epitaxially on silicon. After 2X lots ions/$\textrm{cm}^2$ C+ irradiation, magnetic easy-axis was changed from surface normal to in-plane as shown in the hysteresis loop of magneto-optical Kerr effects. It became manifest from analysis of X-ray reflectivity and grazing incident X-ray diffraction that even though interface between top Cu layer and Ni layer became rougher, the contrast of Cu and Ni's electron density became manifest after ion irradiation. In addition, the strain after deposition of the films was relaxed after ion irradiation. Strain relaxation related with change of magnetic properties and mechanism of intermixed layer's formation was explained by thermo-chemical driving force due to elastic and inelastic collision of ions.

• Journal of the Korean GEO-environmental Society
• /
• v.21 no.12
• /
• pp.35-41
• /
• 2020

Recently, underground spaces have been developed variously due to the concentration of the building structure in downtown area and reconstruction of the apartment. However, various problems such as differential settlement are occurring in the waterproof and reinforcement construction. In grouting method, which is frequently used for the ground reinforcement, quality control was performed by measuring the injection quantity of grouting materials and performing laboratory tests using boring samples, but it is difficult to determine whether the ground reinforcement has been performed properly during the construction stage. In order to solve this problem, a research is needed to carry out quality control by measuring electric resistivity after grouting is performed using grouting materials mixed with conductive materials. In this research, as a basic study of the new grouting method using conductive materials, uniaxial compression tests were performed using cement specimen with 0, 3, 5, 7% of carbon fiber to evaluate the effect of conductive material on the performance of grouting material. Based on the test results, the uniaxial compressive strength is increased with the mixed proportion of the carbon fiber increase. Furthermore, the carbon fiber can also affect on the early-strength of the grouting materials.

• Proceedings of the Korean Quaternary Association Conference
• /
• 2004.06a
• /
• pp.46-46
• /
• 2004

Van Mijenfjorden은 스발바드 군도의 Spitsbergen 서부에 위치하는 두 번째로 큰 피오르드로 온난하고 염분도가 높은 북대서양의 표층수가 북극해로 유입되는 Gateway에 위치하기 때문에 전지구적이며 지역적인 기후변화의 영향을 받는 지역이다. 1999년 IMAGES 프로그램의 일환으로 프랑스 탐사선인 'R/V Marion Dufresne'을 이용하여 북극해의 스발바드 군도에 위치하는 Van Mijenfjorden (77$^{\circ}$ 46.87'N and 15$^{\circ}$ 17.81'E)에서 약 18m의 빙ㆍ해양 퇴적물 코아(MD99-2305)를 시추하여 마지막 최대 빙하기 이후의 고환경변화를 연구하였다. AMS 14C 연대 측정에 의하면 diamicton 층인 하부 2m를 제외한 16m의 퇴적층은 지난 12cal. ka BP경에 피오르드에 존재하던 조수빙하(tidewater glacier)가 해빙되기 시작한 이후에 퇴적되었다. 특히 유기지화학 자료와 부유성과 저서성 유공충의 산출양상 그리고 저서성 유공충인 C. reniforme의 산소ㆍ탄소 안정동위원소 비에 의하면 코아 MD99-2305에는 Van Mijenfjorden에서 홀로세 동안에 일어난 퇴적환경변화를 잘 기록하고 있다. 특히 홀로세 동안에 피오르드내의 퇴적환경 변화는 조수빙하의 확장과 후퇴와 밀접한 관계가 있으며, 유기물의 탄소동위원소(13Corg) 비는 -24에서 -22$\textperthousand$ 값의 변화를 보인다. 이는 Van Mijenfjorden 퇴적물에 공급된 유기물은 육상과 해양기원이 혼합되어 퇴적되었음을 지시한다. 지난 12 cal. ka BP 이후 13Corg 값이 뚜렷하게 변하는 것은 Van Mijenfiorden에서 조수빙하의 변동과 표층수에서의 생산력의 변화를 강하게 반영한다. 강하게 반영한다.53%가 이공계 출신, 100대 기업 CEO의 38.4%가 이공계 출신, 대입수능시험에서 자연계 지원비율이 감소 -40.1%('99)\$\longrightarrow$34.7%('00)\$\longrightarrow$29.4%('01)\$\longrightarrow$26.9%('02)\$\longrightarrow$30.3%('03)\$\longrightarrow$31.5%\$\longrightarrow$'04)필요성, 효과적인 운전자 교육 정책 등이 그것이다. 자동차 긴급 피난 차선은 유용한 시설로 여러곳에서 그 기능이 발휘되고 있으므로 많은 고속도로 관계자들은 설계, 시공 및 유지 관리 측면에서 유의해야 할 것이다.미세조직을 광학현미경으로 압출방향에 평행한 방향과 수직방향으로 관찰하였고, 열간 압출재 이방성을 검토하기 위하여 X선 회절분석을 실실하여 결정방위를 확인하였다. 전기 비저항 및 Seebeck 계수 측정을 위하여 각각 2$\times$2$\times$10$mm^3$ 그리고 5$\times$5$\times$10TEX>$mm^3$ 크기의 시편을 준비하였다.준비하였다.전류를 구성하는 주요 입자의 에너지 영역(75~l13keV)에서 가장 높은(0.80) 상관계수를 기록했다. 넷째, 회복기 중에 일어나는 입자들의 유입은 자기폭풍의 지속시간을 연장시키는 경향을 보이며 큰 자기폭풍일수록 현저했다. 주상에서 관측된 이러한 특성은 서브스톰 확장기 활동이 자기폭풍의 발달과 밀접한 관계가 있음을 시사한다.se that were all low in two aspects, named "the Nonsignificant group". And the issues were

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.47 no.11
• /
• pp.1-5
• /
• 2010

We developed a novel micro-electro mechanical systems (MEMS) test socket using silicon on insulator (SOI) substrate with the cantilever array structure. We designed the round shaped cantilevers with the maximum length of $350{\mu}m$, the maximum width of $200{\mu}m$ and the thickness of $10{\mu}m$ for $650{\mu}m$ pitch for 8 mm x 8 mm area and 121 balls square ball grid array (BGA) packages. The MEMS test socket was fabricated by MEMS technology using metal lift off process and deep reactive ion etching (DRIE) silicon etcher and so on. The MEMS test socket has a simple structure, low production cost, fine pitch, high pin count and rapid prototyping. We verified the performances of the MEMS test sockets such as deflection as a function of the applied force, path resistance between the cantilever and the metal pad and the contact resistance. Fabricated cantilever has 1.3 gf (gram force) at $90{\mu}m$ deflection. Total path resistance was less than $17{\Omega}$. The contact resistance was approximately from 0.7 to $0.75{\Omega}$ for all cantilevers. Therefore the test socket is suitable for BGA integrated circuit (IC) packages tests.