• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.219-222
• /
• 2003

$0.2(PbMg_{1/3}Nb_{2/3}O_3)-0.8(PbZr_{0.475}Ti_{0.525}O_3)$ 조성을 이용하여 $5{\times}5{\times}5mm^3$의 적층형 세라믹 액츄에이터 소자를 tape casting 방법으로 제작하였다. 전극재로서는 Ag-Pd를 이용하여 총 50층의 layer를 적층하였으며, 적층된 액츄에이터를 $1100^{\circ}C$의 온도에서 소결하였다. X-ray diffractometer를 이용하여 제작된 소자와 열화된 소자의 구조적인 특성을 분석하였다. 제작된 소자의 열화 특성을 알아보기 위하여 60 Hz 의 triangular wave를 인가하여 열화전과 후의 p-E hystcresis loop의 변화를 살펴보았으며, 인가된 전압의 변화에 따라서 소자에서 발생되는 양의 열을 측정하였다. 파괴된 소자의 파단면에 대한 SEM 분석을 통하여 소자의 파괴 메카니즘을 알아보도록 하였다. 이로부터 전기적 기계적 열화가 소자의 동작에 미치는 영향에 대해서 알아 보았다.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.33 no.4
• /
• pp.1665-1673
• /
• 2013

Recently, the interest and demand on free formed structure providing aesthetic value as well as functionality has been increasing. Formwork has numerous advantages such as high strength, convenience, accuracy and good quality of surface roughness. Nevertheless, it increases construction cost and period to build complex shapes. For these purpose, deposition construction systems such as Contour Crafting and Concrete Printing have been developed with active collaboration between university and industry by applying the rapid prototyping technology to the construction industry in USA and England. Since there has been no related research in Korea, the possibility of spin-off technology and its fusion cannot be expected. In this paper, design elements including mechanical system and control system related to automatic deposition construction system prototype for constructing a free curved structure without mold are described. As for an appropriate material for the system, fiber reinforced mortar was selected by experiments on compressive strength, fluidity, viscosity and setting time. By performing transfer and extrusion experiments, the possibility of the development of deposition construction system was demonstrated. Based on this research results, it is required to keep the automatic deposition construction system improve and extend it into the new application area in construction industry.

• Proceeding of KASS Symposium
• /
• 2008.05a
• /
• pp.74-79
• /
• 2008

In this study, impact transient responses of (Graphite/Epoxy) laminated composite subjected to low-velocity impact are investigated using a finite element method. Dynamic von-Karman plate equations considering large deflection of plate are modified to include the effect of transverse shear deformations as in Mindlin plate theory and also the rotary inertia effect is considered. The convergence of transient responses is used contact law established through the statical indentation test. We investigate displacements, contact forces and strains by thickness variation of various laminated composite. We compare and analyze each results.

• Journal of Aerospace System Engineering
• /
• v.17 no.2
• /
• pp.86-93
• /
• 2023

Pyrotechnic separation devices have been widely used as holding and release mechanism for deployable appendage. However, pyro-shock can cause temporal or permanent damage on shock sensitive components such as electronics, mechanism, and brittle components. This study proposed a low-stiffness blade based passive shock absorber using a multi-layered stiffener laminated with viscoelastic acrylic tapes for reducing transmitted pyro-shock upon explosion of pyrotechnic separation devices. The multi-layered structure with viscoelastic tape has high-damping characteristics to effectively secure structural integrity of low-stiffness blades under the launch environment. The design effectiveness was verified through a shock test by dropping a pendulum. The structural integrity of the shock absorber under a launch environment was evaluated through structural analysis under load conditions with a deployable payload.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2004.10a
• /
• pp.56-60
• /
• 2004

2단 또는 3단형으로 설계되고 있는 KSLV-I 발사체의 단연결부는 직경의 변화에 따라 원뿔대(Truncated cone) 구조물이 필요하다. 원뿔대형 구조물이 발사체의 외피일 경우에는 일반적인 실린더형 동체와는 다르게 공력에 의한 버페팅(buffeting)과 공력가열 등이 추가적인 설계인자로 고려되어야 한다. 복합재료 샌드위치 구조물은 외피의 굽힘 강성이 크고, 일체성형으로 실린더형 혹은 원뿔대형 구좁물을 쉽게 제작할 수 있어 단연결부에 적용되고 있다. 또한 위성어댑터(Payload Adapter)등에도 사용되어 우주발사체에는 매우 일반적인 구조물이다. 복합재료 샌드위치 구조물의 제작과 정적시험을 통하여 구조 특성을 알아보았다. 일체형 샌드위치 구조물의 효율을 높이기 위해서는 프레임과의 체결부를 효율적으로 설계하여야 하며 하중의 종류에 따라서 면재의 적층각도가 중요함을 알 수 있었다.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2017.05a
• /
• pp.529-530
• /
• 2017

Electrical coupling of monolithic 3D inverter(M3D-INV) consisting of Junctionless FET(JLFET) was investigated. Depending on the thickness of Inter Layer Dielectirc (ILD) between top and bottom JLFETs, $N_{gate}-N_{gate}$ capacitance and transconductance $g_m$ are changed by the gate voltage of bottom JLFET. Therefore, when using a stacked structure with the ILD below tens nm, AC electrical coupling between two transistors in M3D-INV should be considered.

• Korean Journal of Materials Research
• /
• v.11 no.6
• /
• pp.448-452
• /
• 2001

The ZnS:Cu,Cl thick film electroluminescent devices with the stacking type(separated with phosphors and insulator layers) and the composite type (mixed with phosphor and insulator materials) emission layers were fabricated on ITO/glass substrates by the screen printing methods. The opical and electrical properties were investigated as fundations of applied voltages and frequencies. In the stacking type, the luminance was about 58 cd/$\m^2$ at the applied voltage of 400Hz, 200V and increased to 420 cd/$\m^2$ with increasing the frequency to 30Hz. For the composite type devices, the threshold voltage was 45V and the maximum luminance was 670 cd/$\m^2$ at the driving condition of 200V, 30Hz. The value of luminance of the composite type device showed 1.5 times higher than that of stacking type device. The main emission peak was 512 nm of bluish-green color at 1Hz frequency below and shifted to 452 nm in the driving frequency over 5Hz showing the blue omission color. There were no distinct differences of the main emission peaks and color coordinate for both samples.

• Proceedings of the Korea Water Resources Association Conference
• /
• 2020.06a
• /
• pp.360-360
• /
• 2020

조립식 빗물침투형 저류블록은 우수유출 저감시설로, 황토 및 친환경 무기질 결합재를 이용하여 제작한 고강도 투수성 블록의 적층 및 요철에 의한 끼움식 조립에 의해 형성된 공간에 빗물을 저류하고, 저장된 빗물은 시간이 지남에 따라 지반으로 침투시키는 우수유출 저감용 빗물관리시설로, 집중강우 시 유출수가 발생하는 해당지역에 분산식으로 설치하여 국지적 호우 발생에 대처할 수 있으며, 지속적인 침투를 통한 지하수위 확보 및 가뭄현상의 저감은 물론, 미기후 조성과 건전한 물순환 구조 형성에 이바지하는 빗물관리기술이다. 본 기술은 집중형 대규모 빗물저류조의 적용상의 문제점과 단순저류의 한계성을 극복하고, 기존 침투시설의 낮은 침투능을 증대시키고자 저류기능과 침투기능을 동시에 확보하여 집중호우시 빠른 침투저류능을 향상시킨 조립식 빗물침투형 저류시설이다. 보다 구체적으로는 집중강우에 대한 방재적 측면과 함께 가뭄으로 발생하는 지하수위 저하 등에 친환경적으로 대응하기 위한 복합적인 빗물관리 기술로서, 빗물 유출저감과 함께 물순환 회복 및 저영향개발을 위한 각 지자체의 지침과도 부합될 수 있다. 또한, 콘크리트 제품의 환경적 문제점과 플라스틱 제품의 낮은 물성을 극복하였고, 시공 시에는 보다 현장상황에 맞게 가변적 형태로 적용이 가능한 단순조립 적층공법으로 공기단축에 탁월한 장점이 있으며, 유지관리 시에는 별도의 동력이 요구되지 않는 형태로 개발하였다. 조립식 빗물침투저류블록의 구조체를 이루는 단위 블록유닛은 투수성 소재로 제작되며, 상하부가 개방되어 있고 사각형의 내부에 힘을 받는 격벽과 전후벽이 상호 대응되는 요철로 형성되어 있으며, 단위블록 유닛 다수개가 수직수평으로 연속적으로 조립되어 규모의 제한, 형태의 제한이 없는 구조물 형성이 가능하다. 본 구조체의 저류공극율은 80%이상 확보 가능하며, 또한 블록자체의 투수율이 0.83mm/sec로서 순모래나 순자갈의 포화투수계수보다 투수율이 높아 침투저류 효율성이 높으며 시공 후 상부 토지는 자유롭게 활용 가능하다. 본 조립식 빗물 침투형 저류블록을 이용하여 저영향개발 계획, 우수유출 저감대책 수립, 빗물관리시설 계획시 기존의 시설들에 비하여 경제적, 효율적인 설계가 가능하다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.129-129
• /
• 2010

적외선 검출소자(Infrared Photodetector)는 근적외선에서 원적외선 영역에 이르는 광범위한 파장 범위의 적외선을 이용하는 기기로서 대상물이 방사하는 적외선 영역의 에너지를 흡수하여 이를 영상화할 수 있는 장비이다. 적외선 관련 기술은 2차 세계대전 기간에 태동하였으며, 현재에는 원거리 감지기술 등과 접목되면서 그 활용 분야가 다양해지고 있다. 특히 능동형 정밀 타격무기를 비롯한 감시 정찰 장비 및 지능형 전투 장비 시스템 등에 대한 요구를 바탕으로 보다 정밀하고 신속한 표적 감지 및 정보처리 기술에 관한 연구가 선진국을 통해서 활발히 진행되고 있다. 기존의 Bolometer 형식의 열 감지 소자는 반응 속도가 느리고 측정 감도가 낮은 단점이 있으며, MCT(HgCdTe)를 이용한 적외선 검출기의 경우 높은 기계적 결함과 77K 저온에서 동작해야하기 때문에 발생하는 추가 비용 등이 문제점으로 지적되고 있다[1]. 이에 반해 화합물 반도체 자기조립 양자점(self-assembled quantum dot)을 이용한 적외선 수광소자는 양자점이 가지는 불연속적인 내부 에너지 준위로 인하여, 높은 내부 양자 효율과 온도 안정성을 기대할 수 있으며, 고성능, 고속처리, 저소비전력 및 저소음의 실현이 가능하다. 본 연구에서는 적층 InAs/InGaAs dot-in-a-well 구조를 유기금속화학기상증착법을 이용하여 성장하고 이를 소자에 응용하였다. 균일한 적층 양자점의 성장을 위해서 원자현미경(atomic force microscopy)을 이용하여, 각 층의 양자점의 크기와 밀도를 관찰하였고, photoluminescence (PL)를 이용하여 발광특성을 연구하였다. 각 층간의 GaAs space layer의 두께와 온도 조절 과정을 조절함으로써 균일한 적층 양자점 구조를 얻을 수 있었다. 이를 이용하여 양자점의 전도대 내부의 에너지 준위간 천이(intersubband transition)를 이용하는 n-type GaAs/intrinsic InAs 양자점/n-type GaAs 구조의 양자점 적외선수광소자 구조를 성장하였다. 이 과정에서 상부 n-type GaAs의 성장 온도가 600도 이상이 되는 경우 발광효율이 급격히 감소하고, 암전류가 크게 증가하는 것을 관찰하였다. 이는 InAs 양자점과 주변 GaAs 간의 열에 의한 상호 확산에 의하여 양자점의 전자 구속 효과를 저해하는 것으로 설명된다.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.62.2-62.2
• /
• 2010

박막 실리콘 태양 전지는 저가격화 및 대량생산, 대면적화에 유리하다는 장점을 가지고 있다. 단점으로 지적되는 낮은 효율을 극복하기 위해 광흡수층의 밴드갭이 서로 다른 두 개 이상의 박막을 적층하여, 넓은 파장 대역의 빛을 효과적으로 흡수함으로써 광변환 효율을 올리기 위한 많은 연구가 이루어지고 있다. 서로 다른 밴드갭의 광흡수층을 가진 p-i-n 구조를 다중 적층하여 고효율의 태양 전지를 제작하기 위해서는 n-도핑층과, p-도핑층 간에 전자와 정공이 빠르게 재결합할 수 있는 터널 접합(Tunnel Recombination Junction)의 형성이 필수적이며, 이때 광손실이 최소화되도록 해야한다. 만약 터널 접합이 적절하게 형성되지 않으면 결합되지 않은 전자와 정공이 도핑층 사이에 쌓이게 되고, 도핑층 사이의 저항 증가로 태양 전지의 광변환 효율은 크게 하락한다. 이번 연구에서는 터널 접합이 잘 이루어지게 하기 위한 n-도핑층 및 p-도핑층 박막의 특성과, 터널 접합의 특성에 따른 적층형 태양 전지의 광효율 변화를 확인하였다. 광흡수층 및 도핑층은 TCO($SnO_2:F$, Asahi) 유리 기판 위에 PECVD를 사용하여 p-i-n 구조로 RF Power 조건에서 증착되었고, ${\mu}c$-Si 광흡수층의 경우에는 VHF Power 조건에서 증착되었다. 광흡수층이 a-Si/${\mu}c$-Si의 구조를 가지는 이중 접합 태양 전지에서 ${\mu}c$-Si n-도핑층/${\mu}c$-Si p-도핑층 사이의 터널 접합 실험 결과 n-도핑층 및 p-도핑층의 결정화도와 도핑 농도를 조절하여 터널 접합의 저항을 최소화했고, 터널 접합 특성이 이중 접합 셀의 광효율 특성과 유사한 경향을 보임을 확인하였다. 광흡수층이 a-Si/a-SiGe/${\mu}c$-Si의 구조를 가지는 삼중 접합 태양 전지 실험의 경우 a-Si과 a-SiGe 광흡수층 사이에 ${\mu}c$-Si n-도핑층/${\mu}c$-Si p-도핑층/a-SiC p-도핑층의 구조를 적용하여 터널 접합을 형성하였으며, ${\mu}c$-Si p-도핑층의 두께 및 박막 특성을 개선하여 광손실이 최소화된 터널 접합을 구현하였고, 삼중 접합 태양 전지에 적용되었다.