• Analytical Science and Technology
• /
• v.10 no.1
• /
• pp.18-30
• /
• 1997

Na, TPA-ZSM-5 with Si / Al mole ratio of about 130 was synthesized at low temperature and atmospheric pressure. These intermediate products were characterized by using XRD, XRF, FT-IR, NMR, and SEM. As a result, intermediate product were different from those that synthesized by autoclave method but spectroscopic characteristics of the final products showed to be in the typical ZSM-5 region. The defect sites were observed in the final product and removed by calcination at $540^{\circ}C$. Na, TPA-ZSM-5, aboveall, was synthesized at this condition within 48hr.

• Proceedings of the Korean Environmental Sciences Society Conference
• /
• 2001.11a
• /
• pp.46-47
• /
• 2001

황을 포함하는 촉매는 황을 포함하지 않은 촉매보다 저온영역에서 상대적으로 우수한 활성을 갖는 것으로 관찰하였다. $V_2$$O_{5}$가 담지된 촉매는 황에 인해 표면에 polymeric vanadate가 형성되었기 때문인 것으로 확인되어 polymeric vanadate가 탈질제거 활성에 유리한 활성점으로 확인되었다. 또한 활성저하 실험에서 반응온도의 영향이 큰 것으로 확인되었는데 $300^{\circ}C$이상의 반응온도에서는 생성된 염이 제거되는 온도영역이므로 염의 생성으로 인한 활성 저하는 확인 할 수 없다. 그러므로 $300^{\circ}C$이상의 반응온도에서는 활성저하가 관찰되지 않아 본 연구에서 제조된 촉매는 $300^{\circ}C$이상의 온도에서 조업되는 것이 바람직하다.

• Electrical & Electronic Materials
• /
• v.2 no.2
• /
• pp.103-108
• /
• 1989

새로운 전도성물질 중간체 합성기술의 기초연구의 일환으로 N, N-dialkylbenzamide를 ether 용액에서 lithiation 및 carboxylation시킨 결과, 저온 (-78.deg.~-20.deg.), 짧은 반응 시간에서는 방향족 고리 Ortho-위치에 carboxylation이 일어났고 상대적 고온 (0.deg.이상)에서는 아미드의 카보닐에 치환된 ketone이 얻어졌다. 이는 온도 조건에 따라 두 반응이 상호 경쟁적으로 진행되기 때문이라고 사료된다.

• Proceedings of the Korea Air Pollution Research Association Conference
• /
• 2002.11a
• /
• pp.449-450
• /
• 2002

DBD (Dielectric Barrier Discharge)를 사용한 저온 플라즈마 기술은 오래 전부터 효과적인 오조나이저로서 연구되고 있으며 현재에는 반응기를 이용한 NOx와 SOx, VOCs 와 같은 유해 가스를 분해, 제거에 관한 많은 연구가 진행되고 있다. 그러나 DBD 반응기내의 높은 전자 밀도와 에너지를 이용하여 입자를 대전시켜 전기 집진기 등을 이용하여 제거하는, 입자상 물질 처리에 관한 연구는 아직까지 미흡하다. (중략)

• Clean Technology
• /
• v.19 no.3
• /
• pp.306-312
• /
• 2013

We investigated the effects of the concentration of carbon dioxide on the char-$CO_2$ gasification reaction under isothermal conditions of $850^{\circ}C$ using the Drayton coal. Potassium carbonate was used to improve the low-temperature gasification reactivity. The enhancement of carbon dioxide concentration increased the gasification rate of char, while gasification rate reached a saturated value at the concentration of 70%. The best $CO_2$ concentration for gasification is determined to be 70%. We compared the shrinking core model (SCM), volumetric reaction model (VRM) and modified volumetric reaction model (MVRM) of the gas-solid reaction models. The correlation coefficient values, by linear regression, of SCM are higher than that of VRM at low concentration. While the correlation coefficients values of VRM are higher than that of SCM at high concentration. The correlation coefficient values of MVRM are the highest than other models at all concentration.

• Applied Chemistry for Engineering
• /
• v.4 no.1
• /
• pp.82-93
• /
• 1993

To extract the tungsten component from the scheelite by the chlorination process, effects of major variables such as the reducing agent, reaction temperature, reaction time, flow rate of the $Cl_2$ gas, and the particle size of the sample, were examined in the batch-boat system. The optimum conditions for this chlorination process were as follows ; reaction temperature above $700^{\circ}C$, carbon weight ratio to the scheelite 0.08, reaction time 20 min, flow rate of the $Cl_2$ gas $0.6{\ell}/min$, particle size of scheelite ore -200 mesh. Under the above conditions, 99% of tungsten component was extracted from scheelite ore. The diffusion step and chemical reaction step were the rate-determining steps at high and low temperature, respectively. Activation energy was 7.98kcal/mol at high temperature region and 31.2kcal/mol at low temperature one.

• Proceedings of the Korea Air Pollution Research Association Conference
• /
• 2000.04a
• /
• pp.233-234
• /
• 2000

저온 플라즈마 탈황탈질 동시처리 공정은 경제적인 장점과 함께 2차 오염물 발생 없이 비료성분을 부산물로 얻을 수 있다는 이점 때문에 국내외적으로 많은 연구가 진행되고 있다 이와 같은 저온 플라즈마 공정은 크게 가스상 물질을 제거하기 위한 플라즈마 반응 공정과 가스상 물질 제거이후 발생하는 고형화된 부산물 제거를 위한 부수 공정으로 구분할 수 있는데, 지금까지의 연구분야는 가스상 오염물질을 제거하는 공정에 초점이 모아져 왔다. (중략)

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.05a
• /
• pp.106-106
• /
• 2009

저온에서 CNT를 Thermal CVD방법을 이용하여 성장시켰다. 균일한 밀도와 크기의 CNT성장에 큰 역할을 하는 catalyst 형성제어를 위해 분산방법 및 catalyst의 종류를 달리하였다. 반응성가스의 유량 및 온도를 제어하여 수직방향으로 CNT를 성장시켰다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.107-108
• /
• 2013

플라스틱 기판 표면을 플라즈마 처리시 형성되는 수산화기에 실란화합물을 반응시키면 상온에서도 플라스틱 표면에 다양한 유기기를 도입할 수 있다. 아민기와 에폭시기가 상온에서도 강력한 화학결합을 이루는 원리를 이용하여, 유기기로써 아미노기와 에폭시기를 갖는 두 실란화합물을 선정, 두 고분자 기판에 각각 도입 후 접합시킨 결과, 저온 및 대기압 조건에서도 강력한 본딩을 이루는 것을 확인할 수 있었다.

• Electrical & Electronic Materials
• /
• v.6 no.2
• /
• pp.168-174
• /
• 1993

두가지 부분수산법, 즉 부분수산법(1)과 수정된 부분수산법에 의해 합성한 미분말을 사용하여 PZT 세라믹스를 저온소성하고 그 전기적 제특성을 조사하였다. 두가지 부분수산법에 의해 합성한 분말의 소결거동을 조사해본 결과 고상반응법보다 훨씬 낮은 소결온도인 950.deg.C에서도 단일상의 페로브스카이트상이 얻어지고 치밀화가 이루어졌을 뿐만 아니라 비유전율, 전기기계 결합계수, 압전정수 등 유전 및 압전특성이 고상반응법에 비해 손색이 없었다. 특히 두가지의 부분수산법에 의해 얻어진 PZT 세라믹스는 물리적 전기적 제특성이 서로 비슷하게 나타났으며 이 결과로부터 부분수산법(1)에서 수반되는 ZTO 분말을 따로 합성하는 공정이 불필요한 수정된 부분수산법이 편리함을 알았다.