• Resources Recycling
• /
• v.23 no.1
• /
• pp.48-57
• /
• 2014

In this study, we have investigated the influence of the nature of solvent on the grafting reaction of maleic anhydride onto polyethylene wax obtained as a by-product in a high density polyethylene plant. The results show that the grafting ratio in xylene as a solvent was higher than toluene. This is because xylene has excellent monomer solubility, swelling property and miscibility. It has been also observed that grafting degree shows an initial jump in percentage of grafting with increasing amount of solvent, from 0% v/w to 200% v/w giving maximum grafting in 200% v/w and then slightly decreases on further increase in the amount of solvent and becomes almost constant. It can be also seen that gel content was not formed under the use of solvent. It means that solvent prevented cross-linking reaction due to chain transfer reactions to solvent molecules. Studies of melt viscosity at $140^{\circ}C$ showed that viscosity increased after grafting of maleic anhydride onto polyethylene wax.

• The Journal of Korean Academy of Prosthodontics
• /
• v.50 no.2
• /
• pp.112-118
• /
• 2012

Purpose: The purpose of this study was to evaluate the difference in shear bonding strength between resin cements to dental materials when a universal primer (Monobond plus) was applied in place of a conventional primer. Materials and methods: Four groups of testing materials: gold alloy (Argedent Euro, n = 16), non precious metal (T-4, n = 20), zirconia (Cercon, n = 20) and glass ceramic (IPS e.max press, n = 20), were fabricated into discs, which were embedded in an acrylic resin matrix. The gold alloy specimens were airborne-particle abraded, 8 of the specimens were coated with Metal primer II, while the remaining 8 specimens were coated with Monobond plus. The non precious and zirconia specimen were airborne-particle abraded then, the control group received Alloy primer coating, while the other was coated with Monobond plus. Glass ceramic specimens were etched. 10 specimens were coated with Monobond-S and the remaining specimens were coated using Monobond plus. On top of the surface, Multilink N was polymerized in a disc shape. All of the specimens were thermal cycled before the shear bonding strength was measured. Statistical analysis was done with Two sample $t$-test or Mann-Whitney U test (${\alpha}$=.05). Results: There were no significant differences in bonding strength depending on the type of primer used in the gold alloy and glass ceramic groups ($P$>.05), however, the bonding strengths of resin cements to non precious metal and zirconia groups, were significantly higher when the alloy primer was used ($P$<.05). Conclusion: Within the limitations of this study, improvement of universal primers which can be applied to all types of restorations is recommended to precious metals and zirconia ceramics. But, the bond strengths of non precious metals and zirconia ceramics were significantly lower when compared to a 10-MDP primer. More research is needed to apply universal primers to all types of restorations.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.46 no.2
• /
• pp.165-172
• /
• 2019

The purpose of this study was to evaluate the effect of application time and phosphoric acid etching of 8th generation adhesives containing functional monomer on adhesive performance in primary teeth. 80 extracted non-carious human primary teeth were selected and divided into 8 groups based on 3 factors: (1) adhesive: G-Premio bond and Single bond universal; (2) application time: shortened time and manufacture's instruction; (3) acid etching mode: self-etching and total-etching. Shear bond strength was measured using a universal testing machine, and fractured surface were observed under scanning electron microscope. Microleakage was evaluated by dye penetration depth. G-Premio bond were not significant different in shear bond strength and microleakage depending on application time of adhesive and acid etching mode. In Single bond universal, shear bond strength of short application time was significantly lower than that of long adhesive application time (p = 0.014). Clinically applicable shear bond strength values (> 17 MPa) were identified in all groups. These results suggested that G-Premio bond be used clinically for a short application time without phosphoric acid etching.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.12
• /
• pp.482-487
• /
• 2016

Ultra-violet rays are very harmful to eye health care. The blocking of ultra-violet rays and a reduction of optical reflection in the visible light range, which is to increase the share of transmitted light, and avoid the formation of ghost images in imaging, are important for the applications of polymer eyeglasses lenses. In this study, the high-refractive index polymer lenses, n=1.67, were fabricated by injection-molded method with the xylene diisocyanate monomer, 2,3-bis-1-propanethiol monomer, and benzotriazol UV absorber (SEESORB 709) mixture. To reduce the reflection of the polymer lens surfaces, multi-layer anti-reflection (AR) coatings were coated for both sides of the polymer lens using an E-beam evaporation system. The optical properties of the UV blocking polymer lens were characterized using a UV-visible spectrometer. The material properties of the thin films, which were composed AR coating layers, refractive index, and surface roughness, were analyzed by ellipsometry and atomic force microscopy. As a result, the fabricated polymer lens perfectly blocked ultra-violet rays below 395 nm with a blocking rate greater than 99%.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.12
• /
• pp.10-15
• /
• 2020

Ultraviolet rays, which have wavelengths smaller than 400 nm, are very harmful to the eyes. Recently, high-energy visible light was also revealed to be harmful to retinal cells. Therefore, polymer eyeglass lenses that can block UV and high-energy visible light are needed for eye health. In this study, high-refractive-index polymer eyeglass lens, n=1.67, were manufactured using the injection-mold method with the m-xylene diisocyanate monomer, 2,3-bis((2-mercaptoethyl)thio)-1-propanethiol monomer, benzotriazole UV absorber, release of alkyl phosphoric ester, dye mixture of CI solvent violet 13, and catalyst of dibutyltin dichloride mixture. A multi-layer anti-reflection coating was applied to manufactured polymer eyeglass lenses for both sides using an E-beam evaporation system. The optical properties of the manufactured lenses with the UV and high-energy visible light-blocking function were analyzed by UV-visible spectrophotometry. As a result, the polymer eyeglass lens with a UV absorber of 0.5 wt. % blocked 99% of UV and high-energy visible light shorter than 411 nm. The average transmittance of the polymer eyeglass lens with a UV absorber of 0.5wt.% was 97.9% in the range of 460 ~ 660 nm for photopic eye sensitivity higher than 10%. Therefore, clear image acquisition in photopic vision is possible.

• Applied Chemistry for Engineering
• /
• v.28 no.1
• /
• pp.73-79
• /
• 2017

Maleic anhydride (MAH) grafted polypropylene (PP-g-MAH) copolymers were prepared by changing MAH and styrene monomer (SM) content, using a twin screw extruder at $190^{\circ}C$. The grafting degree was measured by non-aqueous back titration method. The grafting degree of PP-g-MAH-SM copolymer was higher than that of PP-g-MAH at the same MAH content. PP-g-MAH-SM/kenaf fiber (KF) composites were also prepared by using a PP-g-MAH as a matrix at $200^{\circ}C$ and the KF content was fixed at 20 wt%. Based on the degradation temperature investigated by TGA, the thermal stability of PP-g-MAH-SM/KF composites was more enhanced than that of PP-g-MAH only. Mechanical properties of the composites were also improved when MAH and SM applied together. The adhesion degree between the copolymer and KF was confirmed by both SEM pictures of the fractured surface and contact angles.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.1
• /
• pp.216-221
• /
• 2017

Reducing optical reflection in the visible light range, in order to increase the share of transmitted light and avoid the formation of ghost images in imaging, is important for polymer lens applications. In this study, polymer lenses with refractive indices of n=1.56, 1.60, and 1.67 were fabricated by the injection-molding method with a polymer lens monomer, dibutyltin dichloride as the catalyst and an alkyl phosphoric ester as the release agent. To investigate their anti-reflection (AR) effects, various AR coating structures, viz. a multi-layer AR coating structure, tri-layer AR coating structure with a discrete approximation Gaussian gradient-index profile, and tri-layer AR coating structure with a quarter-wavelength approximation, were designed and coated on the polymer lens by an E-beam evaporation system. The optical properties of the polymer lenses were characterized by UV-visible spectrometry. The material properties of the thin films, refractive index and surface roughness, were analyzed by ellipsometry and AFM, respectively. The most effective AR coating structure of the polymer lens with low refractive index, n=1.56, was the both side coating of multi-layer AR coating structure. However, both side coating of the tri-layered discrete approximation Gaussian gradient-index profile AR coating structure gave comparable results to the both side coating of the multi-layer AR coating structure for the polymer lens with a high refractive index of n=1.67.

• The Journal of Korean Academy of Prosthodontics
• /
• v.53 no.4
• /
• pp.295-300
• /
• 2015

Purpose: The aim of this study was to evaluate the shear bond strength between Ni-Cr alloy and composite resin using universal adhesive systems coMPared to conventional method using metal primers. Materials and methods: For this study, a total of 120 cast commercial Ni-Cr alloy (Vera Bond 2V) disks were embedded in acrylic resin, and their surfaces were smoothed with silicon carbide papers and airborne-particle abrasion. Specimens of each metal were divided into 6 groups based on the combination of metal primers (Metal primer II, Alloy primer, Metal & Zirconia primer, MKZ primer) and universal adhesive systems (Single Bond Universal, All Bond Universal). All specimens were stored in distilled water at $37^{\circ}C$ for 24 hours. Shear bond strength testing was performed with a universal testing machine at a cross head speed of 1 m/min. Data (MPa) were analyzed using one-way ANOVA and the post hoc Tukey's multiple comparison test (${\alpha}$=.05). Results: There were significant differences between Single Bond Universal, All Bond Universal, Metal Primer II and Alloy Primer, MKZ Primer, Metal & Zirconia Primer (P<.001). Conclusion: Universal Adhesive system groups indicated high shear bond strength value bonded to Ni-Cr alloy than that of conventional system groups using primers except Metal Primer II. Within the limitations of this study, improvement of universal adhesive systems which can be applied to all types of restorations is recommended especially non-precious metal alloy. More research is needed to evaluate the effect of silane inclusion or exclusion in universal adhesive systems.