• Polymer(Korea)
• /
• v.30 no.4
• /
• pp.298-304
• /
• 2006

Blends of poly (acrylic acid-co-maleic acid)(PAM) with poly (vinyl alcohol)(PVA) were obtained by solution blending. The blends were solvent-on to a film to examine thermo-mechanical properties and gas permeability. The transition temperatures $(T_g\;and\;T_m)$ of the blends remained constant regardless of PAM contents. However, the values of enthalpy changes corresponding to melting transition $({\Delta}H_m)$ and initial degradation temperature $({T_D}^i)$ were decreased with increasing PAM content. The values of ultimate strength and initial modulus gave the maximum value at the 12 wt% PAM then decreased with further increase of PAM content up to 15 wt%. To measure the gas permeability of the PVA/PAM blend films, the PVA blend solutions were coated onto both biaxially oriented propylene (BOPP) and poly (ethylene terephthalate)(PET) films. The oxygen transmission rate $(O_2\;TR)$ permeability values mono- tonically decreased with increasing PAM content. However, moisture vapor transmission rate was not affected by PAM content.

• Polymer(Korea)
• /
• v.31 no.4
• /
• pp.283-288
• /
• 2007

Polymer blends containing poly(acrylonitrile-butadiene-styrene) (ABS) and polycarbonate(PC) (70/30, wt%) with compatibilizer were prepared using twin screw extruder. Compatibilizers were prepared by reactive extrusion with the ABS, maleic anhydride(MAH) and dicumyl peroxide(DCP) using twin screw extruder In the ABS/PC (70/30) blends, tensile strength did not change significantly, but increased from 52.25 to 55.03 MPa when the ABS-g-MAH was added in the amount of 5 phr. From the results of rheological properties, storage modulus of the ABS/PC/ABS-g-MAH blends at low frequencies showed lager value than that of the ABS/PC(70/30) blend. From the results of the morphological properties of the ABS/PC(70/30) blend, it was observed that the drop size of the PC ranged from 1.2 to $1.5\;{\mu}m$ and did not change significantly with the addition of the ABS-g-MAH($1{\sim}10\;phr$). From the results of the storage modulus, complex viscosity, and tensile strength of the ABS/PC (70/30) blends, it is found that the ABS-g-MAH is an effective compatibilizer in the ABS/PC (70/30) blends when the ABS-g-MAH is added in the amount of 5 phr.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.235-235
• /
• 2003

The development of a buffer layer is an important issue for the second -generation wire, YBCO coated metal wire. The buffer layer demands not only on the prohibition of the reaction between YBCO and metal substrate, but also the proper lattice match and conductivity for high critical current density (Jc) of YBCO superconductor, In order to satisfy these demands, we suggested CaRuO3 as a useful candidate having that the lattice mismatches with Ni (200) and with YBCO are 8.2% and 8.0%, respectively. The CaRuO3 thin films were deposited on Ni substrates using various methods, such as e-beam evaporation and DC and RF magnetron sputtering. These films were investigated using SEM, XRD, pole-figure and AES. In e-beam evaporation, the deposition temperature of CaRuO3 was the most important since both hi-axial texturing and NiO formation between Ni and CaRuO3 depended on it. Also, the oxygen flow rate had i[n effect on the growth of CaRuO3 on Ni substrates. The optimal conditions of crystal growth and film uniformity were 400$^{\circ}C$, 50 ㎃ and 7 ㎸ when oxygen flow rate was 70∼100sccm In RF magnetron sputtering, CaRuO3 was deposited on Ni substrates with various conditions and annealing temperatures. As a result, the conductivity of CaRuO3 thin films was dependent on CaRuO3 layer thickness and fabrication temperature. We suggested the multi-step deposition, such as two-step deposition with different temperature, to prohibit the NiO formation and to control the hi-axial texture.

• Korean Journal of Food Science and Technology
• /
• v.23 no.1
• /
• pp.88-92
• /
• 1991

To analyze the effects of the system parameters on the target parameters, which include the amount of water evaporation, water solubility index(WSI) and water absorption index(WAI), test trials of fractional factorial design of the three process variables at three levels were carried out for corn grit with a laboratory twin-screw extruder with three different screw configurations. The system parameters collected from the trials, such as extrusion temperature, specific mechanical energy input(SME) and mean residence time(RT), were showed the ranges of $129{\sim}182^{\circ}C$, $67{\sim}163\;kwh/ton$ and $12{\sim}34\;sec$, respectively. Within these ranges of the system parameters, the target parameters were able to be quantified by using multiple regression equations. The correlation of results with the system parameters blocked by the screw configuration as dependent variables, yield correlation coefficients above 0.90, and the correlation using the system parameters obtained from whole experiment system as the dependent variables yield correlation coefficients around 0.80. The functional relationship, which can be quantified by second order polynomial regression equation with only two system parameters within necessary degree of accuracy, can he graped in three dimensional surface response and contour diagrams.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.6
• /
• pp.4039-4045
• /
• 2014

The crystallization behavior of irradiated polypropylene (PP) and the blend is an important parameter for polymer processing. Blends of PP/low density polyethylene (LDPE) with different LDPE contents were prepared by melt mixing in a twin screw extruder. The effect of the LDPE content on the irradiation effectiveness of the PP/LDPE blend with trimethylolpropane-trimetacrylate (TMPTMA) as a crosslinking co-agent was investigated in conjunction with the LDPE loading in the blend. The non-isothermal crystallization and crystal structure were measured by DSC, X-ray diffraction (XRD), and polarized optical microscopy (POM). A decrease in the melting temperature of PP was observed due to irradiation, which may be due to the PP chain scissioning effect of irradiation. The Ozawa component n represents a rod shaped, disc shaped and sphere-shaped geometry of the crystal if the value corresponds to 2, 3 and 4, respectively. Based on Ozawa analysis, the values of n were 3.8 and 2.3 for the pure PP and PP blends with 30 wt% LDPE, respectively. The fact that the crystal geometry of PP changed from spherical to disc and rod shaped was confirmed by Ozawa analysis and POM. The ${\beta}$ form XRD peak of the PP/LDPE blend at $16.1^{\circ}$ disappeared after irradiation due to the crosslinking reaction.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.6
• /
• pp.3990-3996
• /
• 2014

Because the physical properties can be decreased when a Nylon 66/glass fiber composite is injected into a mold over $300^{\circ}C$, a systematic study of the thermal history in the case of re-use is needed. Nylon 66/glass fiber extrudates as a function of the extrusion number were prepared using a twin screw extruder at 305/290/273/268/265/$260^{\circ}C$. The chemical structure, thermal properties, melt index, crystal structure, Izod impact strength, and rheological properties were measured by Fourier transform infra-red (FT-IR), melt indexer, DSC, TGA, XRD, Izod impact tester, and dynamic rheometer. The FT-IR spectra indicated that the number of extrusions did not affect the chemical structure. The decrease in molecular weight with increasing extrusion number was confirmed by the melt index and the complex viscosity of extrudates. Based on the DSC and TGA results, the thermal history had no effect on the melting temperature, regardless of the number of extrusions, but the degradation temperature decreased up to $20^{\circ}C$ with increasing extrusion number. The Izod impact strengths of the extrudates were found to decrease with increasing extrusion number. No structural change after extrusion was also confirmed because there was no change in the slope and shape of the G'-G" plot.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.28-29
• /
• 2006

The magnetic properties of a series of both annealed and as-rolled Ni-$W_y$ alloy tapes with compositions y = 0, 1, 3, and 5 at.%, were studied. To compare with Ni-W alloys, the magnetic properties of a series of both annealed and as-rolled $[Ni_{97at.%}W_{3at.%}]_{100-x}Cu_x$ alloy tapes with compositions x = 0, 1, 3, 5 and 7 at.%, were studied, as well. Both the isothermal mass magnetization M(H) of a series of samples, such as both Ni-W and [Ni-W]-Cu alloy tapes, at different fixed temperatures and M(T) in fixed field, were measured using a PPMS-9 (Quantum Design). The degree of ferromagnetism of Ni-$W_y$ alloys have reduced as W-content y increases. Both the saturation magnetization $M_{sat}$ and Curie temperature $T_c$ decrease linearly with W-content y, and both $M_{sat}$ and $T_c$ go to zero at critical concentration of $y_c$ ~ 9.50 at.% W. The effect of Cu addition on both the saturation magnetization $M_sat$ and Curie temperature $T_c$ decrease linearly with Cu-content x in $[Ni_{97at.%}W_{3at.%}]_{100-x}Cu_x$ alloy tapes with compositions x = 0, 1, 3, 5, and 7 at.%. The results confirm that [Ni-W]-Cu alloy tapes can have much reduced ferromagnetism as Cu-content x increases.

• Elastomers and Composites
• /
• v.46 no.4
• /
• pp.335-342
• /
• 2011

The virgin and recycled polyethylene composites with various ratio of fly ash were manufactured by using a fully intermeshing co-rotating twin screw extruder for the reuse of fly ash from power plant and post-consumed polyethylene. Fly ash were blended with virgin HDPE and recycled polyethylene at the weight fraction of 0 to 40 wt.%. Mechanical properties such as yield strength, abrasion resistance, and slow crack resistance were measured with ISO and ASTM standards. The experimental results for the various composites showed that the elongation at break and the yield stress of the composites decreased with increasing fly ash contents. Generally, the abrasion resistance of PEs decreased with increasing sandpaper grits but the abrasion resistance of the composites increased with fly ash content at finer abrasive surface. The slow crack growth resistance of virgin HDPE, recycled JRPE and the JRPE composite showed higher slow crack growth resistance up to 50% of load at notch depth of 20% and 30%, but KRPE and the KRPE composite showed much lower resistance than virgin HDPE, JRPE and the JRPE composite. Time to break, measured with NCLS test method, of all PEs and the composites satisfies the regulation of Korean Industrial Specification for sewer pipe and support application.

• Korean Journal of Food Science and Technology
• /
• v.31 no.4
• /
• pp.1011-1016
• /
• 1999

This study was performed to search a physical method having high yield and quality and minimum environmental pollution for extraction of pectin from apple pomace. Based on the physical solubilization of plant cell wall under the condition of high temperature, pressure and shearing stress, apple pomace was treated by a corotating intermeshing type twin-screw extruder with the diameter-to-length ratio of 1/20. The specific mechanical energy of extruder was introduced as system parameter for extrusion process modeling and the shaft speed, feed rate and moisture content as process variables. The yield, average molecular weight and galacturonic acid content of water-soluble polysaccharides obtained by extrusion were, respectively, modeled with the linear functions of the system parameter which was of the form as a linear function of process variables. The specific mechanical energy increased with increase of shaft speed and with decrease of feed rate and moisture content. Out of process variables, moisture content had the greatest effect on specific mechanical energy. The yield increased with increase of specific mechanical energy while the average molecular weight and galacturonic acid content increased with its decrease. In aspects of yield and quality of pectin, the results from this study showed the possibility to replace a traditional acidic method with the extrusion treatment of this study.

• Journal of the Korean Ceramic Society
• /
• v.40 no.8
• /
• pp.751-757
• /
• 2003

Rapid densification of a SiC-30 wt% TiC powder with additive 10 wt% A1$_2$O$_3$-Y$_2$O$_3$-CaO was conducted by Spark Plasma Sintering(SPS). The fully-densified materials can be obtain through the SPS process with very fast heating rate and short holding time. In the present work, the heating rate and applied pressure were kept to be $100^{\circ}C$/min and 40 MPa, while sintering temperature varied from $1600^{\circ}C$ to $1800^{\circ}C$ for 10 min. The full densification of SiC-30 wt% TiC composites with the addition of $Al_2$O$_3$, $Y_2$O$_3$ and CaO was achieved at the temperature above $1700^{\circ}C$ by spark plasma sintering. The XRD found that 3C-SiC and TiC were maintained the entire SPS process temperature, without phase transformation of SiC and formation of YAG phase to $1800^{\circ}C$. The microstructures of the rapidly densified SiC-30 wt% TiC composites consisted of smaller equiaxed SiC grains and larger TiC grains. The biaxial strength of 635.2 MPa and fracture toughness of 6.12 MPaㆍ$m^{1/2}$ were found for the specimen prepared at $1750^{\circ}C$.