In this paper, rapid solidified Mg-4.3Zn-0.7Y (at.%) alloy powders were prepared using an inert gas atomizer, followed by a severe plastic deformation technique of high pressure torsion (HPT) for consolidation of the powders. The gas atomized powders were almost spherical in shape, and grain size was as fine as less than $5\;{\mu}m$ due to rapid solidification. Plastic deformation responses during HPT were simulated using the finite element method, which shows in good agreement with the analytical solutions of a strain expression in torsion. Varying the HPT processing temperature from ambient to 473 K, the behavior of powder consolidation, matrix microstructural evolution and mechanical properties of the compacts was investigated. The gas atomized powders were deformed plastically as well as fully densified, resulting in effective grain size refinements and enhanced microhardness values.

• 한국재료학회지
• /
• 제9권3호
• /
• pp.263-268
• /
• 1999

본 연구에서는 Al-기지 복합재료의 새로운 개념과 in-situ 공정의 가능성을 Al-Ti계의 연구결과들을 토대로 제시하고자 하였다. 가스아토마이제이션법에의해 $Al_3Ti$가 미세한 편상형상을 갖도록 Al-10%Ti 조성의 합금분말을 제조하고, 고온 압출 공정을통하여 25V/o $Al_3Ti/Al $ 복합재를 제조하였다. 복합재의 미세구조를 광학현미경, SEM, TEM 등을 이용하여 조사하였고, 상온과 고온에서의 기계적 특성을 인장시험을 통하여 측정하였다. 제조된 복합재료의 미세구조 및 고온 기계적 성질을 상용되고 있는 $SiC_w/2124$ 복합재료와 유사한 거동을 보여준다. 제조된 $Al_3Ti/Al$ 복합재료의 장점과 단점이 물성향상의 가능성과 더불어 제시되었다.

• 대한금속재료학회지
• /
• 제50권12호
• /
• pp.897-905
• /
• 2012

Directional solidification experiments were carried out in a hypoeutectic Al-11.3Si-3.5Cu system to investigate the microstructural evolution with the solidification rate. At a fixed temperature gradient, a dendritic microstructure was observed at a constant speed of more than $25{\mu}ms^{-1}$, a cellular interface developed at $5{\mu}ms^{-1}$ and the growth rate of $0.5{\mu}ms^{-1}$ led to the stability of the planar interface. The results revealed that primary silicon phases formed among cells, even though the studied Al-Si alloy system formed the composition within a hypoeutectic silicon composition. This suggests that the liquid concentration among cells during solidification reached a higher concentration, i.e., the eutectic concentration. It is, however, interesting that primary silicon phases did not form during a dendritic growth of more than $25{\mu}ms^{-1}$. These experimental observations are explained using the theoretical models on the interface temperatures.

• 공업화학
• /
• 제26권1호
• /
• pp.53-58
• /
• 2015

3 phr의 그래핀 옥사이드(GO)를 포함하는 폴리카보네이트(PC)/GO를 클로로포름에서 용액 혼합하여 응고물 침전한 후 240, 260, $280^{\circ}C$의 이축압출기를 이용하여 PC/GO 복합체를 제조하였다. DSC와 TGA 측정결과 PC/GO 복합체의 유리전이 온도($T_g$)의 변화는 거의 없었고, 분해거동을 통해 확인한 열안정성의 경우 $260^{\circ}C$ 압출시편이 우수하게 나타났다. 동적기계적분석(DMA)을 이용한 저장탄성률 측정결과 PC 대비 PC/GO 복합체의 값이 크게 나타났으며 압출온도별로는 큰 차이가 없는 것을 확인하였다. 이들 결과로부터 환원시간에 따른 PC/RGO 복합체의 압출온도를 $260^{\circ}C$로 고정하였다. GO의 환원시간에 따른 PC/RGO 복합체의 화학반응 정도는 $3000cm^{-1}$ 부근에서 나타나는 C-H 신축진동피크를 통해 확인하였고, 환원시간이 1 h일 때의 GO와 유사한 화학반응 정도를 나타내었다. GO의 환원시간에 따른 PC/GO 복합체의 복소점도(complex viscosity)가 감소하는 것을 확인하였으며, 이는 PC-GO 사이의 화학반응에 의한 분산성에 기인한 것으로 주사전자현미경(SEM)을 통해 확인하였다.

• 대한금속재료학회지
• /
• 제49권11호
• /
• pp.882-892
• /
• 2011

The influence of rhenium (Re) and ruthenium (Ru) addition on the solidification and solute redistribution behaviors in advanced experimental Ni-base superalloys has been investigated. A series of model alloys with different levels of Re and Ru were designed based on the composition of Ni-6Al-8Ta and were prepared by vacuum arc melting of pure metallic elements. In order to identify the influence of Re and Ru addition on the thermo-physical properties, differential scanning calorimetry analyses were carried out. The results showed that Re addition marginally increases the liquidus temperature of the alloy. However, the ${\gamma}^{\prime}$ solvus was significantly increased at a rate of $8.2^{\circ}C/wt.%$ by the addition of Re. Ru addition, on the other hand, displayed a much weaker effect on the thermo-physical properties or even no effect at all. The microsegregation behavior of solute elements was also quantitatively estimated by an electron probe microanalysis on a sample quenched during directional solidification of primary ${\gamma}$ with the planar solid/liquid interface. It was found that increasing the Re content gradually increases the microsegregation tendency of Re into the dendritic core and ${\gamma}^{\prime}$ forming elements, such as Al and Ta, into the interdendritic area. The strongest effect of Ru addition was found to be Re segregation. Increasing the Ru content up to 6 wt.% significantly alleviated the microsegregation of Re, which resulted in a decrease of Re accumulation in the dendritic core. The influence of Ru on the microstructural stability toward the topologically close-packed phase formation was discussed based on Scheil type calculations with experimentally determined microsegregation results.

• 한국주조공학회지
• /
• 제41권4호
• /
• pp.349-356
• /
• 2021

우수한 기계적 성질과 가격경쟁력을 갖는 구상흑연주철 합금 개발을 위해 Cu와 Sn을 소량 첨가한 고 Mn 구상흑연주철의 응고 후 냉각조건에 따른 미세조직과 기계적 특성을 분석하였다. 첨가원소인 Cu와 Sn의 경우 펄라이트 형성 촉진을 통한 인장특성 향상을 위해 선택하였다. 또한 물성에 미치는 냉각속도의 영향을 확인하기 위해, Mg 처리된 다양한 조성의 합금을 블록시편에 주입한 후 주형 내 냉각과 800℃에서 주형 해체 후 공랭의 두 가지 냉각 조건을 비교분석하였다. 주형 내 냉각 시편의 경우, 펄라이트 분율은 27-44%, 인장강도와 연신율은 각각 513-568N/mm²와 10.4-14.3%로 나타났다. 반면, 이른 형해체 공랭 시편의 경우에는 펄라이트 분율은 77~85%, 인장강도와 연신율은 각각 728~758N/mm²와 3.2~6.0% 이었다. 결론적으로, 소량의 Cu 및 Sn 함유 Mn 구상흑연주철의 공랭 시 괄목할만한 인장강도와 연신율의 증가를 확인할 수 있었다.