• Journal of Conservation Science
• /
• v.38 no.2
• /
• pp.117-123
• /
• 2022

In this study, investigated the possibility of quantitatively and qualitatively analyzing Korean ancient glasses via Raman Spectroscopy. We subjected four categories of Korean traditional glasses, namely, lead-BaO, lead, potash, and soda glasses (3, 3, 10, and 10 pieces, respectively), to this analytical technique. The results showed significant differences between the stretching and bending Raman vibration regions corresponding to these different Korean ancient glass types. Specifically, the stretching vibration regions corresponding to lead-BaO and lead glasses showed peaks at 1040 and 1000 cm^-1, respectively; the stretching vibration region of normal glass appears at 1100 cm^-1. The bending vibration regions corresponding to potash and soda glass showed Raman peaks at 490 and 560 cm^-1, respectively. Furthermore, the Raman spectra of the lead and lead-BaO glasses showed red shifts, which depended on the amount of PbO present. Thus, our findings highlighted the possibility of quantitatively determining the amount of PbO, a major component of lead glasses, via Raman Spectroscopy.

• Korean Journal of Heritage: History & Science
• /
• v.49 no.2
• /
• pp.158-171
• /
• 2016

The observation and analysis results of 9 glass bead samples collected from Oc Eo site in Vietnam, an outport of the ancient port city Funan in East Asia, are as follows. The type of glass beads is round, the colors are reddish brown, greenish blue, green, black and purplish blue, and the chemical composition is soda glass group. This means that they are similar in type, color and chemical compositions to glass beads from the ancient Korean peninsula. There are limitations in data because the glass beads are not from excavation investigation but from earth surface investigation. But it is significant that similar making technique and chemical composition are being observed in both the glass beads from Oc Eo and those of Korea. According to "Nihon Shoki" Kinmeiki, Baekje king sent Funan's goods and 2 slaves to Japan in 543. It is clear that there were direct or indirect exchanges between Baekje and Funan. The possibility has grown that glass beads could be included among goods.

• Proceedings of the Korea Multimedia Society Conference
• /
• 2001.06a
• /
• pp.107-110
• /
• 2001

본 논문에서는 유리 B 스플라인 곡선을 이용한 새로운 블록 효과 감소 방법들 제안한다. 블록 효과는 매우 낮은 비트율로 블록 기반 부호화 방식을 수행할 때 복원 영상에서 나타나는 블록 형태의 왜곡을 의미한다. 제안된 기법에서는 컴퓨터 그래픽스 분야에서 제어점을 근사하는 부드러운 곡선을 생성하기 위해 사용되는 유리 B 스플라인 곡선을 이용하여 블록 효과를 감소시킨다. 즉 블록 경계의 화소 값들을 제어 점으로 사용하며 블록 효과 발생 정도에 따라 가중치를 가변적으로 설정함으로써 블록 효과가 효율적으로 감소되도록 한다. 모의 실험은 제안된 방법이 기존 방법들에 비해 우수한 블록효과 감소 성능을 가지는 것을 나타낸다.

• Journal of the korean Society of Automotive Engineers
• /
• v.6 no.1
• /
• pp.11-20
• /
• 1984

이글에서는 메타놀의 성상과 재래의 내연기관에 메타놀을 사용하였을 때의 특성을 몇 가지 관 점에서 살펴보았다. 유리한 점으로 판단되는 사실은, 1)옥탄가가 높아 고압축비의채용으로 열 효율을 높일 수 있다. 2)기화참열이 크고 물과의 친화성이 좋다. 이러한 점은 내부냉각방식의 채용으로 이상적인 충상혼합기를 형성할 수가 있을 것이며, 현재의 내연기관의 냉각계통, 즉 방 열기, 물펌프, 냉각휜 등을 줄일 수 있을 것으로 본다. 또 NO.chi.의 배출을 저하시키는 이점도 있다. 3)단일성분 연료이므로 배기가스 조성이 단순하며 깨끗하다. 이는 배기공해상 메타놀연료가 석유계연료보다 유리하다. 그러나 메타놀기관은 앞으로 기술적 연구, 개선을 필요로 하는 점도 있다. 1) 메타놀의 가솔린과 비교하여 인화점이 높고 기화잠열이 커서 시동성이 나쁘고 2) 메타놀은 어느 종류의 금속, 프라스택, 도료 등을 부식시킨다. 3) 메타놀은 세탄가가 낮아, 압축점화는 무리이며 4) 발열량은 석유계 연료의 약 절반이다. 따라서 시동성, 재료, 착화방법, 개질 가스의 이용법, 내부냉각 등의 기술적인 문제가 개발된다면 질, 량, 가격적인 면에서도 내연기관용에는 메타놀이 유리하다고 본다. 그러나 현시점에서는 기관측으로 보아 자동차용연료로는 가솔린에 혼합하는 방법이고 그렇게 된다면 20-30%의 연료가 절감되리라고 믿는다.

• Journal of Conservation Science
• /
• v.27 no.3
• /
• pp.323-332
• /
• 2011

Microtexture and components of 7 glass bead fragments excavated from Andong tumulus in Gildu-ri, Goheung have been analyzed to determine the characteristics of their weathered condition as well as chemical compositions. Firstly, status of microtexture shows that there is a large quantity of pollutants which were presumably transferred from the buried environment into the surface and the gap of the cracks. The examination has displayed that there are less amount of alkali metal components such as sodium (Na) and potasium (K) in the gap of the cracks than on the surface. The chemical compositions analysis has confirmed that two samples belongs to potash glass group ($K_2O-SiO_2$), four to soda glass group ($Na_2O-SiO_2$), and one to the mixed alkali glass group. Chromophoric elements of the glass varies by different colours: blue and navy are cobalt (Co); greenish blue is copper (Cu) and iron (Fe); and light brown is Fe respectively. Such kind of scientific analysis of the excavated glass beads will contribute to the understanding of interchange between various local cultures and arts within the southwest region of Korean Peninsula during the 4th and the 5th centuries.

• Journal of Conservation Science
• /
• v.32 no.1
• /
• pp.63-73
• /
• 2016

This study defined material and characteristics of 24 glass fragments and 26 whole glass beads. The feature of glass beads shape are divided into 5 types following color, size, weathering condition and manufacturing techniques. Through the chemical composition, the first and second type is soda glass, the third type is potash glass, the fourth and fifth type is lead barium glass. This site showed the aspect that the chemical composition is changed according to the feature of glass shape and was found that various chemical compositions. Looking at the flow of glass culture, the tomb that are lead barium glass IItype and potash glass I, IItype is relatively preceding period and the tomb that are soda glass and lead barium glass IIItype is following period.

• Information Display
• /
• v.23 no.4
• /
• pp.12-21
• /
• 2022

반도체 기반 양자점 (QD)소재와 CsPbX3 (X=Cl, Br, I)기반 perovskite 양자점 또는 나노결정 소재(PNC)는 매우 우수한 양자효율과 좁은 발광 선폭으로 고색재현성 디스플레이 색변환 소재 또는 발광 소재로서 각광을 받고 있다. 그러나, 기존 화학적 합성법을 통해 제조되는 QD 및 PNC 소재는 취약한 열 및 화학적 안정성으로 인해 장기 내구성의 개선이 요구된다. 이들 QD 및 PNC 소재는 모두 완전 무기 소재인 산화물 기반 유리 소재내에 생성이 가능하며, 이를 통해 장기 내구성을 근본적으로 개선할 수 있다. 반도체 기반 QD 함유 유리소재 (QDEG)의 경우, 유리 내 core/shell 구조를 가진 QD의 생성으로 양자효율의 향상이 가능했으나, 콜로이드 기반 양자점 (cQD)과 달리 다중 shell의 형성이 어려워 양자효율이 제한되고, 발광 선폭이 넓어 고색재현성 디스플레이용 색변환 소재로 적용되기에는 아직 한계가 있다. 한편, Perovskite 양자점 (또는 나노결정) 함유 유리소재 (PNEG) 소재는 QDEG과 달리 콜로이드 기반의 PNC (c-PNC)가 가지는 우수한 양자효율과 20 nm 수준의 좁은 선폭을 유리 내에서도 가지며, c-PNC 대비 열적, 화학적 및 광학적 안정성이 획기적으로 향상되어 실질적인 응용 가능성을 높이고 있다. 특히, 일반적인 용융-급랭법으로 제조하여 대량생산에 용이하고, 분말 또는 판상 등 다양한 형태로의 제작이 가능한 장점이 있다. 현재까지 제조된 PNEG의 최대 PL-QY는 450 nm 여기 시 녹색 및 적색에서 약 60% 수준이며, Al₂O₃ 분말을 이용할 경우 최대 80% 수준까지 달성이 가능하다. 또한, PNEG과 blue LED를 이용하여 백색 LED를 구현할 경우 color filter를 적용하지 않을 때, NTSC 대비 최대 약 130 % 수준의 높은 색재현 영역을 보여 주고 있으며, 실제 LCD용 BLU로 적용 시 기존 상용 c-QD 소재와 동등 이상의 색재현 영역을 보이고 있어, 실질적인 응용 가능성이 매우 높음을 확인하였다. PNEG의 상업적인 응용을 위해서는 몇 가지 추가적인 연구 개발이 필요하다. 기존 c-QD 또는 c-PNC는 나노 수준 크기의 입자가 액상에 분산된 형태로 입도 제어가 용이하나, PNEG의 경우 분말 제조 시 유리 형성 후 분쇄를 통해 제조되며, 입도가 대개 수십 ㎛ 이하로 작아질 경우 PL-QY가 저하되어, 향후 잉크젯 공정 응용을 위해서는 고효율의 분말 제조공정 개발이 필요하다. 또한, 유리 소재의 경우 절연체로서 기존 QD 소재 대비 electro-luminescence(EL) 소자의 활성층으로 사용하는데 제약이 있어 PNEG을 이용한 EL 소자 제작에 대한 연구도 필요하다. 마지막으로, 기존 c-PNC 소재와 같이 Pb가 함유되지 않은 PNEG 소재의 개발이 선결되어야 할 것으로 판단된다. 이와 같은 해결 과제들에도 불구하고, PNEG 소재는 기존 c-QD 소재 대비 매우 우수한 안정성을 기반으로 고품위 고색재현 디스플레이용 색변환 소재로서 다양한 응용에 활용될 수 있을 것으로 기대된다.

• 보존과학연구
• /
• s.32
• /
• pp.113-121
• /
• 2011

Four glass beads from Hakso-ri site, O'chang were analyzed for thirteen oxides with SEM/EDS and lead isotope ratios with TIMS respectively. These samples were classified to potash glass system($K_2O-CaO-SiO_2$) with HCLA(High CaO, Low $Al_2O_3$). However three samples with above 4% for lead could be classified to potash-lead ($K_2O-PbO-CaO-SiO_2$)glass system and it seemed that coloring agent for greenish blue was Cu. Lead isotope ratio data for four samples did not make a group but scattered to the space respectively. It needs more study for compositions and lead iosotope data of potash-lead glasses with regions and ages.

• Journal of the KSME
• /
• v.32 no.8
• /
• pp.666-672
• /
• 1992

유리의 제조공정에 있어서 열적 문제들을 고찰하여 보았다. 비단 유리뿐 아니라, 여러 가지 다른 재료의 공정 (예컨대 철강, 세라믹 등)에 있어서도 다양한 열적 문제가 관찰되며, 이러한 점에서 열공학자들의 관심의 확대가 절실하다고 하겠다. 이 글이 우리 열공학자들의 시야를 넓히는 데 일조를 하였기를 바라마지 않는다.

• Conservation Science in Museum
• /
• v.22
• /
• pp.69-84
• /
• 2019

This study investigated the formal characteristics and chemical compositions of eighty beads excavated from a Silla tomb complex at Deokcheon-ri, Uljin in order to reveal the methods of production and the characteristics of the raw materials involved, thereby illuminating characteristics of the relics from each tomb. The beads excavated from these Silla tombs include one curved bead, one tubular bead, and 78 globular beads. Among them, the curved and tubular beads and three globular beads were identified to be made of minerals, and the remaining 75 beads are made of glass. Most of the glass beads are thought to have been produced using the drawing technique. The characteristics of the beads were classified according to their site of excavation. The globular beads from Tomb No. 34 belong to the lead-barium glass and potash glass groups, indicating that these beads were produced at a relatively earlier period in time. The glass beads excavated from the tombs in the northern portion of the complex differ in color and chemical composition from those in the southern portion, which indicates the character that each group of beads had different aspect according to site location. Considering that the excavated beads were mainly from fifth- and sixth-century tombs, it is likely that certain groups of people living around Uljin used and buried beads in their tombs. As the governance of Silla became more centralized in the sixth century, the use of beads for burial purpose appears to have come to an end in this region.