• 기계와재료
• /
• v.19 no.1 s.71
• /
• pp.58-67
• /
• 2007

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.10 no.1
• /
• pp.15-19
• /
• 2014

A Failure or degradation of reactor upper head penetration is a recurring problem due to long term operation at nuclear power plants. And a flaw in the reactor upper head penetration has caused unplanned plant shutdown for repair as well as high economic impact on the plants. Consequently, a detection of flaws is of the utmost importance. Prior to the replacement of reactor upper head penetration, some utilities have repaired the flaws of reactor upper head penetration generated by overlay weld. Until now, only the base metal in reactor upper head penetration has been inspected according to 10 CFR 50.55a and ASME code case N-729-1. Accordingly, it is difficult to detect manufacturing defects and repair defects in overlay weld. This paper presents a case study on the application of Time of Flight Diffraction technique for reactor head penetration mockup with artificial flaws in overlay weld. This study offers a way to understand the flaws detected in reactor upper head penetration overlay weld.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.11 no.2
• /
• pp.1-5
• /
• 2015

A failure or degradation of reactor upper head penetration is a troublesome problem at Nuclear Power Plants. A flaw in the reactor upper head penetration can result in unplanned plant shutdown for repair, and cause serious economic losses on the plants. Consequently, a detection of flaws is a matter of more importance. Until now, only the base metal, not including J-groove weld, in reactor upper head penetration has been inspected in accordance with 10 CFR 50.55a and ASME code case N-729-1 requirements. Accordingly, it is rather difficult to detect manufacturing defects and repair defects in J-groove weld. This paper presents a case study on the application of Time of Flight Diffraction UT technique to examine the J-groove weld in reactor head penetration using reactor head penetration mockup with artificial flaws. We expect that this study result will offer a way to understand the non-destructive examination technology for J-groove weld in reactor upper head penetration.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2008.06a
• /
• pp.179-180
• /
• 2008

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.37 no.9
• /
• pp.1159-1168
• /
• 2013

In pressurized water nuclear reactors (PWRs), the reactor pressure vessel (RPV) upper head contains penetration nozzles that use a control rod drive mechanism (CRDM). The penetration nozzle uses J-groove weld geometry. Recently, the occurrence of cracking in alloy 600 CRDM penetration nozzle has increased. This is attributable to primary water stress corrosion cracking (PWSCC). PWSCC is known to be susceptible to the welding residual stress and operational stress. Generally, the tensile residual stress is the main factor contributing to crack growth. Therefore, this study investigates the effect on weld residual stress through different analysis methods for normal operating conditions using finite element analysis. In addition, this study also considers the effect of repeated normal operating condition cycles on the weld residual stress. Based on the analysis result, this paper presents a normal operating condition analysis method.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.6
• /
• pp.637-647
• /
• 2014

In pressurized water reactors, the upper head of the reactor pressure vessel (RPV) contains numerous control rod drive mechanism (CRDM) nozzles. These nozzles are fabricated by welding after being inserted into the RPV head with a room temperature shrink fit. The tensile residual stresses caused by this welding are a major factor in primary water stress corrosion cracking (PWSCC). Over the last 15 years, the incidences of cracking in alloy 600 CRDM nozzles have increased significantly. These cracks are caused by PWSCC and have been shown to be driven by the welding residual stresses and operational stresses in the weld region. Various measures are being sought to overcome these problems. The defects resulting from the welding process are often the cause of PWSCC acceleration. Therefore, any weld defects found in the RPV manufacturing process are immediately repaired by repair welding. Detailed finite-element simulations for the Korea Nuclear Reactor Pressure Vessel were conducted in order to predict the magnitudes of the repair weld residual stresses in the tube materials.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.10
• /
• pp.1337-1345
• /
• 2011

In pressurized water reactors (PWRs), the reactor pressure vessel (RPV) upper head contains numerous control rod drive mechanism (CRDM) nozzles. In the last 10 years, the incidences of cracking in alloy 600 CRDM nozzles and their associated welds has increased significantly. Several axial and circumferential cracks have been found in CRDM nozzles in European PWRs and U.S. nuclear power plants. These cracks are caused by primary water stress corrosion cracking (PWSCC) and have been shown to be driven by welding residual stresses and operational stresses in the weld region. Therefore, detailed finite-element (FE) simulations for the Korea Nuclear Reactor Pressure Vessel have been conducted in order to predict the magnitudes of the weld residual stresses in the tube materials. In particular, the weld residual stress results are compared in terms for nozzle location, geometry factor$r_o$/t, geometry of fillet, and adjacent nozzle.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.36 no.10
• /
• pp.1115-1130
• /
• 2012

In nuclear power plants, the reactor pressure vessel (RPV) upper head control rod drive mechanism (CRDM) penetration nozzles are fabricated using J-groove weld geometry. Recently, the incidences of cracking in Alloy 600 CRDM nozzles and their associated welds have increased significantly. The cracking mechanism has been attributed to primary water stress corrosion cracking (PWSCC), and it has been shown to be driven by welding residual stresses and operational stresses in the weld region. The weld-induced residual stress is the main factor contributing to crack growth. Therefore, an exact estimation of the residual stress is important for ensuring reliable operation. This study presents the residual stress computation performed for an RPV CRDM penetration nozzle in Korea. Based on two and three dimensional finite element analyses, the effect of welding variables on the residual stress variation is estimated for sensitivity analysis.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.36 no.9
• /
• pp.1047-1052
• /
• 2012

Primary water stress corrosion cracking (PWSCC) instances have been reported in the Alloy 600 reactor pressure vessel head penetration nozzle and the Alloy 82/182 dissimilar metal butt weld nozzle in several PWRs. Therefore, in-service inspection programs have been adopted worldwide to prevent failure at the weld region. If a PWSCC is observed at the dissimilar metal weld region during inspection, its structural integrity should be evaluated; however, this requires considerable time and effort, and this might lead to a decrease in the plant utilization coefficient. To prevent this, KHNP-CRI have established integrity assessment criteria and developed a computer program for the fast evaluation and judgment of PWSCC. In this paper, the results and current status of the same are presented. Through this study, criteria for the structural integrity evaluation of PWSCC have been established, and a computer program has been developed to realize technical means for the evaluation of PWSCC structural integrity.

• Proceedings of the KWS Conference
• /
• 2005.06a
• /
• pp.185-187
• /
• 2005

The reactor pressure vessel head of PWR has penetrations for control rod drive mechanism and instrumentation systems. The Primary coolant water and operating temperature can cause the stress-corrosion cracking of these nickel-based alloy penetrations. It is difficult to detect and size flaws such as SCC in the reactor head penetrations using conventional W methods because of complex geometry, Therefore, the utilities are using the TOFD technique for the detection and sizing of the flaw. This study shows the correlation between the ultrasonic wave direction and the orientation of the flaw and the range of flaw depth which can be detected by the TOFD techniques.