• Journal of the Korea institute for structural maintenance and inspection
• /
• v.12 no.6
• /
• pp.119-128
• /
• 2008

In this study, new moment-resisting precast concrete beam-column joint is proposed for moderate seismic regions. It has the connection reinforcing bars, penetrated the joint and lap-spliced with the bottom bars of precast U-shaped PC beam. To evaluate the performance for noncontact lapped splice, experimental and analytical works were conducted. Major variables for tests are the length of lap, the diameter of connection reinforcing bars, and the distance between lapped bars. Analytic research was performed nonlinear finite element method. Analytic research focused on crack pattern, load-deflection curve, comparison of internal force, evaluation of ductility strains of reinforcement bar. Results of experimental and analytical works show that the these variables has much influence on flexural strength and ductility, and joint behavior.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.3
• /
• pp.40-48
• /
• 2014

In this study, experimental research was carried out to evaluate and improve the seismic performance of reinforced concrete beam-column joint regions using strengthening materials (embedded CFRP rod and CFRP sheet) in existing reinforced concrete building. Therefore it was constructed and tested six specimens retrofitting the beam-column joint regions using such retrofitting materials. Specimens, designed by retrofitting the beam-column joint regions of existing reinforced concrete building, were showed the stable failure mode and increase of load-carrying capacity due to the effect of crack control at the times of initial loading and confinement of retrofitting materials during testing. Specimens RBCJ-SRC2, designed by the retrofitting of CFRP Rod and CFRP Sheet in reinforecd beam-column joint regions were increased its maximum load carrying capacity by 1.97 times and its energy dissipation capacity by 2.08 times in comparison with standard specimen RBCJ for a displacement ductility of 4 and 7. Also, specimens RBCJ-SRC2 were increased its maximum load carrying capacity by 1.09~1.11 times in comparison with specimen RBCJ-SR series. And Specimens RBCJ-CS, RBCJ-SR series, RBCJ-SRC2 were increased its energy dissipation capacity by 1.10~2.30 times in comparison with standard specimen RBCJ for a displacement ductility of 5, 6.

• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.29 no.6
• /
• pp.563-569
• /
• 2016

This paper presents the resizing method of columns and beams that considers column-to-beam strength ratios to simultaneously control the initial stiffness and ductility of steel moment frames. The proposed method minimizes the top-floor displacement of a structure while satisfying the constraint conditions with respect to the total structural weight and column-to-beam strength ratios. The design variable considered in this method is the sectional area of structural members, and the sequential quadratic programming(SQP) technique is used to obtain optimal results from the problem formulation. The unit load method is applied to determine the displacement participation factor of each member for the top floor lateral displacement; based on this, the sectional area of each member undergoes a resizing process to minimize the top-floor lateral displacement. Resizing members by using the displacement participation factor of each member leads to increasing the initial stiffness of the structure. Additionally, the proposed method enables the ductility control of a structure by adjusting the column-to-beam strength ratio. The applicability of the proposed optimal drift design method is validated by applying it to the steel moment frame example. As a result, it is confirmed that the initial stiffness and ductility could be controlled by the proposed method without the repetitive structural analysis and the increment of structural weights.

• 한국신재생에너지학회:학술대회논문집
• /
• 2008.05a
• /
• pp.382-385
• /
• 2008

박막형 태양전지 분야는 저가이고 가볍다는 특징을 가지고 있으며, 휘어지는 기판재를 적용하여 플렉서블 태양전지를 제조할 수도 있다는 장점을 가지고 있다. 본 연구에서 플렉서블 태양전지에 적합한 금속기판재를 제조하는 연구를 수행하였다. 일반적으로 기판재와 cell을 구성하는 반도체 층의 열팽창 거동 차이에 의한 열변형이 태양전지의 공정안정성에 영향을 주는 것으로 알려져 있었으며, cell을 구성하는 반도체 층과 열팽창 거동이 유사한 금속기판재의 적용이 필요하다. 이러한 특성을 쉽게 제어할 수 있는 금속기판재를 얇게 제조하기에 적절한 방법은 전주법이다. 전주법을 적용하여 조성 및 두께가 다른Ni 계 합금의 열팽창 거동을 TMA 장비를 사용하여 측정하였으며, 태양전지 제조에 사용되는 고온공정시 안정성 확보를 위하여 열처리후에 금속기판재의 열팽창 거동을 측정하였다. 그리고 전산해석tool 을 활용하여 가상의 CIS 플렉서블 태양전지 제조공정을 설정하고 고온공정온도에서 상온으로 냉각시 발생되는 층간 열변형 연구를 수행하였다. 그리고 플렉서블 태양전지용 기판재로 Ni 계 합금표면에 절연체인 $SiO_2$ 증착 연구를 수행하여 Fe-52Ni 합금에서 안정적인 절연층을 얻을 수 있었다.

• Journal of the Korea Concrete Institute
• /
• v.23 no.1
• /
• pp.39-48
• /
• 2011

The present investigation evaluates the flexural behavior of pre-tensioned lightweight concrete beams under two-point symmetrical concentrated loads according to the variation of the partial prestressing ratio and the effective prestress of prestressing strands. The designed compressive strength of the lightweight concrete with a dry density of 1,770 $kg/m^3$ was 35 MPa. The deformed bar with a yield strength of 383 MPa and three-wire mono-strands with tensile strength of 2,040 MPa were used for longitudinal tensile reinforcement and prestressing steel reinforcement, respectively. According to the test results, the flexural capacity of pre-tensioned lightweight concrete beams increased with the increase of the partial prestressing ratio and was marginally influenced by the effective prestress of strands. With the same reinforcing index, the normalized flexural capacity of pre-tensioned lightweight concrete beams was similar to that of pre-tensioned normal-weight concrete beams tested by Harajli and Naaman and Bennett. On the other hand, the displacement ductility ratio of pre-tensioned lightweight concrete beams increased with the decrease of the partial prestressing ratio and with the increase of the effective prestress of strands. The load-displacement relationship of pre-tensioned lightweight concrete beam specimens can be suitably predicted by the developed non-linear two-dimensional analysis procedure. In addition, the flexural cracking moment and flexural capacity of pre-tensioned lightweight concrete beams can be conservatively evaluated using the elasticity theorem and the approach specified in ACI 318-08, respectively.

• Composites Research
• /
• v.32 no.3
• /
• pp.148-157
• /
• 2019

In this study, $C_f/SiC$, $SiC_f/SiC$ and $C_f-SiC_f/SiC$ ceramic composites reinforcing carbon fiber, SiC fiber and hybrid fiber were fabricated by hybrid TGCVI and PIP process. After the thermal shock cycle, 3-point bending and Oxy-Acetylene torch test, their mechanical behavior, oxidation and erosion resistance were evaluated. The $C_f/SiC$ composite showed a decrease in mechanical property along with increasing temperature, a pseudo-ductile fracture mode and a large quantity of erosion. The $SiC_f/SiC$ composite exhibited stronger mechanical property and lower erosion rate compared to the $C_f/SiC$, but brittle fracture mode. On the other hand, hybrid type of $C_f-SiC_f/SiC$ composite gave the best mechanical property, more ductile failure mode than the $SiC_f/SiC$, and lower erosion rate than the $C_f/SiC$. During the Oxy-Acetylene torch test, the $SiO_2$ formed by reaction of the SiC matrix with oxygen prevented further oxidation or erosion of the fibers for $C_f-SiC_f/SiC$ and $SiC_f/SiC$ composites particularly. In conclusion, if a hybrid composite with low porosity is prepared, this material is expected to have high applicability as a high temperature thermo-structural composite under high temperature oxidation atmosphere by improving low mechanical property due to the oxidation of $C_f/SiC$ and brittle fracture mode of $SiC_f/SiC$ composite.

• Journal of the Korea Concrete Institute
• /
• v.29 no.2
• /
• pp.209-216
• /
• 2017

One of the important considerations in structural designing the flat plate system is ensuring the resistance to punching shear caused by axial loads and the ductile ability to follow horizontal deformation under earthquake. In this study, the ECC (Engineered Cementitious Composite) has been placed in the critical section zone of punching shear at slab-column joint to improve ductility and the advanced details of shear reinforced area nearby critical section zone has been developed using stud and steel fiber. The shear performance tests were performed on the specimens with parameters of fiber type mixed with ECC, stud and steel fiber set into the shear reinforced area in which the failure pattern, joint strength, displacement and strain of the specimen were compared and analyzed. The test results showed that the strength and ductility of specimens with ECC applied to joint were better than those of RC flat plate system. Also, the shear reinforcement effect of stud and the ductility improvement of steel fiber concrete were confirmed in the shear reinforcement area.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.3
• /
• pp.10-19
• /
• 2014

Corrugated steel plates are made by fabricating thin steel plates to have trapezoidal or sinusoidal corrugation, and the corrugated plates are able to maintain high out-of-plane rigidity even when they are used instead of thick flat plates. Also, corrugated steel plates have almost no axial rigidity due to the accordion effect. Thus, if they are applied to the webs of plate girders, designing can be easily conducted so that the webs bear only shear stresses. However, unlike flat plates, the shear buckling of corrugated steel plates has very complex characteristics where buckling occurs due to the interaction of local and global buckling, besides local buckling and global buckling. For the investigation of the cause and characteristics of this interactive buckling, studies on sinusoidal corrugated steel plates are fewer than studies on trapezoidal corrugated steel plates. Therefore, in this study, the shear buckling characteristics of sinusoidal corrugated steel plates and the occurrence pattern of interactive buckling were investigated. For the calculation of shear buckling strength, a finite element program was used, and the analysis results were compared with the exact solution. In addition, the characteristics of buckling stress change and the change of buckling mode shape depending on corrugation thickness and shape parameter were analyzed, and by comparing these results with the results of a theoretical equation, the timing of buckling mode change was analyzed.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.20 no.6
• /
• pp.752-757
• /
• 2017

Analysis has been performed for the penetration of a long-rod into MMC/Ceramic layered armour system with several shot test and a series of simulations. Two types of MMC plate have been fabricated by a liquid pressing method; A356/45%vol.%SiCp with a uniform distribution of SiC particle and Al7075/45%vol.B4Cp with B4C particle. The mechanical properties were measured with the high-speed split Hopkins bar test, hardness test and compression test. The popular Simplified Johnson-Cook model was adopted to represent the material characteristics for FEM simulations. The performance of the MMC applied armour system has been made by comparing with the semi-infinite mild steel target using the depth of penetration(DOP). The results show that placing ceramic front layer provides a certain gain in protection, and that placing another ductile front layer provides a further gain. The application of MMC is found to be attractive.

• Korean Journal of Environmental Biology
• /
• v.36 no.4
• /
• pp.680-686
• /
• 2018

Nitrogen fertilizers, hairy vetch, and slow-release complex fertilizers were applied to the soil during the cultivation of crops. The impact of these factors on $N_2O$ emission was quantitatively assessed and the GHGs reduction effect comprehensively evaluated. Among the three factors, the significant factors affecting $N_2O$ emission were mineral nitrogen>soil moisture>temperature. Yield and fertilizer utilization efficiency were highest in the slow-release complex fertilizer treatment. There was no significant difference in $N_2O$ emissions between the slow-release complex fertilizer treatments and the NPK+hairy vetch treatments. Comprehensive results showed that slow-release complex fertilizers treatment has high yield and fertilizer utilization efficiency but low $N_2O$ emission.