• Korean Journal of Materials Research
• /
• v.5 no.5
• /
• pp.606-610
• /
• 1995

Diglycidyll ether of bisphenol A(DGEBA)/4, 4'-methylene dianiline(MDA)계에 반응성 첨가제 malononitrile(MN)을 첨가하면 내충격성은 크게 향상되나 반응속도는 감소하게 된다. 에폭시 수지의 경화반응은 에폭시기가 개환되어 생성되는 히드록시기가 촉매로 작용하는 자촉매 반응이며, 외부에서도입된 히드록시기도 같은 효과를 나타낸다. 따라서 본 연구에서는 DGEBA/MDA/MN 계의경화 반응속도를 증가시키기 위해 히드록시기를 가진 촉매로서 hydroquinone(HQ)을 도입하였고 이들 계의경화특성 및 열적성질을 고찰하였다. HQ가 첨가됨으로 인해 활성화 에너지는 감속하고 속도상수는 증가하였으며, 발열곡선에서 반응 시작온도가 낮아졌다. 이 결과로부터 HQ가 반응 가속제로 작용하고 있음을 알 수 있다.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.4
• /
• pp.592-601
• /
• 2001

Fiber reinforced metal laminates(FRMLs) are new types of hybrid materials. FRMLs consists of high strength metal(Al 5052-H34) and laminated fiber with structural adhesive bond. The mixture ratio effect of epoxy resin$.$curing agent$.$accelerator on the fatigue behavior of FRMLs was investigated in this study. The epoxy, diglycidylether of bisphenol A(DGEBA), was cured by methylene dianiline(MDA) with or without an accelerator(K-54). Eight different kinds of resin mixture ratios were selected for the test ; five kinds of FRMLs(1) and three others of FRMLs(2). The relationship between da/dN and ΔK with variation of resin mixture ratio was studied. FRMLs(1) and FRMLs(2) indicated approximately 2 times and 2.2 times more improved maximum bending strengths in comparison with those of Al 5052-H34. The resin mixture ratio <1:1> in case of FRMLs(1) indicated the maximum fatigue life, while the resin mixture ratio <1:1:0.2> in case of FRMLs(2) indicated the maximum fatigue life. As results, FRMLs(2) turned out to have more effective characteristics on the fatigue properties and the bending strength than those of FRMLs(1).

• Elastomers and Composites
• /
• v.40 no.3
• /
• pp.166-173
• /
• 2005

Effect of thermal aging on the weight loss and water absorption of epoxy adhesives was investigated in the presence of three types of different hardeners, such as D-230, G-5022, and HN-2200. Thermal and mechanical properties of the cured epoxy resins were also studied througth the glass transition temperature and shear adhesion strength measurements. Weight losses of DGEBA/D-230 and DGEBA/HN- 2200 systems were not varied. However, the weight of DGEBA/G-5022 system was significantly decreased with increasing the thermal aging time. The water absorption of the specimens was increased as the thermal aging time increased except that using G-5022. DEGBA/HN-2200 system showed higher $T_g$ value than those of other systems, due to the formation of the fine three-dimensional network structure containing aliphatic ring. Shear adhesion strength of all systems was increased with increasing the thermal aging tine, which is attributed to increased degree of cure and fine three-dimensional network structure formation. And $T_g$ values and shear adhesion strength of all specimens exposed to water was decreased as the immersion time increased.

• Applied Chemistry for Engineering
• /
• v.7 no.5
• /
• pp.963-969
• /
• 1996

Cure characteristics of DGEBA(diglycidyl ether of bisphenol A)/dicy(dicyandiamide) system containing diuron(3-(3,4-dichloro phenyl) -1,1-dimethylurea) as an accelerator was investigated. The system has shelf life of six months because dicy is insoluble in liquid/solid resins at room temperature. It is generally known that dicy is an adequate curing agent for one component adhesive due to its highly latent property. With increasing the amount of added dicy, reaction heat of DGEBA/dicy system increased and degree of conversion was not varied. For DGEBA/dicy/diuron system, cure temperature decreased about $40^{\circ}C$ and cure reaction became fast by the addition of diuron which activates dicy. $T_g$ of the mixed resin decreased with the amount of accelerator. which was interpreated with molecular structure forming loose chain. Cure kinetics of DGEBA/dicy and DGEBA/dicy/diuron system were explained using Kamal's autocatalytic reaction model. The effect of acceleration was confirmed with that reaction model.

• Journal of Conservation Science
• /
• v.32 no.4
• /
• pp.459-469
• /
• 2016

The goal of this study was to examine property changes induced by the choice of filler used with an epoxy resin that was developed in 2014 to restore cultural assets and consider the applicability of the resin as a restorative agent. The properties of putty mixed with 9 types of fillers and as-developed resins were compared with those of existing materials with regard to stability, superiority and applicability. The potential of the putty as an alternative material was also examined. The materials produced the best adhesiveness, color change and hardness results when mixed with lime. Micro balloon produced the best wear rates and hardening times, while diatomite produced the best tensile and compressive strengths. A plaster and white mineral pigment mixture produced the best specific gravity. Every material except for lime exhibited about 2.5-20 times higher wear rates than the existing material, which is thought to exhibit an excellent cutting force. The hardening time was enhanced by about 0.5-9 times to improve convenience. The stability of the relic was also ensured by improving hand staining without any shrinkage or deformation. The material exhibited about 0.5-27 times less yellowing. Thus, it is thought to be a material that can reduce property changes and reduce the degree of relic fatigue which occurs during reprocessing and sense of difference from relic.

• Journal of Adhesion and Interface
• /
• v.13 no.4
• /
• pp.171-181
• /
• 2012

The demand characteristics of the conventional 12 kinds of epoxy resins which have been used for restoration of the ceramic relics were investigated to provide standards of the effective materials in this study. The result of durability analysis showed that a liquid type is more effective in ceramic relics (low damage, high strength), and a paste type is more effective in earthenware relics (high damage, low strength). The result of workability analysis appears that the liquid type is higher than the paste type, and a slow curing type is higher than a fast curing type in surface hardness. Therefore, in the case of the liquid type which is hard to reprocess due to high surface hardness, it is necessary to conduct a study on improving physical properties by adding filler. The result of the gloss analysis on epoxy resins showed that the liquid type (colorless) has higher gloss than the paste type, and the slow curing type has higher gloss than the fast curing type in liquid types. CDK-520A/520B and Araldite SV 427-2/HV 427-1 showed the most similar gloss to $700^{\circ}C$ earthenware, Devcon 5 minute, EPO-TEK 301-2, and Quik Wood showed the most similar gloss to celadon and whiteware, Quik Wood, EPO-TEK 301-2, and Devcon 5 minute showed the most similar gloss to buncheongware. It is necessary for conservator to decide the range of the restoration surface by predicting the increase and decrease of the restoration surface because most of the epoxy resins caused the volume change in curing process.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1988.10a
• /
• pp.12-13
• /
• 1988

• Proceedings of the KIEE Conference
• /
• 1987.07a
• /
• pp.719-721
• /
• 1987

• Journal of the Korean Wood Science and Technology
• /
• v.35 no.3
• /
• pp.36-44
• /
• 2007

The purpose of this study was to investigate thermal stability, reactivity, and bonding strength of existing epoxy resin mixed with the epoxidized soybean oil (ESBO) in order to use soybean oil economically. In the dry shear test, the marked strengths showed $30.5kgf/cm^2$ at the ratio of ESBO to epoxy resin 9 : 1 and $6.2kgf/cm^2$ at the ratio 8 : 2. The bonding strengths of the others, except mixing ratios 2 : 8 and 1 : 9, exceeded the requirement of Korean plywood standard of $7.0kgf/cm^2$. In the wet shear test, the result was $5.8kgf/cm^2$ at the ratio 9 : 1. There were no thickness swelling and moisture absorption in the water resistance of the film. The value of activation energy, Tg (${\Delta}E$), by DSC analysis showed between $110^{\circ}C$ and $120^{\circ}C$ through all ratios. Epoxy in the epoxy resin fully reacted with the hardener (TETA), but it is difficult to decide that epoxys in the ESBO were reacted directly with the hardener from FT-IR analysis. As the mixing ratio of ESBO increased, the thermal stabilities dropped from TGA analysis. From the comprehensive view on the results of above experiments, it could be confirmed through experiments that the ESBO in the mixed adhesive of epoxy resin/ESBO played a role as an extending agent level of epoxy adhesive, and we were able to know that in order to utilize ESBO as an adhesive, a study should be performed on the condition of hardening, inducible of the hardening reaction.

• Polymer(Korea)
• /
• v.25 no.2
• /
• pp.168-176
• /
• 2001

The effect of novel N-crotyl-N,N-dimethyl-4-methylanilinium hexafluoroantimonate (CMH) curing agent as a thermal latent initiator on thermal behaviors, rheological properties, and thermal stability of diglycidylether of bisphenol A (DGEBA) epoxy cationic system was investigated. From DSC measurements of DGEBA/CMH system, it was shown that this system exhibits an excellent thermal latent characteristic at a given temperature. The conversion and conversion rate of DGEBA/CMH system increased with increasing the concentration of initiator, due to high activity of CMH. Rheological properties of the system were investigated under isothermal condition using a rheometer The gelation time was obtained from the analysis of storage modulus (G'), loss modulus (G"), and damping factor (tan $\delta$). As a result, the reduction of gelation time was affected by high curing temperature and concentration of CMH, resulting in high degree of network formation in cationic polymerization, due to difference of activity. The thermal stability of the cured epoxy resin was discussed in terms of the activation energy for decomposition and thermal factors determined from TGA measurements.ents.