• Fire Science and Engineering
• /
• v.25 no.5
• /
• pp.69-75
• /
• 2011

It was performed to test the combustive properties of low density polyethylene and ethylene vinyl acetate (LDPE-EVA) composite by the addition of magnesium hydroxide. Flame retardant of natural magnesium hydroxide was added to the mixture of LDPE-EVA in 40 to 80 wt% concentration. The composite was compounded to prepare specimen for combustive analysis by cone calorimeter (ISO 5660-1). Comparing with virgin LDPE-EVA, the specimens including the magnesium hydroxide had lower flashover possibility. It is supposed that the combustive properties in the composites decreased due to the endothermic decomposition of magnesium hydroxide. The specimens with magnesium hydroxide showed both the lower total heat release rate (THR) and lower CO production rate than those of virgin polymer. As the magnesium hydroxide content increases, the total smoke release (THR) and smoke extinction area (SEA) decreased.

• Applied Chemistry for Engineering
• /
• v.22 no.4
• /
• pp.439-443
• /
• 2011

It was performed to test the combustive properties of low density polyethylene and ethylene vinyl acetate (LDPE-EVA) mixture by the addition of magnesium hydroxide. Flame retardant of natural magnesium hydroxide was added to the mixture of LDPE-EVA in 40 to 80 wt% concentration. The composite was compounded to prepare specimen for combustive analysis by cone calorimeter (ISO 5660-1). Comparing with virgin LDPE-EVA, the specimens including the magnesium hydroxide had lower combustive properties. It is supposed that the combustion-retardation properties in the composites improved due to the endothermic decomposition of magnesium hydroxide. The specimens with magnesium hydroxide showed both the lower peak heat release rate (PHRR) and lower effective heat of combustion (EHC) than those of virgin polymer. As the magnesium hydroxide content increases, time to ignition increased and the peak heat release rate decreased.

• Proceedings of the Korea Institute of Fire Science and Engineering Conference
• /
• 2011.11a
• /
• pp.458-461
• /
• 2011

수산화마그네슘을 첨가한 저밀도 폴리에틸렌-에틸렌 비닐 아세테이트 복합체의 연소성을 시험하였다. 저밀도 폴리에틸렌-에틸렌 비닐 아세테이트에 수산화마그네슘을 40~80wt% 첨가하여 용융 혼합하고 성형 후 콘칼로리미터(ISO 5660-1)를 이용하여 연소성을 시험하였다. 수산화마그네슘을 첨가한 시편은 첨가하지 않은 시험편에 비하여 그의 플래시오버 가능성이 감소하였다. 수산화마그네슘을 첨가한 시험편은 첨가하지 않은 시험편에 비해 낮은 총열방출량과 낮은 CO 발생량을 나타내었고, 수산화마그네슘 함량이 증가할수록 총연기발생량과 비소화면적이 감소하였다.

• Journal of Adhesion and Interface
• /
• v.19 no.2
• /
• pp.68-73
• /
• 2018

In this study, conductive EVA foams including multi-wall carbon nanotubes (MWCNT), glass beads were prepared. The electrical conductivity and physical properties of the foams were confirmed with varying amount of MWCNT, mixing time, and amount of glass beads. The electrical conductivity increased with the amount of MWCNT. Dispersity of MWCNT in EVA foams were improved with glass beads. It can be suggested that conductive EVA foams can be successfully prepared with improved dispersity of MWCNT in ethylene-vinyl acetate by using glass beads.

• Polymer(Korea)
• /
• v.38 no.3
• /
• pp.307-313
• /
• 2014

The physical properties of functionalized graphene sheet (FGS)/poly(ethylene-co-vinyl acetate) (EVA) was examined with various kinds of EVA, having vinyl acetate (VA) contents in the range of 0 to 40 wt%. The compatibility between FGS and EVA was enhanced as the polar VA content of EVA increased. Thus, the dispersion of FGS in EVA became finer, and the decrease of surface resistivity and the increase of tensile modulus by the added FGS became more effective when the VA content of EVA was high. When the VA content was low, the elongation at break was reduced drastically by added FGS due to the poor adhesion of FGS/EVA interface. The crystallization of EVA was generally retarded by the interaction with dispersed FGS. However, when both the VA content of EVA and the added amount of FGS were low, the crystallization of EVA was enhanced, probably due to the predominant nucleating effect by FGS.

• Polymer(Korea)
• /
• v.28 no.6
• /
• pp.468-477
• /
• 2004

The polymer blends of waste poly(vinyl chloride) (RPVC) and waste polyethylene (RPE) were prepared by melt mixing. Various ethylene-vinyl acetate copolymers (EVA) and ethylene-methacrylic acid Na salt copolymer (ionomer) were used as compatibilizer. Their morphologies and mechanical properties were evaluated as a funtion of mixing sequence and time. EVA with high vinyl acetate contents showed a rapid increment of tensile properties when small amount was added. Tensile properties of the blends were gradually increased with the addition of ionomer. Morphologies of RPVC/RPE blends were analyzed by scanning electron microscopy. FT-IR data showed that EVA was a good compatibilizer in RPVC/RPE blend compared to ionomer. Mechanical properties of the blends were highly enhanced when RPVC and compatibilizer were mixed and first RPE was added later.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.552-555
• /
• 1999

In this paper, the volume resistivity properties due to mixture ration of linear low density polyethylene(LLDPE) and ethylene vinyl acetate(EVA) are studied. Electrodes is composed of upper electrode 37(mm $\Phi$), guardring electrode(inner 55(mm $\Phi$ ), and lower electrode 87(mm $\Phi$ In order to measure the leakage current, We used electrometer and stable oven with temperature controller. Measurement method is to measure the leakage current of next specimen after applying the voltage according to 'Step Apply Methods' for ten minutes. In order to measure the volume resistivity properties, the micro electrometer is used, the range of temperature and applying voltage are 25 to 100[$^{\circ}C$] to 100[V] respectively.

• Korean Chemical Engineering Research
• /
• v.53 no.3
• /
• pp.282-288
• /
• 2015

A new energetic thermoplastic elastomer based on the azidated polybutadiene(Az-PBD)/ethylene vinyl acetate copolymer (EVA) blends was prepared, and structure and properties of the blends were invetigated by SEM, DSC, DMA, tensile testing and combustion test. The Az-PBD was synthesized via a two-step process involving the addition reaction of commercially available 1,2-PBD with $Br_2$ and subsequent nucleophilic substitution reaction of the brominated PBD with $NaN_3$. EVA/Az-PBD with 90/10, 80/20, 70/30 (wt/wt) was prepared by a solution blending. SEM, DSC, and DMA results revealed that the blends are partially compatible and Az-PBD is dispersed in continuous EVA matrix. Tensile test showed that modulus and tension set increased while elongation-at-break of the blends decreased with increasing Az-PBD content in the blends, but all the blends showed a elongation at break as high as 700% and a tension set of less than 5%, indicating that the blends are typically elastomeric. Combustion test showed that, with increasing Az-PBD content in the blend, higher energy can be released.

• Journal of the Korean Society of Safety
• /
• v.14 no.2
• /
• pp.83-89
• /
• 1999

The electrical properties due to mixture ratio of linear low density polyethylene(LLDPE) and ethylene vinyl acetate(EVA) films are studied. An experimental specimen is selected as LLDPE/EVA of thickness 200${\mu}{\textrm}{m}$ produced by mixture ratio of 50 : 50, 60 : 40, 70 : 30 and 80 : 2 wt%. In temperature range from $25^{\circ}C$ to 12$0^{\circ}C$, the measurement of volume resistivity using a highmegohm meter is performed within 10 minutes since each voltage of DC 100 V, 250 V, 500 V and 1000 V is applied, according to the step voltage method. From FT-IR spectrum for an analysis of physical properties, it can be confirmed that LLDPE blended with EVA shows an absence of carbonyl groups(1735 $cm^{-1}$, C=0) and ether groups(1242 $cm^{-1}$, C-O). The peak of LLDPE and EVA made of mixture ratio of 70 : 30 at 2$\theta$ =21.4$^{\circ}$ in the results of XRD is higher than the others. In the experiment for volume resistivity characteristics in order to investigate the electrical properties of specimen, it is confirmed that volume resistivity is decreased with the increase of the molecular motion and temperature.

• Polymer(Korea)
• /
• v.33 no.2
• /
• pp.131-136
• /
• 2009

The effect of the chemical structure of the peroxide crosslinking agent on the reactive crosslinking reaction of EVA was investigated and the physical properties of the crosslinked EVA were studied as well. It was found that peroxide with one peroxy group (perbutyl peroxide) is more effective than peroxides with two peroxy group (2,5 dimethyl 2,5 di(tert-butylperoxyl) hexane and 1,1-di(tert-buthylperoxy)-3,3,5-tri-methylcyclohexane) in melt reactive crosslinking reaction of EVA. The rate of crosslinking was increased by the use of crosslinking acceleration agent but the noticeable effect on degree of crosslinking was not found. Crosslinking caused the lowering of melt flow ability of EVA but mechanical properties were enhanced by the crosslinking of EVA.