• Maxillofacial Plastic and Reconstructive Surgery
• /
• v.28 no.5
• /
• pp.434-444
• /
• 2006

This study was performed to evaluate the effects of three different implant surface treatments to the bone formation during osseous healing period under unloading conditions. Machined, double-acid etched and anodic oxidized implants were inserted into tibia of 3.0 - 3.5 kg NZ white male rabbits and 2 animals of each group were sacrificed at 2, 4 and 8 weeks. The specimens containing implant was dehydrated and embedded into hard methylmethacrylate plastic. After grinding to $50{\mu}m$, the specimens were stained with Villanueva bone stain. From each specimen, histomorphometric evaluation and the bone implant contact rate were analysed with optical microscope. The results were as follows; 1. In the scanning electronic microscopic examination, machined surface implant had several shallow and paralleled scratches on plain surface, double acid-etched implant had lots of minute wrinkles, rough valley and also irregularly located craters that looked like waves, anodic oxidized surface implant had porosity that minute holes were wholly distributed on the surface. 2. After 2 weeks of implantation, the percentages of bone-to-implant contact in the machined implant, double acid-etched implant and anodic oxidized implant were 26.85%, 62.64% and 59.82%, after 4 weeks of implantation they were 64.29%, 77.85% and 75.23%, and after 8 weeks they were 82.66%, 85.34% and 86.39%. 3. After 2 weeks of implantation, the percentages of bone area between threads in the machined implant, double acid-etched implant and anodic oxidized implant were 21.55%, 42.81%, and 40.33%, after 4 weeks of implantation they were 49.32%, 62.60% and 75.56%, and after 8 weeks they were 71.62%, 87.73% and 83.94%. In summary, percentages of implant surface contacted to bone trabeculae and bone formation area inside threads in double acid-etched implants and anodic oxidized implants were greater than machined implants in early healing stage. These results suggest that double acid-etched and anodic oxidized surface implants could reduce the healing period for osseointegration and may enable to do early function.

• Applied Chemistry for Engineering
• /
• v.25 no.5
• /
• pp.447-454
• /
• 2014

Organic solar cells (OSCs) have intensively studied in recent years due to their advantages such as cost effectiveness and possibility of applications in flexible devices. In spite of the high power conversion efficiency (PCE) of 10 %, the OSCs still have a draw back of their low environmental stability due to the oxidization of aluminum cathode and etching of transparent conducting oxide as electrode. To solve these problems, the inverted structured OSCs (I-OSCs) having greatest potential for achieving an improvement of device performances are suggested. Therefore, there are a lot of studies to develope of interface layer based on organic/inorganic materials for the electron transport layer (ETL) and passivation layer, significant advancements in I-OSCs have driven the development of interface functional materials including electron transport layer. Recent efforts to employing 2D/3D zinc oxide (ZnO) based ETL into I-OSCs have produced OSCs with a power conversion efficiency level that matches the efficiency of ~9 %. In this review, the technical issues and recent progress of ZnO based ETL in I-OSCs to enhancement of device efficiency and stability in terms of materials, process and characterization have summarized.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.22 no.4
• /
• pp.349-365
• /
• 2006

State of problem : A number of investigation about increase of surface area via various surface treatments and modification of surface constituent have been carried out. Purpose : The surface characteristics and stability of implants treated with anodic oxidation, fluoride ion incorporation, and groups treated with both methods were evaluated. Material and method : Specimens were divided into six groups, group 1 was the control group with machined surface implants, groups 2 and 3 were anodic oxidized implants (group 2 was treated with 1M $H_2SO_4$ and 185V, group 3 was treated with 0.25M $H_2SO_4$ and $H_3PO_4$ and 300V). Groups 4, 5 and 6 were treated with fluoride. Group 4 was machined implants treated with 0.1% HF, and groups 5 and 6 were groups 2 and 3 treated with 10% NaF respectively. Using variable methods, implant surface characteristics were observed, and the implant stability was evaluated on rabbit tibia at 0, 4, 8 and 12 weeks. Result : 1. In comparison of the surface characteristics of anodic oxidized groups, group 2 displayed delicate and uniform oxidation layer with small pore size containing Ti, C, O and showed mainly rutile, but group 3 displayed large pore size and irregular oxidation layer with many crators. 2. In comparison of the surface characteristics of fluoride treated groups 4, 5, 6 and non-fluoride treated groups 1, 2, 3, the configurations were similar but the fluoride treated groups displayed rougher surfaces and composition analysis revealed fluoride in groups 4, 5, 6. 3. The fluoride incorporated anodic oxidized groups showed the highest resonance frequency values and removal torque values, and the values decreased in the order of anodic oxidized groups, fluoride treated group, control group. 4. According to implant stability tests, group 2 and 3 showed significantly higher values than the control group (P<.05). The fluoride treated groups showed relatively higher values than the non fluoride treated groups and there were significant difference between group 4 and group 1 (P<.05). Conclusion : From the results above, it can be considered that the anodic oxidation method is an effective method to increase initial bone stability and osseointegration and fluoride containing implant surfaces enhance new bone formation. Implants containing both of these methods should increase osseointegration, and reduce the healing period.

• The Journal of Korean Academy of Prosthodontics
• /
• v.49 no.1
• /
• pp.16-21
• /
• 2011

Purpose: The purpose of this study was to investigate the bioactivity of precalcified nanotubular $TiO_2$ layer on Ti-6Al-7Nb alloy. Materials and methods: Anodic oxidation was carried out at a potential of 20 V and current density of 20 mA/$cm^2$ for 1 hour. The glycerol solution containing 1 wt% $NH_4F$ and 20 wt% deionized water was used as an electrolyte. Precalcification treatment was obtained by soaking in $Na_2HPO_4$ solution at $80^{\circ}C$ for 30 minutes followed by soaking in saturated $Ca(OH)_2$ solution at $100^{\circ}C$ for 30 minutes, followed by heat treatment at $500^{\circ}C$ for 2 hours. To evaluate the activity of precalcified nanotubular $TiO_2$ layer, specimens were immersed in a simulated body fluid with pH 7.4 at $36.5^{\circ}C$ for 10 days. Results: 1. Nanotubular $TiO_2$ layer showed the highly ordered dense structure by interposing small diameter nanotubes between large ones, the shape of nanotubes was enlarged as going down. 2. The mean length of nanotubes was $517.0{\pm}23.2\;nm$ innm glycerol solution containing 1 wt% $NH_4F$ and 20 wt% $H_2O$ at 20 V for 1 hour. 3. The bioactivity of Ti-6Al-7Nb alloy was improved with formation of nanotubular $TiO_2$ layer and precalcification treatment in $80^{\circ}C$ 0.5 M $Na_2HPO_4$ and saturated $100^{\circ}C$ $Ca(OH)_2$ solution. Conclusion: Bioactivity of precalcified nanotubular $TiO_2$ layer on Ti-6Al-7Nb alloy was improved.