• Applied Chemistry for Engineering
• /
• v.8 no.5
• /
• pp.756-762
• /
• 1997

The experiment was carried out to fabricate alumina membrane which has a cylindrical pore structure by anodizing aluminium plate in sulfuric acid solution with the electrochemical technique. The aluminium plate for anodizing was prepared by the pretreatment process such as chemical, electro-polishing and thermal treatment. The pore size distribution and the film thickness of alumina membrane were investigated by the implementation of scanning electron microscope(SEM) and BET method. The results show that the oxide film has a geometrical structures like a Keller model and that the membrane has a uniform pore distribution. The pore size and the oxide film thickness are dependent on the anodizing process variables such as the electrolyte concentration, the reation temperature and the anodizing current density.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.274-274
• /
• 2015

양극산화를 통해 생기는 다공성 알루미나 산화막의 기공은 전해질과 적절한 온도 등 제작 조건에서 자기 조립하여 고도로 정렬된 (Highly ordered) 나노기공을 가지는 AAO (AnodicAluminum Oxide)를 제조하는데 주로 쓰이고 있다. 본 연구에서는 다단계 산화방법으로 빛의 파장에 무관하게 빛의 반사를 매우 효과적으로 줄이는 포물선 형태의 Moth-eye 구조를 가지는 템플릿을 제조하였다. SEM 측정을 통해 구조체 다공성 알루미늄 산화막의 표면적 변화를 알 수 있었고, 일정한 크기와 모양의 pore가 규칙적으로 형성된 것을 확인하였다. 그리고 제조된 템플릿 내부에 고분자를 채워 포물선 형태의 나노핀을 갖는 필름을 제조할 수 있었다.

• Applied Chemistry for Engineering
• /
• v.19 no.3
• /
• pp.249-258
• /
• 2008

Nanoporous alumina with highly ordered pore arrays, which is prepared based on electrochemical anodization under the controlled conditions, has attracted great attention due to the variety of its applications. In case of porous alumina, the manipulation of nanoporous structures under different electrochemical conditions and their formation mechanisms have been studied for a long time. Recently, its principles have been applied to other valve metals. Especially, there have been a big success in the preparation of titania nanotubes via the anodization of titanium. In this paper, we review the anodization of aluminum and recent trends in anodization of Ti and other valve metals based on the principles of aluminum anodization.

• Applied Chemistry for Engineering
• /
• v.9 no.4
• /
• pp.536-541
• /
• 1998

The porous size alumina membrane was prepared by anodic oxidation with current method in an aqueous solution of oxalic acid. The aluminum metal plate was pretreated with thermal oxidation, chemical polishing and electropolishing before anodic oxidation. Membrane thickness and pore size distribution were investigated with several anodizing conditions; reaction temperature, cumulative charge, electrolyte concentration and current density. The porous alumina membrane obtained was $55{\sim}75{\mu}m$ thick with straight micropore of 45~100nm. Also, the porous alumina membrane has an uniform pore diameter and pore distribution. It was inorganic ultrafiltration membrane as a kind of the ceramic membrane.

• Journal of Advanced Marine Engineering and Technology
• /
• v.29 no.1
• /
• pp.107-115
• /
• 2005

The effects on the formation of anodic oxide films on Mg-Al alloy (AZ91) in 1M-NaOH solution was investigated using parameters of current density and time during anodizing The general tendency has been confirmed that the increase of anodizing time improves the corrosion resistance. It is considered that the formation of anodic oxide film was increased by increasing the applied current and the anodizing time to generate active dissolution reaction In anodizing at constant current density. passivity potentials shifted to noble direction with increasing current densities. It was confirmed that oxygen quantify in anodic oxide films increased with anodizing time. The compact films above 4 $mA/cm^2$ were formed with the shape of an island in grooves at early stage and then grew with combination of the islands

• Proceedings of the Korean Vacuum Society Conference
• /
• 2008.02a
• /
• pp.334-334
• /
• 2008

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.298-298
• /
• 2013

플라즈마 전해산화기술은 알루미늄 소재에 대해 기존의 양극 산화막, 전해 경질크롬 도금 및 플라즈마 세라믹 용사기술 등에 의해 구현할 수 없는 고기능성을 부여하여 월등히 우수한 경도, 내부식, 내마모, 전기절연, 열저항, 피로강도 등을 얻을 수 있는 획기적인 기술이다. 또한 최근 환경에 대한 관심이 점차 높아지면서 친환경적 공정과정과 경금속 소재의 제품에 내구성을 향상시킬 필요성이 높아지고 있다. 이러한 요구에 부합하는 플라즈마 전해 산화기술은 알칼리 수용액 중에서 Al, Ti, Mg 등의 표면에 산화 피막을 형성시키는 기술로써 기존의 양극산화(Anodizing)을 대체 할 수 있다. 본 연구에서는 Al6061을 이용하여 플라즈마 전해산화 공정에 사용되는 전해액의 종류 및 농도, 시간의 변화에 따른 산화 피막의 변화를 내전압 측정 및 FE-SEM, EDS, XRD를 통해 분석하였다. 전해액에 sodium hexameta phosphate과 potassium phosphate를 이용하여 phosphate 종류의 변화에 따른 피막 특성의 변화를 연구하였다. 그로인해 phosphate의 종류 및 농도, 시간 변화를 이용하여 플라즈마 전해산화공정의 산화 피막 물성 제어를 할 수 있다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.830-833
• /
• 2002

최근 나노 구조 (nano structure)를 만들기 위한 시도 중 하나로서 스스로 조직화(self organization)하여 나노 구조를 형성하는 물질을 나노 소자 제작을 위한 형틀 (template)로 이용하려는 시도가 활발히 진행되고 있다. 이러한 물질로서 주목을 받고있는 것 중 하나가 전해질 용액에서 알루미늄을 양극산화(anodization) 시켰을 때 형성되는 다공성 알루미나 박막이다. 본 연구에서는 고 순도 알루미늄을 기계적으로 연마(mechanical polishing)하고 공기 분위기에서 어닐링 (annealing)하여 알루미늄을 재결정화(recrystallization) 시키고 인가 전압이 40 V인 정 전압하에서 0.3 M의 수산(oxalic acid)을 전해질로 사용하면서 양극산화를 수행하여 평균 직경이 65 nm인 고도로 배열된 육방밀집구조의 나노 다공성 박막을 제작하였다. 또한 같은 방향의 육방밀집 배열은 크기가 수 ${\mu}m$인 영역(grain)을 형성하고 있었으며, 평균적인 pore의 밀도는 $1.1{\times}10^{10}/cm^2$였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2000.05a
• /
• pp.29-30
• /
• 2000

• Journal of the Korean Graphic Arts Communication Society
• /
• v.7 no.1
• /
• pp.40-48
• /
• 1989