• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.26 no.3D
• /
• pp.425-433
• /
• 2006

The presented work provided a predictive equation for dynamic modulus of hot mix asphalt, which showed higher reliability and more simplicity. Lots of test result by UTM at laboratory has been used to develop the precise predictive equation. Evaluation of dynamic modulus for 13mm and 19mm surface course and 25mm of base course of hot mix asphalt with granite aggregate and two asphalt binders (AP-3 and AP-5) were carried out. Superpave Level 1 Mix Design with gyrator compactor was adopted to determine the optimum asphalt binder content (OAC) and the measured ranges of OAC were between 5.1% and 5.4% for surface HMA, and around 4.2% for base HMA. The dynamic modulus and phase angle were determined by testing on UTM, with 5 different testing temperature (-10, 5, 20, 40, & $55^{\circ}C$) and 5 different loading frequencies (0.05, 0.1, 1, 10, 25 Hz). Using the measured dynamic modulus and phase angle, the input parameters of Sigmoidal function equation to represent the master curve were determined and these will be adopted in FEM analysis for asphalt pavements. The effect of each parameter for equation has been compared. Due to the limitation of laboratory tests, the reliability of predictive equation for dynamic modulus is around 80%.

• The Journal of Engineering Geology
• /
• v.33 no.4
• /
• pp.573-586
• /
• 2023

Joints or weak planes can induce anisotropy in the strength and deformability of fractured rock masses. Comprehending this anisotropic behavior is crucial to engineering geology. This study used plaster as a friction material to mold specimens with a single joint. The strength and deformability of the specimens were measured in true triaxial compression tests. The measured results were compared with three-dimensional numerical analysis based on the distinct element method, conducted under identical conditions, to assess the reliability of the modeled values. The numerical results highlight that the principal stress conditions in the field, in conjunction with joint orientations, are crucial factors to the study of the strength and deformability of fractured rock masses. The strength of a transversely isotropic rock mass derived numerically considering changes in the dip angle of the joint notably increases as the intermediate principal stress increases. This increment varies depending on the dip of the joint. Moreover, the interplay between the dip direction of the joint and the two horizontal principal stress directions dictates the strength of the transversely isotropic rock mass. For a rock mass with two joint sets, the set with the steeper dip angle governs the overall strength. If a rock bridge effect occurs owing to the limited continuity of one of the joint sets, the orientation of the set with longer continuity dominates the strength of the entire rock mass. Although conventional three-dimensional failure criteria for fractured rock masses have limited applicability in the field, supplementing them with numerical analysis proves highly beneficial.

• Polymer(Korea)
• /
• v.28 no.1
• /
• pp.77-85
• /
• 2004

It has been widely used ultra high molecular weight polyethylene (UHMWPE) for the biomaterials due to its excellent mechanical properties and biocompatibility. In the case of blend of UHMPE with another polymeric biomaterials, however, UHMWPE might have low blend compatibility due to surface inertness. In this study, in order to improve the mechanical properties of poly(methyl methacrylate) (PMMA) bone cement by means of the impregnation of UHMWPE powder, we developed the novel surface modification method by the mixture of methyl methacrylate (MMA) and xylene. We investigated the variation of composition of MMA/xylene. It was confirmed by the analysis of Fourier transform infrared-attenuated total reflectance, scanning electron microscope, universal transverse mercator, and digital thermometer. The maximum mechanical strength of surface modified UHMWPE powder impregnated PMMA bone cement compound was observed the ratio of 1 : 1 (v/v％) MMA/xylene. Also its curing temperature decreased from 103 $^{\circ}C$ to 58 ∼ 73 $^{\circ}C$ The mechanism of surface modification of UHMWPE powder by the mixture of MMA/xylene has been proposed.

• Polymer(Korea)
• /
• v.35 no.2
• /
• pp.157-160
• /
• 2011

In this paper, poly (dimethyl siloxane) (PDMS) was modified using electron beam irradiation and its property was investigated. PDMS sheets prepared using a conventional thermal curing method were irradiated by electron beams at absorbed doses between 20 and 200 kGy and their properties were characterized using swelling degree and contact angle measurements, universal testing machine (UTM), thermogravimetric analyzer (TGA), and X -ray photoelectron spectrometer (XPS). The results of the swelling degree measurements, UTM, and TGA revealed that the swelling degree of the irradiated PDMS sheets was reduced down to 24% in comparison to the control sheet, and their compression strength and thermal decomposition temperature increased up to maximum 2.5 MFa and $10^{\circ}C$, respectively, due to the increase in crosslinking density by irradiation. In addition, on the basis of the results of contact angle measurements and XPS, the wettability of the PDMS sheets was enhanced up to 24% owing to the generation of hydrophilic functional groups on the PDMS surface by oxidation during electron beam irradiation.

• Proceedings of the Korea Inteligent Information System Society Conference
• /
• 2000.11a
• /
• pp.257-266
• /
• 2000

산업 및 가정용 기기들이 점차 복잡해짐에 따라 다양한 공학 분야의 해석 기술을 동시에 고려하면서 이들 원리를 적용한 최적의 설계를 결정하는 방법론의 필요성이 대두되고 있다. 다분야통합최적설계 또는 MDO(Multidisciplinary Design Optimization)라 일컫는 새로운 기술은 이러한 필요에 대응하는 기술로서 국내외적으로 활발한 연구가 진행되고 있다. 이러한 MDO 기술을 구현하는 소프트웨어와 하드웨어 복합 체계를 MDO 프레임웍(framework)이라 한다. 일반적으로 프레임웍이란 실제 응용프로그램의 용도에 맞는 주문제작(customization)이 가능한 일종의 전단계 프로그램이라 할 수 있다 MDO 프레임웍은 설계 및 해석 도구들간의 인터페이스를 제공하고, 이들 도구들이 사용하는 설계 데이터를 효율적으로 공유할 수 있도록 지원하여, 설계 작업을 정의, 실행, 관리하는 역할을 한다. 이러한 MDO 프레임웍은 설계 작업을 통합적으로 관리하고 자동화하여 설계 도구간의 데이터 전달과 변환에 소묘되는 설계자의 부담을 경감시키며 다분야 전문가가 참여하는 공통 작업 환경을 제공함으로써 설계 효율성을 증진시킨다. 본 논문에서는 이러한 효용을 달성하기 위한 MDO 프레임웍(framework)을 제시하고 프레임웍 설계의 논리적 근저와 타당성을 밝힌다. 본 논문에서 제안하는 다분야 통합 최적화를 위한 분산형 지능 시스템인 DisMDO는 사용자가 GUI를 동해서 편리하게 다분야통합최적화 문제를 해결할 수 있도록 지원하며, 제공되는 스크립트 언어를 동해서도 이를 정의할 수 있도록 지원하여 일괄처리도 가능하도록 한다. 또한, 집중화된 데이터베이스를 관리하여 다분야 전문가들이 공통의 데이터를 안전하게 공유할 수 있도록 지원하며, 외부에서 제공되는 해석 도구나 최적화 모듈을 손쉽게 프레임웍에 통합시킬 수 있도록 하는 인터페이스 제작기(factory) 기능을 제공한다.ackscattering spectroscopy, X-ray diffraction, secondary electron microscopy, atomic force microscoy, $\alpha$-step, Raman scattering spectroscopu, Fourier transform infrared spectroscopy 및 micro hardness tester를 이용하여 기판 bias 전압이 DLC 박막의 특성에 미치는 영향을 조사하였다. 분석결과 본 연구에서 제작된 DLC 박막은 탄소와 수소만으로 구성되어 있으며, 비정질 상태임을 알 수 있었다. 기판 bias 전압의 증가에 따라 박막의 두께가 감소됨을 알 수 있었고, -150V에서는 박막이 거의 만들어지지 않았으며, -200V에서는 기판 표면이 식각되었다. 이것은 기판 bias 전압과 ECR 플라즈마에 의한 이온충돌 효과 때문으로 판단되며, 150V 이하에서는 증착되는 양보다 re-sputtering 되는 양이 더 많을 것으로 생각된다. 기판 bias 전압을 증가시킬수록 플라즈마에 의한 이온충돌 현상이 두드러져 탄소와 결합하고 있던 수소원자들이 떨어져 나가는 탈수소화 (dehydrogenation) 현상을 확인할 수 있었으며, 이것은 C-H 결합에너지가 C-C 결합이나 C=C 결합보다 약하여 수소 원자가 비교적 해리가 잘되므로 이러한 현상이 일어난다고 판단된다. 결합이 끊어진 탄소 원자들은 다른 탄소원자들과 결합하여 3차원적 cross-link를 형성시켜 나가면서 내부 압축응력을 증가시키는 것으로 알려져 있으며, hardness 시험 결과로 이것을 확인할 수 있었다. 그리고 표면거칠기는 기판 bias 전압을 증가시킬수록 더 smooth 해짐을 확인하였다.인하였다.을 알 수 있었다. 즉 계면에서의 반응에 의해 편석되는 Ga에 의해 박막의 strain이 이완되면, pinhole 등의 박막결함

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.22 no.2
• /
• pp.378-385
• /
• 2021

The production of plum jangachi requires the cleaning of plums, immersion in saltwater, separation of seed and pulp, removal of impurities, and addition of sugar. In most farms, the separation of plum seed and pulp is carried out manually, requiring considerable labor, which is why plum jangachi is expensive. To solve this problem, this study designed and manufactured automatic, semi-automatic plum seed and pulp separators. During the design process, the characteristics were compared, and the machine power was determined through on-site test after manufacture. As a result, automatic machines used plums 180° arrayed and six reverse-edged blades, semi-automated plums 180° arrayed, and six blades, each with a 68% and 57% pulp recovery rate and a machine power of 80 kg/h and 62 kg/h respectively. Overall, the mechanization of plum processed food will reduce labor and increase the market value of plums compared to the previous method.

• Tunnel and Underground Space
• /
• v.32 no.6
• /
• pp.353-362
• /
• 2022

The wet shotcrete refers to a method in which all materials are mixed and then supplied to the spraying device, compressed air is added to the nozzle, and the spraying speed is improved to spray on the target surface. In order to reproduce the amount of shotcrete used in the wet method in the field and the situation at the laboratory scale, it is essential to control the discharge amount of the equipment. In this study, in order to increase the reproducibility of field conditions at the laboratory scale, a flow control system for shotcrete mortar spraying equipment was developed and applied to the equipment. To verify the developed equipment, a discharge control test using water and mortar was performed. In the developed control system, the discharge was smoothly controlled according to the user input value for the mono pump, but the discharge was not properly controlled according to the input value for the screw pump because of a reducer. When a speed reducer is attached, it is necessary to adjust the operation rate of the screw pump close to the target flow rate by increasing the operation rate of the screw pump while lowering the operation rate of the mono pump.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.3
• /
• pp.1-7
• /
• 2018

As part of a research dedicated to the field evaluation of the durability of concrete subjected to freezing-thawing, this study analyzes the relationship between the surface roughness and the relative dynamic elastic modulus through image analysis. Four mix compositions with water-to-binder ratios (W/B) of 40%, 50%, 60% and 70% and without AE agent were considered to provoke early freezing. The basic physical properties of the mixes including the relative dynamic elastic modulus and the compressive strength were first evaluated experimentally according to W/B. Then, tests were performed to measure the surface roughness followed by photographs and SEM image analysis. The measured surface roughness tended to increase with larger number of freezing-thawing cycles regardless of W/B. The relative dynamic elastic modulus appeared to increase gradually with the number of cycles for the relatively denser mixes with W/B of 40% and 50%. Besides, the surface roughness increased only at rupture for the mixes with W/B of 60% and 70%. Moreover, the analysis of the photographs of the surface of the mixes with W/B of 40% and 50% revealed that the degradation progressed gradually from the surface with the freezing-thawing cycles. However, for the mixes with W/B of 60% and 70%, apparent change of the surface remained very insignificant until rupture at which damage like cracking could be observed. Consequently, the analysis of surface photograph or the measurement of the surface roughness presented some limitation in assessing the degree of freezing-thawing-induced degradation in case of relatively porous specimens. On the other hand, the photograph and surface roughness appeared to be sufficient for assessing such degradation for the mixes with W/B of 40% and 50%. Accordingly, the image of the surface and the surface roughness are potentially applicable on site for the assessment of freezing-thawing damages in relatively dense mixes.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.11 no.4
• /
• pp.1798-1802
• /
• 1969

The experiment was carried out as one of the basic studies to improve the alkali-resistance of cement mortars and it was conducted to investigate some propetties of mortars relating to weight losses when exposed to 0.1 N salution of sodium hydroxide. The experiment and the results obtained are summarized as follow; 1. The specimens used in this experiment were made of 5 centi-meter cubes of mortar having such various ratios of mix by weight as 1 : 1, 1 : 3, 1 : 5, 1 : 7 and 1 : 10. 2. Physical tests included compressive strengths at 7 days, 28 days, 3 months, and 6 month, and 5 hour boiling absorption test. 3. In alkali test, every specimen was immersed into 0.1 N solutions of sodium hydroxide. The specimens exposed to the alkali solution were weighed to determine the weight losses of the alkail-corroded at one week interval for 7 week's exposure and the old alkali solutions were also changed to fresh solutions when weighed the weight losses by alkali attack at one week interval. 4. According to the alkail test after 7 week's exposure, no weight losses were observed on ratios of mix 1:1 and 1:3 and slight weight losses occurred on ratios of mix 1:5 and 1:7, but relatively large amount of weight losses were showed by 36.6 per-cent on ratios of mix 1:10. It was also found that the weight losses of the alkali-corroded were extremely lower than those of the acid-corroded at the some concentrations as 0.1 N of solutions. 5. In order to make better quality of alkali-resistant mortar it might recomend that a 1:7 mix or richemixes, use of small amount of mixing water for watertight, 20 per cent or less absorption by 5 hour boiling 1,600 kirogram per cubic meters or denser densities by absolute dry base are available for physical properties of mortar. It could conclude acid-resistant mortars were so high alkali-resistant, that it is expected to make and improve the acid-resistant mortars for getting rid of damages by alkali attack.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.26 no.2
• /
• pp.121-143
• /
• 2010

To investigate the effect of implant types and bone resorption on the fracture characteristics. 4 types of Osstem$^{(R)}$Implant were chosen and classified into external parallel, internal parallel, external taper, internal taper groups. Finite elements analysis was conducted with ANSYS Multi Physics software. Fatigue fracture test was performed by connecting the mold to the dynamic load fatigue testing machine with maximum load of 600N and minimum load of 60N. The entire fatigue test was performed with frequency of 14Hz and fractured specimens were observed with Hitachi S-3000 H scanning electron microscope. The results were as follows: 1. In the fatigue test of 2 mm exposed implants group, Tapered type and external connected type had higher fatigue life. 2. In the fatigue test of 4 mm exposed implants group, Parallel type and external connected types had higher fatigue life. 3. The fracture patterns of all 4 mm exposed implant system appeared transversely near the dead space of the fixture. With a exposing level of 2 mm, all internally connected implant systems were fractured transversely at the platform of fixture facing the abutment. but externally connected ones were fractured at the fillet of abutment body and hexa of fixture or near the dead space of the fixture. 4. Many fatigue striations were observed near the crack initiation and propagation sites. The cleavage with facet or dimple fractures appeared at the final fracture sites. 5. Effective stress of buccal site with compressive stress is higher than that of lingual site with tensile stress, and effective stress acting on the fixture is higher than that of the abutment screw. Also, maximum effective stress acting on the parallel type fixtures is higher. It is careful to use the internal type implant system in posterior area.