• Journal of the Korean Society for Precision Engineering
• /
• v.27 no.3
• /
• pp.66-72
• /
• 2010

Recently, the use of means of transportation of the lightweight aluminum to temper the trend is increasing. More efficient use of lightweight aluminum material to Friction stir welding has been widely attempted. Types of welding tools at the right screw to rotate anti-clockwise direction, when the tensile stress exerted on the location of the top plate to the left in the direction of the welding process to the installation was able to obtain high tensile strength. A5052 to the top of the left in the direction of the welding process to install and, when you installed the right under the A6061 was not easily come up to the top of the A5052. Conversely, at the bottom left to install on top of the A6061 and A5052 have been installed at the bottom of the upper area of the A6061 and A5052 intrude easily form the shape of the hill you can see that it was formed.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.9
• /
• pp.663-668
• /
• 2016

Increasing fuel economy and reducing air pollution have been unavoidable issues in the development of new cars, and one of the important methods is decreasing vehicle weight. Weight can be reduced by using lightweight materials such as aluminum alloy. Dynamic stiffness analysis was performed and compared for different materials for the knuckle for a car. The dynamic stiffness of 6061 aluminum alloy was about 30% higher than that of FCD600 cast iron. Usually, materials that have high dynamic stiffness show excellent vibration resistance because the dynamic stiffness can affect the vibration characteristics. In order to design a lighter and more reliable chassis component using 6061 aluminum alloy (AA6061-T6), a new knuckle shape is suggested by adding section ribs to an existing knuckle model. The effect of each design change on the reliability and component weight was investigated using computer aided engineering (CAE).

• Korean Chemical Engineering Research
• /
• v.53 no.6
• /
• pp.677-681
• /
• 2015

Aluminum alloy was examined as a material of low weight reactor for hydrolysis of $NaBH_4$. Aluminum is dissolved with alkali, but there is NaOH as a stabilizer in $NaBH_4$ solution. To decrease corrosion rate of aluminum, decrease NaOH concentration and this result in loss of $NaBH_4$ during storage of $NaBH_4$ solution. Therefore stability of $NaBH_4$ and corrosion of aluminum should be considered in determining the optimum NaOH concentration. $NaBH_4$ stability and corrosion rate of aluminum were measured by hydrogen evolution rate. $NaBH_4$ stability was tested at $20{\sim}50^{\circ}C$ and aluminum corrosion was measured at $60{\sim}90^{\circ}C$. The optimum concentration of NaOH was 0.3 wt%, considering both $NaBH_4$ stability and aluminun corrosion. $NaBH_4$ hydrolysis reaction continued 200min in aluminum No 6061 alloy reactor with 0.3 wt% NaOH at $80{\sim}90^{\circ}C$.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.67-67
• /
• 2009

알루미늄 합금 재질은 무게의 경량화와 기계적강도가 우수하며 다른 비철금속에 비하여 값이 저렴한 장점이 있다. 현재 산업현장에서 활용하는 가장 흔한 접합법으로 TIG, RSW 등과 같은 용융 용접법을 현재는 많이 사용 하고 있지만 열전도도가 높아 열 확산이 빠르고, 이에 따라 모재의 팽창이 일어나 열변형을 유발하며, 산화피막은 그 내부에 함유된 결정수가 아크용접 중 분해되어 수소를 방출함으로 기공이 발생하여 부도체로 저항용접시 전도성을 방해하는 등의 문제를 발생시킨다. 또한 철에 비해 4배정도 큰 전기전도율에 따라 저항용접시 대전류를 사용해야 하는 등의 문제점이 발생하고 있다. 이와 같은 알루미늄 합금의 용융용접 과정에서 발생하는 단점을 극복하는 기술로 고상접합 방법인 마찰교반용접법(Friction Stir Welding)이 활용되고 있다. FSW는 1991년 영국의 TWI에서 개발된 최신 용접법으로 모재를 용융점 아래에서 고상용접시키는 방법으로 용융에 따른 열변형과 흄가스(hume gas)와 스패터(spatter)를 억제시켜 주는 친환경적인 용접법이다. 이러한 마찰교반용접의 기술은 그동안 특허에 따른 로열티가 산업현장에서 사용하는데 문제가 되었으나 특허보호 기간인 20년이 1년정도의 기간밖에 남지 않은 상황에서 그 사용은 날로 증가하리라 본다. 이러한 마찰교반용접부의 결함을 평가하는 방법에는 UT, RT 등이 활용되고 있으나 얇은 박판에서의 결함검출은 용이하지 않다. 이리한 문제점을 해결하기위하여 초음파 가진을 이용한 적외선 열화상 검출 기법을 이용하여 마찰교반용접부의 결함 검출 가능성을 연구하였다. 20kHz의 주파수를 400Watt로 가진시켜 겹치기(lap joint) 마찰교반용접이된 A6061-T6의 용접부에 초음파를 입사하였을 때 발생하는 열을 적외선 열화상 카메라를 이용하여 측정함으로써 마찰교반겹치기 용접부의 결함 검출에 활용하였다. 용접부에 초음파를 입사하였을 때 부분적으로 온도차이가 발생하였고, 그에 따른 열화상을 검출 할 수 있었다. 이러한 열화상과 실제 시험편의 용접부의 강도를 평가하기 위하여 인장시험을 하였다. 그 결과 초음파 적외선 열화상 검출에서 발열부위가 나타난 부분이 인장시험에서 낮은 인장강도를 보였다.