• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.445-448
• /
• 2008

It is essential that concrete component is made up with aggregate, cement and water. But today, Public concern is increasing of a variety structure and ocean environmental, resource recycle. Also, According to heat of hydration rising, Concrete is make a causative of concrete-crack. Concrete-crack cause a falling-off in quality of concrete. consequently, High-performance concrete is evaluated by concrete material properties and carbonation resistance with different admixture(fixing fly-ash 20%), granulated blast furnace slag replacement ratio (30%, 45%) different W/B (26%, 30%, 34%) and XRD(X-ray Diffraction) analysis.

• Journal of the Korea Institute of Building Construction
• /
• v.20 no.5
• /
• pp.433-440
• /
• 2020

In this study, a new type of Durometer was invented by modifying the currently used Durometer with the hemisphere shaped needle to columnar shaped needle. The aim of the study is, hence, to provide the feasibility of the advanced Durometer for assessing setting time of the concrete. Generally, the finishing of concrete surface should be conducted to secure the smooth surface, improve the permeability, and prevent the plastic shrinkage cracking. Although this surface finishing work should be conducted during the plastic phase between initial and final setting, currently in practical situations, the timing of starting the finishing work was determined by the sense of the worker. To improve this situation, Kato Junji suggested to use the hemisphere and needle shaped Durometers to determine the initial and final setting time, respectively. However, in this case, there are difficulties of using two different Durometers and of occurring failure of the Durometer due to the intruded cement paste. To prove the feasibility of new typed Durometer, setting time and surface hardness were evaluated by applying for the concrete with various replacing ratios of fly-ash and coal gasification slag as an aggregate.

• Journal of the Korea Institute of Building Construction
• /
• v.20 no.5
• /
• pp.409-416
• /
• 2020

In this paper, strength correction factors of the concretes incorporating ordinary Portland cement(OPC), fly ash(FA) and blast furnace slag(BS) with 50% of water to binder ratio due to temperature drop for standard room temperature(20±3℃) are provided. For this, strength development was done based on equivalent age method. For calculating the equivalent age, apparent activation energy was obtained with 24.69 kJ/mol in OPC, 46.59 kJ/mol in FA, 54.59 kJ/ol in BS systems. According to the estimation of strength development of the concretes, the use of FA and BS resulted in larger strength drop than that of OPC under low temperature compared to standard room temperature. Hence, strength correction factors(Tn) for OPC, FA and BS are suggested within 4~17℃ with every 3MPa levels.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.1
• /
• pp.111-118
• /
• 2016

The scaling of concrete caused by the combined effects of frost and deicing salt is one of the principle causes of damage to transportation infrastructure in cold-climate regions. In this study, to evaluate the factors affecting scaling resistance of concrete, the relationship between the properties of concrete, such as the mechanical properties and pore structure, and scaling resistance was examined experimentally. The test results showed that the scaling resistance was strongly dependent on the absorption properties of concrete, but not on the compressive strength. Furthermore, it is believed that both the spacing factor and specific surface of the air voids was not a good parameter for evaluating the scaling resistance of concrete. SGC concrete was less durable than OPC and SFC concrete with respect to the scaling resistance in the scope of the present study.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.2
• /
• pp.216-222
• /
• 2021

This is an experiment to complement new ways of using concentrated water discharged from the seawater desalination plant. In this study, metakaolin, which has excellent chloride ion immobilization effect, was used as the main binder, and 10% and 20% of calcium oxide were substituted with the activator. In addition, tap-water(TW) and reverse osmosis brine water(RW) were used as mixed water. As a result of the experiment, the mixture using RW showed higher compressive strength than TW. It also showed low water absorption and high density. In the mixture using RW as mixed water, a hydration reaction substance called Friedel's salt could be observed. Considering the corrosion problem of steel, RW is considered to be applicable to products such as non-reinforced concrete, brick, and curb stone. Through this study, it is thought that it is meaningful to propose a new application method other than the ocean release of RW.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.1
• /
• pp.1-7
• /
• 2019

Recently, studies on alkali activated slag(AAS) binders that do not use cement have been actively conducted. It is known that AAS concrete is highly resistant to chloride damage based on the test method used for ordinary concrete. However, it is fully not understood whether the test method used for concrete can be applied to AAS mixtures. Therefore, in this study, we verified the consistency of NT Build 492 and ASTM C 1202 test methods by applying various experimental variables. According to the experimental results, the two tests yielded opposite results. Therefore, the chloride durability of AAS mortar can be different depending on the evaluation method.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.11 no.6
• /
• pp.143-151
• /
• 2007

This study presents the experimental results of frost durability including resistance to freezing-thawing and surface scaling of concrete. Mixing design was proportioned with the various water-binder ratio between 0.37 and 0.47 and three different binder compositions corresponding to Type I cement without any supplementary cementitious materials(OPC), Type II cement with 50% blast-furnace slag replacement(BFS50), and ternary cement with Type III cement, 15% fly ash, and 35% slag replacement (BFS35%+FA15%). Test results showed that the mixing design with BFS50% and BFS35%+FA15% exhibited higher durability factor than that made with OPC only. Finally, the use of blend cement containing slag can be used effectively in terms of frost durability of the concrete exposed to severe condition under coastal environment like as flying salt, sea water spray, etc.

• Journal of the Korea Concrete Institute
• /
• v.27 no.2
• /
• pp.95-102
• /
• 2015

In this paper, the effects of sodium hydroxide (NaOH) and aluminum potassium sulfate ($AlK(SO_4)_2{\cdot}12H_2O$) dosage on strength properties were investigated. For evaluating the property related to the dosage of alkali activator, sodium hydroxide (NaOH) of 4% (N1 series) and 8% (N2 series) was added to 1~5% (K1~K5) dosage of aluminum potassium sulfate ($AlK(SO_4)_2{\cdot}12H_2O$) and 1% (C1) and 2% (C2) dosage of calcium oxide (CaO). W/B ratio was 0.5 and binder/ fine aggregate ratio was 0.5, respectively. Test result clearly showed that the compressive strength development of alkali-activated slag cement (AASC) mortars were significantly dependent on the dosage of NaOH and $AlK(SO_4)_2{\cdot}12H_2O$. The result of XRD analysis indicated that the main hydration product of $NaOH+AlK (SO_4)_2{\cdot}12H_2O$ activated slag was ettringite and CSH. But at early ages, ettringite and sulfate coated the surface of unhydrated slag grains and inhibited the hydration reaction of slag in high dosage of $NaOH+AlK(SO_4)_2{\cdot}12H_2O$. The $SO_4{^{-2}}$ ions from $AlK(SO_4)_2{\cdot}12H_2O$ reacts with CaO in blast furnace slag or added CaO to form gypsum ($CaSO_4{\cdot}2H_2O$), which reacts with CaO and $Al_2O_3$ to from ettringite in $NaOH+AlK(SO_4)_2{\cdot}12H_2O$ activated slag cement system. Therefore, blast furnace slag can be activated by $NaOH+AlK(SO_4)_2{\cdot}12H_2O$.

• Journal of the Korea Concrete Institute
• /
• v.20 no.3
• /
• pp.405-412
• /
• 2008

Six alkali-activated (AA) concrete mixes were tested to explore the significance and limitations of developing an environmental friendly concrete. Ground granulated blast-furnace slag and powder typed sodium silicate were selected as source material and an alkaline activator, respectively. The main parameter investigated was the replacement level of lightweight fine aggregate to the natural sand. Workability and mechanical properties of lightweight AA concrete were measured: the variation of slump with time, the rate of compressive strength development, the splitting tensile strength, the moduli of rupture and elasticity, the stress-strain relationship, the bond resistance and shrinkage strain. Test results showed that the compressive strength of lightweight AA concrete sharply decreased when the replacement level of lightweight fine aggregate exceeded 30%. In particular, the increase in the discontinuous grading of lightweight aggregate resulted in the deterioration of the mechanical properties of concrete tested. The measured properties of lightweight AA concrete were also compared, wherever possible, with the results obtained from the design equations specified in ACI 318-05 or EC 2, depending on the relevance, and the results predicted from the empirical equations proposed by Slate et al. for lightweight ordinary Portland cement concrete. The stress-strain curves of different concrete were compared with predictions obtained from the mathematical model proposed by Tasnimi. The measured mechanical properties of lightweight AA concrete generally showed little agreement with the predictions obtained from these equations.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.2
• /
• pp.117-125
• /
• 2014

This paper examines the fundamental properties of alkali-activated slag cement (AASC) activated by sodium hydroxide (NaOH). The water to binder (W/B) ratio was 0.4 and 0.5. And concentration of activator were 2M and 4M. Five mix design of each W/B ratios was considered. The N0 mixture was KS L 5109 method and N1~N4 were varied in different mixing time, mix step and entering points of fine aggregate. Test results clearly showed that the flow value, strength and drying shrinkage development of AASC were significantly dependent on the entering point of fine aggregate. The flow value tended to decreases with delaying entering point of fine aggregate. The compressive strength and flexural strength increases with delaying entering point. Moreover, the XRD analysis confirmed that there were sustain these results. The drying shrinkage increases with delaying entering point of fine aggregate. Futhermore, a modified mixing method incorporating all hereby experimentally derived parameters, is proposed to improvement the physical properties of AASC.