• Applied Chemistry for Engineering
• /
• v.24 no.3
• /
• pp.247-252
• /
• 2013

Sulfonated poly(ether ether ketone) (SPEEK) with a certain degree of sulfonation were synthesized by reacting PEEK and sulfuric acid at different reaction time. Then ion-selective composite carbon electrodes (ISCCE) were fabricated by coating the prepared SPEEK on the surface of carbon electrodes. The specific capacitance and resistance of the ISCCE were analyzed by electrical impedance spectroscopy. The ion exchange capacities (IEC) of the SPEEKs were measured in the range of 1.60~2.57 meq/g depending on the sulfonation time. The SPEEK more than 2.5 meq/g of IEC was considered unsuitable for fabricating the ISCCE because it was dissolved in water. The specific capacitance of the prepared ISCCE increased with increasing the IEC of coated SPEEKs and the capacitance was improved up to about 20% compared to that of uncoated carbon electrode. In addition, the electrical resistance of coating layer decreased significantly with increasing the IEC of coated SPEEKs. It is expected that the desalination efficiency of conventional capacitive deionization process can be improved by using the prepared ISCCE coated with SPEEK.

• KSBB Journal
• /
• v.14 no.3
• /
• pp.297-302
• /
• 1999

The polymeric matrices coated with poly(DL-lactide) were prepared using chitosan derivatives such as chitosan, chitosan hydrochloride, and sulfonated chitosan for application of drug delivery systems. The drug release study using prednisolone as a model drug was performed in the hydrochloride solution at pH 1.2. The release rate of drug was decreased according to the increased content of matrices. The release rate of prednisolone according to the kinds of polymeric matrices coated were decreased in the order to chitosan, sulfonated chitosan, and chitosan hydrochloride. Drug release rate of polymeric matrices coated with poly(DL-lactide) was not only two times slower than noncoated one, but also the burst effect of initial period of drug release was decreased in comparison with noncoated one. From these results, it was expected that these formulations based on the chitosan derivative matrices coasted with poly(DL-lactide) were acceptable drug delivery devices for a sustained-release dosage form of drug.

• Membrane Journal
• /
• v.21 no.3
• /
• pp.270-276
• /
• 2011

A nascent membrane was prepared by using the solution evaporation method with a solution of sPEEK, EdAn (cross-linking reagent), and PEA (grafting reagent) in DMAc. Then, after the imination and sulfonation process the cross-linked and grafted ion-exchange membrane, CG-sPEEK, was obtained. The sulfonation and imination reactions were confirmed by FTIR analysis. In order to evaluate the possibility of prepared membrane for the use of an ion-exchange membrane in PEMFC, proton conductivity, water uptake and volume change were measured and compared with a commercial membrane, Nafion 115. It was revealed that since the proton conductivity (0.17 S/cm) of prepared membrane were much higher than those of Nafion 115 (0.10 S/cm) the prepared membrane could be used for the ion-exchange membrane in PEMFC. However, the high water uptake (130%) of CG-sPEEK should be reduced for the dimension stability.

• Membrane Journal
• /
• v.24 no.4
• /
• pp.292-300
• /
• 2014

Chlorine-resistant sulfonated poly(arylene ether sulfone) random copolymer (SPAES)-thin film composite (TFC) membranes for desalination are prepared using monoglyme as a selective solvent, which dissolves SPAES, but should be inert to porous polysulfone layer (e.g., Udel$^{(R)}$). Different from formic acid and diethylene glycol used as other selective solvents, monoglyme is environmentally friendly and has much lower boiling temperature. After a pretreatment of Udel$^{(R)}$ support film in isopropyl alcohol-glycerine mixture to minimize pore penetration leading to fairly reduced water flux, coating of SPAES solution in monoglyme onto the support and stepwise drying processes are conducted for defect-free TFC formation. The transport behavior through SPAES-TFC membranes is observed, correlating with the effects of sulfonation level, protonation, and physical and chemical crosslinking of SPAES selective layers.

• Membrane Journal
• /
• v.26 no.2
• /
• pp.146-151
• /
• 2016

Sulfonated poly (arylene ether sulfone) (SPAES) random copolymers have merits such as high proton conductivity, relatively low production cost, and thermochemical resistance when applied as polymer electrolyte membranes for fuel cells. However, it is difficult to directly employ SPAES copolymers into practical fuel cell membrane applications owing to their low chemical stability and dimensional instability under harsh operation conditions. A plausible solution is to impregnate SPAES copolymers into support films (e.g., electrospun polyimide support) with interconnected pore structures and high thermochemical toughness. In this study, a SPAES copolymer with a swivel group, which induces high free volume for fast ion transport, is chosen as ionomers to prepare pore-filling membranes (PFMs). The feasibility of the resulting membranes is evaluated via membrane characterizations.

• Membrane Journal
• /
• v.16 no.4
• /
• pp.276-285
• /
• 2006

Acid-doped sulfonated poly(aryl ether benzimidazole) (S-PAEBI) copolymers were synthesized by a direct polymerization technique and a doping with phosphoric acid as a dopant, and the polymer electrolyte membranes were fabricated from them by a solution casting method. To optimize the reaction condition, the degree of sulfonation and doping level were varied in the ranges of $0{\sim}60%\;and\;0.7{\sim}5.7$, respectively. Physiochemical properties of the doped membranes were investigated by AFM, TGA and the measurement of proton conductivity. It was found that proton conductivities depend on doping levels of membranes. Conductivity determined at the condition of $130^{\circ}C$ and no humidity was $7.3{\times}10^{-2}S/cm$ for the $H_3PO_4$-doped PAEBI membrane with a doping level of 5.7.

• Transactions of the Korean hydrogen and new energy society
• /
• v.30 no.3
• /
• pp.227-236
• /
• 2019

In this work, preparation and characterizations of hybrid membranes containing sulfonated poly(arylene ether sulfone) (SPES) and sulfonated poly(vinylidene fluoride-co-hexafluoropropylene) (SPVdF-co-HFP) (20, 30 or 40 wt%) were carried out. The structure of hybrid membranes was confirmed using X-ray diffraction (XRD) analysis and the Fourier transform infrared (FT-IR) spectroscopy. The prepared SPAES/SPVdF-30 membrane exhibits higher ionic conductivity of 68.9 mS/cm at $90^{\circ}C$ and 100% RH. Besides, the other studies showed that the hybrid membrane has good oxidation stability, thermal stability, and mechanical stability. Thus, we believe that the prepared hybrid membrane is suitable for the development of membranes for fuel cell applications.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.11a
• /
• pp.85.2-85.2
• /
• 2010

There is widespread effort to develop polymer membranes in place of Nafion for high temperature polymer electrolyte membrane fuel cell(PEMFC). In our study, SiO2 membranes are arranged by electrospinning method. For impregnation solution, the modified sulfonated poly(ether ether ketone)(SPEEK) polymer is prepared from sulfonation, sulfochlorination, partial reduction and lithiation reaction. The modified polymer is cross-linked with 1,4-diiodobetane in NMP solvent and then blended with Heteropoly acid(HPA). The characterization of membranes is confimed by FT-IR, Thermogravimetry(TGA), water uptake test and single cell performance test for PEMFC, etc. The composite membrane shows satisfactory thermal and mechanical properties. Beside, The membrane exhibits good ion exchange capacity and high proton conductivity. As a result, The composite membrane is promising as an alternative membrane in high temperature PEMFC.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.426-426
• /
• 2008

Blend membranes were prepared by solvent casting method from sulfonated fluorinated poly(arylene ether)s (SDFF) and chemically modified polyvinylidene fluoride (mPVdF) in isopropanol and were evaluated as proton exchange membrane electrolytes in PEMFC. $^1H$-NMR, differential scanning calorimeter and thermogravimetric analysis was utilized to characterize the structure of the blend membranes (SDFF/mPVDF) and effects of mPVDF content on the properties of the membrane such as water uptake and proton conductivity were also investigated.

• Transactions of the Korean hydrogen and new energy society
• /
• v.28 no.3
• /
• pp.246-251
• /
• 2017

To fabricate a hydrocarbon polymer electrolyte composite membrane incorporated with Pt nanoparticle, the polymer electrolyte membrane made of a sulfonated-fluorinated hydrophilic-hydrophobic block copolymer (SFBC) and sulfonated poly (ether ether ketone) (SPEEK) blend in the wight ratio of 1 : 1 was synthesized, and a simple drying process was used in order to incorporate Pt nanoparticle into the SFBC/SPEEK film by reducing platinum (II) bis (acetylacetonate), Pt $(acac)_2$. The distribution of the Pt nanoparticles was observed by transmission electron microscopy (TEM), and mechanical and thermal properties were tested by universal testing machine (UTM) and thermogravimetry analyzer (TGA). Cation conductivity, ion exchange capacity (IEC) and I-V characteristics were estimated.