• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2013.11a
• /
• pp.154-155
• /
• 2013

The aim of this work is to have a better knowledge of reactions that take place in a cement paste, blast furnace slag mixed cement paste and fly ash mixed cement paste and know about the change in chemical components exposed to elevated temperature. The results show that the dehydration reactions appeared differently in the each admixture mixed cement paste and can be used as tracers for determining the temperature history of concrete after a fire exposure.

• Proceedings of the KIEE Conference
• /
• 1985.07a
• /
• pp.191-193
• /
• 1985

Reaction temperature md piezoelectric properties of Pb(Mn1/3 Sb2/3)0.08 Ti0.495 Zr0.425 $O_3$ ceramics by hydrothermal synthesis method have been investigated. Sintering density and dielectric constant of sample increased with increasing of hydrothermal reaction temperature, while decreased rapidly above $240^{\circ}C$. Electromechanical coupling factor kp was almost constant at the reaction temperature $160^{\circ}-240^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.37 no.8
• /
• pp.811-816
• /
• 2000

This paper discussed hydrothermal reactivity of Ca(OH)2 and classified bituminous fly ashes which were collected at an electrostatic precipitator in coal fired power plant at 181$^{\circ}C$. The major products of hydrothermal reaction were tobermorite and hydrogrossularite because bituminous fly ashes contained Al2O3 content greater than 20 wt%. As increasing amount of Al2O3 content greater than 20 wt%. As increasing amount of Al2O3 in glass phases, formation of hydrogrossularite increased. Formation rate of crystalline tobermorite increased with content of finer particles, higher glass content and more Al2O3 in glass phases. There was a positive correlation between residue on 45${\mu}{\textrm}{m}$ sieve and hydrothermal reactivity of fly ash up to 3 hours. The hydrothermal reactivity of fly ash at 181$^{\circ}C$ for 12 hours was more affected by fineness than by glass content of fly ash.

• Applied Chemistry for Engineering
• /
• v.30 no.6
• /
• pp.749-756
• /
• 2019

Na-X and Na-A zeolites that give high adsorption capacity for heavy metals in an aqueous system were synthesized from the coal fly ash obtained from a thermoelectric power plant using a fusion method. The characteristics and Cu(II) adsorption capacity of the synthetic zeolites were also compared to those of using a commercial zeolite. For the selection of optimum conditions of zeolite synthesis, the effects of major parameters in the fusion method such as a dosage ratio of NaOH, aging time, hydrothermal reaction time, and also the dosage ratio of NaAlO₂ (Na-A) on the characteristics and Cu(II) adsorption capacity of the synthetic zeolites were studied. For the analysis of characteristics of the synthetic zeolites, X-ray diffraction (XRD), cation exchange capacity (CEC), Brunaue-Emmett-Teller (BET) and scanning electron microscopy (SEM) were used. The optimum conditions for the synthesis of zeolites with a high adsorption capacity for cationic heavy metals including Cu(II) were the aging time of 6 h, hydrothermal reaction time of 6 h and NaOH and NaAlO₂ dosage ratio of 1.5 and 0.5 (Na-A), respectively. According to the Langmuir isotherm test, maximum Cu(II) adsorption capacities of the synthetic and commercial Na-X and Na-A zeolites were found to be 90.1, 105.26, 102.05, and 109.89 mg/g, respectively. This indicates that the adsorption capacity of synthetic zeolites was comparable to commercial ones. The results of this study also suggest that the coal fly ash can be potentially used as a raw material for the zeolite synthesis.

• Applied Chemistry for Engineering
• /
• v.16 no.3
• /
• pp.413-421
• /
• 2005

This study focused on the decomposition of toluene in a plasma-photocatalytic hybrid system. Hexagonally packed meso-structured Mn-titanosilicates (Mn-Ti-MCM-41), as the photocatalysts, have been prepared by the hydrothermal method. The physical properties of the photocatalysts were characterized using XRD, XPS, TEM, BET/ICP, and $NH_3$/Toluene-TPD. Experiments were carried out at the applied voltage of 9.0 kV and at room temperature of $20^{\circ}C$. In the plasma only system, the activity of the toluene decomposition was higher than that in the photocatalytic system. However, the amount of by-products, such as phenol, $C_2{\sim}C_4$ alkene, was also increased in the plasma only system. However, the by-products decreased remarkably in a plasma-photocatalytic hybrid system. When Mn5mol%-Ti-MCM-41 was used as a photocatalyst in a plasma-photocatalytic hybrid system, the $CO_2$ selectivity in products was increased dramatically compared to other catalysts. It was confirmed that a plasma-photocatalytic hybrid system was better for toluene decomposition compared to photocatalytic and plasma only systems.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.12 no.6
• /
• pp.329-334
• /
• 2002

The $CaTio_3$powder with perovskite structure was synthesized by mixing anatase $TiO_2$and $Ca(OH)_2$powders as starting materials, and KOH or NaOH as mineralizer, followed by hydrothermal method. The change of crystal structure, particle shape and size of the synthesized $CaTiO_3$powder was investigated with kind and concentration of mineralizer. It was found that the spherical particles of 0.7 $\mu$m were obtained when using 1N KOH and the hexahedrons particles of 3$\mu$m were obtained for the case of using 10 N KOH. With increasing KOH concentration, the particle shape was changed from sphere to hexahedrons and its size also increased. When using 1 N NaOH, the powder was consisted of 0.5~1 $\mu$m particle in size, whereas hexahedrons of 1~4 $\mu$m and whiskers more than 10$\mu$m in size was obtained for the 10 N NaOH solution. With increasing NaOH concentration, the particle shape was varied from hexahedrons to whiskers, showing the similar result with the KOH case. It was confirmed from EDS analysis that Na element, which was detected in hexahedrones was not contained in the whiskers.

• Journal of the Korean Ceramic Society
• /
• v.40 no.7
• /
• pp.683-689
• /
• 2003

The cylindrical ${\gamma}$-alumina pellets were prepared using amorphous alumina and pore generating agent. Its were immersed in aqueous solution of the mixture of Fe(NO$_3$)$_3$.9$H_2O$ and $CH_3$COOH, Fe(NO$_3$)$_3$.9$H_2O$ and $CH_3$COOH and HNO$_3$, and Fe(NO$_3$)$_3$.9$H_2O$ and HNO$_3$. The pellets thus were hydrothermally treated at 20$0^{\circ}C$ for 3 h in autoclave, and were investigated morphologies and changes of crystal pore characteristics, $N_2$ adsorption and desorption isotherms, active sites and mechanical strength etc. According to the preparation method, acicular platelet pseudo-boehmite crystals of 0.1~0.3 ${\mu}{\textrm}{m}$ size were transformed into acicular pseudo-boehmite cristals of 0.5~2 ${\mu}{\textrm}{m}$ size having the same crystal structure. When ${\gamma}$-alumina pellets were immersed in aqueous solution of the mixture of Fe(NO$_3$)$_3$.9$H_2O$ and $CH_3$COOH and then were hydrothermally treated, pore volume between 100 $\AA$ and 1000 $\AA$ was increased from 0.34 ㏄/g to 0.86 ㏄/g, and the gap of $N_2$ adsorption and desorption hysteresis loop was decreased due to increasement of pore size. New active site that could adsorb the C-H functional group was created on the catalist. Also, mechanical strength of catalyst was increased from 1.06 ㎫ to 1.36 ㎫.

• Korean Chemical Engineering Research
• /
• v.50 no.1
• /
• pp.25-29
• /
• 2012

$TiO_2$ nanotubes are prepared from rutile prticles via an alkaline hydrothermal synthesis and the consequent heat treatment at $300{\sim}500^{\circ}C$. The physical and electrochemical properties of the $TiO_2$ nanotubes are characterized for use as a anode material of rechargeable lithium battery. In particular, the microscale dusts as an impurity component occurred in the purification step after the hydrothermal reaction are completely removed to yield $TiO_2$ nanotube with a higher specific surface area and more obvious crystalline phases. As the annealing temperature increases, the specific surface area is slightly decreased due to some aggregation between the isotropically dispersed nanotubes. Highest initial discharge capacity of 250 mAh $g^{-1}$ is achieved for the $TiO_2$ nanotube annealed at $300^{\circ}C$, whereas the $400^{\circ}C$ $TiO_2$ nanotube shows the superior cycle performance and high-rate capability.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.1
• /
• pp.55-63
• /
• 1998

A and Y type zeolitic crystal films were synthesized on porous supports from the reaction mixture of 1.9 $SiO_2-1.5\;Na_2O-Al_2O_3-40\;H_2O$ and 10 $SiO_2-7\;Na_2O-Al_2O_3-280\;H_2O$ composition, respectively. The zeolite film was characterized by XRD and SEM. The crystals grown on the porous matrix were very closely bound together and the thickness of membrane was about 8-15$\mu \textrm{m}$. The densely intergrown crystals could be also synthesized by the hydrothermal treatment at $100^{\circ}C$ after pressing the reaction mixture without addition of water. A zeolite membrane crystallized as a thin film showed the selective permeability of water from water and methanol mixture through the molecular sieving activity of micropores.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.217-217
• /
• 2008

$BaTiO_3$는 perovskite 구조를 가지는 대표적인 강유전체 재료로서 MLCC (Multi Layer Ceramic Capacitor), PTC thermistor 등에 널리 사용되어지고 있으며, 그 특성을 향상시키기 위하여 많은 연구가 진행되고 있다. 현제 $BaTiO_3$ 분말 제조의 대표적인 합성법으로는 하소와 분쇄공정이 없는 수열합성법이 대표적이나, 나노 사이즈로 제작시 $BaTiO_3$는 마이크로 크기와 달리 입방정상으로 우세한 상태로 존재한다. 이는 제조과정 중의 hydroxyl defect의 영향과 나노 분말의 표면에너지 증가 때문이라고 보고된다. 따라서 본 연구는 이러한 문제점을 해결하기 위해 일반적인 세라믹 제조 방법인 고상반응법을 이용한 나노 사이즈의 $BaTiO_3$ 제조를 위한 최적의 공정 조건을 확립하기 위하여 본 연구를 진행하였다. 조성은 $BaTiO_3$와 반응온도를 낮추기 위한 anatase의 $TiO_2$를 사용하였고, $BaCO_3/TiO_2$ 의 조성비 (1. 1.01, 1.02, 1.03)를 제어하여 혼합한 후, 24h ball-mill 하여 하소 온도 ($860^{\circ}C{\sim}1000^{\circ}C$) 변화에 따른 입자 사이즈와 입도 분포를 측정하였다. 제조된 $BaTiO_3$분말의 결정 구조 분석을 위하여 XRD (X-ray diffraction) 분석을 수행 하였는데, 분석 결과로부터 제조된 분말들이 정방정 (tetragonal)의 perovskite구조를 갖고 있음을 확인하였다. 또한 분말의 미세구조 확인을 위하여 SEM (scanning electron microscope) 관찰을 수행하였는데, 나노 사이즈의 구형 분말을 얻을 수 있음을 확인할 수 있었다.