• Journal of the Korean Wood Science and Technology
• /
• v.36 no.3
• /
• pp.1-8
• /
• 2008

The lateral strength test of bending type was done to investigate the lateral capacity of the double bolt connection of domestic larix glulam according to bolt spacing. In the shear specimen, which is bolted connection in the inserted plate type, the hole of bolt was made, changing the diameter of bolt (12 mm and 16 mm), the number of bolt (single bolt : control and double bolt), the direction of bolt row (in parallel to grain : Type-A and in perpendicular to grain : Type-B) and the bolt spacing (Type-A : 4 d and 7 d and Type-B : 3 d and 5 d). Lateral capacity and failure mode of bolt connection were compared according to conditions. In prototype design (KBCS, 2000), the reduction factor of the allowable shear resistance that the bolt spacing is reduced was calculated. The results were as follows. 1) Bearing stress per bolt in the single and double bolt connection of Type-A was directly proportional to bolt diameter and bolt spacing. Bearing stress of Type-B decreased as bolt diameter was increased, and decreased by 2~10% when bolt diameter was increased. 2) In the single bolt connection and the double bolt connection of Type-A, the splitted failure was formed in the edge direction. When the bolt spacing was 3 d in Type-B, bolt was yielded more in the part of tension than in the part of compression, and the splitted failure started at the bolt in the part of tension. In the 5 d spacing specimen, the bolt in the part of tension was yielded similarly to bolt in the part of compression, and the splitted failure started in the part of compression. 3) In the prototype design, the reduction factor was calculated by non-dimensionizing the yielding load in the standard of bolt spacing (Type A : 7 d and Type B : 5 d). In 12 mm bolt connection, the reduction factor of bolt spacing 4 d (type-A) and single bolt connection was 0.87 and 0.55, respectively, and the reduction factor of bolt spacing 3 d (Type-B) and single bolt connection was 0.91 and 0.55, respectively. In 16 mm bolt connection, the reduction factor of bolt spacing 4 d (type-A) and single bolt connection was 0.96 and 0.76, respectively, and the reduction factor of bolt spacing 3 d (Type-B) and single bolt connection was 0.91 and 0.77, respectively.

• Composites Research
• /
• v.15 no.4
• /
• pp.23-31
• /
• 2002

The two dimensional size effect of specimen gauge section ($length{\;}{\times}{\;}width$) was investigated on the compressive behavior of a T300/924 $\textrm{[}45/-45/0/90\textrm{]}_{3s}$, carbon fiber-epoxy laminate. A modified ICSTM compression test fixture was used together with an anti-buckling device to test 3mm thick specimens with a $30mm{\;}{\times}{\;}30mm,{\;}50mm{\;}{\times}{\;}50mm,{\;}70mm{\;}{\times}{\;}70mm{\;}and{\;}90mm{\;}{\times}{\;}90mm$ gauge length by width section. In all cases failure was sudden and occurred mainly within the gauge length. Post failure examination suggests that $0^{\circ}$ fiber microbuckling is the critical damage mechanism that causes final failure. This is the matrix dominated failure mode and its triggering depends very much on initial fiber waviness. It is suggested that manufacturing process and quality may play a significant role in determining the compressive strength. When the anti-buckling device was used on specimens, it was showed that the compressive strength with the device was slightly greater than that without the device due to surface friction between the specimen and the device by pretoque in bolts of the device. In the analysis result on influence of the anti-buckling device using the finite element method, it was found that the compressive strength with the anti-buckling device by loaded bolts was about 7% higher than actual compressive strength. Additionally, compressive tests on specimen with an open hole were performed. The local stress concentration arising from the hole dominates the strength of the laminate rather than the stresses in the bulk of the material. It is observed that the remote failure stress decreases with increasing hole size and specimen width but is generally well above the value one might predict from the elastic stress concentration factor. This suggests that the material is not ideally brittle and some stress relief occurs around the hole. X-ray radiography reveals that damage in the form of fiber microbuckling and delamination initiates at the edge of the hole at approximately 80% of the failure load and extends stably under increasing load before becoming unstable at a critical length of 2-3mm (depends on specimen geometry). This damage growth and failure are analysed by a linear cohesive zone model. Using the independently measured laminate parameters of unnotched compressive strength and in-plane fracture toughness the model predicts successfully the notched strength as a function of hole size and width.

• Journal of Korean Orthopaedic Sports Medicine
• /
• v.10 no.2
• /
• pp.105-108
• /
• 2011

Extra-skeletal chondroma, characterized by its lack of connection with the adjacent bone, includes synovial chondromatosis, intra-articular and para-articular chondroma, and soft tissue chondroma. Among them, the last two lesions are extremely rare. This is the case about 20-year-old soldier, who had complained of tenderness of the knee, pain and fullness during knee flexion and limitation of motion after a hard military training. We found a mass in the x-ray and MRI and resect the mass surgically, which was a $5.5{\times}4{\times}3$ cm size hard solitary mass. On microscopic finding, it was consisted of lobulated hyaline cartilage and outer fibrous capsule, and we ascertained it as para-articular chondroma. We experienced a case of para-articular chondroma in the infrapatellar fat pad of the knee joint and present its clinical, radiologic and pathologic findings with literature review.

• The Journal of Korean Academy of Prosthodontics
• /
• v.44 no.5
• /
• pp.526-536
• /
• 2006

Statement of problem : Use of fiber composite technology as well as development of nonmetal implant prosthesis solved many problems due to metal alloy substructure such as corrosion. toxicity, difficult casting, expensiveness and esthetic limit. After clinical and laboratory test, we could find out that fiber-reinforced composite prostheses have good mechanical properties and FRC can make metal-free implant prostheses successful. Purpose : The purpose of this study is to evaluate the flexural strength of implant fixed prosthesis using fiber reinforced composite. Material and methods : 2-implant fixture were placed in second premolar and second molar area in edentulous mandibular model, and their abutments were placed, and bridge prostheses using gold, PFG, Tescera, and Targis Vectris were fabricated. Tescera was made in 5 different designs with different supplements. Group I was composed by 3 bars with diameter 1.0mm and 5 meshes, 2 bars and 5 meshes for Group II, 1 bar and 5 meshes for Group III, and only 5 meshes were used for Group IV. And Group V is composed by only 3 bars. Resin (Tescera) facing was made to buccal part of pontic of gold bridge. All of gold and PFG bridges were made on one model, 5 Targis Vectris bridges were also made on one model, and 25 Tescera bridges were. made on 3 models. Each bridge was attached to the test model by temporary cement and shallow depression was formed near central fossa of the bridge pontic to let 5 mm metal ball not move. Flexual strength was marked in graph by INSTRON. Results : The results of the study are as follows. The initial crack strength was the highest on PFG. and in order of gold bridge Tescera I, Tescera II, Targis vectris, Tescera IV, Tescera III, and Tescera V. The maximum strength was the highest on gold bridge, and in order of PFG, Tescera I, Tescera IV Tescera II, Targis vectris, Tescera III, and Tescera V. Conculsions : The following conclusions were drawn from the results of this study. 1. Flextural strength of implant prosthesis using fiber reinforced composite was higher than average posterior occlusal force. 2. In initial crack strength, Tescera I was stronger than Tescera V, and weaker than PFG. 3. Kinds and number of auxillary components had an effect on maximum strength, and maximum strength was increased as number of auxillary components increased. 4 Maximum strength of Tescera I was higher than Targis vectris, and lower than PFG.

• The Journal of Korean Academy of Prosthodontics
• /
• v.35 no.2
• /
• pp.401-412
• /
• 1997

There has been many researches aimed at reinforcing the strength of resin, and these have led to the development and use of numerous materials in recent years. A case in point, is the recent development of plasma-treated polyethylene fiber which has been used mainly in fixed provisional restoration to reduce the incidence of fractures. This study aims at assessing whether plasma-treated polyethylene fiber as applied to composite resin is effective in increasing the flexural strength and how applied portions affect this. Twenty-four applied and eight unapplied composite resin bars were fabricated. Twenty-four applied specimens were divided into three groups. Plasma treated polyethylene fiber was applied to the groups each with different portions of composite resin. In the first group, plasma-treated polyethylene fiber was not applied. In the second group, fiber was applied to the compression side of composite resin. Fiber was applied to the tension side in the third group, while fiber was embedded in the tension side of the composite resin in the fourth group. Each specimen was tested by use of a three-point bending strength test with an instron testing machine, and the flexural strength was calculated. The following results were obtained. : 1. Under the conditions of this study, the third and fourth groups demonstrated a statistically greater flexural strength compared to the first and second groups. 2. But there was no statistically significant difference, not only between the first group and the second group, but also between the third group and the fourth group. Taken together, it can be concluded that plasma-treated polyethylene fiber applied to composite resin is an effective method in increasing flexural strength, and the best way of increasing the flexural strength is by application of plasma-treated polyethylene fiber to the tension side, or the embedding of same in composite resin. It must be mentioned however that this test used a static single-load test method. This method determined the maximum stresses that could be tolerated, but this might not be valid where the prediction of clinical failure is concerned. In order therefore to clinically utilize plasma-treated polyethylene fiber to reinforce the composite resin, it is suggested that a further study which considers the various loads be undertaken.

• Journal of Chest Surgery
• /
• v.30 no.12
• /
• pp.1237-1241
• /
• 1997

Tracheal stenosis is a difficult disease entity to manage. Laser ablation is one effective treatment for treacheal stenosis and can be utilized if tracheal reconstructive surgery is impossible. Potassium titanyl phosphate laser, transmitted via flexible quartz fiber, can be precisely manipulated through flexible bronchoscope under local anesthesia. We treated 7 patients with trach al and broncheal lesion under local anesthesia with KTP laser from January 1995 to July 1996. The patients included three males and four females. The age of patients ranged from 22 to 66 years with a mean of 43.7 years The etiology of tracheal stenosis in patients was stenosis after tracheostomy(3 cases), prolong inturbation in cases of sepsis(1 cases), and the recurrence of lung cancer within endobronchial lesion(2 cases). In the cases of tracheal stenosis treated with laser ablation, there were 2 cases of recurrence of stenosis at the anastomosis site after the operation, 3 cases of stenosis at tracheostomy site, and 2 cases of local recurrence of lung cancer. The site of the tracheal stenosis was the balloon site of the tracheostomy tube(3-4cm inferior to the tracheostomy site, 2-3cm superior to the carina) and the anastomosis site that were narrowed to less than 5mm(4 cases). For the stenosis lesion in the endobronchial area, there were 2 patients with a lesion at the anterior wa l, 1 patient with a lesion at the posterior wall, 2 patients with circumferential stenosis. Laser ablation time was 25.4 $\pm$5.9min and used energy was 1768 $\pm$365J. We have used KTP laser via (lexible bronchoscope without major complications. Adjuvant radiation therapy may prevent fibroblast proliferation which leads to restenosis. In three patients of restenosis after laser ablation, adjuvant irradiation started within 4 hours after laser ablation, and the radiation doses were 1500cGy given in five fraction. In patients with adjuvant radiation therapy, stenosis has not recurred

• Tuberculosis and Respiratory Diseases
• /
• v.40 no.6
• /
• pp.683-693
• /
• 1993

Background: During movement the major inputs to nervous system come from firstly the muscle and joint to maintain posture and motion and secondly the chemoreceptors and baroreceptors to adjust the cardiovascular and respiratory function. Their complex relationships are generally studied for many years but the direct relation between the joint and respiratory system is not studied thoroughly until now. So this experiment was performed to determine whether the natural movement of knee joint can cause the enhancement of respiratory function by observation of the changes of respiratory rate, phrenic nerve activity and inspiratory neuron activity during the stimulation of knee joint in cat anesthetized with $\alpha$-chloralose. Method: Twenty six male adult cats were used and the extracelluar recording using bipolar platinum electrode and carbon filament electrode was done to record the changes in the activities of phrenic nerve and inspiratory neuron movement of knee joint, injection of chemicals into the joint cavity and electrical stimulation of articular nerve were done. Results: The 60 Hz. could not but 120 Hz. flexion-extension movement of knee joint increased respiratory rate(R.R.), tidal neural activity(TNA) and minute neural activity(MNA). Intra-articular injection of lactate could not increase R.R. but significantly increase TNA and MNA which represented the enhanced respiratory function. Injection of potassium chloride showed similar effects with the case of lactate but the duration of effect was shorter. The electrical stimulation of medial articular nerve with IV strength which could activate only group I and II afferents showed increased TNA and MNA during stimulation but 20 V stimulation which could activate all the afferents increased all the respiratory parameters. The changes of inspiratory neuron activity by knee joint stimulation was similar to that of phrenic nerve. Conclusion: The respiratory center could be directly stimulated by the activation of group I and II articular afferents and it seemed that the magnitude of the respiratory center enhancement is proportional to the amount of sensory information from the knee joint. These facts might suggest that the respiratory function could be enhanced even by the normal movement of knee joint.

• Journal of the Korean Wood Science and Technology
• /
• v.6 no.2
• /
• pp.3-19
• /
• 1978

Five species, Abies koreana Wilson (A. koreana), Castanopsis cuspidata var. Sieboldii Nakai (C. Cuspidata). Machilus thunbergii Sieb. et Zucc. (M. thunbergii), Styrax japonica (S. japonica), and Quercus acuta Thunberg(Q. acuta) growing in the southern part of Korea were selected for the investigation of wood properties. In order to evaluate the wood properties of these five species, anatomical, physical, mechanical, chemical and pulping characteristics were investigated. And this study also covered wood technological problems related to the drying, gluing, debarking, flooring, and wood workability so that these species might serve to the best advantage. The results obtained were summarized as follows: 1. The trunk of A. koreana with many knots was straight. However, the trunks of S. japonica and C. cuspidata were crooked. 2. A. koreana showed the longest and the widest ill the fiber morphology; 2.97mm in length, 39.3${\mu}$ in width. In general, fiber width of all the species investigated were greater than those of other Korean hardwoods. 3. The specific gravity of Q. acuta was 0.74${\pm}$0.03, and that of A.koreana was 0.34${\pm}$0.02. The range of specific gravity of the other species was 0.47-0.52. 4. The adsorption of water was propotioned inversely with the specific gravity, but the adsorption of humidity was proportioned with the specific gravity. In spite of their medium density, S. japonica showed the greatest adsorption, and M. thunbergii the least. The water adsorption of cross section was twice greater than that of lateral direction, and there was a slight difference in between the radial and the tangential direction. 5. Shrinkage for tested five species was ranged from 5.36 to 10.24% in tangential direction, and 2.83~6.13% in radial direction. Q. acuta recorded the greatest shrinkage rate, and A. koreana the least. The greater was the specific gravity, the larger was the shrinkage rate. 6. The mechanical properties of Q. acuta were similar to those of Quercus mongolica which grow in Kangwon-Do. Strength properties of C. cuspidata, M. thunbergii, A. koreana were equivalent to those of other Korean commercial woods with similar specific gravity, except S. japonica which showed slightly higher strength than that of other species with similar density. 7. Higher glue joint strength for urea and phenol adhesieves was recorded in the species of M. thunbergii and C. cuspidata, however, high-density species(Q. acuta) and even low-density species(A. koreana) did not show good joint strength. 8. The attractive figure of M. thunbergii in texture seemed to he appreciated for decoration. And the grain and texture of other species were proper for furniture and building materials. 9. All of the species except Q. acuta were considered good for wood workability. 10. The denser the specific gravity was, the longer the drying time took. However, severe drying defects were formed in M. thunbergii whose density was medium. 11. All the species were considered suitable for the flooring wood expect A. koreana whose density was light. 12. Pentosan component in all the species was great, and the amount of extractives in Q. acuta was worth noticing. 13. Yield in kraft pulp was above the level of economic pulp yield, i.e. 45% in all species. 14. Debarking was easy in the species of A. koreana and M. thunbergii, and debarking after being boiled in water was the most efficient in all species.