Sandwich panels with three different joint configurations were tested to design a novel sandwich joint structure that can effectively support both the tensile and compressive loads. The sandwich core was mainly aluminum flex honeycomb but the PMI foam core was limitedly applied to the ramp area which is transition part from sandwich to solid laminate. The face of sandwich panel was made of carbon fiber composite. For configuration 1, the composite flange and the sandwich panel were cocured. For configurations 2 and 3, an aluminum flange was fastened to the solid laminate by HI-LOK pins and adhesive. The average compressive failure loads of configurations 1, 2, and 3 were 295, 226, and 291 kN, respectively, and the average tensile failure loads were 47.3 (delamination), 83.7 (bolt failure), and 291 (fixture damage) kN, respectively. Considering the compressive failure loads only, both the configurations 1 and 3 showed good performance. However, the configuration 1 showed delamination in the corner of the composite flange under tension at early stage of loading. Therefore, it was confirmed that the structure that can effectively support tension and compressive loads at the same time is the configuration 3 which used a mechanically fastened aluminum flange so that there is no risk of delamination at the corner.

• Proceedings of the KAIS Fall Conference
• /
• 2012.05b
• /
• pp.646-648
• /
• 2012

본 연구에서 다루는 복합재료는 알루미늄 폼으로써 다공성 구조체로 고체 알루미늄 금속에 비하여 비중이 1/10 정도로 작고, 충격에너지 흡수가 우수하다. 본 연구에서는 다공성 심재를 갖는 복합재료 알루미늄 폼 코어의 충격실험을 실시하여 기계적 특성을 파악하였다. 시험편은 알루미늄 폼 코어를 갖는 복합재료로써 시험편에 50J의 저 충격에너지를 가하도록 하였다. 그 결과, 모든 실험에서 스트라이커가 상부면재 통과 시 최대하중이 나타났고, 이때의 최대하중 값은 약 5.5 KN으로 나타났다. 또한 최대 하중 발생 시간은 50J일 때 약 4.2 ms가 나왔다. 최대 하중이 발생한 후, 즉 상부 면재 통과 후에 실험에서는 약 10 mm정도를 더 뚫으면서 심재에 까지 손상을 주었지만 하부 면재에는 손상을 주지 못하였다. 이로써 스트라이커가 알루미늄 폼 코어 샌드위치 복합재료를 통과 할 때 상부면재 통과 시 최대 하중이 발생하고 심재를 지나며 서서히 감소되는 것을 볼 수 있었다.

• Composites Research
• /
• v.26 no.2
• /
• pp.116-122
• /
• 2013

In this study, impact behavior of aluminium and glass-fiber structure is studied under low impact velocity. Compression test is carried out to investigate the compressive strength of the specimens. The degree of damage is observed using microscopy and compared with the experimental analysis data. The maximum load capacity, impact strength and elastic energy of glass-fiber honeycomb sandwich panel are more than the aluminium honeycomb sandwich panel.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.47 no.7
• /
• pp.535-540
• /
• 2019

The coupling between different models for MDO (Multi-disciplinary Optimization) greatly increases the complexity of the computational framework, while at the same time increasing CPU time and memory usage. To overcome these difficulties, POD (Proper Orthogonal Decomposition) and RBF (Radial Basis Function) are used to solve the optimization problem of determining the thickness of composites and sandwich cores when composite sandwich structures are used as aircraft wing skin materials. POD and RBF are used to construct surrogate models for the wing shape and the load data. Optimization is performed using the objective function and constraint function values which are obtained from the surrogate models.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2007.11a
• /
• pp.109-110
• /
• 2007

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2011.11a
• /
• pp.938-941
• /
• 2011

This paper deals with the equivalent shear modulus of the egg-box core. There are three approaches to obtain the equivalent shear modulus of core: a finite element analysis, an analytical study, and an empirical method. In this study, an 3-point bending test is used to evaluate the equivalent shear modulus of the Egg-Box core. As a result of the present work, the equivalent shear modulus of egg-box core at room temperature can be obtained. And this result is compared with the result of finite element analysis.

• Composites Research
• /
• v.22 no.2
• /
• pp.24-29
• /
• 2009

This study aims to investigate the residual strength of sandwich composites with Al honeycomb core and carbon fiber face sheets after the quasi-static indentation damage by the experimental investigation. The 3-point bending test and the edge-wise compressive strength test were used to find the mechanical properties, and the quasi-static point load was applied to introduce the simulated damage on the specimen. The damaged specimens were finally assessed by the 3-point bending test and the compressive strength test. The investigation results revealed the residual strength of the damaged specimens due to the quasi-static indentation. The both test results showed that the residual strength of the damaged specimen was decreased according to increases of the damaged depth.

• Journal of the Korean Society for Railway
• /
• v.13 no.4
• /
• pp.382-388
• /
• 2010

This paper describes the standardized finite element model for carbody structures of railway vehicle made of sandwich composites. Recently, sandwich composites were widely used to railway vehicle due to the improvement of energy efficiency, high specific stiffness and strength, weight reduction and space saving in korea. Therefore, structural integrity should be verified using finite element analysis prior to the manufacture of composite railway vehicle. The standardized finite element model for composite carbody structures was introduced through comparing the results of real structural test under vertical, compressive, twisting load and natural frequency test of various railway vehicles in this study. The results show that the quadratic shell element is suitable to model the reinforced metal frame used to improve the flexural stiffness of sandwich panel compared to beam element, and layered shell and solid element are recommended to model the skin and honeycomb core of sandwich panel compared to sandwich shell element. Also, the proposed standard finite element model has the merit of being applied to crashworthiness problem without modifications of finite element model.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.38 no.4
• /
• pp.347-355
• /
• 2014

Thermal problems that are directly related to the lifetime of an electronic device are becoming increasingly important owing to the miniaturization of electronic devices. To solve thermal problems, it is essential to study thermal stability through thermal diffusion and insulation. A honeycomb sandwich plate has anisotropic thermal conductivity. To analyze the thermal deformation and temperature distribution of a system that employs a honeycomb sandwich plate, the thermal and elastic properties need to be determined. In this study, the thermal and elastic properties of a honeycomb sandwich plate, such as thermal conductivity, coefficient of thermal expansion, elastic modulus, Poisson's ratio, and shear modulus, are predicted. The properties of a honeycomb sandwich plate vary according to the hexagon size, thickness, and material properties.

• Journal of Aerospace System Engineering
• /
• v.13 no.4
• /
• pp.18-25
• /
• 2019

Studies on the fabrication of UAV by using 3D printer have been actively carried out. However, research on structural load characteristics in low temperature environment is insufficient. In this study, a composite sandwich structure with ordinary orbs structure was proposed, and the load characteristics for temperature condition changes were analyzed. The ordinary orbs and honeycomb structures were fabricated by using a FDM type 3D printer. The bending load test was carried out at room temperature and low temperature condition. The low temperature condition was classified into four cases. Bending load tests were performed in a low temperature chamber to maintain the required temperature conditions. As a result of the test, it was confirmed that the proposed ordinary orbs structure had better load characteristics at low temperatures than the existing honeycomb structure.