• Journal of the korean academy of Pediatric Dentistry
• /
• v.49 no.2
• /
• pp.197-205
• /
• 2022

This study was conducted to investigate the fluoride release of fluoride-containing restorative materials in fluoride recharging according to the concentration of fluoride toothpaste used in Korea. Samples of glass ionomer cement, resin-modified glass ionomer cement, alkasite restorative material, and composite resin were prepared and fluoride release was measured on days 1, 3, 7, 14, 21, 28. Thereafter, fluoride-free, 500 ppm, and 1450 ppm fluoride toothpaste was applied to each restorative materials, and the fluoride release was measured on days 1, 3, 7. Glass ionomer cement showed the highest cumulative fluoride release until the 7th day of measurement, and from the 14th day onwards, the resin-modified glass ionomer cement showed the highest cumulative fluoride release, but there was no significant difference. When restorative material groups were recharged with 500 ppm of fluoride toothpaste, the fluoride release was significantly higher only for the alkasite restorative material compared to the fluoride-free toothpaste group (p < 0.017). When restorative material groups were recharged with 1450 ppm of fluoride toothpaste, the fluoride release was significantly higher in all restorative groups compared to the fluoride-free toothpaste group (p < 0.017).

• Journal of the korean academy of Pediatric Dentistry
• /
• v.31 no.4
• /
• pp.705-713
• /
• 2004

The objectives of this study were to evaluate the fluoride release and the change of surface roughness of fluoride releasing restorative materials after toothbrush-dentifrice abrasion. Seven commercially available fluoride releasing restorative materials (Fuji II LC Improved: FL, Compoglass F: CG, Dyract AP: DR, F2000: FT, Ariston: AT, Tetric: TR, and Gradia: GD) were selected as experimental materials. The results obtained were summarized as follows: 1. The AT, FL, and CF groups produce an initially large burst of fluoride release and comparatively low but continuous release of fluoride. But other groups produce no initial burst of fluoride and levels of release remain relatively constant. 2. The rate of fluoride release remains steady state after 40 days. The results of Tukey's test (P<.05), the fluoride release showed the order of decreasing rank as follows: AT > FL > compomers > TC and GD. 3. The surface roughness indicated that the highest value was observed in the FT group and the lowest value was observed in the CF group. The surface roughness of Tukey's test showed the significant differences between groups of FT, AT and FL and groups of CF, DR, GD and TC (P<0.05).

• Journal of the korean academy of Pediatric Dentistry
• /
• v.48 no.4
• /
• pp.367-375
• /
• 2021

This study evaluated the fluoride release of alkasite restorative material (ARM) and giomer penetrating the dentin adhesive layer. Twenty specimens were prepared for each restorative material, and dentin adhesive with uniform thickness was applied to half of them. The prepared specimens were placed in a polyethylene tube containing 2.0 mL of deionized water and deposited in a 37.0℃ water bath for the study duration. The amount of fluoride release was measured on the 1^st, 3^rd, 7^th, 14^th, 21^st, and 28^th days after deposition. The dentin adhesive applied to the ARM and giomer could not completely block the fluoride release; however, it significantly reduced its amount. The cumulative amount of fluoride release of the ARM after 28 days was higher than that of the giomer regardless of the application of dentin adhesive.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.34 no.3
• /
• pp.408-419
• /
• 2007

In the child, it is very important that he/she will have the ability to suppress aesthetic restorative materials of secondary caries. With the representative preventive material against caries, the importance of fluoride is more emphasized. This study examined the differences in fluoride release and re-uptake among some restorative materials, following a treatment of APF gel and fluoride varnish. The surface roughness was observed under scanning electron microscope. Studying this will provide for the research to find effective restorative materials and fluoride type in tooth caries prevention. It is applied from presence at a clinic that restorative materials are resin, flowable resin, compomer and glass ionomer. Fluoride release was measured at 24-hour intervals for 7 days, 3-day intervals from 8th to 38th day using an ion-selective electrode and analyzer. Then, the materials were treated with the fluoride gel and fluoride varnish respectively, fluoride release was measured and specimens were evaluated under scanning electron microscope for 4 weeks. It was concluded that 1. Fluoride was released for 38 days from restorative materials under 1 ppm in case of flowable resin, 1-2 ppm in compomer and 2-8 ppm in glass ionomer, a few of fluoride was released after 45 days 2. Fluoride has more releasing after application of APF gel than fluoride varnish. Fluoride re-uptake was observed under 0.6-0.2 ppm in fluoride varnish and 0.6-2.6 ppm in APF gel after starting the procedure one day(p<0.05). For the remaining 4 weeks, they demonstrated a similar release. 3. Specimens were evaluated under scanning electron microscope. Applied fluoride in the experimental group surface was rougher than the control group that did not receive fluoride application. Fluoride varnish group had a smoother surface than both the APF gel group and the varnish APF gel group that received a fluoride application.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.37 no.3
• /
• pp.288-297
• /
• 2010

The purpose of this study was to evaluate the effect of light cured fluoride-releasing materials on the inhibition of demineralization. In addition, the pattern of fluoride uptake of adjacent tooth structure was analyzed with EPMA. Eighty intact premolars were restored with $Filtek^{TM}$ Z250(control group, composite), Fuji Filling $LC^{TM}$(RMGI), Dyract $AP^{(R)}$ (compomer) and Beautifil II(giomer). Restored teeth were stored in distilled water for 30 days. Then sixty teeth(n=15) were exposed to demineralizing solution(pH 4.3). Demineralized teeth were bisected and polished. The specimens were observed with confocal laser scanning microscope. The depth of outer lesion and the thickness of inhibition zone were measured. Remained twenty teeth(n=5) were bisected for fluoride uptake analysis. The fluoride analysis were taken at enamel-restoration interface and dentin-restoration interface by electron probe micro-analyzer. The results are as follows: 1. The depth of outer lesion of Fuji Filling $LC^{TM}$ Dyract AP, Beautifil II was shallower than that of $Filtek^{TM}$ Z250 at the margin of restoration(p<0.05). 2. The thickness of caries inhibition zone of Fuji Filling $LC^{TM}$, Dyract AP, Beautifil II was greater than that of $Filtek^{TM}$ Z250 at the margin of restoration(p<0.05). 3. Fuji Filling $LC^{TM}$, Dyract AP, Beautifil II groups showed the greater fluoride uptake into enamel and dentine around restoration than $Filtek^{TM}$ Z250 group. 4. In dentin the difference of fluoride concentration were greater than in enamel, and Dyract AP showed the greatest fluoride concentration in dentin.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.35 no.3
• /
• pp.418-426
• /
• 2008

The objectives of this study were to examine the properties of fluoride-releasing resin composite restorative materials. Four commercially available compomer materials (Compoglass F: CF, $Dyract^{(R)}$ AP: DA, $Dyract^{(R)}$ flow: DF, F2000: FT) and one fluoride-releasing composite resin ($Tetric^{(R)}$ Ceram: TC) were selected as experimental materials. Rectangular-shaped tensile test specimens were fabricated in a teflon mold giving 5mm in gauge length and 2mm in thickness. Disk-shaped specimens were fabricated in the split teflon mold with diameter of 15mm and thickness of 1mm. After curing for an hour, specimens were immersed in deionized water at $37^{\circ}C{\pm}1^{\circ}C$ for 30 days. All specimens were thermocycled for 10,000 cycles with 15 seconds of dwelling time in each $5^{\circ}C$ and $55^{\circ}C$ water baths. Toothbrush abrasion test was conducted under a load of 1.5 N and the abraded surfaces were examined with surface roughness tester (SV-3000, Mitutoyo Co, Japan) and SEM (JSM-5800, JEOL, Japan). Fluoride recharging was done by toothbrushing for 3 min. using a fluoride toothpaste (Perio Alpine Herb, LG Household & Health Care, Korea). The results obtained were summarized as follows; 1. The highest tensile strength value of 32.3 MPa was observed in TC group and the lowest value of 16.8 MPa was observed in CF group. The tensile strength of TC group was significantly higher than those of CF and DF groups (P<0.05). 2. The lowest Ra value of 0.287 was observed in TC group and the highest value of 1.516 was observed in FT group. The Ra value of FT group was significantly higher than other groups (P<0.05). 3. The abraded surfaces revealed the increase of surface roughness due to the protrusion and missing of filler particles. 4. The release of fluoride of compomers after tooth brushing by Perio Alpine Herb was initially large and then followed by small and continuously. But it remains small and constant in fluoride-releasing composite resin of TC. 5. The highest value of fluoride release after toothbrushing by Perio Alpine Herb was $2.064{\mu}g/cm^2$ in CF group and the lowest value was $0.1119{\mu}g/cm^2$ in TC group. The amount of fluoride release of CF group was significantly higher than other groups (P<0.05).

• Journal of the korean academy of Pediatric Dentistry
• /
• v.28 no.1
• /
• pp.54-66
• /
• 2001

The aim of this study was to investigate the fluoride release and some mechanical properties including 3-point bending strength, amount of abrasion, surface hardness, water sorption/solubility and cytotoxicity of the newly developed composite resins containing 8, 16, 24 wt% $SrF_2$ glass filler (VF8, VF16, VF24) and four commercially available composite resins, Heliomolar(HE), Verdonfil(VE), Z100(ZH) and Aelitefil(AE). To investigate cytotoxic effect, agar overlay assay was done. Amount of fluoride released into distilled water was measured over a 62-days period from VF8, VF16, VF24 and HE. Results were as follows: 1. Experimental composite resins showed similar mechanical properties to commercial composite resins, but 3-point bending strength and surface hardness of experimental composite resins were inferior to ZH. 2. Over a 62-day Period, the amount of fluoride released was ordered: VF24>VF16>VF8>HE. In experimental composite resins, the amount of fluoride released was 9-23 times greater than HE and seemed to be proportional to the content of $SrF_2$ glass filler. 3. Experimental composite resins and all control composite resins showed mild cytotoxicity. This study showed significantly greater fluoride release from newly developed composite resins than control(HE) and addition of $SrF_2$ glass filler did not decrease mechanical properties or increase cytotoxicity of composite resin. The results from this study imply that newly developed composite resin have adequate mechanical properites, mild cytotoxicity and some potential for secondary caries prevention.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.35 no.2
• /
• pp.81-89
• /
• 2019

Purpose: This study aimed to investigate the correlation between the solubility and the amount of fluoride release when a resin surface coating agent is applied to RMGIC. Materials and Methods: To measure the fluoride release and solubility, Fuji II $LC^{(R)}$and $Filtek^{TM}$ Z350XT without a surface coating, Fuji II $LC^{(R)}$ with G coat $plus^{TM}$ and Fuji II $LC^{(R)}$ with $Permaseal^{(R)}$ were prepared. And the amount of fluoride release and solubility were measured. Results: There was no significant difference in the daily fluoride release between the surface coating agents. The cumulative fluoride release was significantly different between the groups using RMGIC at 56 days (P < 0.05). In the solubility measurement, RMGIC without surface coating was significantly different only on the 7th day compared to the other three groups (P < 0.05). Conclusion: Surface coating agents can prevent the degradation of properties by the initial solvent in RMGIC. Therefore, fluoride is preserved inside the restorative material and the effect of surface coating after the addition is reduced, so that the effect on fluoride release and storage is also reduced.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.21 no.1
• /
• pp.25-32
• /
• 2005

The purpose of this study was to examine an effect of fluoride recharging on fluoride release and surface change of fluoride-releasing restorative materials. Six commercially available fluoride releasing restorative materials (Fuji II LC Improved: FL, Compoglass F: CF, Dyract AP: DA, F2000: FT, Gradia Direct: GD, and Tetric Ceram: TC) were selected as experimental materials. Disk specimens were fabricated with split teflon mold to the final dimensions of 15 mm in diameter and 1 mm in thickness. Ten samples of each material were fabricated and stored in deionized water at $37^{\circ}C{\pm}1^{\circ}C$ for 3 months. Before fluoride recharging, all specimens were polished sequentially from #800 to #2000 emery papers. Fluoride recharging was done at 5-day interval using 2.0% NaF gel. The release of fluoride into the storage water was monitored using a fluoride ion electrode. Data were analyzed by one-way ANOVA and Tukey's multiple range test. The results obtained were summarized as follows; 1. Fluoride recharge capability were FL > CF > DA and TC group after 12 times exposure to 2.0% NaF gel (P<0.05). 2. All the experimental materials, except for FT group, showed the increase of fluoride release and surface roughness. 3. Fluoride-releasing rates returned to base line within 3 days.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.37 no.1
• /
• pp.44-52
• /
• 2010

The objective of this in vitro study was to detect and monitor demineralization and remineralization of primary teeth according to restorative materials using quantitative light-induced fluorescence (QLF). A single bur hole was drilled on the each sound forty eight primary anterior teeth, and the specimens were divided into three groups. The cavity was restored with $Filtek^{TM}$ Z250(Group 1), F2000(Group 2), $Ketac^{TM}$ N100(Group 3) following the manufacturer's instructions. The teeth were subjected to the demineralizing buffer for 3 days, and then subjected to a remineralizing buffer for 14 days. The change of mineral loss(${\Delta}Q$) according to the stages was evaluated by QLF and the following results were obtained: 1. When demineralization was done, ${\Delta}Q$ was increased as follows. : Group 1 ($-110.79\;{\pm}\;27.77$) < Group 2 ($-104.84\;{\pm}\;28.95$) < Group 3 ($-90.16\;{\pm}\;21.87$) : Resistance to demineralization was statistically significant in Group 3. 2. There was a statistically significant increase in ${\Delta}Q$ of all groups since 1st day of remineralization 3. The rate of remineralization, ${\Delta}$(${\Delta}Q$)/day, showed significant high value in each group on the 1st day then decreased rapidly. 4. There was no statistically significant difference in the degree of remineralization among restorative materials.