• Journal of the Microelectronics and Packaging Society
• /
• v.8 no.2
• /
• pp.1-7
• /
• 2001

In order to form a uniform oxidation layer of spinel phase on Kovar which helps the strong bonding in Kovar-to-glass sealing, the humidified $N_2/H_2$ was used as an oxidation atmosphere. The oxidation of Kovar was controlled by diffusion mechanism and the activation energy was 31.61 kacl/mol at 500~$800^{\circ}C$. After oxidation at $600^{\circ}C$, the external oxidation layer was below 0.5 $\mu \textrm{m}$ thick. According to TEM analysis, oxidized Kovar was spinel its lattice parameter of 7.9 $\AA$. Oxidation of under $600^{\circ}C$ and in a humidified $N_2/H_2$ atmosphere, Kovar was found to be appropriate for the Kovar-to-glass sealing.

• 한국태양에너지학회:학술대회논문집
• /
• 2012.03a
• /
• pp.391-393
• /
• 2012

CuInGa 전구체를 여러 분위기에서 급속 열처리 공정 (rapid thermal processing; RTP)을 이용하여 셀렌화하여 CuInGaSe 박막을 제작하였다. 공정조건은 각각 진공상태, 아르곤 가스 유동 상압상태, 아르곤 분위기 상압밀폐에서 덮개 유리를 사용한 상태 및 아르곤 밀폐상압에서 추가로 Se을 공급한 상태이었다. 제작된 CuInGaSe의 특성을 ICP 측정을 통하여 분석하였다. 열처리 조건에서 시스템이 밀폐상태에 가까울수록 Se 증기압이 높을수록 CuInGaSe 박막의 Se 함량이 증가하였다. 아르곤 분위기 상압 밀폐상태에서 제작된 CuInGaSe 박막을 이용하여 제작한 태양전지의 효율은 9.6%이었다.

• 한국신재생에너지학회:학술대회논문집
• /
• 2006.06a
• /
• pp.210-213
• /
• 2006

나노입자를 이용하여 치밀한 $Cu(In,\;Ga)Se_2$ 태양전지용 광흡수층을 제조하기 위해 먼저, 콜로이달 방법으로 합성된 20nm이하의 CIGS 나노입자를 저가의 스프레이 법을 이용하여 CIGS 막을 제조하였다. 제조된 CIGS막을 two-zone RTP (rapid temperature Process) 방법으로 Se 분위기 안에서 열처리를 행하였다. 입자의 치밀화를 위해 기판의 온도, Se 증발온도와 수송가스의 유량을 조절하여 CIGS 입자성장을 행하였다. 그러나, Se의 증발온도가 높을수록 CIGS와 MO 박막 사이에서 $MoSe_2$ 층이 형성되었다. 형성된 $MoSe_2$층의 부피 팽창으로 인해 하부의 유리기판과 Mo층 사이에서 peeling off 현상이 발생했다. 이러한 Peeling off현상을 억제하면서 CIGS 나노입자 성장을 하기 위해, Se 공급을 빨리 할 수 있도록 Se의 증기압을 높였으며, 최적조건에서 급속 열처리 공정을 통해 CIGS 나노입자 성장과 치밀화를 위한 소결거동을 관찰하였다.

• Proceedings of the KAIS Fall Conference
• /
• 2006.11a
• /
• pp.135-138
• /
• 2006

$H_2$ 실험은 마이크로 가스센서를 초기에 공기 분위기에서 초기 저항 값을 측정하였다. $SnO_2/Pd/V_2O_5$으로 구성된 감지물질은 수소 농도 5000ppm에서 초기 저항 값을 기준으로 하여 10배 감소하는 우수한 감도 반응을 확인할 수 있었다.

• Journal of Sensor Science and Technology
• /
• v.5 no.5
• /
• pp.39-46
• /
• 1996

The Pd or Pt-doped $WO_{3}$ thin-film NOx sensor was fabricated. The $WO_{3}$-based thin films as a gas-sensing layer were deposited at ambient temperature in a high-vacuum resistance heated evaporator and annealed at $500^{\circ}C$. The gas sensitivity ($R_{gas}/R_{air}$) to 5 ppm $NO_{2}$ measured at the operating temperature of $300^{\circ}C$ was 50 (highest sensitivity) for the 0.5 wt.% $Pt-WO_{3}$ sensor.

• Clean Technology
• /
• v.20 no.1
• /
• pp.64-71
• /
• 2014

We have investigated the effects of various additives on Eco coal gasification under $CO_2$ atmosphere. The temperature ranges from $750{\sim}900^{\circ}C$ and the gasification experimental was carried out with Eco coal adding 7 wt% $K_2CO_3$, $Na_2CO_3$, $CaCO_3$, Dolomite, and non-additive under $N_2$ and $CO_2$ gas mixture. At $850^{\circ}C$, we observed that the reaction rate increased when the concentration of $CO_2$ increased. However, we also observed that the increment of reaction rate was small at more than 70% of the concentration of $CO_2$. The additives activity was ranked as 7 wt% $Na_2CO_3$ > 7 wt% $K_2CO_3$ > non-additive > 7 wt% Dolomite > 7 wt% $CaCO_3$ at $850^{\circ}C$. At the temperatures of $750^{\circ}C$, $800^{\circ}C$, $850^{\circ}C$, and $900^{\circ}C$, when the temperature increased, the gasification rate increased. The gasification was suitably described by the volumetric reaction model. Using volumetric reaction model, the activation energy of Eco coal including 7 wt% $Na_2CO_3$ gasification was 83 kJ/mol, which was the lowest value among all the alkaline additives.

• Resources Recycling
• /
• v.16 no.1 s.75
• /
• pp.37-43
• /
• 2007

It was studied to prepare anhydrous magnesium chloride which could used as the raw material of a fused salt electrolysis of magnesium by dehydration of magnesium chloride hydrate. The dehydration was carried out in a tube furnace at $350{\sim}580^{\circ}C$. It was confirmed that magnesium chloride hydrate was oxdized to magnesia through the dehydration in ambient atmosphere, but anhydrous magnesium chloride could be obtained in hydrogen chloride gas atmosphere. And the crystallity of the product increased with increasing temperature and time of dehydration. All of the un-reacted hydrogen chloride gases which were generated during the dehydration in hydrogen chloride gas atmosphere could be recovered as hydrochloric solution, and it could be reused for chlorination of magnesia to prepare magnesium chloride hydrate.

• Analytical Science and Technology
• /
• v.14 no.3
• /
• pp.212-220
• /
• 2001

This study was performed to establish the analytical method of radium and radon in various environmental samples with the ${\gamma}$-ray spectrometry. The major problem in the measurements of low level ${\gamma}$-ray, such as environmental radioactivity, is the fluctuation of ${\gamma}$-ray background spectrum. To overcome this problem, a nitrogen gas was filled up in the detector chamber to reduce the background counts due to airborne radioactivities, i.e., $^{214}Pb$ and $^{214}Bi$, the daughters of $^{222}Rn$ in air. When nitrogen gas flowed around the detector, peak counts of ${\gamma}$-rays from the daughters of $^{222}Rn$ decreased about 80% below 1 MeV and about 20~50% above 1 MeV. The use of nitrogen purging results in approximately tenfold increment of sensitivity.

• Journal of the Korean Vacuum Society
• /
• v.1 no.3
• /
• pp.389-394
• /
• 1992

용액분무법으로 (100) MgO 단결정 기판위에 YBa2Cu3O7-x 초전도박막을 제조하 였다. YBa2Cu3O7-x 초전도 박막의 Y, Ba, Cu 원자의 상대적인 비는 EDX의 검출 한계내에 서 1 : 2 : 3이었고, 이는 분무 용액속의 금속이온의 비와 같았다. YBa2Cu3O7-x 초전도 박 막의 결정구조는 단일 상의 사방구조였으며, 기판에 수직인 c축의 방향으로 grain이 성장되 었고, 격자상수 c0는 11.678$\AA$였다. 95$0^{\circ}C$의 공기중에서 10분간 열처리한 박막의 Tc-on=100K, Tc-zero=80K, Jc=2.5 $\times$ 104A/cm2였고, 95$0^{\circ}C$의 흐르는 산소분위기에서 10분간 열처리한 박막의 Tc-on=103K, Tc-zero=80K, Jc=1.0 $\times$ 105A/cm2였다. 초전도 박막의 미세구 조, grain 크기와 grain 경계폭은 제조후 열처리(post-annealing) 시간과 가스 분위기에 강 한 영향을 받았다.

• Journal of environmental and Sanitary engineering
• /
• v.13 no.1
• /
• pp.1-8
• /
• 1998

Musty-odorous compound (Geosmin, 2-Methylisobrneol) 수용액 중에 초음파 (200kHz, $6.0W/cm^{2}$)를 조사시켜 조사시간에 따른 농도 및 취기의 변화를 고찰했다. 초음파 조사에 의해 이 물질들은 빠르게 분해되었고 분해 형태는 농도에 대한 유사1차 반응을 나타내었다. 공기 포화 분위기에서 이들의 초기 분해속도는 각각 2.5 $10^{-3}{\;}Msec^{-1}$(2-MIB), 3.2 $10^{-3}{\;}Msec^{-1}$ (Geosmin)로 나타났다. 초음파 조사 시 포화가스 (Envelope gas)의 영향은 아르곤(Ar) 산소($O_{2}$) 공기(Air) 질소($N_{2}$) 순서로 순수한 아르곤(Ar) 분위기에서 musty-odorous compound 류의 분해가 가장 빠르게 진행되었고 그 분해생성물로 CO, $CO_{2}$ 그리고 HCOOH, $CH_{3}COOH$ 등의 저급 유기산류가 검출되었다. 또한 이들의 분해반응은 물의 초음파분해에 따라 생성된 hydroxylradical에 의한 radical반응, cavitation bubble내에서의 고온고압에 의한 열분해 및 직접연소반응으로 진행됨을 알 수 있었다.