• Journal of the Korean Vacuum Society
• /
• v.18 no.1
• /
• pp.49-53
• /
• 2009

The chemical properties of SiOC film was studied for inter-layer insulator. SiOC film was formed with non polarity due to the appropriate union by the alkyl and hydroxyl group. An amorphous structure of non polarity can induce the low dielectric constant materials. The chemical properties of thin film can define the bonding structure owing to the ionic variation, and the analysis of chemical properties was researched by the carbon content using the FTIR spectra, and induced the film with non polarity. The electrical properties is the electron flow, and is always not the same as the chemical properties. The electrical properties of SiOC film with various flow rate ratios was analyzed and researched the correlation between the chemical properties. SiOC film showed the increasing of the leakage current after annealing process, and abruptly increased the carbon content at some samples. But the sample with increasing the carbon content decreased the leakage current. It means that the chemical properties is not the same as the electrical properties, and the carbon is related with the variation of the bonding structure, and does not contribute the current flow.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.54-54
• /
• 2003

최근 새로운 개념에 물성 구현을 위한 강유전체 산화물 인공격자의 연구가 활발히 진행되고 있다. 본 연구에서는 펄스레이져 증착법을 이용하여 산소분압 100 mTorr와 증착온도 50$0^{\circ}C$에서 LSCO/MgO 기판 위에 PbTiO$_3$(PTO) 와 PbZrO$_3$(PZO)을 주기적으로 적층하여 강유전체 산화물 인공격자를 형성하였다. 인공격자의 주기는 1~100 unitcell 까지 변화시켰다. 적층주기와 두께 변화에 따른 PZO/PTO 인공격자의 성장과 전기적 특성에 대하여 관찰하였다. X선 회절분석을 통하여 PZO/PTO 인공격자는 주기가 25 unit cell 이하의 적층구조에서 초격자의 형성으로 인한 위성피크가 관찰되었으며, 그 이하의 낮은 주기(1~10 unitcell)에서는 위성피크와 강한 (100)과 (200) 성장거동을 보였다. 높은 주기에서는 c축 성장된 PTO와 a축 성장된 PZO 각각의 성장거동을 보였다. 적층 주기가 감소함에 따라 a축 성장된 PTO와 c축 성장된 PZO가 초격자를 형성하였다. 적층주기가 감소함에 따라 유전상수와 잔류분극값이 향상되었다. 유전상수는 1 unitcell 주기에서 800정도의 값을 보였고, 잔류분극값은 2 unitcell 주기에서 2Pr=38.7 $\mu$C/$\textrm{cm}^2$ 정도의 가장 큰 값을 나타냈다. 적층주기가 2 unitcell에서 두께가 감소함에 따라 유전상수가 감소하였고, 20 nm 까지 분극반전에 의한 capacitance-voltage 특성곡선의 이력 현상(강유전성)을 관찰하였다. 이러한 산화물 인공초격자에서의 유전상수와 잔류분극값의 향상에 대하여 논의 할 것이며, 임계크기효과 관점에서 나노사이즈(50 nm~5 nm)에서 인공초격자의 전기적 분극의 안정성에 대하여 또한 논의 할 것이다.소수성 가스의 경우70% 이상 향상되었음을 알 수 있었으며, 본 연구를 통해 광분해를 이용한 스크러버가 기존설비의 장.단점을 충분히 보완 가능한 환경 설비임을 확인할 수 있었다. duty로 구동하였으며, duty비 증가에 따라 pulse의 on-time을 고정하고 frequency를 변화시켰다. dc까지 duty비가 증가됨에 따라 방출전류의 양이 선형적으로 증가하였다. 전압을 일정하게 고정시키고 각 duty비에서 시간에 따라 방출전류를 측정한 결과 duty비가 높을수록 방출전류가 시간에 따라 급격히 감소하였다. 각 duty비에서 방출전류의 양이 1/2로 감소하는 시점을 에미터의 수명으로 볼 때 duty비 대 에미터 수명관계를 구해 높은 duty비에서 전계방출을 시킴으로써 실제의 구동조건인 낮은 duty비에서의 수명을 단시간에 예측할 수 있었다. 단속적으로 일어난 것으로 생각된다.리 폐 관류는 정맥주입 방법에 비해 고농도의 cisplatin 투여로 인한 다른 장기에서의 농도 증가 없이 폐 조직에 약 50배 정도의 고농도 cisplatin을 투여할 수 있었으며, 또한 분리 폐 관류 시 cisplatin에 의한 직접적 폐 독성은 발견되지 않았다이 낮았으나 통계학적 의의는 없었다[10.0%(4/40) : 8.2%(20/244), p>0.05]. 결론: 비디오흉강경술에서 재발을 낮추기 위해 수술시 폐야 전체를 관찰하여 존재하는 폐기포를 놓치지 않는 것이 중요하며, 폐기포를 확인하지 못한 경우와 이차성 자연기흉에 대해서는 흉막유착술에 더 세심한 주의가 필요하다는 것을 확인하였다. 비디오흉강경수술은 통증이 적고, 입원기간이 짧고, 사회로의 복귀가 빠르며, 고위험군에 적용할 수 있고, 무엇보다도 미용상의 이점이 크다는 면에서 자연기흉에 대해 유용한 치료방법임에는 틀림이 없으나 개흉술에 비해 재발율이 높고 비용이 비싸다는 문제가 제기되고 있는 만큼 더 세심한 주의와 장기 추적관찰이 필요하리라 사료된

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.84-84
• /
• 1999

최근 큰 잔류분극을 가진 강유전체 Pb(Zr, Ti)O3 박막을 이용한 비휘발성 기억소자의 연구가 활발히 진행되고 있다. 그러나 Pb(Zr, Ti)O3 박막을 비휘발성 기억소자로 응용하는 경우 분극피로(polarization fatigue), imprint, 누설전류 등의 문제점이 나타나는 것으로 알려져 있다. 특히 분극반전 횟수가 증가할수록 잔류분극이 감소하는 분극피로 현상은 비휘발성 기억소자의 응용에 있어서 치명적인 장애가 되므로 기억소자의 실용화를 위해서는 분극피로 현상의 개선이 무엇보다 중요하다. 본 연구에서는 Pb(Zr, Ti)O3 강유전체 박막의 분극피로 현상을 규명하고 개선하기 위해서 다음과 같은 세가 실험적 방법으로 접근하였다. 먼저 Pt와 금속산화물인 LaNiO3을 이용하여 상·하부 전극을 달리하여 제조한 축전기에 대해서 분극피로 특성을 관찰하고 이로부터 분극피로 현상에 대한 전극의 효과를 조사하였다. 여기서 금속산화물인 LaNiO3 박막과 Pt 박막은 r.f. 스퍼트 법으로 증가하였으며 Pb(Zr, Ti)O3 박막은 LaNiO3/Si(100)/와 Pt/Ti/SiO2/i(100) 기판위에 졸겔법으로 제조하였다. 다음으로 분극피로된 박막의 상부전극에 극성이 다른 직류전압을 인가해주었을 때 나타나는 분극회복 현상을 광범위하게 관찰하였으며, 특히 직류전압의 극성에 따라 비대칭적인 분극회복 특성을 보였다. 마지막으로 이와 같은 직류전압에 대한 비대칭적인 분극회복현상에 착안하여 양과 음의 방향으로 바이어스된 스윗칭 펄스를 인가하여 분극피로 특성을 조사한 결과 비대칭적인 분극피로 현상을 관찰할 수 있었다. 이와 같은 Pv(Zr, Ti)O3 박막의 분극피로와 회복의 비대칭적인 현상은 분극피로 현상의 기구를 밝히는 중요한 근거가 되었으며, 본 연구에서는 하부 계면에서의 산소빈자리의 역할로 분극피로 현상을 모형화하였다.식각하기 시작하였으며, 19.5J/cm2에서 유리기판의 rudraus(격벽 두께 130$\mu\textrm{m}$)까지 식각하였다. 대한 정보(RDF)는 명확하게 얻을 수 있었다.nospec과 SEM으로 관찰하였다. 또한 Ge 함량 변화에 따른 morphology 관찰과 변화 관찰을 위하여 AFM, SEM, XRD를 이용하였으며, 이온주입후 열처리 온도에 따른 활성화 정도의 관찰을 위하여 4-point probe와 Hall measurement를 이용하였다. 증착된 다결정 SiGe의 두게를 nanospec과 SEM으로 분석한 결과 Gem이 함량이 적을 때는 높은 온도에서의 증착이 더 빠른 증착속도를 나타내었지만, Ge의 함량이 30% 되었을 때는 온도에 관계없이 일정한 것으로 나타났다. XRD 분석을 한 결과 Peak의 위치가 순수한 Si과 순수한 Ge 사이에 존재하는 것으로 나타났으며, ge 함량이 많아짐에 따라 순수한 Ge쪽으로 옮겨가는 경향을 보였다. SEM, ASFM으로 증착한 다결정 SiGe의 morphology 관찰결과 Ge 함량이 높은 박막의 입계가 다결정 Si의 입계에 비해 훨씬 큰 것으로 나타났으며 근 값도 증가하는 것으로 나타났다. 포유동물 세포에 유전자 발현벡터로써 사용할 수 있음으로 post-genomics시대에 다양한 종류의 단백질 기능연구에 맡은 도움이 되리라 기대한다.다양한 기능을 가진 신소재 제조에 있다. 또한 경제적인 측면에서도 고부가 가치의 제품 개발에 따른 새로운 수요 창출과 수익률 향상, 기존의 기능성 안료를 나노(nano)화하여 나노 입자를 제조, 기존의 기능성 안료에 대한 비용 절감 효과등을 유도 할 수 있다. 역시 기술적인 측면에서도 특수소재 개발에 있어 최적의 나노 입자 제어기술 개발 및 나노입자를 기능성 소재로 사용하여 새로운 제품의 제조와 고압 기상 분사기술의 최적화에

• Journal of Korean Society of Environmental Engineers
• /
• v.30 no.2
• /
• pp.155-160
• /
• 2008

In this study, the nitrate removal efficiency was examined under a variety of operating conditions, such as different doses of the reducing agent, different electrode types, different HRTs(hydraulic retention times), and different current densities, using the multistep electrochemical process. The nitrate removal efficiency increased and the input energy decreased when the reducing agent was used, and almost no difference was found between the electrode types in terms of their nitrate removal efficiency and current efficiency. So that the Zn reducing agent could be recovered, though, the B-type electrode was chosen(step 1: Pt-Zn; step 2: Pt-Zn; step 3: Pt-Zn; step 4: Pt-Zn). HRT experiments were carried out on constant electric current density unrelated HRTs and various electric current density related HRTs: the constant amount of electric current per unit volume. As a result, HRT and the electric current density caused concentration polarization and the lack of an applied current. That is to say,the lower the HRT, the greater the decrease in concentration polarization and in the amount of applied current per unit volume. Therefore, optimal conditions were found through the experiments that were conducted on HRT and electric current density. When a spacer was installed in the process, the nitrate removal efficiency and energy efficiency increased even more because the diffusion likewise increased.

• Electrical & Electronic Materials
• /
• v.4 no.1
• /
• pp.53-64
• /
• 1991

절연체중에 있는 하전입자의 거동은 절연재료의 특성에 많은 영향을 준다. 본 연구에서는 호핑모델에 의한 수치해석법을 TSC특성과 쌍극자분극에 대한 TSC특성은 차이가 있었다. 실험과 대응시켜 가동이온에 관한 물성정수의 평가를 하였다. 호핑모델에 의해서 불포화 TSC와 I-V특성의 수치계산을 하였다.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.11a
• /
• pp.74.1-74.1
• /
• 2010

수치해석을 이용하여 형상 및 운전 조건에 따른 금속공기전지의 전기화학적 성능 변화를 조사하였다. 저전류밀도 영역에서의 전지 성능은 농도손실에 의한 영향이 미미하므로 활성화 손실과 저항손실만을 고려한 수치해서 모델을 적용하였다. 지배방정식은 전기전도식을 이용하였으며 전극 표면의 활성화손실을 모사하기위해 아연극(음극)에는 butler-volmer식을, 공기극(양극)에는 tafel식을 적용하였다. 실험결과와의 비교/분석을 통하여 수치해석 모델의 타당성을 검증하였다. 또한, 아연극과 공기극 사이의 간격과 전해질 농도 변화에 따른 아연공기전지 내부에서의 전류밀도분포를 조사하였으며, 분극곡선을 통해 전기화학적 성능을 평가하였다.

• Journal of the Microelectronics and Packaging Society
• /
• v.5 no.2
• /
• pp.59-64
• /
• 1998

Pt/SiO2/Si 기판구조위에 스크린인쇄법과 졸-겔법에 의해 (Pb, La)TiO3(PLT) 후막 과 박막을 도포시켜 $650^{\circ}C$후속열처리 온도에서 결정화한후 결정특성과 전기적 특성을 조사 하였다. $650^{\circ}C$ 온도에서 후속열처리된 PLT 시료의 경우 전형적인 perovskite 결정구조를 보 여주었다. SEM 단면형상으로부터 Pt 전극과 PLT막 사이에는 비교적 평활한 계면형상을 보여주었다. PLT 후막과 박막시료의 잔류분극(2Pr) 값은 약 1$\mu$C/cm2 으로각각 나타났으며 이와같이 후막 PLT시료에 비해 박막시료의 잔류분극값이 큰이유는 박막시료가 보다 양호 한 결정성을 지니기 때문이었다. 상온부근에서 후막과 박막시료의 초전계수값은 약 1.5nC/cm2.$^{\circ}C$와 4.0nC/cm2.$^{\circ}C$의 값을 각각 나타내었으며 누설전류의 크기는 약 0.3~0.8$\mu$ A/cm2의 비교적 양호한 누설전류 특성을 얻었다.

• Journal of the Korea Convergence Society
• /
• v.8 no.11
• /
• pp.287-292
• /
• 2017

The electrodeposition of Zn on the automotive parts has been adapted However, because Zn electrodeposit needs to increase thickness for corrosion protection, it has problem of destruction of electrodeposit Zn-based electrodeposit have teen studied for corrosion protection and decreasing electrodeposit thickness. Especially; Zn-Co electrodeposit have much attention In this study, the Composition of Zn-Co electrodeposit in various manufacturing condition such as temperature, current density and electrolyte content was investigated to understand effect of electrolysis condition on Co content of specimen. The results were explained by cathode overvoltage and diffusion coefficient. As the current density increases, the electrolyte temperature decreases, and as the electrolyte concentration decreases, the overvoltage of the cathode increases. As the overvoltage of the cathode increases, the concentration polarization becomes more important than the activation polarization. Concentration polarization is determined by the diffusion of the mass transfer in the diffusion layer. In a constant concentration polarization, a large amount of elements with a large diffusion coefficient is diffused. That is, as the overvoltage of the cathode increases, the Zn content having a large diffusion coefficient increases.

• Proceedings of the KIEE Conference
• /
• 2007.07a
• /
• pp.201-203
• /
• 2007

본 논문에서는, 연료전지 시스템의 기계적 주변장치 (MBOP)와 전기적 주변장치 (EBOP)의 최적 설계를 위해서 PEMFC 스택을 전기화학반응을 기초로 모델링한다. 모델링을 위해 기본적인 PEMFC의 구조와 동작 원리를 설명한다. 연료전지의 이론적 최고 전압인 평형전위를 깁스 자유에너지와 네른스트 방정식으로 유도한다. 전류밀도에 따른 전압 손실인 활성화, 저항, 농도 분극현상을 표현하기 위해서 수식을 유도한다. 수소가 이온화되지 못하고 산소극으로 넘어가서 발생되는 연료손실 및 내부전류와 지속적인 정역반응인 교환전류도 모델링된다. 평형전압에서 각 분극을 뺀 실제 운전 전압을 시뮬레이션하고, 유량과 압력에 따른 출력 특성을 시뮬레이션 한다. 부하변동 시 출력특성을 시뮬레이터와 실험결과로 비교한다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.133-133
• /
• 2003

최근에 강유전체 매체와 원자력 현미경 (Atomic Force Microscopy, AFM)을 이용한 초고밀도 정보 저장 장치에 대한 연구가 활발히 진행되고 있다. 이와 아울러 나도 크기의 도메인에 대하 연구에 있어서 PZT 박막의 분극 방향에 따른 SrRuO$_3$의 저항 변화를 AFM 탐침을 이용하여 감지하는 방법을 제안하였다. 본 연구에서는 Metal tip/semiconductor/barrier oxide/ferroelectric 구조에서 강유전체 분극에 의한 저항 변화의 가능성을 실험하고자, 이와 등가 구조인 Pt tip/n-Si/SiO$_2$ 구조에서 Pt 탐침과 반도체 층 사이의 I-V 특성을 측정함으로써, 게이트 전압에 따른 반도체 층의 저항변화에 대해서 분석해 보았다. 그 결과 게이트 전압에 따라서 과밀 지역 (accumulation layer)과 공핍 지역 (depletion layer)이 형성됨에 따라서 반도체 층의 정항이 변하여 I-V 특성이 변하게 됨을 관찰하였으며, 이 결과로부터 분극 방향에 따라서도 반도체 층의 저항이 변할 수 있음을 알 수 있었다.