• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.13 no.12
• /
• pp.2505-2510
• /
• 2009

The SiOC films were deposited with the variation of flow rate ratios by chemical vapor deposition. It was researched the reason of decreasing the dielectric constant in SiOC film and the relationship between the dielectric constant and the thickness. The thickness of the deposited films tends to in proportion to the refractive index and the sample with the lowest dielectric constant decreased the thickness. The refractive index was decreased after annealing because of the decreasing of the film's thickness by annealing process.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.54-54
• /
• 2003

최근 새로운 개념에 물성 구현을 위한 강유전체 산화물 인공격자의 연구가 활발히 진행되고 있다. 본 연구에서는 펄스레이져 증착법을 이용하여 산소분압 100 mTorr와 증착온도 50$0^{\circ}C$에서 LSCO/MgO 기판 위에 PbTiO$_3$(PTO) 와 PbZrO$_3$(PZO)을 주기적으로 적층하여 강유전체 산화물 인공격자를 형성하였다. 인공격자의 주기는 1~100 unitcell 까지 변화시켰다. 적층주기와 두께 변화에 따른 PZO/PTO 인공격자의 성장과 전기적 특성에 대하여 관찰하였다. X선 회절분석을 통하여 PZO/PTO 인공격자는 주기가 25 unit cell 이하의 적층구조에서 초격자의 형성으로 인한 위성피크가 관찰되었으며, 그 이하의 낮은 주기(1~10 unitcell)에서는 위성피크와 강한 (100)과 (200) 성장거동을 보였다. 높은 주기에서는 c축 성장된 PTO와 a축 성장된 PZO 각각의 성장거동을 보였다. 적층 주기가 감소함에 따라 a축 성장된 PTO와 c축 성장된 PZO가 초격자를 형성하였다. 적층주기가 감소함에 따라 유전상수와 잔류분극값이 향상되었다. 유전상수는 1 unitcell 주기에서 800정도의 값을 보였고, 잔류분극값은 2 unitcell 주기에서 2Pr=38.7 $\mu$C/$\textrm{cm}^2$ 정도의 가장 큰 값을 나타냈다. 적층주기가 2 unitcell에서 두께가 감소함에 따라 유전상수가 감소하였고, 20 nm 까지 분극반전에 의한 capacitance-voltage 특성곡선의 이력 현상(강유전성)을 관찰하였다. 이러한 산화물 인공초격자에서의 유전상수와 잔류분극값의 향상에 대하여 논의 할 것이며, 임계크기효과 관점에서 나노사이즈(50 nm~5 nm)에서 인공초격자의 전기적 분극의 안정성에 대하여 또한 논의 할 것이다.소수성 가스의 경우70% 이상 향상되었음을 알 수 있었으며, 본 연구를 통해 광분해를 이용한 스크러버가 기존설비의 장.단점을 충분히 보완 가능한 환경 설비임을 확인할 수 있었다. duty로 구동하였으며, duty비 증가에 따라 pulse의 on-time을 고정하고 frequency를 변화시켰다. dc까지 duty비가 증가됨에 따라 방출전류의 양이 선형적으로 증가하였다. 전압을 일정하게 고정시키고 각 duty비에서 시간에 따라 방출전류를 측정한 결과 duty비가 높을수록 방출전류가 시간에 따라 급격히 감소하였다. 각 duty비에서 방출전류의 양이 1/2로 감소하는 시점을 에미터의 수명으로 볼 때 duty비 대 에미터 수명관계를 구해 높은 duty비에서 전계방출을 시킴으로써 실제의 구동조건인 낮은 duty비에서의 수명을 단시간에 예측할 수 있었다. 단속적으로 일어난 것으로 생각된다.리 폐 관류는 정맥주입 방법에 비해 고농도의 cisplatin 투여로 인한 다른 장기에서의 농도 증가 없이 폐 조직에 약 50배 정도의 고농도 cisplatin을 투여할 수 있었으며, 또한 분리 폐 관류 시 cisplatin에 의한 직접적 폐 독성은 발견되지 않았다이 낮았으나 통계학적 의의는 없었다[10.0%(4/40) : 8.2%(20/244), p>0.05]. 결론: 비디오흉강경술에서 재발을 낮추기 위해 수술시 폐야 전체를 관찰하여 존재하는 폐기포를 놓치지 않는 것이 중요하며, 폐기포를 확인하지 못한 경우와 이차성 자연기흉에 대해서는 흉막유착술에 더 세심한 주의가 필요하다는 것을 확인하였다. 비디오흉강경수술은 통증이 적고, 입원기간이 짧고, 사회로의 복귀가 빠르며, 고위험군에 적용할 수 있고, 무엇보다도 미용상의 이점이 크다는 면에서 자연기흉에 대해 유용한 치료방법임에는 틀림이 없으나 개흉술에 비해 재발율이 높고 비용이 비싸다는 문제가 제기되고 있는 만큼 더 세심한 주의와 장기 추적관찰이 필요하리라 사료된

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05d
• /
• pp.113-118
• /
• 2003

투어멀린(Tourmaline)은 비대칭 쌍극자를 가진 천연 유극성 결정체로 광물 중에서 영구전기분극을 띄고 있는 유일한 물질로써 일명 "전기석"이라고 알려져 있다. 분극에 의한 자체 미약전류(약 $60{\mu}A$)와 함께 음이온 및 원적외선의 발생으로 최근 우리주변에서 건강과 환경을 위한 관심고조의 대상인 육방정계의 압전성 및 초전성을 띄는 붕규산염(주요성분: Mg, Fe, B, Si, Ca)으로, 투어멀린 원석이나 그 복합세라믹체의 면역지수가 ~1000에서 ~400,000 이상인 점을 비롯하여 그 유용성을 이용하려는 새로운 아이디어 신상품들이 계속 개발되고 있다. 뿐만 아니라 물분자를 만나면 수소$(H^+)$와 수산기 $(OH^-)$로 전기분해 하여 친수기와 소수기 부분으로 구분하며, $H^+$와 $OH^-$는 각각 $H_2O$와 결합하여 활성이 강한 hydronium ion$(H_3O^+)$을 생성하고, 물 속에서 계속 불안정한 상태로 존재하는 수산기는 계면활성 작용이 있는 hydroxyl ion$(H_3O_2^-)$을 형성하여 물을 약 알카리성 (pH~7.4)으로 바꿔주며, 물분자 클러스터 세분화와 미네랄을 용출, 공급하여 이 물이 체내에 흡수되면 살균, 항균성의 면역기능을 갖게 되며, 혈액정화 기능과 자율신경 자극으로 교감신경의 흥분을 억제해 준다. 이와 함께 전기분극을 띈 투어멀린 입자는 다른 물질에 비하여 경이적 수치의 원적외선을 발생하여 강력한 열 효과와 높은 침투력으로 인체의 혈액순환 촉진과 혈전용해 작용을 주어 건강과 활력에 도움을 주는 것으로 확인되어 많은 관심을 끌고 있다. 따라서 유익한 이용가치를 인정받고 있는 천연 투어멀린을 단독 형태나 또는 서로 상승효과를 줄 수 있는 유용한 타 물질과 혼합물을 구성하여 성형 또는 EPD 방법으로 전착한 후 소결 처리하여, 소결체의 특성 분석과 함께 물에 대한 전기 화학적 작용 및 항균 효과를 조사, 확인하여 수질개선 효과를 분석하고 그 응용성을 개발, 확보하였다.

• Korean Journal of Optics and Photonics
• /
• v.27 no.6
• /
• pp.223-228
• /
• 2016

The birefringence of distributed, uniaxially anisotropic molecules like liquid crystals is calculated as the degree of ordering is varied. The relation between the normalized birefringence ${\Delta}n_{rel}$ and the orientational order parameter S is investigated. The distribution function, which enables one to monitor the degree of ordering of liquid crystals including randomly distributed ones, is introduced. Using this distribution function, a series of distributed liquid crystals with order parameters ranging from 0 to 1 are generated, and ${\Delta}n_{rel}$ and S of the correspondingly distributed liquid crystals are calculated. Based on the calculated data, it is revealed that ${\Delta}n_{rel}$ and S satisfy the quasi-linear relation of $S=(1+a){\Delta}n_{rel}-a{\Delta}n^2_{rel}$, where a can be approximated as $n_o{\frac{{\Delta}n}{4}}$. The anisotropy of molecular polarizability is also calculated, using the birefringence, and separately following Vuks' method and Neugebauer's method, and it is shown that the relations between S and the molecular-polarizability anisotropy are also quasi-linear.

• Journal of the Korean Vacuum Society
• /
• v.18 no.1
• /
• pp.49-53
• /
• 2009

The chemical properties of SiOC film was studied for inter-layer insulator. SiOC film was formed with non polarity due to the appropriate union by the alkyl and hydroxyl group. An amorphous structure of non polarity can induce the low dielectric constant materials. The chemical properties of thin film can define the bonding structure owing to the ionic variation, and the analysis of chemical properties was researched by the carbon content using the FTIR spectra, and induced the film with non polarity. The electrical properties is the electron flow, and is always not the same as the chemical properties. The electrical properties of SiOC film with various flow rate ratios was analyzed and researched the correlation between the chemical properties. SiOC film showed the increasing of the leakage current after annealing process, and abruptly increased the carbon content at some samples. But the sample with increasing the carbon content decreased the leakage current. It means that the chemical properties is not the same as the electrical properties, and the carbon is related with the variation of the bonding structure, and does not contribute the current flow.

• The Journal of Engineering Geology
• /
• v.18 no.4
• /
• pp.423-431
• /
• 2008

In general, water-saturated silt or clay alluvium is characterized with relatively low-resistivity. Thus we often encountered the problem that such a low-resistivity layer is misguided to be good aquifer of high-permeability and low-resistivity in the development of groundwater. This research was conducted with an emphasis on the identification of saturated silt or clay layer from the aquifer by performing the laboratory experiment of IP and resistivity methods on the various materials consisting of alluvium aquifer. Silt or clay layer is found to be characterized with the higher chargeability zone, compared to the sand layer. Regarding the mixture of sand and clay, the higher clay volume, the lower resistivity and the higher chargeability. Subsequently chargeability decreases.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.188-188
• /
• 2016

GZO 박막은 상업적으로 사용되는 ITO를 경제적으로 대체할 수 있는 유망한 투명 전도 물질이며, 인체에 무해하고, 공급이 쉬우며, 화학적으로 안정하다. 특히, CIGS와 같은 광전변환 소자 전극에서는 부식 저항이 매우 중요한데, 습한 환경에서 견뎌낼 수 있다는 장점이 있다. GZO는 3가 갈륨이 2가 아연에 도핑된 n타입의 반도체 물질이다. 그리고 육각형의 황화아연 물질의 전기 전도도는 산소 결핍에 매우 의존한다. GZO의 수소는 산소 결핍 집중에 영향을 끼친다. 따라서 이 연구에서는 RF 마그네트론 스퍼터링 실험 동안 수소 함유량을 다양화 시키고, 면 저항, 광 투과도, 부식저항의 효과를 조사한다. 수소량이 증가할수록, 면 저항은 향상되어지고, 특정 지점을 넘으면 감소한다. 분극 실험에 의해 측정되어진 부식 저항은 박막의 미세조직과 결정립계의 특성에 더 의존되어진다. 훨씬 더 많은 수소를 함량한 비정질이 부식 저항성에 있어서 유효한 차이를 나타내지 못하는 동안 결정 내에서 많은 수소를 지닌 작은 결정의 결정립계는 낮은 분극저항, 즉 낮은 부식 저항성의 결과를 도출한다.

• Korean Journal of Materials Research
• /
• v.7 no.6
• /
• pp.479-483
• /
• 1997

Sol-gel법으로 제작한 여러 종류의 Zr/Ti비율을 갖고 있는 PZT박막의 전지적 특성과 신뢰성 특성을 상부 백금 전극을 sputtering으로 증착하고 Ar 기체로 반응성 이온 식각(RIE)방법으로 패턴을 형성한 후 열처리온도의 변화에 따라 조사하였다. Hysteresis loop특성을 되찾게 하였다. Zr/Ti 비율이 감소함에 따라 voltage shift가 증가하였으며 internal field가 없어지는 열처리 온도가 증가하였다. Zr/Ti비율이 감소함에 따라 초기 잔류 분극은 증가하였으나 switching 횟수가 증가됨에 따라 잔류 분극이 급속히 감소하였다.

• Geophysics and Geophysical Exploration
• /
• v.24 no.4
• /
• pp.194-201
• /
• 2021

Induced polarization (IP) effect is known to be caused by electrochemical phenomena at interface between minerals and pore water. Spectral induced polarization (SIP) method is an electrical survey to localize subsurface IP anomalies while injecting alternating currents of multiple frequencies into the ground. This method was effectively applied to mineral exploration of various ore deposits. Titanomagnetite ores were being produced by a mining company located in Gonamsan area, Gwanin-myeon, Pocheon-si, Gyeonggi-do, South Korea. Because the ores contain more than 0.4 w% vanadium, the ore deposit is called as Gwanin vanadiferous titanomagnetite (VTM) deposit. The vanadium is the most important of materials in production of vanadium redox flow batteries, which can be appropriately used for large-scale energy storage system. Systematic mineral exploration was conducted to identify presence of hidden VTM orebodies and estimate their potential resources. In geophysical exploration, laboratory geophysical measurement of rock samples is helpful to generate reliable property models from field survey data. Therefore, we performed laboratory SIP data of the rocks from the Gwanin VTM deposit to understand SIP characteristics between ores and host rocks and then demonstrate the applicability of this method for the mineral exploration. Both phase and resistivity spectra of the ores sampled from underground outcrop and drilling cores were different of those of the host rocks consisting of monzodiorite and quartz monzodiorite. Because the phase and resistivity at frequencies below 100 Hz are mainly dependent on the SIP characteristics of the rocks, we calculated mean values of the ores and the host rocks. The average phase values at 0.1 Hz were ores: -369 mrad and host rocks: -39 mrad. The average resistivity values at 0.1 Hz were ores: 16 Ωm and host rocks: 2,623 Ωm. Because the SIP characteristics of the ores were different of those of the host rocks, we considered that the SIP survey is effective for the mineral exploration in vanadiferous titanomagnetite deposits and the SIP characteristics are useful for interpreting field survey data.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.13 no.3
• /
• pp.1279-1283
• /
• 2012

SiOC films made by the inductive coupled CVD with dimethyldimethoxysilane were analyzed to find out the correlation between the chemical and optical properties by using the Foruier transform infrared spectroscopy, spectrophotometer and ellipsometer. The bonding structure of SiOC film was formed during the depositeion and the adhesion was increased after annealing process. SiOC film decreased the polarization by the chemical reaction between alkyl group and hydroxyl group, and increased the degree of amorphism. For the range of 950 cm-1 in FTIR spectra, the spectra were divided into two types depending on polar sites. The refractive index of SiOC film with the lowest polarization increased and the thickness of that decreased.