• Journal of the Korea institute for structural maintenance and inspection
• /
• v.11 no.5
• /
• pp.189-196
• /
• 2007

The purpose of this study was to analyze steel corrosion resistance of concrete containing copper slag. The specimens were made with normal portland cement and pozzolan materials with various replacement ratio and with W/B ratio ranging from 35% to 55%. Compressive strength, coefficient of chloride diffusion, corrosion area ratio and weight reduction ratio were determinated for the test. The results show that the concrete with pozzolan materials is superior resistant to chloride ions compared to the concrete without pozzolan materials. It was observed that blast furnace slag replacement ratio of 20% gives the best results with respect to chloride ion penetration and corrosion tests and observed that copper slag replacement ratio of 10% gives the seperior resistance compared to normal concrete.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.25 no.1
• /
• pp.67-74
• /
• 2021

This paper evaluated the structural safety of an aging PSC I-girder bridge with rebar corrosion in the deck. The geometry and rebar of the bridge were designed based on an actual PSC I-girder bridge, and the numerical analysis was performed considering the crack of concrete and yielding of steel rebar. According to the evaluation criteria of Korea Infrastructure Safety and Technology Corporation, this study defined two criteria of rebar exposure and corrosion rates to construct a total of 32 corrosion scenarios. Rebar exposure was defined as the exposure of tensile rebars in the bridge deck due to the removal of cover concrete. The results of the analysis showed that the safety and rating factors of the bridge decreased with increasing rebar exposure and corrosion rates. For the rebar corrosion rate more than 50%, the safety grade of the bridge should be carefully evaluated for all the rebar exposure rate. When the rebar corrosion rate exceeds 57%, the bridge was evaluated as E grade regardless of rebar exposure rate. A correlation analysis for a 2% of rebar exposure rate found that the bridge was evaluated as A grade up to 55.8% corrosion rate, C grade up to 56.9%, D grade up to 58.5%, and E grade for corrosion rate greater than 58.5%. This study indicates the necessity of a quantitative evaluation of rebar corrosion for evaluating the structural safety of aging bridges.

• Nuclear Engineering and Technology
• /
• v.22 no.4
• /
• pp.315-325
• /
• 1990

The analytical repository source term (REPS) computer code is developed for the safety assessment of radioactive waste geologic repository. For reliable prediction of the leach rates for various radionuclides, degradation of concrete structures, corrosion rate of waste container, degree of corrosion on the container surface, and the characteristics of radionuclides are considered in this REPS code. For the validation of the radionuclide leach rates predicted by the REPS model, the calculated leach rates of Cs-137, Sr-85, and Co-60 are compared with two reported leaching test results. Cesium and strontium leach congruently, and the leaching test results of these species can be reproduced by the congruent leaching model included in the REPS model. In case of cobalt, the solid diffusion model is in good agreement with the leaching test results.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.10 no.4
• /
• pp.79-86
• /
• 2006

This study was investigated to corrosion resistance of Cr-bearing rebars to macrocell corrosion caused by concrete with crack. Ten types of steel bars having different Cr contents were embedded in concretes with imitation crack. The corrosion resistance of the Cr-bearing rebar was examined by measuring half-cell potential, macrocell corrosion current, corrosion area and weight loss up to 105 cycles of salt spray testing. The results revealed that the Cr content required for corrosion resistance in a macrocell corrosion environment caused by chloride ion gap of $3kg/m^3$ was 9% or more. The corrosion-resisting performance of Cr-bearing rebar was particularly noticeable with a Cr content of 11% or more.

• Corrosion Science and Technology
• /
• v.8 no.2
• /
• pp.53-61
• /
• 2009

In this study, both evaluations by visual imaging for exterior view of coating and by EIS were executed for epoxy primer coated specimens deteriorated by accelerated test, and comparison and analysis were carried out for 2 evaluation methods. In the comparison between total damaged area ratio acquired by image processing method and deterioration point, higher deterioration points were appeared for rusted specimens than for non-rusted specimens. It is attributed that deterioration point per unit area ratio given for rust is higher than for peeling. In the comparison between total damaged area ratio and EIS result, impedance of coating was largely decreased as about TEX>$10^4{\Omega}{\cdot}cm^2$ or less when rust area ratio is more than about 0.1%, and blistering area ratio is more than about 3%. Charge transfer resistance ($R_{ct}$) and double layer capacitance ($C_{dl}$) values were appeared for all specimens except 2 ones, which shows that water is accumulated and steel substrate is corroded at coated film-steel interface. In the comparison between deterioration point and EIS result, more than 10 points as deterioration point were given for specimens of below $10^6{\Omega}{\cdot}cm^2$ of impedance at low frequency. For specimens deteriorated by NORSOK cyclic test, impedance was lowest of all, though deterioration point was not high. It is thought to be attributed that coating system and accelerated deterioration condition of cyclic tested specimens were different from those of main specimens. From the result, it is thought that coating resistance can be relatively more decreased than deterioration degree estimated from exterior view under more severe corrosion environment or in the present of more complex deterioration factors.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2003.05a
• /
• pp.39-43
• /
• 2003

Chloride ions are considered to be the major cause of steel corrosion in concrete structures exposed to seashore environments and also permeation of chloride is controlled by chloride diffusion. Therefore, the study on chloride diffusion of concrete have been done so far by many researchers. It is reported that coating material as surface covering material is effect about deterioration of salt damage and carbonation, therefore these materials are important in durability of concrete structure. In this study, corrosion characteristics of reinforcement concrete according to types of surface covering material were evaluated by water-cement ratio, chloride penetration by age on the corrosion area rate and mass decrement of reinforcement. And it is considered that the result of this study on application of the corrosion characteristics of reinforcements under salt damage environmental will be suggested as fundamental data of control performance of salt damage. It is performed that comparison and examination of control performance of salt damage by the corrosion characteristics under salt damage environmental.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.10 no.3
• /
• pp.115-122
• /
• 2006

Ten types of steel bars having different Cr contents were embedded in concretes with chloride ion contents of 0.3, 0.6, 1.2, and $2.4kg/m^3$ to fabricate specimens assuming such deteriorative environments. After being carbonated to the reinforcement level, these concretes were subjected to corrosion-accelerating cycles of heating/cooling and drying/wetting. The time-related changes in the corrosion area and corrosion loss of the Cr-bearing rebars were then measured to investigate their corrosion resistance. The results revealed that in a deteriorative environment prone to both carbonation and chloride attack, corrosion resistance was evident with a Cr content of 7% or more and 9% or more in concretes with chloride ion contents of 1.2 and $2.4kg/m^3$, respectively.

• Nuclear Engineering and Technology
• /
• v.25 no.1
• /
• pp.63-70
• /
• 1993

A simplified safety assessment is carried out on rock-cavern type disposal of LLW using the analytical repository source term (REPS) model. For reliable prediction of the leach rates for various radionuclides, degradation of concrete structures, corrosion rate of waste container, degree of corrosion on the container surface, and the characteristics of radionuclides are considered in the REPS model. The results of preliminary assessment show that Cs-137, Ni-63, and Sr-90 are dominant. For the parametric uncertainty and sensitivity analysis, Latin hypercube sampling technique and rank correlation technique are applied. The results of the potential public health impacts show that radiological dose to intruder in the worst case scenario will be negligible and that more attention should be given to near-field performance.

• Magazine of the Korea Concrete Institute
• /
• v.10 no.6
• /
• pp.325-333
• /
• 1998

Under the seawater environment, the reinforced concrete structure is deteriorated due to physical and chemical attacks. The main deterioration mechanism is the chloride corrosion of reinforcing steel. The corrosion inhibitors have been used to protect the rebars from corrosion which are susceptible to chlorides in concrete. However, there is not clear conclusion about corrosion inhibitors yet. In this study, it is made the accelerated experiment with 3 kinds of corrosion inhibitors for various chloride ingresses. It is estimated corrosion inhibitors that inhibitors by Half-Cell Potential, corrosion area ratio and weight loss ratio. It is concluded that inhibitors are not effective to corrosion inhibition for excessive chloride ingress. However, the effect of inhibition is directly proportional ot contents of corrosion inhibitors in some chloride ingress.

• Magazine of the Korea Concrete Institute
• /
• v.11 no.2
• /
• pp.221-230
• /
• 1999

Corrosion of rebars can occur if there are cracks, moisture and availability of oxygen or carbonation proceeds, chloride penetrates and diffuses in concrete. Once rebars in concrete corrodes, subsequently accompanied with scaling, spalling in concrete cover. As a result of them, the RC structure is seriously deteriorated. In this study, theoretical review and experiments for cathodic protection(CP) have been performed to control corrosion of rebars in concrete contained chlorides and pre-crack. For CP the impressed current system was applied, the protection effect was investigated when rebars was directly contacted with salt water due to crack and open to much chlorides in concrete. In order to investigate the effect of protection, when CP was energized for 1 year, half-cell potential, potential-decay with current density, corrosion ratio, etc. were measured. With the cathodic protection by impressed current system, the depolarized values of all specimen were met NACE Standard, the effect of 34~84% of the ratio of corrosion area and 84~86% of cross-section reduction were calculated.