• Polymer(Korea)
• /
• v.38 no.5
• /
• pp.566-572
• /
• 2014

Maleic anhydride (MAH) grafted polypropylenes (PP) (MAH-g-PP) were prepared by changing MAH content and styrene monomer (SM)/MAH mole ratio with different type PP, using a twin screw extruder. The types of PP were isotatic PP (iPP), block PP (bPP), and random PP (rPP) and dicumyl peroxide (DCP) was used as an initiator. The graft degree of MAH was confirmed by the existence of carbonyl group (C=O) stretching peak at $3100cm^{-1}$ of FTIR spectrum. Thermal properties of MAH-g-PP and PP/MAH-g-PP/pulp composites were investigated by DSC and TGA. There was no district change in thermal properties of PP/MAH-g-PP/pulp composites. Based on tensile properties and SEM pictures for fractured surface of PP/MAH-g-PP/pulp composites, MAH-g-rPP was the best as the compatibilizer and optimum formulation was MAH content of 1.0 wt%, SM/MAH mole ratio of 1.0, and melt index (MI) of 25 g/10 min. The rheological properties of the composites were investigated by a dynamic rheometer. The complex viscosity, shear thinning effect, and water uptake incresed with pulp content.

• Applied Chemistry for Engineering
• /
• v.25 no.3
• /
• pp.318-323
• /
• 2014

In order to analyze the effect of maleic anhydride (MAH) content and styrene monomer (SM)/MAH mole ratio on reactive extrusion of maleic anhydride grafted random polypropylenes (MAH-g-rPP), MAH-g-rPPs were prepared by using a twin screw extruder. MAH contents were 0.5, 1.0, 3.0, and 5.0 phr and SM/initiator mole ratio was 0.0, 1.0, and 2.0. Dicumyl peroxide (DCP) was used as an initiator. The graft degree of MAH was confirmed by the existence of carbonyl group (C = O) stretching peak at $1700cm^{-1}$ from FT-IR spectrum. The degree of graft reaction increased up to 3.0 phr MAH and showed the optimum value at 1.0 SM/MAH mole ratio from the area ratio of C = O and C-H stretching peak. Thermal and crystallization properties of MAH-g-rPP and PP/MAH-g-rPP/pulp composites were investigated by DSC, TGA, XRD, and POM. There was a decrease in non-isothermal crystallization temperature of PP/MAH-g-PP/pulp composites. Based on tensile properties and SEM pictures for the fractured surface of PP/MAH-g-PP/pulp composites, MAH content of 1.0 wt% and SM/MAH mole ratio of 1.0 were the optimum formulation as the compatibilizer. The rheological properties of the composites were measured by dynamic Rheometer to compare the processability of the composites with and without compatibilizer. The power law index showed slightly low value at the composites with compatibilizer.

• The Journal of Korean Academy of Prosthodontics
• /
• v.52 no.2
• /
• pp.82-89
• /
• 2014

Purpose: The purpose of this study was to observe the change of viscoelastic properties of dental resin cements during polymerization. Materials and methods: Six commercially available resin cement materials (Clearfil SA luting, Panavia F 2.0, Zirconite, Variolink N, RelyX Unicem clicker, RelyX U200) were investigated in this study. A dynamic oscillation-time sweep test was performed with AR1500 stress controlled rheometer at $32^{\circ}C$. The changes in shear storage modulus (G'), shear loss modulus (G"), loss tangent (tan ${\delta}$) and displacement were measured for twenty minutes and repeated three times for each material. The data were analyzed using one-way ANOVA and Tukey's post hoc test (${\alpha}$=0.05). Results: After mixing, all materials demonstrated an increase in G' with time, reaching the plateau in the end. RelyX U200 demonstrated the highest G' value, while RelyX Unicem (clicker type) and Variolink N demonstrated the lowest G' value at the end of experimental time. Tan ${\delta}$was maintained at some level and reached the zero at the starting point where G' began to increase. The tan ${\delta}$and displacement of the tested materials showed similar pattern in the graph within change of time. The displacement of all 6 materials approached to zero within 6 minutes. Conclusion: Compared to other resin cements used in this study, RelyX U200 maintained plastic property for a longer period of time. When it completed the curing process, RelyX U200 had the highest stiffness. It is convenient for clinicians to cement multiple units of dental prostheses simultaneously.