• Composites Research
• /
• v.24 no.5
• /
• pp.23-28
• /
• 2011

In this paper, the bonding strengths of co-cured T800 carbon/epoxy composite-aluminum single lap joints with and without additional pressures were investigated using the pressure information induced by the fiber tension during a filament winding process. The specimens of all the tests were fabricated by an autoclave vacuum bag de-gassing molding being controlled forming pressures (absolute pressures of 0.1MPa, 0.3MPa and 0.7MPa including vacuum). A special device which can act uniform additional pressures on the joining part of the single lap joint specimen was designed to measure the bonding strengths of composite-aluminum liners of type III hydrogen pressure vessel fabricated by a filament winding process. After the three different additional pressures (absolute pressures of 0.1MPa, 0.3MPa and 0.7MPa) were applied to the specimens the effect of the additional pressures on the bonding strengths of the co-cured single-lap joints were evaluated.

• Composites Research
• /
• v.13 no.4
• /
• pp.42-53
• /
• 2000

A study has been made to establish an optimum condition in the surface treatment and curing method that is important for the fabrication of Al 7075/CFRP laminates. PAA(Phosphoric Acid Anodizing) provided a good adhesive strength and FPL(Sulfuric / Sodium Dichromate Acid Etching) had a similar adhesive strength with PAA. On the other hand, the poor adhesive strength was shown on vapor degrease and CAA(Chromic Acid Anodizing). By using the atomic force microscope(AFM), it was found that the PAA oxide surface obviously had a greater degree of microroughness as compared to vapor degrease, CAA and FPL treated surfaces. These results support the concept of a mechanical interlocking of the adhesive with-in the oxide pores as the predominant adhesion mechanism. In curing methods, the adhesive strength of co-curing method was higher than that of secondary curing method. With respect to stability of specimen shape, the secondary curing method was better than co-curing method. DMA(Dynamic Mechanical Analysis) test revealed $T_g$ in curing times over 60 min is nearly same, so it is estimated they will have similar degree of curing and joint durability in using FM300M adhesive film.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.3
• /
• pp.385-392
• /
• 1997

The joint design and manufacture of the composite structure have become an important research area because the structural efficiency of the composite structure is often determined by its joint not by its basic structure. The co-cured joint is an efficient joint technique because both curing and jointing for composite structures are achieved simultaneously. In this paper, the torque capacities of the co-cured tubular lap joint with and without knurling of the pyamid type were experimentally measure. From the experimental resuts, it was found that the excess resin played a role as an adhesive in the co-cured tubular lap joint whose steel adherends were not knurled. Also, it was found that the torque capacity of the co-cured joint was increased as the knurling size of the pyramid type on the surface of the steel adherend was increased.

• Composites Research
• /
• v.19 no.4
• /
• pp.15-22
• /
• 2006

One of the primary factors limiting the application of composite-metal adhesively bonded joints in structural design is the lack of a good evaluation tool for the interfacial strength to predict the load bearing capacity of boned joints. In this paper composite-steel adhesion strength is evaluated in terms of stress intensity factor and fracture toughness of the interface corner. The load bearing capacity of double lap joints, fabricated by co-cured bonding of composite-steel adherends has been determined using fracture mechanical analysis. Bi-material interface comer stress singularity and its order are presented. Finally stress intensities and fracture toughness of the wedge shape bi-material interface corner are determined. Double lap joint failure locus and its mixed mode crack propagation criterion on $K_1-K_{11}$ plane have been developed by tension tests with different bond lengths.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.10 no.3
• /
• pp.130-135
• /
• 2002

This study investigates the effect of curing method on the bonding strength of aluminum/CFRP composites. The surface of aluminum panel was treated by DC plasma. Lap shear tests and T-peel tests were performed based on the procedure of ASTM 906-94a and ASTMD1876-95, respectively. Test samples were fabricated by using the co-curing method and the secondary curing method. The results showed that the shear strength of test samples made by the co-curing method was 2.5 times greater than that of test samples made by the secondary curing method. The T-peel strength of the co-curing method case was almost 2 times greater than that of the secondary curing method case.

• Composites Research
• /
• v.31 no.4
• /
• pp.139-144
• /
• 2018

Long Fiber-reinforced composites have advantages of excellent production efficiency and formability of complex shapes compared to conventional continuous fiber reinforced composite materials. However, if we need to make complicated composite shapes or to assemble parts made of different materials, a variety of joining methods are needed. In general, long fiber prepreg sheet (LFPS) contains mold release agent to facilitate demolding after thermoforming. Therefore, mechanical fastening is required in addition to the adhesive bonding to get proper joining strength. In this study, we proposed a stainless steel insert for co-cure bonding which cures LFPS and bonds the stainless steel insert through thermoforming process. The wing of the insert which is spread during the thermoforming process induces adhesion and mechanical wedging effect and serves as a hook to resist the pulling force. The burn-out method was used to confirm the unfolded state of the stainless steel insert wings inserted into the composite material. The static pull-out test was performed to quantitatively evaluate the joining strength. From these experimental results, the condition which guarantees the most appropriate joining strength was derived.

• Composites Research
• /
• v.24 no.6
• /
• pp.56-63
• /
• 2011

The objective of this study is to investigate appropriate bonding methods of solar cells in order to apply solar cells, which have been receiving particular attention as a renewable energy due to fossil energy depletion and environment issues, to composite structures. Back-contact solar cells with approximately 24.2% energy conversion efficiency were used in this study. Since silicon-based solar cells are mechanically fragile, the secondary-bonding methods using adhesive were examined in this study. The experiment was conducted with three kinds of bonding materials such as EVA film, Resin film and elastic adhesive. The performance of solar cells for three types of adhesives under mechanical loading on test specimens is conducted. In addition, the measuring equipment was designed to evaluate the performance of the solar cells under mechanical loading in real time and the fracture characteristics depending on bonding materials were evaluated. The reason decreasing solar cells efficiency were analyzed and considered by Fractography. The results show that the solar cell performance is largely affected by bonding techniques. Moreover, the bonding method using elastic adhesive shows best solar cell efficiency.