• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.36 no.11
• /
• pp.1345-1352
• /
• 2012

This paper aims to evaluate the low-velocity impact responses and mechanical properties of balsa-wood and urethane-foam core materials and their sandwich panels, which are applied as the impact limiter of a nuclear spent fuel shipping cask. For the urethane-foam core, which is isotropic, tensile, compressive, and shear mechanical tests were conducted. For the balsa-wood core, which is orthotropic and shows different material properties in different orthogonal directions, nine mechanical properties were determined. The impact test specimens for the core material and their sandwich panel were subjected to low-velocity impact loads using an instrumented testing machine at impact energy levels of 1, 3, and 5 J. The experimental results showed that both the urethane-foam and the balsa-wood core except in the growth direction (z-direction) had a similar impact response for the energy absorbing capacity, contact force, and indentation. Furthermore, it was found that the urethane-foam core was suitable as an impact limiter material owing to its resistance to fire and low cost, and the balsa-wood core could also be strongly considered as an impact limiter material for a lightweight nuclear spent fuel shipping cask.

• The Journal of the Korea Contents Association
• /
• v.17 no.10
• /
• pp.300-306
• /
• 2017

The purpose of this study was to investigate the antibacterial effect of functional multiwall carbon nanotube (MWCNT) on the conventional glass ionomer cement(GIC). The MWCNT was incorporated into a commercial powder at 0.125, 0.25, 0.5 and 1.0 wt%. Specimens for vickers hardness(VHN) disks(Ø$10mm{\times}2mm$) each were prepared. Indention were made using a load of 200 N and 20 s dwell on four specimens for each distilled water storage time 1d, 7d, and 14days. The antibacterial effects using agar diffusion test with S. mutans and S. aureus. The diameters of the inhibition zones produced around the materials were measured. The results revealed that all the vickers hardness values were increase significantly with incubation time(p<0.05). Regarding the antibacterial effect for S. mutans, all the tested groups showed a slightly higher value not significantly with the control group(p<0.05). However S. aureus statistical analysis indicated a significant difference for antibacterial agents between control and MWCNT containing 0.25 wt%(p<0.05). These results of this study provide that the conventional GIC with containing MWCNT show good antibacterial effect against and favorable mechanical properties. Further this study on the efficient functionalization of multiwall carbon nanotube will be needed.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.8
• /
• pp.847-853
• /
• 2011

In this study, a hybrid powder-extrusion process involving the control of temperature dwelling time for improving the formability of Zn-22Al powder was developed and the effect of dwelling time on the mechanical properties of a spur gear with a pitch circle having a diameter of 1.8 mm was investigated. General extrusion experiments were carried out at different temperatures such as 290, 300, and $310^{\circ}C$. Spur gears with good qualities and without any surface defects were obtained in the case of extrusion temperature of $310^{\circ}C$ and ball-milling duration of 32 h. The Vickers hardness distribution was non-uniform, and after the sintering process, an internal crack was generated because of the different deformation energy between gear central part and teeth. To overcome the abovementioned problems, research on controlling the dwelling time of the extrusion temperature in the powder-extrusion process was carried out. Good-quality spur gears were obtained when the dwelling time was 15 min.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.196-196
• /
• 2016

치과나 기공소로부터 높은 원가로 인한 재료선택에 어려움을 겪고 있어 귀금속 금합금의 물성을 가질 수 있도록 하면서 가격급등으로 인한 문제 해결하기 위한 비귀금속 합금으로 대체가 필요하기에 이에 따른 연구가 이루어져 국산 제품의 상품화를 위해 파라듐을 이용하여 적합한 새로운 합금을 개발하는 것이 필요하다. 치과용 골드합금은 미국치과의사 협회의 구정에 의하면 1형부터 4형까지 분류하고 있으며 3형에 해당하는 강도와 기계적인 특성을 갖도록 파라듐으로 대체하는 연구가 진행중이거나 시판되고 있다. 따라서 본 연구에서는 2형, 3형 및 4형을 대체가능하도록 팔라듐을 기반으로 한 새로운 합금을 설계하고 합금의 성분원 소인 Au(1~5), Pd(20~25), Ag(70~75), In(1.5) 및 Zn(2)등으로 조성을 변화시켜 측량 후 합금을 제조하기 위하여 아르곤 분위기하의 진공아크용해로를 이용하여 용해하였다. 정량된 금속을 진공아크 용해로에 장입하고 용해는 균질한 합금이 되도록 최소한 6회 이상 용융을 실시하며 합금성분의 손실이 발행하지 않도록 보정을 하였다. 합금의 미세조직 관찰을 위하여 샘플을 고속 다이아몬드 정밀 절단기(Acculom-5, STRUERS, Denmark)를 이용하여 절단한 후 2000 grit의 Sic 연마지에서 단계적으로 $0.3{\mu}m$ 알루미나 분말까지 연마한 후 초음파 세척을 하였다. 준비한 시편은 KCN과 $(NH_4)_2S_2O_8$을 1:1로 혼합한 부식액으로 에칭한 후 OM과 SEM을 이용하여 조직을 관찰하였으며 각 샘플의 성분변화는 EDS 분석을 통해 확인하고 결정구조는 XRD를 사용하여 분석하였다. 경도시험은 비커스경도시험기를 이용하여 5kg의 하중을 30초간 작동시켜 압흔을 연결된 micron으로 평균값을 측정하였다. 각 시편의 부식거동은 POTENTIOSTAT(Model PARSTAT 2273, EG&G, USA)을 이용하여 구강 내환경화 유사한 $36.5{\pm}1^{\circ}C$의 0.9% NaCl에서 실시하였다. 인가전위는 -1500mV에서 1000mV까지 1.67 mV/min의 주사속도로 인가하여 시험을 수행하였으며 분극곡선으로부터 부식전위와 부식전류밀도 및 부동태영역의 전류밀도로 금속의 용출거동을 조사하였으며 부식이 끝난 시편은 FE-SEM과 EDS를 사용하여 조사하였다. 기계적인 특성은 Pd-Ag에 3wt%의 Au를 첨가한 합금이 Pd-Ag에 1.5wt%합금을 첨가한 경우에 비하여 기계적인 특성이 증가하고 내식성이 크게 증가하였다. 이들 합금에 Cu를 11wt%를 첨가한 경우는 비커스경도가 200이상으로 높게 나타났지만 내식성이 크게 감소하였다.

• Journal of the Microelectronics and Packaging Society
• /
• v.29 no.3
• /
• pp.25-29
• /
• 2022

Recently, the importance of electronic packaging technology has been attracting attention, and heterogeneous integration technology in which chips are stacked out-of-plane direction is being applied to the electronic packaging field. The 2.5D integration circuit is a technology for stacking chips using an interposer including TSV, and is widely used already. Therefore, it is necessary to make the interposer mechanically reliable in the packaging process that undergoes various thermal processes and mechanical loadings. Considering the structural characteristics of the interposer on which several thin films are deposited, thermal stress due to the difference in thermal expansion coefficients of materials can have a great effect on reliability. In this study, the mechanical reliability of the metal pad for wire bonding on the silicon interposer against thermal stress was evaluated. After heating the interposer to the solder reflow temperature, the delamination of the metal pad that occurred during cooling was observed and the mechanism was investigated. In addition, it was confirmed that the high cooling rate and the defect caused by handling promote delamination of the metal pads.

• Journal of the Korea Institute of Building Construction
• /
• v.23 no.3
• /
• pp.295-303
• /
• 2023

South Korea has recently witnessed an increasing number of seismic events, leading to a surge in studies focusing on seismic earth pressures, as well as the attributes of geological layers and ground where foundations are established. Consequently, earthquake-resistant design has become imperative to ensure the safety of subterranean structures. The slurry wall method, due to its superior wall rigidity, excellent water resistance, and minimal noise and vibration, is often employed in constructing high-rise buildings in urban areas. However, given the separation between panels that constitute the wall, slurry walls possess limited resistance to seismic loads in the longitudinal direction. As a solution, several studies have probed into the possibility of interconnecting slurry wall panels to augment their seismic performance. In this research, we developed and evaluated a method for linking slurry wall panels using mechanical joints, including concrete-confined steel pipes and headed bars, through mock-up tests. We also assessed the constructability of the suggested method and compared it with other analogous methods. Any challenges identified during the mock-up test were discussed to guide future research in resolving them. The results of this study aid in enhancing the seismic performance of slurry walls through the development of an interconnected panel method. Further research can build on these findings to address the identified issues and improve the efficacy and reliability of the proposed method.

• Journal of the Korean Ceramic Society
• /
• v.51 no.5
• /
• pp.399-405
• /
• 2014

Porous alumina with different porosities, 5.2 - 47.5%, were coated with cover-glass having a thickness of $160{\mu}m$, using epoxy adhesive. We investigated the effect of the porosity of the substrate layer on the crack initiation load, and the size of cracks propagated in the coating layer. Hertzian indentations were used to evaluate the damage behavior under a constrained loading condition. Typically, two types of cracks, ring cracks and radial cracks, were observed on the surface of the glass/porous alumina structure. Indentation stress-strain curves, crack initiation loads, crack propagation sizes, and flexural strengths were investigated as a function of porosities. The results indicated that a porosity of less than 30% and a higher substrate elastic modulus were beneficial at suppressing cracks occurrence and propagation. We expect lightweight mechanical components with high strength can be successfully fabricated by coating and controlling porosities in the substrate layer.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.31 no.10
• /
• pp.1025-1030
• /
• 2007

Three kinds of metallic sandwich panels with quasi-Kagome truss cores have been analyzed on their mechanical behaviors subjected to bending load. According to the results of previous work on the optimal design, they were designed to have similarly high strength per weight with the identical overall sizes, i.e., the total length, the width, the core height. Differences were in the face sheet thickness and/or the thickness of the metal sheet from which the core was fabricated through expanding and bending processes. Under the bending load, they performed well as designed, as far as the maximum load is concerned. However, after the maximum load, the load-displacement curves were different each other depending on the slenderness ratio of the truss elements composing the quasi-Kagome truss cores and the face sheet thickness. Namely, the slenderness ratio and the face sheet thickness governed stability of the elastic and plastic buckling. Therefore, if energy absorption characteristics or structural stability as well as the maximum load capacity are to be achieved, the sandwich panel with thick truss members and thick face sheet should be selected.

• Journal of the Korean Ceramic Society
• /
• v.34 no.3
• /
• pp.257-264
• /
• 1997

The aim of this study was to investigate the degradation of piezoelectric properties with compressive cy-clic loading, the change in bending strength before and after poling treatment and fracture strength in MPB depending on the amount of MnO2 addition. The MPB with 0.25 wt.% MnO2 showed the best resistance against the piezoelectric degradation with compressive cyclic loading. Bending strength increased when pol-ing and loading directions are parallel, however decreased when poling and loading directions are per-pendicular each other. Because, during poling treatment, compressive residual stress is generated in the pol-ing direction but tensile residual stress in the perpendicular direction to poling direction.

• Journal of Korean Society of Steel Construction
• /
• v.17 no.2 s.75
• /
• pp.207-216
• /
• 2005

The maximum strength of the stainless steel square and the circular hollow section columns, which are cold-formed and TIG welded, is experimented on and analyzed. The paper presents centrally compressed experiments, including stub column tests and coupon tests, on stainless steel pipe columns. A total of 24 stainless steel pipe column experiments are conducted, using the slenderness ratios ($L_k/r$ = 20, 30, 40, 50, 60, 70) as parameters. The experimental results were compared with the design standard curves, AIK-LSD and AISC-LRFD, AIJ-LSD, SIJ-ASD curves, and multiple column curves.