• Journal of Dental Rehabilitation and Applied Science
• /
• v.27 no.1
• /
• pp.73-79
• /
• 2011

Purpose of this experiment is to evaluate the effect of titanium on the castability when the titanium is added to the Co-Cr alloy. Raw materials Cobalt, Chrome, Molybdenum, Silicon, Manganase, Carbon, Nitrogen, Titanium were weighted and prepared. $Biosil^F$ (Degudent, Germany) was the control group. To the experimental group, different weight percent of titanium was added from 1 wt% to 4 wt%. The wax pattern is $30{\times}40$ cm in size, rectangular in shape and has total of 160 grids. Centrifugal machine (Neutrodyne Easy Ti: Manfredy) was used for casting. For evaluation of the castability, the number of complete grids was counted by visual inspection and X-ray inspection. The test showed similar castability with the control group in the titanium addition of 1 wt% to 3 wt%. The titanium addition of 4 wt% showed poor result. With titanium lower than 4 wt%, the experiment metals showed proper castability with high expectation of successful clinical use.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.32 no.1
• /
• pp.101-108
• /
• 2005

Children are in mixed dentition during 6 years after 3 years old. this time is very important for sound permanent dentition. There are many factors of influence to tooth eruption stage ; adjacent teeth, tooth resorption, early loss or retention of deciduous tooth, local lesion, lip and tongue, masticatory muscles, ect. These factors should be in balance, if not, relation of adjacent teeth is changed, then severe malocclusion is occurred maybe. These cases revealed influences of resin bonded metal splint on occlusal surface of children's molar to mixed dentition. Splints interfere with falling off of deciduous tooth, tooth eruption, normal occlusion formation, and development of mixed dentition and occlusion. Therefore we removed the metal splint from teeth, follow-up checked occlusion and tooth eruption.

• The Journal of the Korean bone and joint tumor society
• /
• v.16 no.1
• /
• pp.1-7
• /
• 2010

Purpose: With advances in various treatment modalities, limb salvage surgery has been commonly used in osteosarcoma of extremities. An alternative method for skeletal reconstruction is reimplantation of the tumor bearing bone following extracorporeal irradiation (ECI). We report the long-term results of ECI autograft in aspect of the oncological and functional outcomes, and complications. Materials and Methods: We retrospectively reviewed 31 osteosarcoma patients who underwent reconstruction with ECI between July 1995 and January 2006. There were 24 males and 7 females with a mean age of 24 (7-74 years) and a mean follow-up of 117 months (17-177 months). Twenty-five cases were reconstructed with ECI autograft, 6 cases with ECI autograft-prosthesis composite. The pathologic subtypes were conventional in 29 cases, periosteal in 1 case, and parosteal in 1 case. The most common location of tumor was distal femur (15 cases) followed by humerus (3), proximal fibula (3) and proximal tibia (3). Musculoskeletal Tumor Society (MSTS) score was used for functional evaluation. The overall survival rate, local recurrence, complications were analyzed. Results: The overall survival rate was 80.6% and the disease-free survival rate was 64.5%. Five patients died of distant metastasis. One patient required above-knee amputation due to local recurrence. All of them, twenty-three complications occurred, which included nonunion in 7 cases, deep infection in 5 cases, joint instability in 4 cases, metal failure in 2 cases, Limb-length discrepancy (LLD) in 2 cases, periprosthetic fracture in 1 case, epiphyseal collapse in 1, local recurrence in 1 case. The mean MSTS functional score was 62.5%. Conclusion: Extracorporeal irradiated autograft can be achieved relatively good result in aspect of oncological and functional aspect, but is needed to be additional research about occurring many complications. The reconstruction with ECI after intercalary or fragmentary resection is effective reconstruction in aspect of oncological and functional result, complications.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.26 no.4
• /
• pp.373-388
• /
• 2010

Fracture causes serious problems in many instance of prosthetic failures. But it is hard to find the definite causes when fractures occur. Fractography encompasses the examination of fracture surfaces that contain features resulting from the interaction of the advancing crack with the microstructure of the material and the stress fields. All fractured specimens(implant retaining screw) retrieved from Gangneung-Wonju national university dental hospital for 3 years(from 2007 to 2009). After pretreatment of samples, the scanning electon microscope were used for surface examination and fracture analysis. In case of most of the fractured specimens, fracture took place by fatigue fracture and fractured surface represents fatigue striation. Fatigue striation indicate the progression of the crack front under cyclic loading, are characteristic of stage 2 crack growth. The site of crack initiation and stage 1 crack growth were not easily identified in any of the failure, presumably because of the complex microstructural features of the polycrystalline sample. In case of fractured by overload, dimpled or cleavage surface were observed. Using the interpretation of characteristic markings(ratchet mark, fatigue striation, dimple, cleavage et al) in fracture surfaces, failure events containing the crack origin, crack propagation, material deficiency could be understand. Using the interpretation of characteristic markings in fracture surfaces, cause and mechanism of fractures could be analyzed.

• Journal of Biomedical Engineering Research
• /
• v.25 no.2
• /
• pp.157-163
• /
• 2004

Nitrogen ion implantation and ion plating techniques were applied for improvement of the wear resistance of metallic implant materials. In this work, the wear dissolution behaviour of a nitrogen ion implanted super stainless steel (S.S.S, 22Cr-20Ni-6Mo-0.25N) was compared with those of S.S.S, 316L SS and TiN coated 316L SS. The amounts of Cr and Ni ions worn-out from the specimens were Investigated using an electrothermal atomic absorption spectrometry. Furthermore, the Ti(Grade 2) disks were coated with TiN, ZrN and TiCN by use of low temperature arc vapor deposition and the wear resistance of the coating layers was compared with that of titanium. The chemical compositions of the nitrogen ion implanted and nitride coated layers were examined with a scanting auger electron spectroscopy. It wat observed that the metal ions released from the nitrogen ion implanted S.S.S surface were significantly reduced. From the results obtained, it was shown that the nitrogen ion implanted zone obtained with 100 KeV ion energy was easily removed within 200,000 revolutions from a wear dissolution testing under a similar load condition when applied to artificial hip joint. The remarkable improvement in wear resistance weir confirmed by the nitrides coated Ti materials and the wear properties differ greatly according to the chemical composition of the coating layers. for specimens with the same coating thickness of about 3$\mu\textrm{m}$, TiCN coated Ti showed the highest wear resistance. However, after removing the coating layers, the wear rates of all nitrides coated Ti reverted to their normal rates of below 10,000 revolutions from Ti-disk-on-disk wear testing under the same load condition. From the results obtained, it is suggested that the insufficient depth of the 100 Kel N$\^$＋/ ion implanted zone and of the nitrides coated layers of 3$\mu\textrm{m}$ are subject to restriction when used as frictional parts of load bearing implants.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.33 no.4
• /
• pp.260-268
• /
• 2017

Purpose: Manufacturing with AM (Additive manufacturing) technique has many advantages; but, due to insufficient study in the area, it is not being widely used in the general clinic. In this study, differences of flexural strength among various materials of 3 unit fixed dental prosthesis were analyzed. Materials and Methods: A metal jig for specimens that had a 3-unit-fixed dental prosthesis figure were fabricated. The jigs were made appropriately to the specifications of the specimens. Three different kinds of materials of specimens which were NC (mathacrylic esther based), DP-1 (Bisphenol A epoxy acrylate type oligomer based), and DT-1 (urethane acrylate based) were printed with DLP machine. Five specimens for each kind of material were printed with an angle of $30^{\circ}$ from the horizontal surface. The specimens were placed on the jig and the flexural strength was measured and recorded using Universal testing machine. The recorded data was analyzed in SPSS using One-way ANOVA and Tukey HSD to determine the significance of the differences of flexural strength among the groups. Results: The flexural strengths of each group were the followings: NC, $1119{\pm}305$ N; DP-1, $619{\pm}150$ N; DT-1, $413{\pm}65N$. Using One-way ANOVA and Tukey Honestly Significant Difference test, significant difference was found between NC and the other groups (P < 0.05), but there was no significant difference between DP-1 and DT-1 (P > 0.05). Conclusion: Higher flexural strength was shown in 3-unit-fixed dental prosthesis that were 3D printed using a DLP machine with NC material.