A method for the retardation of fatigue crack growth using ring indentation at the vicinity of a crack is examined. Residual stresses near crack tip are evaluated using fracture mechanics approach using the Bueckner weight function. The motivation is to develop a simple and effective method for obtaining an increase in fatigue lives to total failure of materials with crack. Fatigue testing of aluminum specimen showed that the retardation effects are observed after the application of the method.

• Bulletin of the Society of Naval Architects of Korea
• /
• v.26 no.2
• /
• pp.41-48
• /
• 1989

This paper investigates the relationship between strain hardening exponents(n) of various marine materials and fatigue crack retardation effect after applying single overload. Using the four different sheet materials, following results are obtained. (1) The fatigue crack propagation rate after applying single overload was retarded and the effects of this retardation were closely related to the strain hardening exponent. (2) The larger the strain hardening exponents were, the more were the fatigue crack retardation effects after applying single overload. (3) The considerable crack closure with the applying of a overload was observed in matrals with large strain hardening exponent. When n is smaller than 0.1, the fatigue crack retardation effects are negligible. On the contrary, when n is larger than 0.2 the fatigue crack retardation effects are significant.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.8 no.2
• /
• pp.126-136
• /
• 1999

We studied on crack growth retardation in single overloading condition. Crack tip branching which as the second mechanism on crack growth retardation was examined. Crack tip branching was observed to kinked type and forked type. It was found that the branching angle range was from 25 to 53 degree. The variations of crack driving force with branching angle were calculated with finite element method The variation of {{{{ KAPPA _I}}}}, {{{{ KAPPA _II}}}} and total crack driving force(K) were examined respectively So {{{{ KAPPA _I}}}}, {{{{ KAPPA _II}}}} and K mean to mode I, II and total crack driving force. Present model(Willenborg's model) for crack growth retardation prediction was modified to take into consideration the effects of crack tip branching When we predicted retardation with modified model. it was confirmed that predicted and experimental results coincided with well each other.

• International Journal of Highway Engineering
• /
• v.7 no.2 s.24
• /
• pp.1-12
• /
• 2005

This study was conducted to evaluate effect of geogrid and fabric, which are used underneath the overlaid asphalt pavement for retarding reflection cracking by simulated laboratory test. In this study, an interlayer at the interface between old concrete pavement surface and overlaid asphalt mixture, and polymer-modifier were used as an effort of retarding reflection crack initiation and for strengthening mixture. Five products were used in preparation of asphalt concrete beam specimen which was tack coated on top of jointed concrete block. Simulated Mode I and II fracture test were conducted under wheel loading and results were compared among those products. From the test results, several material and reinforcement combinations were observed to have a significant retardation effect against reflection cracking. The most effectively strengthened pavement against reflection cracking was found to be the LDPE-modifier asphalt mixture with a grid reinforcement at the bottom.

• Composites Research
• /
• v.12 no.3
• /
• pp.1-7
• /
• 1999

New hybrid composite material CPAL(Carbon Patched ALuminum alloy), an Al2024-T3 plate doubleside reinforced with carbon/epoxy laminates were made. Fatigue crack growth tests were carried out at R=0.2, 0.5 in the CPAL specimens. The retardation mechanism and behavior of fatigue crack growth were examined basing on investigation of the crack and the delamination using a X-Ray and a ultrasonic C-Scan. The fatigue crack growth rates of CPAL specimens were remarkedly retarded compared to that of the Al2024-T3 specimen. The retardations amounts of the fatigue crack growth rates get higher in $0^{\circ}$/$90^{\circ}$ CPAL specimen than in $\pm$$45^{\circ}$ CPAL specimen, and get higher at R=0.2 than at R=0.5. The retardation of fatigue crack growth rates in CPAL specimen was generated by the crack bridging mechanism, that is the behavior that the fibers in CFRP layers decrease the COD in the Al2024-T3 plate.

• Journal of Welding and Joining
• /
• v.14 no.2
• /
• pp.79-89
• /
• 1996

일정진폭하중과 과대하중비 2.5의 단일 인장과대하중에 의한 4140강 용접부 의 피로균열성장거동을 실온과 -45.deg.C의 저온에서 피로시험과 파면관찰을 통하여 고찰하였다. 이때, 용접부 미시조직의 영향을 평가하기 위해 모재(parent metal), 열영향부(as-welded HAZ), 열처리된 열영향부(PWHT HAZ)로 나누어 응력비 0과 0.5로 CT시험편을 이용하여 피로시험을 실시하였다. 피로균열성장거동은 재료의 미시조직과 온도변화보다는 응력비에 크게 영향을 받았으며, 단일 과대하중에 의한 피로균열성장 지연효과가 모든 재료에서 상당히 크게 나타났다. 전자현미경에 의한 피로파면 관찰 결과, 실온에서는 연성의 스트라이에이숀과 -45.deg.C에서는 의벽개파면과 같은 피로 균열성장거동을 나타내고 있다.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.31 no.9
• /
• pp.26-31
• /
• 2003

Aging aircraft accumulates widespread fatigue damage commonly referred to as multiple site damage(MSO). For ductile material such as 2024-T3 aluminum, MSO may lower the service life below that which is predicted by conventional fracture mechanics. The present paper is concerned with the fatigue life extension by pre-indentation technique for thin 2024-T3 aluminum plate to decelerate the crack propagation rate in the panels with MSO. The panel with fastener holes can be simply modelled by Hole/Slot type Middle-Tension specimen. Results of fatigue testing show significantly improving failure cycles from 10 to 40 times. This retardation effect is decreased by increasing the loading level in the constant amplitude loading. In the sense of retardation mechanism, the crack propagation rate is gradually attenuated by entering the indentation mark and maintains at the lowest value for a long period after the edge of crack passes the center of indentation area.

• International Journal of Highway Engineering
• /
• v.1 no.1
• /
• pp.85-96
• /
• 1999

This study was performed to evaluate performance of polymer-modified asphalt mixtures and specially designed reinforcement techniques against reflection cracking of the asphalt pavement overlay. Selected polymers were used for asphalt modification and polyester fiber, a polypropylene film (vinyl) and a grid were used for mixture reinforcement. Using the asphalt mixture with optimum asphalt content, a slab was made and cut into two pieces of specimen. A layer of grid or vinyl was placed at the bottom of specimen to strengthen the pavement layer against crack. A repeated loading was applied to the asphalt mixture specimen which is Placed on a cement concrete with a pseudo-crack. Crack propagation under repeated loading was monitored and effectiveness of the devised crack retarding techniques was evaluated. From the test results. a significant retardation of mode I crack progress was monitored from some of the modified and reinforced asphalt mixtures.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.7 no.4
• /
• pp.103-113
• /
• 1987

Fatigue tests using a single-peak loading and a two-step loading were carried out to examine the fatigue crack growth behaviar and to find the appropriate analysis method. C-T specimens were made using structural steel SWS58 for the tests. From this, just after a single-peak loading acceleration effect was occured and after some times retardation effect was found. And eminent retardation effect was found after High-Low two-step loading. The transition effect of crack growth due to this variable loading was occured owing to the residual stress and the plastic zone size at the crack tip. And the behaviors of these are well explained by Elber's Crack Closure Model. Also I could find that the Wheeler's Retardation Model is a simple and appropriate theory among analysis methods of fatigue crack growth under the variable loading.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1997.05b
• /
• pp.153-158
• /
• 1997

Zr-2.5%Nb 합금에서 응력방향에 따른 DHC특성의 차이를 알아보고자 하였다. 판상의 CT시편을 이용하여 수소를 200 ppm 주입하고 응력을 압력관의 길이 방향으로 가하고 notch를 윈주방향으로 한 경우와 원주방향으로 응력을 가하고 notch를 길이 방향으로 한 경우의 균열전파속도를 측정하여 본 결과 길이 방향으로 응력을 가하였을 때 균열전파속도가 1/100 정도 감소하였으며, 균열발생을 위한 임계응력확대계수도 커짐을 알 수 있었다. 그리고 균열전파 방향도 원주방향으로 응력을 가하였을 때는 균열이 precrack을 따라 그대로 진행되었으나, 응력을 길이 방향으로 가하였을 때는 precrack을 따라 균열이 전파되지 못하고 균열분리 현상을 보였다 이것은 원래 모재가 보유하고 있는 집합조직과, 응력에의하여 수소화물이 재배열할 때 기존의 a상에서의 특정 방향 관계를 유지하여 석출함으로써 균열이 수소화물을 따라 전파됨이 원인인 것으로 생각된다. 응력을 원주방향으로 가하였을 때 균열주위에 수소화물이 길게 석출하지만, 응력을 길이 방향으로 기하였을 때는 수소화물이 20$\mu\textrm{m}$ 정도의 작은 크기로 분리된 균열과 같은 방향으로 분포하고 있음을 관찰하였다. 이로부터 집합조직을 개량함으로써 DHC저항성에 대한 효과를 얻을 수 있음을 확인 할 수 있었고 DHCV model에서 방향성을 수소화물의 재배열인자로부터 고려할 필요성이 있음을 알게 되었다.