• Transactions of the Korean Society of Mechanical Engineers
• /
• v.14 no.6
• /
• pp.1576-1582
• /
• 1990

To examine small fatigue crack behavior, the crack opening displacement (COD) was measured for surface cracks in the range of few tens to hundreds .mu.m using the computerized Interferometric Strain/Displacement Gage (ISDG) which could measure the relative displacement with a resolution of 0.02 .mu.m. The load-COD record is stored and analyzed after the test to determined the opening load. Single-edge notched specimens, 2.3mm thick, of Al 2024-T3 were precracked at load ratios of 0.0, -1.0 and -2.0 to make small fatigue cracks. The opening loads were measured these small cracks and compared with those of long cracks. The opening load ratios for the short cracks are about 10% smaller than those for long cracks at positive R-ratios, but are about 100% smaller at negative R-ratios.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.19 no.4
• /
• pp.908-917
• /
• 1995

The constant .DELTA.K fatigue tests are performed in SS41 and its weldments to investigate crack opening behavior and fatigue crack propagation behavior at each parts of weldment and its boundary layer. The weldments were annealed after welding for the purpose of relieving residual stress. Every weldments has notch at weld metal zone, and fatigue crack propagates from weld metal zone to vase metal zone perpendicular to weld line. The Laser ISDG method is used in order to determine the crack opening ratio, this method is more precise than indirect measurement method, and faster and easier than other direct measurement method.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.30 no.11 s.254
• /
• pp.1455-1460
• /
• 2006

The relationship between fatigue crack growth behavior and cyclic crack tip opening displacement is studied. An elastic-plastic finite element analysis (FEA) is performed to examine the growth behavior of fatigue crack, where the contact elements are used in the mesh of the crack tip area. We investigate the relationship between the reversed plastic zone size and the changes of the cyclic crack tip opening displacement along the crack growth. We investigate the effect of the element size when predict fatigue crack opening behavior using the cyclic crack tip opening displacement obtained from FEA. The cyclic crack tip opening displacement is related to fatigue crack opening behavior.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1992.03a
• /
• pp.47-58
• /
• 1992

탄소성 재료의 파괴에서 최대하중을 계산할 수 있는 방법이 제시되었다. 사용된 재 료상수는 파괴개시인성, 항복강도, 진행된 균열선단에서 열림 변위 증분에 대한 균열성장의 비이고, 계산을 실험결과에 맞추어 재료상수를 결정한다. 이들 상수로 다른 시편의 최대하 중을 계산하는 간단한 방법을 평면변형하의 A572 강(상온)과 4533(B)강(-10C)에 적용하여 기존의 실험결과와 비교하였다. 또한 균열 선단 열림 변위와 J-적분값에 기초한 다른 방법 과 비교·논의되었다.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.40 no.12
• /
• pp.1021-1026
• /
• 2016

In this study, crack resistance is evaluated by the crack tip opening angle (CTOA) using a wedge splitting test (WST) on a viscoelastic particulate reinforced composite based on an HTPB binder. Generally, CTOA, as a function of crack extension, is used in order to determinate fracture resistance and has a steady state relative angle. Digital image correlation (DIC) is used to measure the crack tip opening displacement (CTOD) and crack extension for the critical crack tip opening angle (CTOAc). In these results, the CTOAc value of a particulate reinforced composite tends to approach a constant angle after a small amount of crack extension. The CTOAc value increases with decreasing temperature, from $50^{\circ}C$ to $-40^{\circ}C$. These CTOAc values may be used to measure fracture mechanics parameters for particulate reinforced composite.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.36 no.12
• /
• pp.1521-1528
• /
• 2012

The present paper provides the elastic stress intensity factors (SIFs) and the crack opening displacements (CODs) of a thick-walled pipe with a slanted axial through-wall crack. For estimating these elastic fracture mechanics parameters, systematic three-dimensional elastic finite element (FE) analyses were performed by considering geometric variables, i.e., thickness of pipe, reference crack length, and crack length ratio, affecting the SIFs and CODs. As for loading condition, the internal pressure was considered. Based on the FE results, the SIFs and CODs of slanted axial through-wall cracks in a thickwalled pipe along the crack front and the wall thickness were calculated. In particular, to calculate the SIFs of a thick-walled pipe with a slanted axial through-wall crack from those of a thick-walled pipe with an idealized axial through-wall crack, a slant correction factor representing the effect of the slant crack on the SIFs was proposed.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.10a
• /
• pp.226-226
• /
• 2003

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.15 no.6
• /
• pp.2002-2014
• /
• 1991

A refined two-dimensional analysis method, taking into account the crack opening deformation, is proposed for the evaluation of stress distributions in transverse cracked cross-ply laminates. The interlaminar stresses which play an important role in laminate failure are evaluated using the concept of interface layer. A series expansion of the displacements is employed and the thermal residual stresses and Poisson's effects in the laminated are taken into consideration in the formulation. The stress distributions are compared with finite element results. The proposed method represents well the characteristics of the stress distributions. The through-the-thickness variation of the stress distribution is remarkable near the transverse crack due to the crack opening deformation. The interlaminar stresses have significant values at the transverse crack tip and the proposed analysis can be applied as a basis for the prediction of the induced delamination onset by using appropriate failure criteria.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.725-726
• /
• 2008

This paper proposes elastic stress intensity factors and crack opening displacements (CODs) for a slanted axial through-wall cracked cylinder under an internal pressure based on detailed 3-dimensional (3-D) elastic finite element (FE) analyses. Based on the elastic FE results, the stress intensity factors along the crack front and CODs through the thickness at the center of the crack were provided. These values were also tabulated for three selected points, i.e., the inner and outer surfaces and at the mid-thickness. The present results can be used to evaluate the crack growth rate and leak rate of a slanted axial through-wall crack due to stress corrosion cracking and fatigue. Moreover, the present results can be used to perform a detailed Leak-Before-Break analysis considering more realistic crack shape development.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.30 no.1 s.244
• /
• pp.60-65
• /
• 2006

The present paper provides experimental J estimation equation for the circumferential through-wall cracked pipe under four-point bending, based on the load-crack opening displacement (COD) record. Based on the limit analysis and the kinematically admissible rigid-body rotation field, the plastic ${\eta}$-factor for the load-COD record is derived and is compared with that for the load-load line displacement record. Comparison with the J results from detailed elastic-plastic finite element (FE) analysis shows that the proposed method based on the load-COD record provides reliable J estimates even for shallow cracks, whereas the conventional approach based on the load-load line displacement record gives erroneous results for shallow cracks. Thus, the proposed J estimation method could be recommended for testing the circumferential through-wall cracked pipe, particularly with shallow cracks.