• Korean Journal of Heritage: History & Science
• /
• v.53 no.2
• /
• pp.64-87
• /
• 2020

Copper trihydroxychloride (atacamite, botallackite, paratacamite, etc.), the first green pigment used in Mogao Grotto's mural paintings of China, has been known as "copper green", "green salt", and "salt green", etc. and has been used as an important green pigment with malachite. At first, the natural mineral atacamite was employed, but after the Five Dynasties (907~960 CE), synthetic copper trihydroxychloride was primarily used. In Chinese literature, copper green, green salt, and salt green are recorded as being made via reaction with copper powder, Gwangmyeongyeom (natural sodium chloride), and Yosa (natural ammonium chloride), and the prepared material was analyzed to be copper trihydroxychloride. Copper trihydroxychloride pigment was not found in paintings prior to the Joseon Dynasty (1392~1910 CE) in Korea. In analysis of the green pigments used in paintings and the architectural paintworks in the Joseon Dynasty, copper trihydroxychloride was also shown to have been used as an important green pigment with malachite (Seokrok). In particular, the proportion of copper trihydroxychloride use was high in Buddhist paintings, shamanic paintings, and dancheongs (decorative coloring on wooden buildings). Some of these turned out to be synthetic copper trihydroxychloride, but it is unclear whether the rest of them are synthetic or natural pigments due to a lack of analyzed data. From literature and painting analyses, the pigment name of copper trihydroxychloride in the Joseon Dynasty turns out to be Hayeob, a dark green pigment. It is believed to have first been prepared by learning from China in the early Joseon period (early 15^th century) and its use continued until the late 19^th century with imported Chinese pigment. Round or oval particles with a dark core of copper trihydroxychloride which were used in Chinese literature were similar to the synthetic copper trihydroxychloride pigments used in the Joseon Dynasty and Chinese paintings. Therefore, the synthetic copper trihydroxychloride pigments of Korea and China are believed to have been prepared in a similar way.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.2
• /
• pp.94-98
• /
• 2017

In the past few years, Sn-3.0Ag-0.5Cu (weight%) solder composition has been a representative material to electronic industries as a replacement of Pb-base solder alloy. Therefore, extensive studies on process and/or reliability related with the composition have been reported. However, recent rapid rise in Ag price has demanded solder compositions of low Ag content. In this study, Sn-3.0Ag-0.5Cu solder bar sample was fabricated by melting of Sn, Ag and Cu metal powders. Crystal structure and element concentration were analyzed by XRD, optical microscope, FE-SEM and EDS. The Sn-3.0Ag-0.5Cu solder sample was composed of ${\beta}$-Sn, ${\varepsilon}-Ag_3Sn$ and ${\eta}-Cu_6Sn_5$ phases.

• Journal of the Korean Chemical Society
• /
• v.48 no.5
• /
• pp.504-509
• /
• 2004

The reaction of Cu metal with mixed alkali metal polyselenide flux ($KNaSe_x$) produced large plate-like crystals of $KCu_4Se_3$. The structure of $KCu_4Se_3$, determined with X-ray single crystal diffraction techniques, is tetragonal (P4/mmm, a=4.013(1))${\AA}$, c=9.712(1))${\AA}$, z=1, R=6.7%). The structure is composed $[Cu_4Se_3]_n^{n-}$double layers which are made of fused anti PbO-type Cu2Se2 layers. Temperature variable resistivity measurement on single crystal of $KCu_4Se_3$ shows metallic behavior ranging from $1.8{\times}10^{-4}{\Omega}{\cdot}cm$ (at 300 K) to $1.0{\times}10^{-6}{\Omega}{\cdot}cm$ (at 20 K).

• Transactions of the Korean hydrogen and new energy society
• /
• v.9 no.4
• /
• pp.169-176
• /
• 1998

An experimental study on effect of vapor-cooled heat stations in a 5.5 liter cryogenic vessel has been performed. The cryogenic vessel is made of stainless steel of thickness of 1mm and insulated by the combined insulation of vacuum, MLI(multi-layer insulation) and vapor-cooled radiation shield. Vapor-cooled heat stations are also constructed based on the 1-dimensional thermal analysis to reduce the heat inleak through a filling tube. Thermal analysis indicates that the vapor-cooled heat stations can substantially enhance the performance of vessel for cryogenic fluids with high $C_p/h_{fg}$ where $C_p$ the specific heat and $h_{fg}$ the heat of vaporization, such as $LH_2$ and LHe. The experimental results for $LN_2$ shows that the total heat inleak into inner vessel consists of 14% radiation and 86% conduction through the filling tube. Therefore, it is expected that the conduction heat in leak of the vessel for high $C_p/h_{fg}$ cryogenic fluids can be significantly reduced. powders. The amount of copper coating was 20wt%. In order to examine corrosion behavior of the electrodes, the corrosion current and the current density, in 6M KOH aqueous solution after removal of oxygen in the solution, were measured by potentiodynamic and cyclic voltamo methods. The results showed that Co in the alloy increased corrosion resistance of the electrode whereas Ni decreased the stability of the electrode during the charge-discharge cycles. The electrode used Si sealant as a binder showed a lower corrosion current density than the electrode used PTFE and the electrode used Cu-coated alloy powders showed the best corrosion resistance.

• Transactions of the Korean hydrogen and new energy society
• /
• v.9 no.4
• /
• pp.161-167
• /
• 1998

It has been investigated the effects of alloying elements and binders on the corrosion behavior of metal hydride electrodes for anode of Ni/MH secondary battery. The $AB_5$-type alloys, $(LM)Ni_{4.49}Co_{0.1}Mn_{0.205}Al_{0.205}$ and $(LM)Ni_{3.6}Co_{0.7}Mn_{0.3}Al_{0.4}$, were used for the experiments. The electrodes were prepared by mixing and cold-pressing of alloy powders with Si sealent or PTFE powders, or cold-pressing the electroless copper coated alloy powders. The amount of copper coating was 20wt%. In order to examine corrosion behavior of the electrodes, the corrosion current and the current density, in 6M KOH aqueous solution after removal of oxygen in the solution, were measured by potentiodynamic and cyclic voltamo methods. The results showed that Co in the alloy increased corrosion resistance of the electrode whereas Ni decreased the stability of the electrode during the charge-discharge cycles. The electrode used Si sealant as a binder showed a lower corrosion current density than the electrode used PTFE and the electrode used Cu-coated alloy powders showed the best corrosion resistance.

• Transactions of the Korean hydrogen and new energy society
• /
• v.9 no.1
• /
• pp.8-15
• /
• 1998

The catalytic hydrogenation of carbon dioxide has been studied for the fixation of carbon dioxide to mitigate global warming problems, but it needed hydrogen, which the price is still high. Recently, the electrochemical reduction of carbon dioxide has been drawn attractions because carbon dioxide could be converted to the valuable chemicals such as methane, ethane and alcohols electrochemically in the electrolyte solution using a catalytic electrode. This system is simple because the water electrolysis and hydrogenation take place at the same time using the surplus electricity at midnight. In this work, a continuous electrochemical reduction system was fabricated, which was composed of the reduction electrode (copper or perovskite type, $2{\times}2cm^2$), reference electrode(platinum, $2{\times}6cm^2$), standard electrode(Ag/AgCl), and potassium bicarbonate electrolyte solution saturated with carbon dioxide. The quality and quantity of the products and reduction current were analyzed, according to the electrolyte concentration and electrode type.

• Korean Journal of Heritage: History & Science
• /
• v.56 no.2
• /
• pp.148-169
• /
• 2023

Hayeob pigment is known as one of the traditional dark green pigments, but the color, raw material, and manufacturing method have not been clearly identified. However, comparing the analysis results of the particle shape and constituent minerals of Hayeob pigments revealed through pigment analysis studies of colored cultural properties such as Dancheong, Gwaebul, and paintings, Hayeob pigments appear to be the same as Dongrok pigments produced by salt corrosion. Therefore, in order to restore Hayeob pigment, the manufacturing method of Dongrok pigment was studied based on the records of old literature. The Dongrok pigment manufacturing method confirmed in the old literature records is a natural corrosion method in which copper powder and a caustic are mixed and then left in a humid condition to corrode. Based on this, artificial corrosion using a corrosion tester was adopted to corrode the copper powder more efficiently, and an appropriate mixing ratio was selected by analyzing the state of corrosion products according to the mixing ratio of the caustic agent. In addition, the manufacturing method of Dongrok pigment was established by adding a salt removal process to remove residual caustic agents and a purification process to increase chroma during pigment coloring. The prepared Dongrok pigments have a bluish green or green color, show an elliptical particle shape and a form in which small particles are aggregated, and a porous surface is observed. The main constituent elements are copper(Cu) and chlorine(Cl), and the main constituent mineral is identified as atacamite [Cu₂Cl(OH)₃]. As a result of an accelerated weathering test to evaluate the stability of the prepared Dongrok pigments, it was found that the greenness partially decreased and the yellowness significantly increased as deterioration progressed. Before deterioration, the Dongrok pigments had lower yellowness compared to the Hayeob pigments of the old Dancheong, but after deterioration, yellowness increased significantly, and it was found to have a similar chromaticity range as Dancheong's Hayeob pigments. As a result, the prepared Dongrok pigments were confirmed to be similar to Dancheong's Hayeob pigments in terms of color as well as particle shape and constituent minerals.

• Journal of the Society of Cosmetic Scientists of Korea
• /
• v.40 no.2
• /
• pp.203-214
• /
• 2014

We measured the contact dermatitis-causing substances concentrations in 28 commercial oxidative hair-coloring products. This study was aimed to provide the fundamental data about oxidative hair-coloring products. We selected 10 oxidation dyes (p-phenylenediamine, toluene-2,5-diamine, m-phenylenediamine, nitro-p-phenylenediamine, p-aminophenol, m-aminophenol, o-aminophenol, p-methylaminophenol, N,N'-bis(2-hydroxyethyl)-p-phenylenediamine sulfate, 2-methyl-5-hydroxyethylaminophenol) and 4 heavy metal (nikel; Ni, chromium; Cr, cobalt; Co, copper; Cu) as contact dermatitis-causing substances. To identify 10 oxidation dyes, hexane-2% sodium sulfite was used for the rapid and simple extraction and ultra performance liquid chromatography (UPLC) analysis was used for simultaneous analysis in 12 minutes. 10 oxidative dyes were detected as indicated on the product packaging and each concentration was lower than prescribed upper concentration limit by pharmaceutical manufacturing standards. And we analysed inductively coupled plasma-optical emission spectrophotometer (ICP-OES) for content search of heavy metal after microwave digestion. The heavy metal average concentration in oxidative hair-coloring products was 0.572 ${\mu}g/g$ for Ni, 3.161 ${\mu}g/g$ for Cr, 2.029 ${\mu}g/g$ for Co, 0.420 ${\mu}g/g$ for Cu, respectively. The average of concentration in powder type (henna) was higher than those of other foam and cream type oxidative hair-coloring products as follows; 1.800 ${\mu}g/g$ for Ni, 10.127 ${\mu}g/g$ for Cr, 7.082 ${\mu}g/g$ for Co, 1.451 ${\mu}g/g$ for Cu. Hair coloring products were classified into the six colors - black, dark brown, brown, dark brown, light brown, red brown and analyzed. Brown color had the highest average concentration of Co and the others had the highest average concentration of Cr.