• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.21 no.4
• /
• pp.169-174
• /
• 2011

Nanoscale-biodegradable behaviors of synthesized biphasic calcium phosphates (BCP) powders were characterized using X-ray diffraction (XRD), lattice parameter, and field emission microscopy (FE-SEM). The calcined BCP powders in vitro tested in Hank's balanced salt solution (pH = 7.4, $36.5^{\circ}C$) for 3 weeks. The calculated unit cell parameters for BCP have shown lattice distortion and expansion as irregular changes in the a and c-axis after in vitro.

• Resources Recycling
• /
• v.7 no.4
• /
• pp.64-75
• /
• 1998

The purpose of this study is to produce high putity composite powder composed of Fe-oxide, Mn-oxide and Mn-ferrite having superior homogencity in composition and particle size distribution by co-roasting process. Binary component metal (Fe, Mn) chloride solutions were produced by dissolving mill scale and ferro-mangancse alloy in hydrochloric acid. These chloride solutions contained the impurities such as SiO$_{2}$, P, Al, Ca and Na, which were originated from the Fe/Mn source materials. The neutralization and polymeric coagulant method were adoped to refine the hydrochloric liquor. When pH is far below the isoelectric point (pH 2-3), the SiO$_{2}$ was the most effectively reduced element, while other impurities remained unchanged. By increasing pH above 3, most of the impurities could be reduced effectively due to the coprecipitation reaction. The polymeric coagulants such as poly vinyl alcohol, resin amine and ammonium molybdate were found to have no effect on the spray roaster designed by the authors. The produced oxide powders were confirmed to be mixtures of Fe-oxide, Mn-oxide and mn-ferrite. the powders were homogeneously mixed and the particle size increased sleeply with increasing co-roasting temperature.

• Applied Chemistry for Engineering
• /
• v.22 no.2
• /
• pp.185-189
• /
• 2011

In this work, nano-sized M-ferrites (M=Co, Ni, Cu, Zn) for the decomposition of carbon dioxide were synthesized by the chemical co-precipitation. From the thermogravimetric analysis, it was clear that the maximum weight loss of each sample took place below $350^{\circ}C$. High temperature calcination resulted in more systematic crystallines, smaller specific surface area and larger particle size. An analysis by FTIR in the range of $375{\sim}406cm^{-1}$ revealed the presence of chelates at the octahedral site, which implies the formation of spinel structure in the ferrites. The current work showed that a $500^{\circ}C$ is the optimum heat treatment temperature of metal ferrites for $CO_2$ decomposition reaction.

• Applied Chemistry for Engineering
• /
• v.33 no.5
• /
• pp.466-470
• /
• 2022

The catalytic thermal oxidizer process has recently attracted considerable attention for the oxidation and decomposition of volatile organic compounds at low temperatures (< 450 ℃) with high efficiency (> 95%). Although many noble metal catalytic materials are well established, they are expensive and hazardous. Herein, highly active and low-cost Cu-Mn bimetallic catalysts were prepared using a simple and facile synthesis method involving the co-precipitation of Cu and Mn precursors. The synthesis of the catalyst was optimized by controlling the composition ratio of Cu and Mn. The optimized catalyst exhibited a large surface area of 230.8 m²/g with a mesoporous structure. To demonstrate the catalytic performance, the Cu-Mn catalyst was tested for the oxidation reaction of ethyl acetate, showing a high conversion efficiency of 100% at a low temperature of 250 ℃.

• Journal of the Korean Applied Science and Technology
• /
• v.33 no.1
• /
• pp.129-135
• /
• 2016

CO oxidation was performed with Cu-Mn and Cu-Zn co-precipitated catalysts as differential precipitant, metal ratio and calcination temperature. The effects of differential metal mole ratio and calcination temperature in mixed metal oxide catalyst were investigated with CO oxidation reaction. Physiochemical properties were studied by XRD, $N_2$ sorption and SEM. 2Cu-1Mn with $Na_2CO_3$ catalyst calcined at $270^{\circ}C$ has a large surface area $43m^2/g$ and the best activity for CO oxidation. $Cu_{0.5}Mn_{2.5}O_4$ in XRD peak shows the lower activity than others. The catalytic activity over the catalyst calcined $270^{\circ}C$ displayed the highest conversion, and it was better activity comparing with Pt catalysts CO conversion.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.20 no.2
• /
• pp.93-100
• /
• 2010

The calcium to phosphate ratio (Ca/P) in biphasic calcium phosphates powders using X-ray diffraction analysis (XRD) was characterized. The BCP powders with various stoichiometric Ca/P molar ratio were synthesized with coprecipitation process and calcination. Compositions of the powders with Ca/P molar ratio between 1.5 and 1.67 were subjected to starting Ca/P molar ratio, pH = 10, and thermal treatment up to $900^{\circ}C$. The structural, morphological and chemical characterizations for BCP powders with stoichiometric Ca/P ratio were carried out with scanning electron microscope (SEM) and inductively coupled plasma atomic emission spectroscopy (ICP-AES) and a phase quantification was investigated by XRD. The solubility of HAp, $\beta$-TCP, and BCP powders was tested in the phosphate buffer solution (PBS) at $36.5^{\circ}C$ and pH = 7.4.

• Applied Chemistry for Engineering
• /
• v.3 no.4
• /
• pp.717-721
• /
• 1992

Mechanical mixtures of vanadium molybdate and copper molybdate catalysts prepared by coprecipitation method, and those of $MoO_3$ and $V_2O_5$ were used to study the synergistic effects between each metal oxide for the selective oxidation of acrolein. The catalytic activity results revealed that the conversion of acrolein and yield of acrylic acid were increased with the mixture catalysts and it could be explained by a remote control mechanism. Thermal gravimetric analysis confirmed the evolution of lattice oxygen in the mixture catalysts.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.68.1-68.1
• /
• 2017

수소에너지의 무한한 가능성이 주목됨에 따라 과전압이 높은 산소 발생 촉매의 효율 향상 및 제작비용의 절감은 중요한 문제가 되어왔다. 백금계 촉매는 높은 효율과 낮은 과전압을 가지고 있지만 적은 매장량과 비싼 가격으로 수전해의 상용화에 큰 장애물이 되어왔다. 전이 금속 산화물 촉매는 가격이 저렴하고 형상과 크기 등에 따라 백금계 촉매에 비등한 성능을 발휘할 수 있다. 본 발표에서는 산소발생을 위한 촉매로서 Cu와 Co를 co-precipitation법을 이용하여 $Cu_xCo_{(3-x)}O_4$를 제작하고 이를 셀, 스택에 적용한 방법을 소개한다. 본문에서는 용액의 pH를 다르게 합성하여 Cu와 Co의 비율을 변화시켜 형상, 결정성을 조절할 수 있었고, 이러한 다른 조건에서 산소 발생 성능의 변화를 측정하였다. 최종적으로 최적의 성능을 나타내는 산소 발생 촉매를 셀 및 스택에 적용하여 실제적인 성능을 측정하였다.

• Clean Technology
• /
• v.22 no.1
• /
• pp.9-15
• /
• 2016

xAl-yZr mixed oxide catalysts with different molar ratios of Al/(Al+Zr) were prepared by a co-precipitation method and its catalytic performance was compared in the iso-propanol dehydration as a model reaction. The catalysts were characterized by X-ray diffraction (XRD), differential thermal analysis (DTA), N₂ adsorprion-desorption, NH₃ temperature programmed desorption (NH₃-TPD), and iso-propanol TPD analyses. The addition of Al into ZrO₂ promoted the formation of relatively small particles with large surface areas and retarded the transformation of teragonal phase to monoclnic phase. NH₃-TPD results revealed that the relative acidity of the catalysts increased along with the increase of Al molar ratio. The catalytic activity for the dehydration of iso-propanol to propylene was also increased with the same tendency. The catalytic activity could be correlated with high surface area, acidity and easy desorption of iso-propanol.

• Clean Technology
• /
• v.20 no.3
• /
• pp.330-336
• /
• 2014

Mg-Al mixed oxides with molar ratio of Mg/Al = 1-3 were prepared by co-precipitation and characterized by using X-ray diffraction, scanning electron microscopy, BET surface area and pore volume measured by $N_2$ sorption analysis, and temperature programmed desorption of iso-propanol. As Al content in Mg-Al mixed oxide increased, the acidity and BET surface area proportionally increased. This increase of acidity directly influenced the catalytic activity of iso-propanol conversion and selectivity to propylene.