• Journal of the Korea institute for structural maintenance and inspection
• /
• v.12 no.5
• /
• pp.161-168
• /
• 2008

The freeze-thaw deterioration and chloride attack, which are the typical degradation factors for durability of marine concrete, are significantly affected by pore structures in terms of penetration and diffusion. These pore structures of concrete are closely related to the types and amount of AE agent, used to guarantee the resistance of freeze-thaw deterioration, and the elapsed time before concrete pouring. This paper evaluates the durability of concrete based on the results of tests on cylinder specimens and core specimens from mock-up members with different air content of 4~6% and 8~10%, respectively. According to the test results, the air content of hardened concrete is 2.5~5.2% at 7 days and 2.4~5.1% at 28 days. These air contents are about half of the initial values just after the concrete mixing. Judging from the amount of scale after the freeze-thaw test completed, air content of 8~10% is slightly more beneficial against the deterioration of concrete than air content of 4~6%. Meanwhile, the core specimens from mock-up members exhibit somewhat unfavorable freeze-thaw deterioration and chloride migration characteristic compared with the cylinder specimens tested in the laboratory under the same mixing condition, as to show 106% in freeze-thaw test and 160% in chloride diffusion coefficient test, respectively.

• Journal of the Korea Concrete Institute
• /
• v.27 no.4
• /
• pp.419-426
• /
• 2015

The purpose of this study is to investigate experimentally the optimum mix design and site application case of soil mixing wall (SMW) method which is cost-effective technique for construction of walls for cutoff wall and excavation support as well as for ground improvement before constructing LNG storage tank typed under-ground. Considering native soil condition in site, main materials are selected ordinary portland cement, bentonite as a binder slurry and also it is applied $1,833kg/m^3$ as an unit volume weight of native soil, Variations for soil mixing wall are as followings ; (1) water-cement ratio 4cases (2) mixing velocity (rpm) 3levels (3) bleeding capacity and ratio, compressive strength in laboratory and site application test. As test results, bleeding capacity and ratio are decreased in case of decreasing water-cement ratio and increasing mixing velocity. Required compressive strength (1.5 MPa) considering safety factors in site is satisfied with the range of water-cement ratio 150% below, and test results of core strength are higher than those of specimen strength in the range of 8~23% by actual application of element members including outside and inside in site construction work. Therefore, optimum mix design of soil mixing wall is proposed in the range of unit cement $280kg/m^3$, unit bentonite $10kg/m^3$, water-cement ratio 150% and mixing velocity 90rpm and test results of site application case are satisfied with the required properties.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.1
• /
• pp.59-65
• /
• 2018

RC(Reinforced Concrete) structures are exposed to various exterior conditions, and the performances of both chloride resistance and freezing/thawing action are evaluated for those exposed to corrosive environment-sea shore. Recently developed FRP Hybrid Bars which is coated with glass fiber and epoxy with core steel has an engineering advantage of higher Elasticity than FRP rod. In this work, corrosion resistance, weight loss, and bond strength are evaluated for the FRP Hybrid Bar tested through freezing/thawing action for 300cycles. The double coated FRP Hybrid Bar shows the least weight loss without defection due to freezing/thawing action. Bond strength in FRP Hybrid Bar increases to 120% of normal steel through torturity effect with Si-coating. Bond strength in normal steel shows 0.86~0.89times in 3-day corrosion acceleration and 0.35~0.38times in 5-day corrosion acceleration, however, that in FRP Hybrid Bar shows little changes in bond strength before and after freezing/thawing action.

• Journal of the Mineralogical Society of Korea
• /
• v.17 no.3
• /
• pp.277-288
• /
• 2004

Alkali-silica reaction (ASR) is a chemical reaction between alkalies in cement and chemically unstable aggregates and causes expansion and cracking of concrete. In the Present study, we studied the effects of metakaolin, which is a newly introduced mineral admixture showing excellent pozzolainc reaction property, on the inhibition of ASR. We prepared mortar-bars of various replacement ratios of metakaolin and conducted alkali-silica reactivity test (ASTM C 1260), compressive strength test and flow test. We also carefully analyzed the mineralogical changes in hydrate cement paste by XRD qualitative analysis. The admixing of metakaolin caused quick pozzolanic reaction and hydration reaction that resulted in a rapid decrease in portlandite content of hydrated cement paste. The expansion by ASR was reduced effectively as metakaolin replaced cement greater than 15%. This resulted in that the amounts of available portlandite decreased to less than 10% in cement paste. It is considered that the inhibition of ASR expansion by admixing of metakaolin was resulted by the combined processes that the formation of deleterious alkali-calcium-silicate gel was inhibited and the penetration of alkali solution into concrete was retarded due to the formation of denser, more homogeneous cement paste caused by pozzolanic effect. Higher early strength (7 days) than normal concrete was developed when the replacement ratios of metakaolin were greater than 15%. And also, late strength (28 days) was far higher than normal concrete for the all the replacement ratios of metakaolin. The development patterns of mechanical strength for metakaolin admixed concretes reflect the rapid pozzolanic reaction and hydration properties of metakaolin.

• Journal of the Korea Concrete Institute
• /
• v.17 no.3 s.87
• /
• pp.427-434
• /
• 2005

An experimental investigation was carried out in order to verify the compressive strength, flexural strength, equivalent bending strength, rebound rate of shotcrete according to silicate accelerator, aluminate accelerator, cement mineral accelerator respectively and to especially evaluate the performance of shotcrete using cement mineral accelerator for high quality. The test result of compressive strength was showed that all accelerators were satisfied the required test value for each age, for the requirement of having the $75\%$ or higher compressive strength ratio to plain concretes at 28 days, cement mineral accelerator with $87\%$ compressive strength ratio was only satisfied. In flexural strength test, cement mineral accelerator was satisfied the flexural strength requirement in steel fiber reinforced shotcrete for each age. Aluminate type was conformed to the requirement for 28 days, but not at 1 day, silicate type was failed to satisfy standard requirement. Rebound rate was measured between $11{\~}19\%$ and cement mineral accelerator was showed comparatively lower rebound rate. Based on the test results, cement mineral accelerator exhibited excellent strength improvement and lower rebound rate compared to the conventional accelerator, its result is showed the possibility of making high performance shotcrete.

• Journal of the Korea Concrete Institute
• /
• v.19 no.3
• /
• pp.333-339
• /
• 2007

The purpose of this study was to enhance bond performance between recycled PET (polyethylene telephthalat) fiber and cement composites through hydrophilic treatment using maleic anhydride grafted polypropylene(mPP). The mPP with various concentration of 0%, 5%, 10%, 15% and 20% to determine effect on bond behavior of recycled PET fiber were applied as experimental variables. Dog bone shaped specimens according to JCI SF-8 was applied to evaluate the bond strength and pullout energy. The results showed increased bond strength and pullout energy as concentration of mPP. Concentration of 15% mPP showed the most effective results while 20% showed reduced performance results. Because 15% mPP ensures perfect coating while 20% makes thick coating area that resulted in crack propagation and consequent separation of PET fiber and coated area during pullout load occurred. Enhancement mechanism of bond performance of recycled PET fiber and cement composites with each concentration of mPP could be conformed through investigation of microstructure of fiber surface.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.4
• /
• pp.18-24
• /
• 2015

Non-destructive testing (NDT) methods are widely used in the construction industry to diagnose the defects/strength of the concrete structure. However, it has been reported that the results obtained from NDT are having low reliability. In order to resolve this issue, four kinds of NDT test (ultrasonic velocity measurements by P-wave and S-wave and the impact resonance methods by longitudinal vibration and deformation vibration) were carried out on 180 concrete cylinders made with two kinds of mix proportions. The reliability of the NDT results was analyzed and compared through the measurement of the actual compressive strength of the concrete cylinders. The statistical analysis of the results was revealed that the ultrasonic velocity method by S-wave is having lowest coefficient of variation and also most capable of stable observation. Analytical equations were established to estimate the compressive strength of the concrete from the obtained NDT results by relating the actual compressive strength. Moreover the equation established by the ultrasonic velocity method by S-wave had the highest coefficient of determination. Further studies on the stability of non-destructive testing depending on various mixing conditions will be necessary in the future.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.1
• /
• pp.139-146
• /
• 2015

The amount of by-product from sulphur increases in domestic industrial facilities. However, the amount of its consumption is limited so that the amount of unused sulphur continues to increase. Therefore, in this study, the use sulfur polymer as the concrete surface protecting material was conducted. The compressive strength showed that as the substitution ratio of filler increased up to 40%, the compressive strength also increased. A high compressive strength was shown at the curing temperature of $40^{\circ}C$ (SS, FA) and $60^{\circ}C$ (OPC) according to the type of filler. The difference of compressive strength between air dry curing and water curing was insignificant so that there was no significant influence of moisture during curing process. The evaluation result of bond strength showed that the highest bond strength was shown at the air-dry condition of $40^{\circ}C$ regardless of type of filler. Bonding didn't occur properly during water curing in comparison to air dry curing. Also, in case of the specimen cured at $60^{\circ}C$, discoloration and hair cracks appeared due to the influence of temperature, and the highest bond strength was shown at the substitution ratio of 20% (SS, FA) and 30% (OPC) according to the type of filler. The releasing test result of harmful substance showed that no harmful substance was released, so there is no harmfulness in the surface protecting material using sulfur polymer. As a conclusion drawn in this study, it is most appropriate to substitute silica by approximately 20%, mix and cure at the air-dry condition of $40^{\circ}C$ in order to use sulfur polymer as the surface protecting material.

• 한국방재학회:학술대회논문집
• /
• 2011.02a
• /
• pp.86-86
• /
• 2011

토목 기술의 발달로 장대교량이 증가함에 따라 교면 포장도 더 심각한 진동 및 충격, 기상조건에 노출되게 된다. 교면 포장은 차량의 주행의 편리성뿐 아니라 교량 구조물을 보호해야 하는 역할도 함께 수행하기 때문에 일반 토공부의 포장과 다른 성능을 필요로 한다. 교면 포장의 특수함을 감안하여 교면 포장의 품질을 평가하고, 설계와 적용시 반영 한다면 교량의 내구 연한 및 시공, 유지관리 비용을 절감 할 수 있을 것이다. 본 논문에서는 교면 포장에 요구되는 성능을 조사하고, 교면 포장 특히, 장대 교량 적용시 교면 포장의 성능 평가를 위한 평가 방법을 고찰하였다. 교면 포장의 가장 큰 구조적 특징은 교량의 진동과 휨에 의해 포장이 받게 되는 휨응력이다. 특히 교량의 장경간화에 따라 더 큰 진동과 변형을 경험하게 되는 교면 포장은 그에 따른 충분한 휨 추종성과 피로 저항성을 확보하여야 한다. 기존 토공부 포장에서는 실험이 간단한 원통형 공시체를 이용한 간접인장강도 모드의 실험으로 피로 성능을 평가하였으나, 교면 포장은 실제 거동 특성과 유사한 빔 피로 시험 모드가 보다 신뢰성이 높을 것으로 판단된다. 빔 피로시험 모드로는 3점, 4점, 5점 휨 피로 시험 모드가 있으며, 각각의 모드는 지지점의 개수, 재하점의 개수에 따라 다른 거동 특성을 평가 할 수 있다. 최근 개발된 5점 휨 시험의 경우 교량에서 발생하는 부(-)모멘트를 모사할 수 있어 보다 현실적인 검증이 가능할 것으로 예상된다. 이 외에도 실제 크기 모형을 이용하여 윤하중을 가하는 Full-scale 모델의 경우 비용과 시간이 많이 소요되는 단점이 있으나 가장 신뢰성이 높은 방법이라고 할 수 있다. 교면 포장은 교량구조부로 수분이 침투되는 것을 막아주는 역할을 하여야 하며, 특히 해상 교량의 경우의 염분과 겨울철 사용되는 제빙화학제는 콘크리트의 열화와 강구조물의 부식을 발생시키므로 교면 포장의 방수 성능 검토는 매우 중요한 역할을 한다. 일반 토공부 포장과 달리 교면 포장은 하부층이 대기에 노출되어 있기 때문에 겨울철에 더 낮은 온도로 포장체의 온도가 내려가게 되고, 온도가 떨어진 포장층은 스티프니스가 증감함에 따라 저온 균열의 발생확율이 높아지며, 휨추종성도 나빠질 가능성이 높다. 따라서 저온에서의 균열 저항성 및 스티프니스를 평가하는 것은 교면 포장 재료의 중요한 인자 중 하나이다. 포장과 포장 하부층의 접착은 포장층의 일체화된 거동을 할 수 있게 하기 때문에 내구성 향상에 중요하다. 특히 교량과 같이 진동과 변형이 많은 경우에 있어 포장 접착층의 성능은 포장과 교량 구조물의 파손에 더 큰 영향을 미치게 된다. 접착성능은 실내에서의 직접인장모드와 전단접착강도 시험 모드의 실험이 있으며, 현장에서 측정하는 Pull-off 실험 등이 있다. 최근에 교통량과 중차량의 증가와 더불어 교량이 장경간화 되어 가면서 평가방법과 기준을 과거보다 엄격하게 할 필요성이 있다. 하지만 현실은 교면포장에 대한 시방규정이 모호하기 때문에 본 논문에서 제시한 국내외의 다양한 평가방법을 통해 적절한 교면포장의 성능을 평가하고 교면포장의 거동특성에 대한 이해를 함으로써 보다 발전된 교량기술을 확보할 수 있을 것이다.

• Journal of the Korea Concrete Institute
• /
• v.15 no.1
• /
• pp.87-94
• /
• 2003

Construction plan and strength control have limitations in construction production field because it is difficult to predict the form removal strength and development of specified concrete strength. However, we can have reasonable construction plan and strength control if prediction of concrete strength is available. In this study, firstly, the newly proposed strength prediction model with maturity method was compared with the logistic model to test the adaptability. Secondly, the determination of time of form removal was verified through the new strength prediction model. As the results, it is found that investigation of the activation energy that are used to calculate equivalent age is necessary, and new strength prediction model was proved to be more accurate in the strength prediction than logistic model in the early age. Moreover, the use of new model was more reasonable because it has low SSE and high decisive factor. If we adopt new strength prediction model at construction field, we can expect the reduced period of work through the reduced time of form removal.