• Journal of the Korea Institute of Building Construction
• /
• v.14 no.1
• /
• pp.37-44
• /
• 2014

Recently, many efforts related to the utilization of industrial by-products have been made to reduce carbon dioxide emissions in the construction industry. Of these various efforts, concrete incorporating ground granulated blast furnace slag (BFS) provides many advantages compared to conventional concrete, such as high long-term compressive strength, improved durability and economic benefits because of its latent hydraulic property, and low compressive strength at early curing age. This paper investigates the compressive strength of high-activated ground granulated blast furnace slag blended mortar with slag by-product S type(SBP-S). The results of the experiment revealed that incorporating high-activated ground granulated blast furnace slag would affect the compressive strength of mortar. It was found that increasing the Blaine fineness and replacement ratio of slag by-product S type shows high compressive strength of mortar at early curing age because of its high $SiO_2$ and CaO contents in the slag. It is confirmed that an increase of curing age does not affect the compressive strength of mortar made with slag by-product S type at a high curing temperature. Moreover, it is possible to develop and design concrete manufactured with high-activated ground granulated blast furnace slag as binder considering the acceleration curing conditions and mix proportions.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2013.11a
• /
• pp.66-67
• /
• 2013

Replacing a large amount of ground granulated blast furnace slag is limited because early age strength is low due to latent hydraulic property despite excellence of long-term strength. This study aimed to examine produceableness of high-activated ground granulated blast furnace slag using slag by-product from steel process. As experimental variable, the properties of strength development were analyzed by setting fineness and replacement ratio of slag by-product, curing conditions, and W/B. The results of study showed that high-activated ground granulated blast furnace slag using slag by-product as an activator improve the compressive strength of mortar. It is expected to be used as binder for secondary product of concrete considering curing and mixing conditions because high-activated ground granulated blast furnace slag can be hydrated by itself.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.2
• /
• pp.63-69
• /
• 2012

Recently, the cement industries brought very severe environment problems such as resource depletion and global warming with massive carbon dioxide during its production. The number of cases using industrial by-products such as the ground granulated blast furnace slag (GGBFS) in concrete mixtures is increasing to resolve the environmental issue. GGBFS is mainly used in the range between 20 to 50% to replace cement, but nowadays lots of researches are carried out to develop the alkali-activated slag (AAS) concrete with no cement. In this study, the early age properties of alkali activated slag (AAS) mortar are investigated to obtain the fundamental data for AAS concrete application to structural members. The experimental variables were the water-binder ratios of 0.3, 0.4, and 0.5 and NaOH as the alkali activator of 4%, 8%, and 12% by the mass of GGBFS, and compressive strength, flow, setting time, and ultrasonic pulse velocity of AAS mortars were measured and analyzed. It is found from the test results that as the normal concrete the lower W/B, the higher compressive strength. However, superplasticizer has to be used for producing high strength AAS concrete because the workability of AAS mortar are significantly lowered.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.1
• /
• pp.33-40
• /
• 2013

The cement industry brought very severe environment problems with massive carbon dioxide during its production. To solve this problem, attempts on Alkali-Activated Slag (AAS) concrete that perfectly substitutes industrial by-products such as ground granulated blast furnace slag (GGBFS) for cement are being actively made. AAS concrete is possible to have high strength development at room temperature, however, it is difficult to ensure the working time due to the fast setting time and the loss of workabillity because of the alkali reaction. In this study, the early age properties of alkali activated slag mortar are investigated to obtain the fundamental data for AAS concrete application to structural members. The water-binder ratio (W/B) was fixed at 0.35 and sodium hydroxide and waterglass as alkali activator was used. The compressive strength, the flow and the ultrasonic pulse velocity were measured according to the type of superplasticisers, which were naphthalene(N), lignin(L), melamine(M) and PC(P), up to a maximum of 2 percent by the mass of GGBFS. The results showed that adding melamine type of superplasticizer improved the fluidity of AAS mortar without decreasing the compressive strength, while naphthalene and polycarbonate type of superplasticizer had little effect on the fluidity of AAS mortar.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.2
• /
• pp.130-137
• /
• 2018

In the construction industry, research on alkali activated cement using fly ash or blast furnace slag fine powder has been published in Korea and abroad as a way to reuse industrial byproducts without using cement at all and to obtain economical effects at the same time. the purpose of this paper is to evaluate the effect of the ratio and coefficient of hydration ratio and lime saturation degree on the strength of alkali activated slag cement by chemical quantitative analysis of alkali activated slag cement used in the management of existing portland cement. as a result, it was confirmed that the ratio and coefficient of hydration ratio and lime saturation are all within a certain range.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.25 no.1
• /
• pp.85-92
• /
• 2021

The purpose of this study is to investigate the properties of hardener-free epoxy-modified mortars(EMMs) using ground granulated blast furnace slag(GGBFS) and alkali activators. The hardener-free EMMs with a GGBFS content of 20% using 4 types of alkali activators were prepared with various polymer-binder ratios, and tested for strengths, water absorption, carbonation depth, chloride ion and H2SO4 penetration depth. The conclusions obtained from the test results are summarized as follows: The compressive strength of the EMMs with a GGBFS content of 20% attains a maximum at a polymer-binder ratio of 10%. The flexural strength of the hardener-free EMMs using Ca(OH)2 as a alkali activator is improved with increasing polymer-binder ratios. However, the flexural strength of the EMMs using NaCO3, Na2SO4 and Li2CO3 is gradually decreased with increasing polymer-binder ratios. Regardless of the type of alkali activator, the water absorption, chloride ion penetration and carbonation depth are remarkably decreased with increasing polymer-binder ratios due to the epoxy film formed in the EMMs. The H2SO4 penetration depth of the hardener-free EMMs with a GGBFS content of 20% is gradually increased with increasing polymer-binder ratio. In this study, the properties of hardener-free EMMs using Ca(OH)2 as a alkali activator are more excellent than those of other alkali activators.

• Journal of the Korea Concrete Institute
• /
• v.25 no.3
• /
• pp.261-269
• /
• 2013

In this study, it was developed eco-friendly inorganic binding material concrete using ground granulated blast furnace slag and alkali activator (water glass, sodium hydroxides). Eight reinforced concrete beam using inoganic binding material concrete were constructed and tested under monotonic loading. The major variables were mixture ratio of alkali activator, type of admixture and admixture. Experimental programs were carried out to improve and evaluate the flexural performance of such test specimens, such as the load-displacement, the failure mode, the maximum load carrying capacity, and ductility capacity. All the specimens were modeled in scale-down size. The eco-friendly concrete using inorganic binding material encouraged alkali activation reaction was rapidly hardening speed and showed possibility as a high strength concrete. Also, the RC beams using new materials showed similar behavior and failed similarly with RC beam used portland cement. It is thought that eco-friendly inorganic binding material concrete can be used with construction material and product as a basic research to replace cement concrete. If there is application to structures in PC member as well as production of 2nd concrete product, it could be improved the productivity and reduction of construction duration etc.

• Journal of the Korean GEO-environmental Society
• /
• v.15 no.3
• /
• pp.33-40
• /
• 2014

In this paper, mechanical and germination characteristics of stabilized dredged soils were investigated to recycle dredged soil in eco-friendly manner such as waterfront construction. Non sintering binder (NSB), which was developed by using interchemical reactions between slag, high-calcium fly ash, alkali activator on the dredged marine clay, was added to dredged soil. Ordinary portland cement was also used for the comparison of two binders. Experimental tests such as flow test and unconfined compressive test were carried out to evaluate characteristics of stabilized dredged soil. Leaching test, pH measure, vegetation germination test were also conducted to consider environmental applicability. The unconfined compressive tests shows that unconfined compressive strength (UCS) also increases with the increase of curing time and mixed ratio. UCS of NSB mixtures were higher than those of OPC mixtures. Germination tests showed that germination and sprouting date are better in NSB mixture than OPC mixture. It can be explained that germination decreased as pH and 7-day strength increased.