• Journal of the Korea Concrete Institute
• /
• v.20 no.3
• /
• pp.325-333
• /
• 2008

This study evaluated the mechanical performance, shrinkage crack and fire resistance of hybrid fiber (blended steel and polypropylene fiber with different diameter and length) reinforced concrete at elevated temperature. The compressive, splitting tensile, flexural, plastic shrinkage test were conducted to the evaluate the mechanical properties and the resistance of shrinkage crack. Also, the surface investigation, reduction rate of mass and residual compressive test were performed to evaluate the physical and mechanical properties after 400$^{\circ}C$, 600$^{\circ}C$, 800$^{\circ}C$ and 1,200$^{\circ}C$ exposure. Test results showed that the hybrid fiber reinforced concrete improved the mechanical performance, shrinkage crack and fire resistance. The reduction of performance with a temperature change were high at the temperature of $600\sim800^{\circ}C$.

• Journal of Welding and Joining
• /
• v.10 no.2
• /
• pp.1-10
• /
• 1992

저탄소강은 일반적으로 용접성이 우수하지만 완전한 접합 강도와 용접부에서의 결함을 방지하기 위해서는 많은 주위가 필요하다. 용접부의 기계적 성질은 그 미세구조에 따라 좌우되는데, 이 구조는 모재의 화학조성, 용접 조건 그리고 후열처리에 의하여 결정이 된다. 이와 같이 용융용 접에 의한 저탄소강의 접합부는 저탄소함량으로 응고 균열에 대한 저항이 높다. 그러나 탄소의 함량이 증가하므로서 용접성은 저하하여, 0.3% 이상에서 용접부는 과열, 과냉, 저온 균열과 porosity에 취약하게 된다. 구조용강애 있어서는 용접성에 대한 일반적인 기준이 없으므로 이 러한 재료는 모재와 용접부의 기계적 성질, 고온 및 저온 균열성, 열간 및 냉각가공성등을 고려 하게 된다. 그러나 가장 중요한 것은 용접부의 신뢰도이다. 탄소강과 저합금강에 있어서 용접은 높은 강도를 얻을 수 있어야 하며 접합부에서 모재의 원래의 특성을 유지하여야 하고 결함이 없어야 할 것이다. 이와 같은 결함은 모재의 융접 이하에서 접합을 실시하는 고상접합으로 충 분히 억제할 수가 있다. 고상접합에서는 근본적인 미세조직의 결정화도 피할 수 있으며 고온균 일과 같은 결함의 위험도 배제할 수 있다. 고상접합은 용융용접과는 달리 모재를 용융시키지 않고 고체상태에서 접합을 하는데, 신금속 및 신소재의 개발과 첨단산업의 발달로 고상접합 기 술이 크게 각광을 받고 발전하게 되었다. 이와 같은 접합기술의 발전으로 기존의 용접으로는 접합이 불가한 소재, 용접기술의 적용이 곤란한 복잡한 형상, 복합기능 소재, 고품질 및 고정밀 성이 요구되는 소재등이 접합이 가능하게 되었다. 이러한 접합기술로는 brazing, 확산접합, 마찰 용접 등이 주로 많이 이용되고 있다. Brazing은 융점이 낮은 filler metal이 모재의 사이에서 용 융상태로 유입되어 냉각되면서 접합되는 방식이고 확산접합은 모재의 접합계면에서 원자의 상호 확산으로 접합을 하게 된다. 한편 마찰용접은 계면에서 회전에 의한 마찰열고 접합하는 방식 이다. 본 기술해설에서는 이러한 고상접합 기술을 이용한 철강재료의 접합에 대하여 고찰하도록 하겠다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.494.1-494.1
• /
• 2014

태양광은 세계적으로 유망한 에너지 중의 하나이며, 태양광 모듈은 실제 옥외 조건에 따라 다르지만 장기 신뢰성과 수명을 보장하기 위해 최소 20년 이상을 안정적으로 작동될 필요성이 있다. 하지만 실제 태양전지는 옥외에 장기 노출됨에 따라 성능이 저하되며, 그 원인으로는 셀 균열, 부식, 접착 강도 손실 및 박리, 그리고 변색 등이 있다. 본 논문에서는 부식으로 인한 성능 저하를 완화하기 위해 희생금속을 이용하여 태양전지 모듈의 성능 향상에 대해 연구하였다. 태양전지는 4 cell 결정질 실리콘 태양전지 미니 모듈을 이용하였고, 희생금속의 영향을 확인하기 위해 두 종류의 시료를 준비하였다. 한 시료에는 Al 희생금속을 태양전지 리본 위에 부착하였으며, 나머지 한 시료는 비교 시료로 Al 희생금속을 부착하지 않았다. 시료는 $85^{\circ}C$ 85%의 상대습도인 고온고습 조건에서 2500시간을 진행하였다. 그리고 2500시간의 고온고습 시험이 진행된 시료의 전기적 특성을 분석하였다. 시험 결과, 희생금속이 없을 경우 28.8%의 출력 저하가 있었으며, 희생금속이 있을 경우 19.3%의 출력 저하가 확인되었다. 또한, 희생금속이 없을 경우, 충실도는 21.5% 감소하였으며, 단락전류 역시 약 6% 정도 감소하였다. 반면, 희생금속이 있을 경우, 충실도는 16.1%로 감소하였고, 단락전류는 거의 변화가 없었다.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.39 no.12
• /
• pp.1257-1263
• /
• 2015

A correlation between the transient regime and steady state regime on the creep crack growth (CCG) for Grade 91 steel, which is used as the structural material for the Gen-IV reactor systems, was investigated. A series of CCG tests were performed using 1/2" CT specimens under a constant applied load and at a constant temperature of $600^{\circ}C$. The CCG rates for the transient and steady state regimes were obtained in terms of $C^*$ parameter. The transient CCG rate had a close correlation with the steady-state CCG rate, as the slope of the transient CCG data was very similar to that of the steady state data. The transient rate was slower by 5.6 times as compared to the steady state rate. It can be inferred that the steady state CCG rate, which is required for long-time tests, can be predicted from the transient CCG rate obtained from short-time tests.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1990.11a
• /
• pp.36-40
• /
• 1990

세라믹재료는 ductility가 작아 그 강도가 균열의 가혹성, 즉 크기와 모양에 의하여 결정되는 특징을 가지고 있다. 한편 마모는 표면에 균열을 생성시킬 수 있기 때문에 강도에 큰 영향을 미칠 수 있다. 그러나 지금까지 강도에 미치는 마모의 영향은 잘 밝혀져 있지 않다. 따라서 본 연구에서는 세라믹재료중에서도 물리적 성질들이 잘 알려져 있는 알루미나를 택하여 마모기구를 관찰하고 마모가 강도에 미치는 영향을 관찰하였다. 소결후 고온등방가압 처리된 알루미나 소결체를 입수하여 3mmX4mmX40mm크기의 굽힘시험시편으로 가공하였다. 두개의 4mmX40mm면중에서 한명을 diamond paste $1\mu m$까지 사용하여 polishing하였다. 시편의 polishing된 면위에 질화규소 볼을 올려 놓고, 하중을 가한 상태에서 볼을 와복운동시켰다. 시편위에 형성되는 마모흔적의 길이를 16mm이상이 되도록 하였다. 왕복속도는 약 2 헤르쯔도 하였다. 하중은 300, 600, 900N으로 하였다. 윤활유로는 paraffin oil을 사용하였다. 마모시험이 끝난 시편을 광학현미경 및 주사전자현미경으로 관찰한 후, 4-점굽힘시험하여 강도를 구하였다. 4-점굽힘시험시 외부 및 내부 지지점간의 거리는 30mm, 10mm로 하였으며, cross head speed는 분당 0.5mm로 하였다.

• Journal of Welding and Joining
• /
• v.14 no.6
• /
• pp.48-57
• /
• 1996

The weldability of high purity aluminum-lithium binary alloys has been investigated using the Varestraint test. Autogenous GTAW (gas-tungsten-arc-welds) were run along specimens of different lithium concentration using three sets of welding parameters. Welding voltage was held constant at 10 volts. Welding current (70∼100 amps) and travel speed (23∼33 cm/min) were the parameter varied. Hot-tearing susceptibility varied with lithium content and exhibited a steep peak at 2.6 weight percent lithium. Depth of penetration increased with increasing heat input and lithium concentration. The susceptibility is influenced by the wettability of dendrites by the interdendritic eutectic liquid as well as the time available for back-Siting by eutectic liquid. The welding condition of welding current 70A and travel speed 23 cm/min was showed good resistance to cracking in aluminum-lithium alloys. Suggestions for improving weld cracking resistance are also provided.

• Journal of Ocean Engineering and Technology
• /
• v.16 no.5
• /
• pp.73-79
• /
• 2002

In this paper, the effect of the compressive residual stresses was obtained at the test conditions of the higher temperature than the ambient temperature. The examination was performed with the CT specimen result of the material(JISG SUP9) which is being commonly used for the marine engine parts and the ocean structures. As a result, the test conditions at the higher temperature were acquired considering the peak values of the compressive residual stresses of the specimens and the effect on the fatigue crack propagation speed da／dN in stage II and the threshold stress intensity factor range Δth in stage I. Also the material constant C and the fatigue crack propagation index m in the formula of Paris Law da／dN＝C (ΔK)$^{m}$ were suggested to estimate the dependence on the test temperature.

• Journal of Ocean Engineering and Technology
• /
• v.12 no.3 s.29
• /
• pp.60-67
• /
• 1998

In this study, the J-Resistance Curve and material tearing modulus of SA508-C3 steel, which is one of the used nuclear pressure vessel steel, are measured ar room temperature, $200^{circ}C$ and $300^{circ}C$ according to load ratio analysis and ASTM E813, ASTM E1152, respectively. It is observed that J-R curve and Tmat value decrease as the temperature level increase. Applicability of $T_j$ proposed by Paris et al as instability parameter for ductile material is investigated. It is concluded that results are the $T_j$ parameter may be used as a crack instability parameter.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2000.04a
• /
• pp.164-169
• /
• 2000

The remote measurement system(RMS) as a new experimental method is limited in its application to crack measurements at elevated temperatures because of the oxide layer on the specimen surface. Since TiAlN and Cr coating layers have a high resistance to oxidation and wear, this paper proposed a TiAlN and Cr coating technique for specimens to facilitate the measurement of crack growth behavior using RMS. To investigate the effects of the coating layer, tension and fatigue tests were carried out at room temperature and at 538$^{\circ}C$, using specimens of 1Cr-1Mo-0.25V steel. From the experimental results, it was found that the mechanical properties of the TiAlN and Cr coated specimens were similar to those of the substrate. Accordingly, the TiAlN and Cr coated layer had hardly any influence on the fatigue crack propagation.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.3 s.174
• /
• pp.676-684
• /
• 2000

In this study, behavior of $C_t$ which is a well-known fracture parameter characterizing creep crack growth rate, is investigated for weld interface cracks. Finite element analyses were per formed for a C(T) specimen under constant loading condition for elastic-plastic-creeping materials. In modeling C(T) geometry, an interface was employed along the crack plane which simulated the interface between weld and base metals. The $C_t$ versus time relations were obtained under various creep constant combinations and plastic constant combinations for weld and base metals, respectively. A unified $C_t$ versus time curve is obtained by normalizing $C_t$ with $C^*$ and t with $t_T$ for all the cases of material constant variations.