• 한국주조공학회지
• /
• 제33권3호
• /
• pp.103-112
• /
• 2013

Effect of Fe and Mn contents on the tensile properties of Al-4 wt%Mg-0.9 wt%Si alloy system has been studied. Common phases of Al-4 wt%Mg-0.9 wt%Si alloy system were ${\alpha}$-Al, $Mg_2Si$, ${\alpha}-Al_{12}(Fe,Mn)_3Si$ and ${\beta}-Al_5FeSi$. As Fe content of Al-4 wt%Mg-0.9 wt%Si alloy system increased from 0.15 wt% to above 0.3 wt%, ${\beta}-Al_5FeSi$ compound appeared. When Mn content of the alloy increased from 0.3 wt% to 0.5 wt%, morphology of plate shaped ${\beta}-Al_5FeSi$ compound changed to chinese script ${\alpha}-Al_{12}(Fe,Mn)_3Si$. As Fe content of Al-4 wt%Mg-0.9 wt%Si-0.3 wt%Mn alloy increased from 0.15 wt% to 0.4 wt%, tensile strength of the as-cast alloy decreased from 191 MPa to 183 MPa and, elongation of the alloy also decreased from 8.0% to 6.2%. Decrease of these properties can be explained as the formation of plate shape, ${\beta}-Al_5FeSi$ phase with low Mn/Fe ratio of the alloy. However, when Mn content of Al-4 wt%Mg-0.9 wt%Si-0.3 wt%Fe alloy increased from 0.3 wt% to 0.5 wt%, tensile strength of as-cast alloy increased from 181 MPa to 194 MPa and, elongation of the alloy increased from 6.8% to 7.0%. These improvements attribute to the morphology change from ${\beta}-Al_5FeSi$ phase to chinese script, ${\alpha}-Al_{15}(Fe,Mn)_3Si_2$ phase shape-modified from with high Mn/Fe ratio of the alloy.

• 한국자동차공학회논문집
• /
• 제9권5호
• /
• pp.188-194
• /
• 2001

Metal matrix composites with whisker reinforcements have significant potential for demanding mechanical applications including defense, aerospace, and automotive industries. Especially, metal matrix composites, which are reinforced with aluminum borate whisker, have been used for the part of piston head in automobile because of good specific strength and wear resistance. Aluminum alloy-based metal matrix composites with whisker reinforcements have been produced using squeeze casting method, which is kind of an infiltration method. In this study, AC4CH-based metal matrix composites with $Al_{18}B$_4$O_{33}$ reinforcement have been produced using squeeze casting method, after T6 heat treatment, we evaluated mechanical properties of matrix and MMC composite were evaluated.

• 대한기계학회논문집A
• /
• 제25권10호
• /
• pp.1583-1589
• /
• 2001

Metal matrix composites with whisker reinforcements have significant potentials for demanding mechanical applications including defense, aerospace, and automotive industries. Especially metal matrix composites, which are reinforced with aluminum borate whisker, have been used leer the part of piston head in automobile because of good specific strength and wear resistance. In this study, AC4CH-based metal matrix composites with $Al_{18}$B$_{4}$ $O_{33}$ reinforcement have been produced using squeeze casting method, after T6 heat treatment, we evaluated fatigue life property of matrix and MMC composite and investigated fracture mechanism.m.

• 한국주조공학회지
• /
• 제40권3호
• /
• pp.66-75
• /
• 2020

The aim of this study was to optimize a solid solution treatment for a high pressure die casting Al-10Si-0.3Mg-0.6Mn alloy to avoid blistering and to improve the strength of the alloy. To achieve this goal, the number density of the blisters and the strength of the alloy under various solid solution treatment (SST) conditions were evaluated. The SST was performed at 470, 490, 510 and 530℃ for 20, 60, 120, 240 and 480 min on the alloy. The number density of the blisters increased with the increasing temperature and time of the SST and the defect area fraction. The yield strength of the alloy after the T6 heat treatment increased with the increasing SST temperature and time. Based on the results, it is suggested that SST should be performed at 510℃ within 60 min. or at 470 and 490℃ within 240 min. to avoid blistering and to improve the strength.

• 한국주조공학회지
• /
• 제20권4호
• /
• pp.230-239
• /
• 2000

High pressure wear characteristics of DCI(Ductile Cast Iron) were investigated through unlubricated pin-on-disc wear test. Wear test were carried out at speed of 23m/min, under pressure of 3MPa and 3.3 MPa. Cu and/or Mn were added to examine the effect of alloying elements on the high pressure wear characteristics of DCI. To investigate the relationship between wear characteristics and mechanical properties of DCI, Brinell hardness and V-notched Charpy impact energy were tested. Wear surface of each specimen was observed by SEM to determine the wear mechanism of DCI under high pressure wear condition. In the mild wear region, wear characteristics of alloyed DCI specimens were very similar to that of unalloyed DCI. But mild-severe wear transition was occurred at different wear distance and wear rate of DCI specimens were changed by alloying elements. In severe wear condition, wear rate of DCI was dramatically increased by the addition of Mn. Although the addition of Cu 0.46wt% did not decrease the wear rate of DCI in the severe wear region, but it delayed the mild-severe wear transition. Under high pressure wear condition, wear rate and mild-severe wear transition were not concerned with hardness of DCI specimens, but they were deeply associated with impact energy changed by alloying elements.

• 한국주조공학회지
• /
• 제20권4호
• /
• pp.240-246
• /
• 2000

Surface layer properties such as composition, phase, hardness, and oxide layer condition are very important if the main failure mechanism of metals is wear. Generally, stable and dense oxide layers are known to decrease the wear rate of metals by prohibition of metallic junction occurred between bare metals. Addition of Si above 4 wt% to DCI(Ductile Cast Iron) is reported to enhance the significant oxidation resistance by forming the silicon-rich surface layer which inhibits further oxidation. And addition of up to 2 wt% Mo to high Si ductile iron produces significant increases in high temperature tensile strength, creep strength, thermal fatigue resistance and oxidation resistance. High pressure wear characteristics of unalloyed DCI(Ductile cast Iron), 4.46 wt% Si ductile iron, 4.3 wt% Si-0.52 wt% Mo ductile iron were investigated through unlubricated pin-on-disc wear test. Wear test was carried out at speed of 23m/min, under pressure of 3 MPa and 3.3 MPa. Wear surfaces of each specimen were observed by SEM to determine the wear mechanism under high pressure wear condition. Addition of Si 4.46 wt% severely deteriorated wear property of ductile iron compared to unalloyed DCI. But combined addition of Si 4.3 wt%andMo0.52wt%decreasedthefrictioncoefficient(${\mu}$)ofductileironsandremarkablydelayedthemild-severeweartransition.

• 한국주조공학회지
• /
• 제27권1호
• /
• pp.31-35
• /
• 2007

본 연구에서는 Mg합금의 반응고성형 공정기술을 개발하기 위하여 여러 가지 전단속도와 냉각속도에 따른 Mg합금의 점도와 딕소트러픽 거동을 분석하였으며, 이를 전산모사연구와 비교 검토하였다. 전산모사연구에서는 미세조직과 공정변수를 고려한 반응고 슬러리의 유변학적 거동을 분석하였다. 반응고 온도영역에서의 Mg합금(AZ91D) 슬러리의 점도는 고상율에 따라 지수함수적으로 증가하였으며, 전단속도가 증가하면 감소하는 경향을 나타났다. Mg합금 슬러리의 유변학적 거동을 정확하게 분석하기 위하여 Carreau 모델을 사용하여 ANYCAST 프로그램에서 고압다이캐스팅용 금형으로의 Mg합금 반응고 슬러리의 충진거동을 모사하였다. 전산모사된 결과는 동일한 조건에서의 실제 실험결과와 잘 일치하였다.

• 대한기계학회논문집A
• /
• 제40권7호
• /
• pp.653-658
• /
• 2016

가스터빈엔진의 고온 부품은 초내열 합금 재료를 이용하며, 냉각설계 적용으로 형상이 복잡하여 정밀 주조 과정을 거치게 된다. 터빈 부품에 주로 적용이 되는 일방향 응고 및 단결정 재료는 제조 과정에서 결정립 성장 방향이 설계와 다르게 섭동을 가지게 되며, 이는 각 방향에 대한 재료 상수의 섭동을 유발하여 응력 분포의 변화와 함께 피로 수명에 큰 산포를 야기하게 된다. 본 연구에서는 일방향 응고 재료 노즐에 대하여 결정립 성장 방향의 섭동에 대한 구조 건전성의 영향을 저주기 피로 수명을 통해 확인하여, 향후 제작 허용값에 대한 제안 및 좀 더 정교한 통계적 접근이 필요함을 확인하고자 한다. 이를 위해 복합 열전달 해석을 통해 금속 온도 분포를 계산하고 이를 근거로 구조 해석 및 저주기 피로 수명을 계산하였다.

• 한국산업융합학회 논문집
• /
• 제9권4호
• /
• pp.301-308
• /
• 2006

Today's automobiles are changing into miniaturization and light weight for saving natural resources and energies. In order to raise the sufficiency of fuel consumption, new mechanism and components are required. Therefore, the expectations on the new materials are very high. Especially, Al materials are widely used to reduce the motors weight. Al using in automobiles is mostly casting material, and the material is developing rapidly in step with technical innovation. Al die casting has become an important field, as we are turning today's motor into light weight. One of the parts in steering system, valve housing, plays a role to reduce the operating effort of drivers. If valve housing being a part of steering system is produced by gravity casting, the space that manufacturing equipments are installed will be increased, and more energies and workers will be needed.

• 한국재료학회지
• /
• 제16권11호
• /
• pp.698-704
• /
• 2006

In this study, the effect of chill layers occurred in shot sleeve on the molten metal filling was analyzed through computer simulation. The behavior of chill layers with temperature variation of shot sleeve set from 200 to $280^{\circ}C$ was also investigated. The simulation results showed the chill layers set in the in-gates during the injection process change the main filling direction and cause turbulent flow pattern, resulting in porosities inside the castings. The amount of chill layers with the increasing temperature of shot sleeve was considerably reduced. Particularly, at the setting temperature of $280^{\circ}C$ by heat control unit, the biggest reduction in chill layers, excellent trimmed surface and the highest density were achieved, suggesting that as the optimal sleeve condition in aluminum high pressure diecasting, especially for highly complex parts like valve body.