• Transactions of the Korean Society of Automotive Engineers
• /
• v.11 no.4
• /
• pp.110-116
• /
• 2003

In this paper, an evaluation method of fracture toughness on interface cracks has been investigated under various mixed-mode conditions of the bonded scarf joints. Two types of the bonded scarf joints with an interface crack were prepared to analyze the stress intensity factors using boundary element method(BEM) and to perform the fracture toughness test. From the results of fracture toughness experiments and BEM analysis, an evaluation method of fracture toughness on interface cracks in the bonded dissimilar materials has been proposed and discussed.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.10
• /
• pp.2089-2095
• /
• 2002

Ceramic/metal composites have many attractive properties and great potential fur applications. Interfacial fracture properties of different layered composites are important in material integrity. Therefore, evaluation of fracture toughness at interface is required in essence. In this study, the mechanical characteristics for interface of ceramic/metal composites were investigated by indentation test of micro-hardness method. Apparent interfacial toughness of TBC system could be determined with a relation between the applied load and the length of the crack formed at the interface by indentation test.

• Proceedings of the KWS Conference
• /
• 1999.10a
• /
• pp.273-276
• /
• 1999

• Composites Research
• /
• v.18 no.3
• /
• pp.31-37
• /
• 2005

In this work, poly(ethylene oxide) (PEO) nanofibers were fabricated by electrospinning to prepare the nanofibers-reinforced composites. And the PEO powders-impregnated composites were also prepared to compare the mechanical interfacial behaviors of the composites. Morphology and fiber diameter of PEO nanofibers were determined by SEM observation. Mechanical interfacial properties of the composites were investigated in fracture toughness $(K_{IC})$ and interlaminar shea. strength (ILSS) tests. As a result, the fiber diameter was decreased with increasing the applied voltage. And optimum condition for the fiber formation was 15 kV, resulting from increasing of jet instability at high voltage. The PEO-based nanofibers-reinforced epoxy composites showed the improvements of both $K_{IC}$ and ILSS, compared to the composites impregnated with PEO powders. These results indicated that the nanofibers had higher specific surface area and larger aspect ratio than those of the powders, which played an important role in improving the mechanical interfacial properties of the composites.

• Composites Research
• /
• v.17 no.1
• /
• pp.10-17
• /
• 2004

In this work, the blend system prepared from epoky(DGEBA)/polymethylmethacrylate(PMMA) was investigated in thermal and mechanical interfacial property measurements. The thermal properties were carried out by DSC, DMA, and TGA measurements. Also, the surface free energy and fracture toughness were determined by contact angle and critical stress intensity factor($K_{IC}$), respectively. And the fracture surface was observed by SEM after $K_{IC}$ tests. As experimental results, the curing temperature and glass transition temperature were slightly increased in addition of PMMA. Surface free energy of the blends showed an improved value at low contents of PMMA which could be attributed to the both increasings of London dispersive and polar components. From measurement of $K_{IC}$ of the blends, the highest value was found at 5 phr. This was due to the increasing of compatibility or physical interaction in macromolecular chains between DGEBA and PMMA of the blends.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2011.06a
• /
• pp.201-201
• /
• 2011

• Restorative Dentistry and Endodontics
• /
• v.32 no.3
• /
• pp.208-221
• /
• 2007

The fracture toughness test is believed as a clinically relevant method for assessing the fracture resistance of the dentinal restoratives. The objectives of this study were to measure the fracture toughness $(K_{1C})$ and microtensile bond strength of dentin-resin composite interface and compare their relationship for their use in evaluation of the integrity of the dentin-resin bond. A minimum of six short-rod specimens for fracture toughness test and fifteen specimens for microtensile bond strength test was fabricated for each group of materials used. After all specimens storing for 24 hours in distilled water at $37^{\circ}C$, they were tensile-loaded with an EZ tester universal testing machin. Statistical analysis was performed using ANOVA and Tukey's test at the 95% confidence level, Pearson's coefficient was used to verify the correlation between the mean of fracture toughness and microtensile bond strength. FE-SEM was employed on fractured surface to describe the crack propagation. Fracture toughness value of Clearfil SE Bond (SE) was the highest, followed by Adper Single Bond 2 (SB), OptiBond Solo (OB), ONE-STEP PLUS (0S), ScotchBond Multi-purpose (SM) and there was significant difference between SE and other 4 groups (p < 0.05). There were, however, no significant difference among SB, OB, OS, SM (p > 0.05). Microtensile bond strength of SE was the highest, followed by SB, OB, SM, OS and OS only showed significant lower value (p < 0.05). There was no correlation between fracture toughness and microtensile bond strength values. FE-SEM examination revealed that dentin bonding agent showed different film thickness and different failure pattern according to the film thickness. From the limited results of this study, it was noted that there was statistically no correlation between K1C and ${\mu}TBS$. We can conclude that for obtaining the reliability of bond strength test of dentin bonding agent, we must pay more attention to the test procedure and its profound scrutiny.

• Journal of the Korea Concrete Institute
• /
• v.14 no.4
• /
• pp.474-482
• /
• 2002

The purpose of the study is to establish an optimum geometry and optimum geometry factor through bond test of a structural synthetic fiber, which fully utilizes matrix anchoring without fiber fracturing with the maximum pullout resistance. Seven deformed structural synthetic fibers with widely different geometries were investigated and pullout test was conducted. Included parameters are seven different types of fiber and two of mortar matrixes. The test result shows that the crimped type structural synthetic fiber is significant improvement in the interface toughness(pullout energy) and pullout load. The pullout test was performed with various size of crimped type structural synthetic fiber in order to invest optimum geometry factor, In the basis of the test results, optimum geometry factor is established such as D=b$^{{\alpha}0{\alpha}}$h$^{λ{\beta}}$.

• Composites Research
• /
• v.24 no.4
• /
• pp.11-16
• /
• 2011

Retention of interfacial shear strength (IFSS) of polymer composites at cryogenic temperature application is very important. In this work, single carbon tiber reinforced epoxy compositc was used to evaluate IFSS and apparent modulus under room and cryogenic temperatures. The property change of carbon and selected epoxy for particularly cryogenic temperature application were tested in tension and compression. Tensile strength and elongation of carbon fiber decreased at cryogenic temperature, whereas tensile modulus was almost same. On the other hand, epoxy matrix showed the increased tensile strength but decreased elongation. It can be due to maximum thermal contraction existing free volume in cryogenic temperature. IFSS increased up to $-10^{\circ}C$ and then decreased steadily. However, IFSS at cryogenic temperature was still similar to that at room temperature. This result is very useful to cryogenic application since selected epoxy toughness and interfacial adhesion can keep at such low temperature.

• Journal of Adhesion and Interface
• /
• v.4 no.1
• /
• pp.1-8
• /
• 2003

In this work, the effect of PMR-15 content on the variation of surface free energy of the DGEBA/PMR-15 blend system was investigated in terms of contact angles and mechanical interfacial tests. Based on FT-IR result of the blend system. C=O (1,772, $1,778cm^{-1}$) and C-N ($1,372cm^{-1}$) peaks appeared with imidization of PMR-15 and -OH ($3,500cm^{-1}$) peak showed broadly at 10 phr of PMR-15 by ring-opening of epoxy. Contact angle measurements were performed by using deionized water and diiodomethane as testing liquids. As a result, the surface free energy of the blends gave a maximum value at 10 phr of PMR-15, due to the significant increasing of specific component. The mechanical interfacial properties measured from the critical stress intensity factor ($K_{IC}$) and the critical strain energy release rate ($G_{IC}$) showed a similar behavior with the results of surface energetics. This behavior was probably attributed to The improving of the interfacial adhesion between intermolecules, resulting from increasing the hydrogen bondings of the blends.