• Journal of the Korean Magnetics Society
• /
• v.11 no.2
• /
• pp.63-71
• /
• 2001

The effects of an Ag seed layer on the magnetic properties and the microstructural evolution of SmCo/Cr thin films deposited on glass substrates were investigated. Coercivity of the films is 2.0 kOe when the thickness of Ag seed layer was 1nm thick, but it increased to 2.7 kOe when the Ag seed layer thickness is 3 nm. The increase of coercivity for film with 3 nm-thick Ag is due to roughness of Cr and grain size of Cr by the Ag microbumps. Ar partial pressure influenced on the formation of Ag microbumps, for example, they were formed at 5 mTorr when Ag thickness was 1 nm. The mechanism of magnetization reversal of the SmCo films changed from domain wall motion to domain rotation as the Ag inserted. This was thought to be due to inhibition of domain wall motion by the reduction of Cr grain size and the increase of roughness.

• Journal of the Korean Vacuum Society
• /
• v.12 no.3
• /
• pp.193-199
• /
• 2003

Ti-Cu-N and Ti-Ag-N nanocomposite films with various copper and silver contents were synthesized by arc ion plating and magnetron sputtering hybrid system. The structure and mechanical properties of these films were found to be dependant on the copper and silver concentration. The maximum hardness of Ti-Cu-N and Ti-Ag-N films showed approximately 40 ㎬ below 2 at%Me. The role of soft metallic phase in Ti-Me-N nanosturctured films containing one hard and one soft phase is also discussed.

• Journal of the Korean Magnetics Society
• /
• v.4 no.2
• /
• pp.122-125
• /
• 1994

The magnetic properties of Nd-Fe-B alloys of containing 4 at.% Nd have been studied for the development of new type rare-earth magnets. The amorphous phase of a melt-spun $Nd_{4}Fe_{85.5}B_{10.5}$ alloy is transformed into the phases which have a small amount of $Nd_{2}Fe_{14}B_{1}$ in ${\alpha}-Fe$ matrix by annealing above their crystallization temperature. The addition of Mo, Nb, V or Cu to $Nd_{4}Fe_{85.5}B_{10.5}$ alloy results in the reduction of grain size and the sub¬sequent improvement of the coercivity. The coercivity of $Nd_{4}Fe_{82}B_{10}M_{3}Cu_{1}$(M = Mo, Nb, V) alloys increases in the order of M = V < Nb < Mo and shows the highest value of 2.7 kOe when M = Mo. On the other hand, the rem¬anence of these alloys shows the opposite trend and the rn>st improved value of 1.35 T is observed when M = V.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2002.11a
• /
• pp.63-63
• /
• 2002

현재 기계적 합금화법에서는 주로 합금을 구성하는 성분원소 분말을 불활성분위기에서 볼밀처리 함으로써 함금화를 시키거나 모합금에 산화물을 분산시켜 복합화시키는 공정을 통하여 각종 화합물, 비정질상 및 과포화고용체등의 준안정상의 합성 뿐만이 아니라 초미세조직의 생성에 관한 폭 넓은 분야의 연구가 행하여지고 있다. 한편 MA에서는 볼멀처리중 기계적 에너지의 투여에 의하여 실제 반응온도보다 낮은 온도에서 발생하는 특이한 화학반응 즉 Mechanochemical 반응을 일으키 기도 한다. 본 연구에서는 헤마타이트($Fe_20_3$)와 금속윈소인 Ti의 MA처리에 의하여 고상환원반응 을 유기시켜 $Fe-TiO_2$계 nanocomposite 분말재료를 제조하고자 한다. 특히 MA 공정에 있어서 자기 물성의 변화와 X선 회절을 통하여 고상환원반응에 의한 복합분말의 생성과정을 조사하였다. 출발원료는 $Fe_20_3$(고순도화학제,99.9%, 평균입경 0.1$\mu\textrm{m}$)와 금속원소인 Ti(99.9%, 명균업경 150$\mu\textrm{m}$)을 몰비 2:3의 조성이 되도록 하여 MA를 실시하였다. 볼멀은 고에너지 유성형 볼밀장치(독일 제, Fritsch P-5)를 이용하였으며 진공치환형 용기에 원료분말을 장입하여 2회정도 진공배기한 후 아르곤 가스를 충전하여 볼밀을 행하였다. 얻어진 분말시료에 대하여 x-선 회절장치, 전자현미경 (SEM) 및 진동시료형자력계(VSM)를 통하여 결정구조, 미셰조직 빛 자기특성을 조사하였다. $Fe_2O_3-Ti$ 혼합분말의 MA처리 에 의하여 초기단계부터 환원반응과 함께 $Fe_3TIO_{lO}$ 중간상이 관찰 되었으나 30hrs의 MA처리 후 Fe와 산화물 $TiO_2$로 모두 환원되어 $Fe-TiO_2$계 나노복합분말이 얻어짐을 알 수 있었다. 이 때 X션 회절피크의 line broadening으로부터 복합분말의 Fe 명균 결정립 크기는 24nm로 초미세 결정럽의 분말합금이었다. 포화자화값은 볼밀처리에 따라 점점 증가하여 MA 30시간에는 20.3emu/g로 포화됨을 알 수 있었다. 또한 보자력 Hc는 MA초기단계에 350e로 매우 낮으나 30시간 후에는 Hc값이 2600e로 매우 큰 값을 나타내었다. 이것은 환원반응결과 초기에 생성된 Fe의 결정립이 비교적 크고 결정결함이 적으나 볼밀처리를 30시간까지 행하면 Fe 결정렵의 미세화 빛 strain 증가로 magnetic hardening이 일어나기 때문인 것으로 사료된다.

• Journal of the Korean Ceramic Society
• /
• v.38 no.6
• /
• pp.587-592
• /
• 2001

난소결성의 TiN에 방전 플라즈마 소결법을 적용하여 고밀도 TiN 소결체를 제조하였다. 제조된 TiN 시편의 소결특성 및 입성장 정도를 평가하였으며, 전자현미경을 이용하여 미세구조를 분석하였다. Milling 과정동안 잠입된 $Al_2$O$_3$는 1$700^{\circ}C$ 이상의 소결온도에서 TiN 분말과 반응하여 부분적으로 액상을 형성하여 물질이동을 가속화함으로써 치밀화가 저온에서 시작하도록 함으로써 궁극적으로 결정립성장 제어에 기여하는 것으로 확인되었다. 이러한 현상은 굽어진 TiN 결정입계와 결정입계 삼중점에 존재하는 $Al_2$O$_3$를 포함하는 2차 결정상 cluster의 존재로 설명되어진다.

• Journal of the Korean Magnetics Society
• /
• v.9 no.3
• /
• pp.154-158
• /
• 1999

Magnetic properties and microstructure of nanocrystalline $\alpha$-(Fe, Co)-based Nd-(Fe, Co)-B-Nb-Cu alloys have been investigated. $Nd_x(Fe_{0.9}Co_{0.1})_{90-x}B_6Nb_3Cu_1$(x=2, 3, 4, 5, 6) alloys prepared by rapid solidification process show amorphous phase except the one with x=2. By a proper annealing, the amorphous in the alloy is changed to a nanocrystalline phase. It is confirmed that the nanocrystalline alloys are composed of $\alpha$-(Fe, Co) and $Nd_2(Fe, Co)_{14}B_1$ phase. The optimally annealed $Nd_3(Fe_{0.9}Co_{0.1})_87B_6Nb_3Cu_1$ alloy shows the highest remanence of 1.55 T. The coercivity increases with the increase of Nd content The maximum coercivity of 4.6 kOe is obtained from an optimally annealed $Nd_6(Fe_{0.9}Co_{0.1})_84B_6Nb_3Cu_1$ alloy, resulting in the maximum energy product of 10.6 MGOe.

• Journal of the Korean Magnetics Society
• /
• v.3 no.1
• /
• pp.41-47
• /
• 1993

Effects of Ta addition on Co-Cr pependicular magnetic recording media were studied to obtain high perpen-dicular coercivity at lower substrate temperature. For the purpose. magnetic properties and microstructures of Co-Cr-(Ta) films were studied by varying the Cr contents from 17 to 21 at.% and Ta contents for 0 to 3.2 at.%. Effectiveness of Ta addition in increasing perpendicular coercivity was significant for lower Cr content films. The increasement of perpendicular coercivity was more pronounced for the films deposited on $100^{\circ}C$ heated substrate in the case of ${(Co_{83}Cr_{17})}_{98.4}Ta_{1.6}$ composition. The cause of the increase of perpendicular coercivity was considered due to not the grain refinement effects and the improvement of c-axis alignments but increase of Ta and Cr segregation.

• Journal of the Korean Magnetics Society
• /
• v.3 no.4
• /
• pp.320-324
• /
• 1993

The effect of sputtering conditions on magnetic properties of CoCrMo/Cr magnetic thin film was investigated. Substrate temperature were controlled from R. T to $250^{\circ}C$. The thickness changes of Cr underlayer and CoCrMo magnetic layer were in the range of $1000-2500\AA$ and $300-800\AA$, respectively. Grain size was found to be decreased with increasing magnetic layer thickness(from $500\AA$ to $800\AA$). CoCrMo magnetic layer microstructure showed relatively small dependence on Cr underlayer thickness, substrate temperature. Coercivity increased with increasing Cr underlayer, magnetic layer thickness and substrate temperature. CoCrMo/Cr thin film showed a coercivity of 880 Oe in $700\AA$ magnetic layer thickness and $1000\AA$ Cr underalyer thickness.

• Journal of the Korean Society for Heat Treatment
• /
• v.17 no.3
• /
• pp.139-145
• /
• 2004

Equal channel angular pressing (ECAP) technique had been adapted to the Mg alloy (AZ31) for achieving effective grain refinement through severe deformation. The average grain size of $2.5{\mu}m$ could be obtained after 4 passes. The stability of the ECAPed structure at elevated temperatures was examined by annealing the ECAPed materials over a wide range of temperature between 473 and 748 K. The average activation energy, Q, for static grain growth of 1, 2 and 3 passes was 33.7 kJ/mole (=0.25QL, activation for lattice diffusion). The abnormally low Q value in the lower temperature range may indicate that grain growth occurs in the unrecrystallized microstructure where non-equilibrium grain boundaries containing a large number of extrinsic dislocations exist. The yield stresses of the ECAPed alloys decreased whereas the elongations increased after the ECAP process. These results should be related to the modification of texture for easier slip on basal plane.

• Journal of the Korean Magnetics Society
• /
• v.5 no.5
• /
• pp.874-879
• /
• 1995

Magnetic properties of FeMoN, FeMoTaN, FeTaN and FeTaC films deposited by DC magnetron reactive sputter were investigated, and correlated with their microstructure. FeMoN films were not showen the soft magnetic prop¬erties, because of generated $Fe_{2}Mo$, $Fe_{3-2}N$ and $Fe_{4}N$ phases. Ta added films, however, effectivly retarded the $\alpha$-Fe grain growth and suppressed the generation of Fe nitrides or carbides during heat treatement. The soft magnetic properties of $B_{s}:15\;kG,\;H_{e}:0.25\;Oe,\;\mu':4000(at\;5\;MHz),\;and\;B_s:14.5\;kG,\;He:0.25\;Oe,\;\mu':2700(5MHz)$ were observed in $Fe_{78.8} Ta_{8.5}N_{12.7}\;and\;Fe{75.6}Ta_{8.1}C_{16.3}$ films, respectively.